With a view to sustainable development and circular economy, this work focused on the possibility to valorize a secondary waste stream of recycled carbon fiber (rCF) to produce a 3D printing usable material with PA6,6 polymer matrix. The reinforcing fibers implemented in the present research are the result of a double recovery action: starting with pyrolysis from which long fibers are obtained, used to produce non-woven fabrics and, subsequently, fiber agglomerate wastes obtained from this last process are ground in a ball mill. The effect of a different amount of reinforcement at 5% and 10% by weight on the mechanical properties of 3D printed thermoplastic composites was investigated. Although the recycled fraction was successfully integrated in the production of filaments for 3D printing and therefore in the production of specimens via Fused Deposition Modeling technique, the results showed that fibers did not improve the mechanical properties as expected, due to an unsuitable average size distribution and the presence of a predominant dusty fraction ascribed to the non-optimized ball milling process. PA6,6 + 10 wt.% rCF composites exhibited a tensile strength of 59.53 MPa and a tensile modulus of 2.24 GPa, which correspond to an improvement in mechanical behavior of 21 5 % and 5 21 % compared to the neat PA6,6 specimens, respectively. The printed composite specimens loaded with the lowest content of rCF provided the greatest improvement in strength (+ 9% over the neat sample). Then, a prediction of the “optimum” critical length of carbon fibers was proposed that could be used for future optimizations of the recycled fiber processing.

Titanium (Ti) and Ti-based alloys are commonly used in dental implants, and surface modifications of dental implants are important for achieving osseointegration (i.e., direct connection between the implant surface and bone). This study investigated the effect of an eco-friendly etching solution—a hydrogen peroxide–sodium bicarbonate mixture—on the surface properties and contact angles of and osteoblast adhesion and proliferation on Ti surfaces. Disk-shaped Ti specimens were prepared using different surface treatments (machining, sandblasting, and sandblasting/acid-etching), and they were immersed in the etching solution and then ultrasonically cleaned. Surface characterization was performed using scanning electron microscopy, digital microscopy, contact angle analysis, and X-ray photoelectron spectroscopy. MG-63 osteoblasts were cultured on the specimens, and their adhesion to the specimen surface and their proliferation were examined using staining and the MTT assay, respectively. Additional etching with the etching solution caused the formation of nano/micro hierarchical structures, increased the surface roughness, and enhanced the hydrophilicity. Osteoblast adhesion and proliferation were found to improve on the modified surfaces. The eco-friendly etching method has the potential to enhance the biological properties of Ti implant surfaces and to thereby improve the dental implant performance.

Current conventional methods of evaluating microstructures are characterized by a high degree of subjectivity and a lack of reproducibility. Modern machine learning (ML) approaches have already shown great potential in overcoming these challenges. Once trained with representative data in combination with an objective ground truth, the ML model is able to perform a task properly in a reproducible and automated manner. However, in highly complex use cases, it is often not possible to create a definite ground truth. This study addresses this problem using the underlying showcase of microstructures of highly complex quenched and quenched and tempered (Q/QT) steels. A patch-wise classification approach combined with a sliding window technique provides a solution for segmenting entire microphotographs where pixel-wise segmentation is not applicable due to the problem of reproducibly creating unambiguous training masks. Using correlative microscopy, consisting of light optical microscope (LOM) and scanning electron microscope (SEM) micrographs as well as corresponding data from electron backscatter diffraction (EBSD), a training dataset of reference states that covers a wide range of microstructures was acquired in order to train accurate and robust ML models. Despite the enormous complexity associated with the steels treated here, classification accuracies of 88.8% in the case of LOM images and 93.7% for high-resolution SEM images were achieved. These high accuracies are close to super-human performance, especially in consideration of the reproducibility of the automated ML approaches compared to conventional methods based on subjective evaluations through experts.

The control of alumina morphology is crucial yet challenging for its various applications. Un-fortunately, traditional methods for preparing alumina particles suffer from several limitations such as irregular morphology, poor dispersibility, and restricted application areas. In this study, we develop a novel method for preparing spherical mesoporous alumina using chitin and Plu-ronic P123 as mixed templates. The effects of reaction temperature, time, and the addition of mixed templates on the phase structure, micromorphology, and optical absorption properties of the samples were investigated. The experimental results indicate that lower temperature and shorter reaction time facilitated the formation of spherical mesoporous alumina with excellent CO2 adsorption capacity. The periodic density functional theory (DFT) calculations demonstrate that both (110) and (100) surfaces of γ-Al2O3 can strongly adsorb CO2. The difference in the amount of CO2 adsorbed by Al2O3 is mainly due to the different surface areas, which give dif-ferent number of exposed active sites. This approach introduces a novel strategy for utilizing bi-ological compounds to synthesize spherical alumina and greatly enhances mesoporous alu-mina's application efficiency in adsorption fields. Moreover, the study explored the electro-chemical performance of the synthesized product using cyclic voltammetry and discovered im-proved loading of electrocatalysts and enhanced electrocatalytic activity.

Air pollution is related to the development of people's livelihood. As one of the main pollutants in the air, formaldehyde affects people's physical and mental health. In order to remove formaldehyde and better protect the health of residents, it is very necessary to develop efficient adsorption materials. In this study, a cellulose composite aerogel Microcrystalline Cellulose/ N-(2- aminoethyl) -3- aminopropyl methyl dimethoxysilane (MCC/APMDS) modified by APMDS was explored. The pore volume and specific surface area of the modified aerogel decreased, the average pore diameter increased, and the adsorption capacity of formaldehyde was stronger. The adsorption experiment shows that the sample prepared under the conditions of APMDS dosage of 6 wt%, reaction time of 4 h and reaction temperature of 90℃ has the largest average pore size (14.56 nm) and the largest formaldehyde adsorption capacity (9.52 mg/g). The excellent adsorption of the composite aerogel is due to high porosity and rich active amino groups on the surface. This study provides valuable information for the preparation of adsorption materials with high formaldehyde adsorption capacity for air purification.

Titica vine fibers (TVFs) extracted from aerial roots of Heteropsis flexuosa, from the Amazon region, were 10, 20, 30 and 40 vol% incorporated into an epoxy matrix for applications in ballistic multilayered armor systems (MASs) and stand-alone tests for personal protection against high-velocity 7.62 mm ammunition. The back-face signature (BFS) depth measured for composites with 20 and 40 vol% TVFs used as an intermediate layer in MASs was 25.6 and 32.5 mm, respectively, below the maximum limit set by the international standard. Fracture mechanisms found by scanning electron microscopy (SEM) attested the relevance of increasing the fiber fraction for applications in MASs. The results of stand-alone tests showed that the control (0 vol%) and samples with 20 vol% TVFs absorbed the highest impact energy (Eabs) (212 – 176 J), and consequently limit velocity (VL) values (213 – 194 m/s), when compared with 40 vol% fiber fractions. However, the macroscopic evaluation found that the plain epoxy, referring to control samples, shattered completely. In addition, for 10 and 20 vol% TVFs, the composites were fragmented or exhibited delamination fracture, which contributed to their physical integrity. On the other hand, the composite with 30 and 40 vol% TVFs, whose Eabs and VL varied between 166 – 130 J and 189 – 167 m/s, respectively, showed the best dimensional stability. The SEM images indicated that for composites with 10 and 20 vol% TVFs the fracture mode was predominantly brittle, due to the greater performance of the epoxy resin and the discrete action of the fibers. While for composites with 30 and 40 vol% TVFs, there was the activation of more complex mechanisms such as pullout, shearing and fiber rupture.

Metal organic frameworks (MOFs) are used in catalysis due to their high specific surface area and porous structure. The dispersed active sites and limited reaction space render MOFs have the potential for highly selective electrocatalytic CO2 reduction reaction (ECO2RR). Meanwhile, formic acid (HCOOH) is attracting attention as a liquid product with high economic benefits. This review summarizes the MOFs and their derivatives applied for ECO2RR into HCOOH products. The preparation methods of MOFs as electrocatalysts and their unique advantages are discussed. A series of MOFs, and MOFs derivatives obtained by electrochemical reduction or carbonization processes are highlighted, including metal nanomaterials, carbon-based nanocomposites, single-atom catalysts, and bimetallic nanocomposites. Depending on the MOFs building units (metal ions and organic linkers) and the reaction conditions of derivatization, MOFs-based catalysts exhibit rich diversity and controllable modulation of catalytic performance. Finally, the challenges encountered at this stage and the future research directions of MOFs-based catalysts are proposed.

A new approach to preparing a series of Co/Sm2O3 catalysts for hydrogen production by dry re-forming of methane (DRM) is developed. The catalysts precursors are synthesized by a simple method, including evaporation of aqueous solutions of cobalt and samarium nitrates, followed by a short-term calcination of the resulting material. The as-prepared and spent catalysts are characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), temperature-programmed reduction (H2-TPR), and thermogravimetric analysis (TGA). It is shown that the content of cobalt in the synthesized materials affects their phase composition and carbonization resistance in the DRM reaction. It is demonstrated that preheating under N2 affords catalysts providing stable hydrogen and CO yields of 94-98 % for at least 50 h at 900°C. These yields are among the highest ones currently available for DRM catalysts derived from Co-Sm complex oxides. It is found that reduction in the amount of cobalt in the catalyst and its preheating to an operating temperature of 900°C in a nitrogen flow con-tribute to preventing catalyst carbonization and metal particles sintering.

Graphene nanostructures (GNS) are among the most promising materials for creating supercapacitors. However, GNS are still not used in creating supercapacitors due to the impossibility of obtaining large volumes of high-quality material at an acceptable cost. In this work, we investigated the efficiency of using few-layer graphene (FLG) with the number of layers is not more than 5 synthesized under Self-propagating high-temperature synthesis (SHS) conditions as basic material for supercapacitors. Using the SHS process makes it possible to synthesize large volumes of FLG without Stone-Wales defects. It was found that the synthesized FLG makes it possible to obtain better results than using classical materials, namely activated carbon (AC). It was found that the sample based on FLG has a higher specific capacitance – 65 F×g-1 compared to the sample from AC, the specific capacitance of which is 35 F×g-1, for a speed of 5 mV×s-1 these values are 170 and 64 F×g-1, respectively. The drop in capacitance over 1000 cycles was 4%, which indicates a sufficiently high stability of FLG and allows us to consider FLG as perspective material for use in supercapacitors.

A self-consistent charge density-functional tight-binding method combined with molecular dynamics simulations is employed to reveal the effect of polymorph on the thermal decomposition stability of 1,1-Diamino-2,2-Dinitroethylene (FOX-7). Two types of heating, constant temperature heating and temperature-programmed heating, are adopted. Potential evolution indicates that γ-FOX-7 possesses the lowest thermal stability, as it is closer to the decomposition state. Crystal form has an important influence on the thermal decomposition of FOX-7, resulting in different decomposition rates and initial reactions. In general, β- and γ-FOX-7 always decompose more completely than α-FOX-7. This work emphases the importance of polymorph dependent initial decay of an energetic polymorphic compound once heated in a volume constrained condition.

This publication describes the influence of residue monomers in synthesized pressure-sensitive adhesives based on acrylics on main performance such as tack, peel adhesion, shear strength and shrinkage in form of transfer tapes used for joining wooden elements in furniture industry. The discussed carrier-free adhesive tapes are synthesized by photo-crosslinking and photopolymerization with UV radiation of photoreactive prepolymers sandwiched between two adhesive siliconized polyester films. The simultaneous crosslinking and polymerization process under UV lamps carried out under UV lamps placed simultaneously above and below the crosslinked photoreactive polymer layer leads to the production of a carrier-free adhesive film. In this test series it were investigated to what how the intensity of UV radiation and the time of its exposure affect the viscosity of photoreactive compositions, and then the content of unreacted monomers in them and, subsequently, the method of their crosslinking and polymerization, and the concentration of the photoreactive crosslinking compound leading to the obtaining of transfer adhesive tapes, and thus on their tray, peel adhesion, shear strength and shrinkage on the surface of the wood.

Electrically conductive adhesives (ECA’s) are used widely to replace or reinforce lead soldering or conductive metal components in electronic packaging applications such as die attachment, solderless interconnections, component repair, display interconnections, and heat dissipation. Their conductive behavior as well as the associated behaviors such as heat conduction and mechanical behavior (strength, rigidity, deformation and viscoelastic behavior, which may be affected by moisture ingression) are affected by adhesive film thickness, volume fraction, size and shape of the conductive filler, as well as uncured base adhesive viscosity, substrate and filler surface treatment and the applied pressure (during bonding and during conduction). The adhesive resistivity decreases precipitously above a characteristic filler volume fraction called the percolation threshold. In general, micron-sized metal fillers mixed in an adhesive (often an epoxy) resulting with different film thicknesses exhibit thickness thresholds for transition from three-dimensional conductivity to two-dimensional conductivity with considerable increases in thickness-direction (z-axis) resistivity when the film thicknesses are smaller than these threshold values. Recently, the use of conductive nanoparticles allowed decreases in percolation threshold levels as well as increases in mechanical strength and durability of ECA’s. Most ECA’s are supplied in liquid or paste form in varying viscosities and therefore, the method of their application also affects their performance. This work intends to provide an understanding of these effects on conduction behavior in (usually high-priced) equipment in which they are used.

Polyethylene terephthalate (PET) is nowadays one of the most used polymers for packaging applications. Modifications induced by service conditions and the optimal mean to recycle this matter several times have to be perfectly understood to allow a reuse for similar application (from bottle to bottle for example). The present study aims to compare physico-chemical properties, crystalline organization, and mechanical behaviour of virgin (vPET) and recycled PET (rPET). Using different combined experimental methods (Calorimetry, Small Angle X-ray Scattering, Atomic Force Microscopy, DMA, and uni-axial tensile test), it has been proven that even if there is no change in the crystallinity of PET, the crystallisation process shows some differences (size and number of spherulites). The potential impact of these differences on local mechanical characterization, at the lamella scale, is explored and tends to demonstrate the development of homogeneous microstructure, leading to well-controlled and relevant local mechanical properties. This approach increases the understanding of crystallisation of PET and recycled PET during forming processes such as thermoforming or injection stretch blow moulding (ISBM) where elongation at break can depend on the microstructure conditioned by the crystallisation process.

In this study, composite nanofiber films comprising polyvinyl alcohol, wheat gluten, and glucose (PWG) were fabricated using electrospinning, followed by cross-linking via the Maillard cross-linking. Various mass concentrations of ferulic acid (FA) were incorporated into the PWG films. The results indicate that the average diameter of the FA-PWG films decreased from 449 nm to 331 nm as the concentration of FA increased, until reaching a concentration of 12%, after which a significant increase in diameter was observed. Subsequent Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) and differential scanning calorimetry (DSC) results suggested that FA was distributed in the sample films in an amorphous form through hydrogen and ester bonds. Additionally, release experiments and antimicrobial tests on FA-PWG sample films showed good con-trolled release of FA and excellent anti-Escherichia coli and Staphylococcus aureus activity of this film. These findings all indicate that the FA-PWG nanofiber film is a potential candidate for food active packaging.

Lewis acid zeolites play an important role in industrially important green reactions closely related to fine chemicals and biomass conversion. Titanium-doped TS-1 zeolite is a milestone Lewis acid zeolite, which widely uses in industrially significant green oxidation processes with hydrogen peroxide as an oxidant under mild conditions. TS-1 Zeolites are normally synthesized in basic condition under hydrothermal treatment. Up to now, it is still not successful to synthesize active TS-1 Lewis acid zeolite by using inorganic alkali, e.g. NaOH or KOH as base, which are cheaper and more stable compared with quaternary ammonium hydroxide or organic amines used in the traditional synthesis. Here, inorganic base of NaOH was firstly employed in synthesizing active TS-1 zeolites. The crucial factor was the control of adverse effects of sodium cations on the incorporation of active titanium cations. A higher catalytic activity could be achieved by further reducing the size of the TS-1 crystal by seed-added strategy, which could approach the catalytic activity of commercial catalyst while the production cost was much lower than the commercial TS-1 catalysts, indicating great commercial potential and the possibility of preparing other cheap Lewis acid catalysts by using inorganic alkali.

Cancer has been considered one of the most serious diseases in recent decades. Early diagnosis of cancer is a crucial step for an expedited treatment. Ideally, detection of cancer biomarkers, which are usually elevated because of cancer, is the most straightforward approach to detect cancer. Consequently, the accurate, effective, and prompt detection of these compounds is an insistent need for the medical diagnosis of the disease in order to start an early therapy plan for the patients. Among these biomarkers, Carcinoembryonic antigen (CEA) is considered one of the most important tumor markers for colorectal cancer, but it has been also used as a biomarker for other types of cancers, including breast, gastric, ovarian, pancreatic, and lung cancers. Typically, conventional CEA testing depends on immunoassay approaches, which are known to be complex, highly expensive, and time-consuming. In this context, many biosensors were designed for the aim of detecting cancer biomarkers. The main prerequisites of these biosensors are high sensitivity, fast response, and low cost. Many nanostructures have been involved in the design of biosensors. Metal organic frameworks (MOFs) were found to be one of the most potential and promising materials for biosensing. MOFs are highly porous and crystalline materials that consist of metal clusters surrounded by organic linkers, where the assembly of these components gives rise to the exquisite geometric 3D structures of MOFs. Moreover, the unique structure and geometry of MOFs allow for a better tailoring of their design to provide properties that are needed by different categories of biosensors. In the past few years, researchers have extensively considered MOFs for their fabrication of biosensors that can be used for the early detection of cancer biomarkers. In this regard, MOFs were used solely or were further decorated with other nanostructures to introduce more accurate signals and lower limits of detection. This review briefly classifies and describes MOFs-based biosensors trials that have been published recently for the aim of detecting CEA.

In the present study, the ability of novel carbon microspheres (CMs) derived from a date palm (Phoenix dactylifera) biomass using a hydrothermal carbonization (HTC) process and activated using phosphoric acid in removing methylene blue dye was investigated. Three types of palm-based wastes (seeds, leaflet and inedible crystallized date palm molasses) were used and converted to CMs via HTC process. The prepared samples were then activated using phosphoric acid via incipient wetness impregnation method. The CMs samples before and after activation were analyzed using scanning electron microscopy (SEM), elemental analysis and scanning (CHNS), Fourier Transform-Infrared (FTIR) and Brunauer–Emmet–Teller (BET) method. The samples exhibited high BET surface areas after activation (1,584 m2/g). The methylene blue adsorption results showed good fittings to the Langmuir and Redlich-Peterson isotherm models for all activated samples. The maximum adsorption capacity achieved was 409.84 mg/g for activated CM obtained from the palm date molasses, indicating high potential for application as dye-based adsorption materials.

Thermal processing of Zr-loaded ion-exchangers is a facile route to synthetize (ZrO2, ZrC)@C composites. The chemical character of the functional groups in the cation exchanger is an essential factor in the composition and properties of the (ZrO2, ZrC)@C composites. In the present paper furnace and RF-thermal plasma processing of ZrOCl2 loaded thiourea-functionalized styrene-divinylbenzene copolymer was investigated that led to various composites containing ZrO2 and ZrC. Depending on the synthesis conditions, different ZrO2@C composites were formed between 1000 and 1400 °C in 2 h, whereas the composite containing ZrC was created at 1400 °C in 8 h. The ratio of ZrO2/ZrC, the prevailing ZrO2 modifications, and the crystallite sizes strongly depend on the synthesis conditions. The ZrC-containing composites formed only at 1400 °C in 8 hours and by the plasma treatment of the ZrO2@C sample prepared in the furnace, resulting in 8 and 16% ZrC content, with 44 and 41 nm ZrC crystallite sizes, respectively. The ZrO2-containing composites (tetragonal, monoclinic, and cubic modifications with 65–88 nm ZrO2 crystallite sizes and 15–43 m2/g BET surface areas, depending on the carbonization temperature) formed in a tube furnace between 1000 and 1400 °C in 2 h. The tube furnace–prepared sample formed at 1400 °C in 8 h contained ZrC, ZrO2 modifications, and amorphous carbon, whereas the plasma-treated sample contained ZrC, ZrO2 modifications, and graphite. All ZrO2@C composites had both amorphous carbon and graphite, and their ratio is temperature-dependent. The carbonaceous compounds of the prepared composites were characterized by Raman spectroscopy, with analysis of the G and D band intensities. XPS studies showed the surface oxidation of ZrC.

The influence of hafnium metal (Hf) and sulfate ions (SO₄^-2) on the acidic properties of SiO₂ mesopores synthesized by a non-hydrothermal method was studied using the following characterization techniques; TG-DTG, XRD, BET, SEM, TEM, EDS, FTIR, n-butylamine titration, FTIR-pyridine, and alcohol dehydration. The incorporation of 3.6% mol of Hf during the silicate synthesis step caused the characteristic structural arrangement of MCM-41 to collapse. However, an increase in the acid strength of the catalyst of up to 315 mV was observed, with Brönsted and Lewis-type acid sites being mostly present therein. Furthermore, the acidity of Hf- and (SO₄^-2) -modified SiO₂ in the dehydration of ethanol and methanol was evaluated, resulting in a selectivity towards ethylene and dimethyl ether, respectively. Acid solids have enormous potential to produce important compounds for the chemical industry using alternative routes other than petrochemical processes. They also represent a significant advance for biorefineries.

Acetaldehyde decomposition was performed under heating at the temperature range of 25-125oC and UV irradiation on TiO2 doped by the metallic Ni powder and TiO2 supported on the nickel foam. Process was carried out in high temperature reaction chamber “The Praying MantisTM”, with simultaneous in situ FTIR measurements and UV irradiation. Ni powder was added to TiO2 in the quantity of 0.5 to 5.0 wt%. Photothermal measurements of acetaldehyde decomposition indicated, that the highest yield of acetaldehyde conversion on TiO2 und UV irradiation was obtained at 75oC. Doping of nickel to TiO2 did not increase its photocatalytic activity. Contrary to that, application of nickel foam as a support for TiO2 appeared to be highly advantageous, because increased decomposition of acetaldehyde from 31 to 52% at 25oC and then to 85% at 100oC by comparison with TiO2 itself. At the same time mineralisation of acetaldehyde to CO2 increased two times at the presence of nickel foam. However, oxidised nickel foam used as support for TiO2 was detrimental. Most likely, different mechanisms of electrons transfer between Ni-TiO2 and NiO-TiO2 occurred. Application of nickel foam greatly enhanced separation of free carriers in TiO2. As a consequence, high yields of the photocatalytic reactions were obtained.

Mechanochemical technology is developing rapidly, judging by the scientific information in both basic and applied studies. However, many issues and points of view remain to be discussed. This review presents some new key issues for the optimization of mechanochemical processes in theoretical and practical aspects. Emphasis is placed on powder technology aspects, which are not always discussed compared to functional or microscopic viewpoints. The transfer of chemical species across the interparticle interface between organic and inorganic species during the mechanosynthesis of nanocomposite oxides offers many new possibilities, which are discussed here in detail. Since all material transport is preceded by charge transfer, its driving force has been searched for using terminology beyond the well-established electrochemical ones. The role of organic compounds during the whole process is emphasized, regardless of their survival in the final product. The similarity with the pharmaceutical phenomena is pointed out, although its mentality is very different from that of the synthesis of nanocomposites. Not only for the rational amorphization of the active pharmaceutical ingredient, but also for the stabilization of molecular dispersion states with the participation of excipients are discussed. The effects of liquids, either added or formed by mechanochemical auto-liquefaction, are presented with reference to the comparison between wet and dry grinding. Finally, mechanisms of apparent stabilization of mechanically activated states of products are elucidated to investigate the practical applicability of mechanochemically synthesized products

The study reported the analytical approach on nine coins found in the wreck A of Fontanamare for understanding the complex corrosion processes that take place in underwater conditions. Optical microscopy (OM), combined with micro-Raman (µ-Raman) spectroscopy, and X-ray diffractometry (XRD) and scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM + EDS) were used to analyse the nature and the microstructure of the corrosion patina in comparison with the non-degraded state of coins. Three main type of corrosion patina based on copper, lead chloride and carbonate were identified: white-green, black and the obtained results for understanding the complex corrosion processes that take place in underwater conditions.

The ultrasonic vibration assisted pressing process can improve the fluidity, the uneven distribution of density and particle size of WC-Co powder. However, the microscopic mechanism of ultrasonic vibration on the powder remains unclear. In this paper, WC and Co particles are simulated by three-dimensional spherical models of two particle sizes with the aide of the secondary development of Python. At the same time, the forming process of powder at mesoscale is simulated in the virtue of the finite element analysis software ABAQUS. The influence of vibration amplitude on the fluidity, the filling density and the stress distribution of WC-Co powder is investigated when the ultrasonic vibration is applied to the conventional pressing process. From simulation results, the ultrasonic vibration amplitude has great influences on the density of the compact. With the increase of the ultrasonic amplitude, the compact density also increases gradually. At the initial stage of the compaction, the particles move violently under the action of ultrasonic vibration, the fluidity is obviously enhanced, the arch bridge effect between particles is destroyed, the fine particles quickly fill the pores between the large particles, which increase the density, and the residual stress in the billet decreases after the compaction. From the experimental results, the size distribution of the billet is more uniform, the elastic aftereffect is reduced, the dimensional instability is improved, and the density curves obtained by experiment and simulation are within a reasonable error range.

The possibility of increasing the resource of steel fingers working in tandem with bronze bushings by plasma-electrolytic nitrocarburizing of the surface of medium carbon steel is shown. The phase composition, microhardness, morphology and surface roughness were studied. Tribological tests were carried out under dry friction conditions according to the shaft-pad scheme. It has been established that plasma-electrolytic nitrocarburizing of the surface of medium carbon steel at a temperature of 700 °C for 5 minutes leads to a decrease in a friction coefficient by 2.3 times, weight wear of steel by 24.9 times, and bronze counterbody by 5.9 times. At the same time, the contact stiffness increases 2.6 times. The type of wear is fatigue with dry friction and plastic contact. Changes in tribological characteristics are associated with the high hardness of the hardened steel surface together with the influence of dispersed nitrides and iron carbonitrides distributed in it.

The potential use of nanostructured dipeptide self-assemblies in materials science for energy harvesting devices is a highly sought-after area of research. Specifically, aromatic cyclo-dipeptides containing tryptophan have garnered attention due to their wide-bandgap semiconductor properties, high mechanical rigidity, photoluminescence, and nonlinear optical behavior. In this study, we present the development of a hybrid system comprising biopolymer electrospun fibers incorporated with the chiral cyclo-dipeptide L-Tryptophan-L-Tyrosine. The resulting nanofibers are wide-bandgap semiconductors (bandgap energy 4.0 eV) and consist of self-assembled nanotubes embedded within a polymer matrix, exhibiting intense blue photoluminescence. Moreover, the cyclo-dipeptide L-Tryptophan-L-Tyrosine incorporated into polycaprolactone nanofibers displays a strong effective second harmonic generation signal of 0.36 pm/V and also shows notable piezoelectric properties with a high effective coefficient of 22 pCN−1. These hybrid systems hold great promise for applications in the field of nanoenergy harvesting and nanophotonics.

The possibility of increasing wear resistance of the CP-Ti surface using a duplex surface treat-ment combining plasma electrolytic nitrocarburizing in a solution of ammonia, acetone and ammonium chloride and subsequent plasma electrolytic polishing is shown. Morphology and surface roughness, structure and microhardness of the modified layer were studied. The correla-tion of weight wear with hardness of diffusion layer at a low processing temperature and thick-ness of oxide layer is established – the largest decrease in weight wear occurs after nitrocarbu-rizing at 750 °C for 5 min (by 4.3 times). The possibility of an additional increase in wear re-sistance by subsequent polishing of the nitrocarburized CP-Ti surface at a voltage of 275–300 V for 3–5 min in chloride and fluoride electrolytes and 5–10 min in a sulfate electrolyte was re-vealed. Under these conditions, the hardened layer is preserved when the porous outer oxide layer is removed. According to the microtopology of the friction tracks, the wear mechanism is estimated as fatigue in dry friction and plastic contact.

The study presents the synthesis and characterization of dual-layer sulfonated polyphenylenesulfone (SPPSu) nanocomposite hollow fiber nanofiltration membranes incorporating titanium dioxide (TiO2) nanoparticles using the phase inversion technique. The newly developed membranes were systematically characterized using advanced tools and methods to evaluate their properties and performance. The study focused on investigating the effects of TiO2 addition in the SPPSu inner layer on pure water permeability, and salt rejection. The nanocomposite hollow fiber nanofiltration membranes exhibited a significant enhancement in pure water permeability, with a three-fold increase compared to the pristine membranes, achieving a flux of 5.4 L/m2h.bar. The addition of TiO2 also led to an improvement in the mechanical properties of the membranes, as evidenced by the increase in the expected tensile strength from 2.4 to 3.9 MPa. To evaluate the salt rejection performance, rejection tests were conducted using a laboratory-scale filtration setup in recycle mode. Aqueous solutions containing different divalent ions, specifically magnesium sulfate (Mg2SO4) and sodium sulfate (Na2SO4) at a concentration of 500 ppm, were used as the feed solution. The modified dual-layer hollow fiber nanocomposite membranes exhibited a maximal rejection of 95% for Mg2SO4, demonstrating their effective separation capabilities for divalent ions. The findings of this study highlight the successful synthesis and characterization of dual-layer SPPSu nanocomposite hollow fiber nanofiltration membranes incorporating TiO2 nanoparticles. The incorporation of TiO2 resulted in improved pure water flux, mechanical strength, and salt rejection performance. These enhanced properties make the developed nanocomposite membranes promising candidates for applications in nanofiltration processes, particularly for the selective separation of divalent ions from aqueous solutions.

Soluble noble metal salts are widely used for loading noble metals as nano-catalysts in many applications. In this paper, Pt-SnO2 composite nanoceramics were prepared from SnO2 nanoparticles and H2PtCl6 using two Pt-loading methods separately: For the solution reduction method, the H2PtCl6 solution was added to a suspension of SnO2 and zinc powder to form Pt on SnO2 nanoparticles; and for the impregnation method, Pt was formed from H2PtCl6 in the course of sintering. Although a series of samples prepared using both Pt loading methods showed a strong response to H2 at room temperature, the ones prepared using the solution reduction method exhibited much better room temperature hydrogen sensing characteristics. For two samples of 0.5 wt% Pt and sintered at 825°C, the response value for the sample prepared using the solution reduction method was 5300 to 1% H2-20% O2-N2, which was much larger than that of 150 for the sample prepared using the impregnation method. Samples prepared using the two Pt loading methods have similar microstructures as characterized by XRD, FESEM, EDS, TEM, and HRTEM. However, the residual chlorine content in those using the impregnation method was found to be higher than that using the solution reduction method through analysis. It is proposed that the striking difference in the room temperature hydrogen sensing characteristics among samples prepared using these two different Pt loading methods separately resulted from their different chlorine removal process. This study demonstrates the importance of a proper method in loading noble metals from their soluble salts as nano-catalysts in many applications.

This paper presents a new method of preparing a coating on the Ti65 titanium alloy by a two-step procedure comprising hot-dipped aluminum and solid carburization. The effects of the carburization in the presence of NaCl deposit at 810oC have been systematically studied. In this article, the microstructure, morphology, phase composition of the coating, and the corrosion products were investigated by SEM, EDS, and X-ray diffraction. Results indicated that the corrosion resistance of hot dip aluminum/carburizing composite coating was not significantly enhanced by hot dip aluminum coating. This can be attributed to the formation of TiC and Ti3AlC after carburization, which promoted the formation of loose and unprotected TiO2 in the coating during molten salt corrosion. In addition, the oxidation of the carbon atom into CO2 /CO leaded to a high concentration of vacancy in the coating, creating channels for NaCl to penetrate the coating and accelerated the corrosion rate.

The present work describes the synthesis, characterization and photomineralization activity of synthesized Ce1-xZnxO2-x solid solution catalysts allowing the degradation of Diclofenac as a model of anti-inflammatory medicines in water. Oxygen deficient photocatalysts Ce1-xZnxO2-x (CeZnx), produced with mixing ZnO and CeO2 have been characterized for their crystallographic parameters, specific surface area and morphology. Photomineralization activity determinations using TOC analysis have shown efficient diclofenac photooxidation under sunlight. Moreover, results indicate that coexistence of Zn2+, Ce4+ and oxygen vacancies rate in CeZnx solid solution are key factors for strong drug mineralization. Finally, CeZn0.1 which is one of the photocatalysts synthesized in the present work represents a cheap and efficient reagent for organic matter photomineralization in wastewater.

Bond Properties were performed on Ag-2.35Au-0.7Pd-0.2Pt-0.1Cu alloy wire with a diameter of 25 µm under different process parameters. Effects of electrical flaming off (EFO) current and EFO time on deformability of the free air ball (FAB) were investigated using scanning electron microscopy (SEM) as well as the effects of ultrasonic power and bonding force on the bond characteristic. The experimental results showed that, FAB grows from a preheated tip to a small ball, a regular ball and finally to a golf ball with increasing either the EFO current or the EFO time, and the FAB presented optimal shape at 25 mA and 650 μs. Moreover, a nonlinear relationship between FAB diameter and EFO time is obtained at the EFO current of 25 mA, which could be expressed by a cubic equation. Further, at a constant bonding force, as the ultrasonic power increased, the mashed ball diameter grew larger and larger, the capillary hole imprint became more and more obvious, and the tail width also increased larger and larger, and vice versa. The optimal ultrasonic power and bonding force are 70 mW and of 45 gf for ball bond and 90 mW and 75 gf for wedge bond, respectively. Finally, for all the bonded wire samples prepared under optimal process parameters, no ball and wedge bond lifts happened after destructive pull test, and full intermetallic compound coverage with perfect morphology occurred on the bond pad after ball shear test, which meant that the bonded wire samples have high bond strength, and hence improved the reliability of microelectronic products.

A new process is reported for the incorporation of a fluoropolymer into a solid perovskite film. Poly(trifluoroethyl methacrylate) [CH2C(CH3)(CO2CH2CF3)]n was delivered to methylammonium lead iodide (CH3NH3PbI3) perovskite films by crystallizing the film in supercritical carbon dioxide/ethanol containing the dissolved fluoropolymer. The surface was characterized before and after fluoropolymer exposure using scanning electron microscopy, Raman spectroscopy and contact angle measurements. The results indicate that the fluoropolymer was incorporated into the perovskite film during the supercritical fluid crystallization process.

Tribological testing of moving shaft/sealing pairs in complex environments is at the frontline of research. Machines working in abrasive conditions are subject to different wear effects. It is valid not only on the Earth but especially valid for rovers and future robots used in Mars and Moon missions. The aim of our joint research with the European Space Agency is to study the abrasion phenomena of moving machine elements on Mars and the Moon, by using artificial soil samples (“simulants”). This review detail the available simulant sources and recommend a selection of the most suitable ones for tribological testing. Moreover, the potential mating structural materials subjected to abrasive space applications are reviewed. The tribological tests are exploring the features of the rotary shaft/seal relationship that is subject to dry friction and intense abrasion. By using the simulants, measurements are performed under laboratory conditions with both a sample test and a real shaft/seal connection. Parameters of the selection criteria have been defined and classification of the simulant sources were made. It was found that simulant particle size distribution and chemical substance content is detailed enough only for a limited type of available artificial Moon and Mars soil samples. 4 simulants have been identified and applied later in the tribological testing. For the shaft materials, based on a detailed case study of polymers, steel and aluminium alloys, a high-strength aluminium alloy with a hard anodized surface and a stainless steel were selected for further abrasion tests.

Due to the severe environmental impact of the CO2 emissions associated with the production of Ordinary Portland Cement (OPC) and the increasing demand for this commodity material, the development of alternative products has become a global concern. One alternative to OPC, or alitic-based clinkers, are amorphous-wollastonitic low calcium hydraulic binders (AWLCs). This new class of hydraulic binders, described in the literature for the first time in 2015, may significantly reduce the CO2 emissions associated with its production, resulting from its lower calcium content, but also from the fact that its production technology can be fully electrified. In this paper it is provided a state-of-the-art review, providing a comprehensive description on the latest research, summarizing both the physico-chemical and mechanical characteristics for this type of hydraulic binders, as well as possible routes for its production at an industrial scale.

In current work, we illustrate the effect of adding small amount of Carbon to very common Co2MnSi Heusler alloy based-glass coated microwires. A significant change in the magnetic and structure structural properties has observed for the new alloy Co2MnSiC compared to the Co2MnSi alloy. The magneto-structural investigations have performed to clarify the main phys-ical parameters i.e., structural & magnetic at a wide range of measuring temperature. The XRD analysis illustrated the well-defined crystalline structure with average grain size (Dg = 29.16 nm) and a uniform cubic structure with A2-type compared to the mixed L21 and B2 cubic structures for Co2MnSi-based glass coated microwires. The magnetic behaviour has investigated at a tem-perature range (5 to 300 K) and an external applied magnetic field (50 Oe to 20 kOe). The adding of small amount of Carbon to the Co2MnSi matrix enhance the magnetic thermal stability, where the thermomagnetic behaviour of Co2MnSiC glass-coated microwires show a perfect stable be-haviour for a temperature range from 300 K to 5 k, the differences between the coercivity value is only 0.3 Oe compared to 4 Oe for Co2MnSi-sample. In addition, M-H loops measured at tempera-ture below 50 K show unsaturated loops; meanwhile the Co2MnSi loops shows a strong antifer-romagnetic coupling for the loops measured below 50 K. By studying the field cooling (FC) and field heating (FH) magnetizations curves at a wide range of external applied magnetic field we detected a critical magnetic field (H = 1 kOe) where FC and FH curves have a stable magnetic behavior for Co2MnSiC sample, such stability does not find in Co2MnSi sample. We proposed a phenomenal expression to estimate the magnetization thermal stability, ΔM (%), of FC and FH magnetization curves and the maximum value is detected at the critical magnetic field where ΔM (%) ≈ 98 %. The promising magnetic stability of Co2MnSiC glass-coated microwires with tem-perature is due to the changing of the microstructure induced by adding Carbon, as the A2-type structure show a unique stability by variation the temperature and the external magnetic field. In addition, a unique internal mechanical stress, which induced during the fabrication process and plays on controlling magnetic behavior with temperature and external magnetic field. The ob-tained results make Co2MnSiC promising candidate for magnetic sensing devices based Heusler glass-coated microwires.

In this work, we compiled our research on lanthanide-based luminescent materials, prepared down-shifter layers, and studied their effect on photovoltaic (PV) mini-modules. The compounds we have prepared (C1-C17), with formulas [Eu2(phen)2(bz)6] (C1), [Eu2(bphen)2(bz)6] (C2), [Eu(tta)3bphen] (C3), [Eu(bta)3pyz-phen] (C4), [Eu(tta)3pyz-phen] (C5), [Eu(bta)3me-phen] (C6), [Er(bta)3me-phen] (C7), [Yb(bta)3me-phen] (C8), [Gd(bta)3me-phen] (C9), [Yb(bta)3pyz-phen] (C10), [Er(tta)3pyz-phen] (C11), [Eu2(bz)4(tta)2(phen)2] (C12), [Gd2(bz)4(tta)2(phen)2] (C13), [EuTb(bz)4(tta)2(phen)2] (C14), [EuGd(bz)4(tta)2(phen)2] (C15), [Eu1.2Gd0.8(bz)4(tta)2(phen)2] (C16) and [Eu1.6Gd0.4(bz)4(tta)2(phen)2] (C17), can be grouped into three families based on their composition: Series C1–6 were synthesized using Eu3+ ions and phenanthroline derivatives as the neutral ligands, and fluorinated β-diketonates as the anionic ligands. Complexes C7–11 were prepared with ligands similar to those of compounds C1–6 but were synthesized with Er3+, Yb3+, or Gd3+ ions. Series C12–17 exhibit the general formula [M1M2(bz)4(tta)2(phen)2], where M1 and M2 can be Eu3+, Gd3+, or Tb3+ ions, and the ligands are benzoate (bz–), 2-thenoyltrifluoroacetone (tta–) and 1,10–phenanthroline (phen). All compounds were characterized using X-ray techniques, and their photoluminescent properties were studied. We then examined their impact on the EQE (External Quantum Efficiency) of PV mini-modules and their durability in a climate chamber when embedded in PMMA and EVA films. This review emphasizes the methodology employed and the key findings, including enhanced mini-module efficiency. Additionally, we present promising results on the application of compound C6 in a bifacial solar cell.

The temperature-dependent energy storage properties of four tungsten bronze phase compounds are studied together with an investigation of their structure and temperature-dependent permittivity response, i.e., Ba6Ti2Nb8O30 (BTN), Ba6Zr2Nb8O30 (BZN), Sr3TiNb4O15 (STN) and Sr3ZrNb4O15 (SZN) ceramics. It was found that BZN has smaller grains and a more porous structure than BTN. SZN shows no clear grain boundaries with the most porous structure among all samples, exhibiting a much lower permittivity response than other samples with no signs of phase transitions from room temperature to 400 °C. Though the energy storage response of those samples is generally quite low, it exhibits rather good temperature stability. It was suggested that by obtaining a denser structure through chemical modification or other methods, those tungsten bronze ceramics with good temperature stability could be promising as energy storage devices when improved energy storage properties are achieved.

A self-protective metal/ liquid microcapsule composite plating coating has been prepared in our previous research. The release speed of liquid core material from microcapsules is crucial for the coating surface properties. The aim of this paper is to study the permeability rule of liquid microcapsules within composite coatings. According to permeability experimental data’s linear characteristics, multiple linear regression is firstly used to set up permeability model of liquid microcapsules. The results show that a reliable mathematical model about membrane porosity, viscosity of core material and membrane thickness is established under ambient temperature and moisture. Meanwhile, the predictive capacity and reliability of this model are analyzed carefully.

Nanoporous carbons were prepared by chemical and physical activation from mangosteen peel-derived chars. The removal of atrazine was studied due to the bifunctionality of the N-groups. Pseudo-first-order, pseudo-second order and intraparticle pore diffusion kinetic models were analyzed. Adsorption isotherms were also analyzed according to Langmuir and Freundlich models. Results obtained were compared against two commercial activated carbons with comparable surface chemistry and porosimetry. The highest uptake was found for the carbons with higher content of basic surface groups. The role of the oxygen-containing groups on the removal of atrazine was estimated experimentally by the surface density. Results were compared with the adsorption energy of atrazine theoretically estimated on pristine and functionalized graphene with different oxygen-groups using periodic DFT methods. The energy of adsorption follows the same trend observed experimentally, namely the more basic the pH the more favored is the adsorption of atrazine. Micropores play an important role in the uptake of atrazine at low concentration but the presence of mesoporous is also required to inhibit the pore mass diffusion limitations. The present work contributes to the understanding of the interactions between triazine-based pollutants and the surface functional groups on nanoporous carbons in the liquid-solid interface.

Starch is widely applied in various industrial sectors, including the food industry. Starch is used as a thickener, stabilizer, or emulsifier. However, arrowroot starch generally has weaknesses, such as unstable under heating and acidic conditions, which are generally applied to processing in the food industry. Modifications were applied to improve the characteristics of native arrowroot starch. In this study, arrowroot starch was modified by heat-moisture treatment (HMT), octenylsuccinylation (OSA), and dual modification between OSA and HMT in a different sequence, namely HMT followed by OSA, and OSA followed by HMT. This study aims to determine the effect of different modification methods on the physicochemical and functional properties of native arrowroot starch. The result shows that both single HMT and dual modification caused damage to native starch granules, such as the formation of cracks and roughness. Especially for single OSA treatment, there is no significant change in granule morphology after modification. All modification treatments did not change the crystalline type of starch but reduced the RC of native starch. Both single HMT and dual modifications (HMT-OSA, OSA-HMT) increased pasting temperature and setback, conversely decreasing the peak and breakdown viscosity of native starch. Whereas, single OSA has the opposite trend compared with the other modifications. HMT played a greater role in increasing the thermal stability and retrogradation ability of arrowroot starch. Both single modifications (HMT and OSA) increase the hardness and gumminess of native starch, conversely for dual modifications. HMT has a greater effect on color characteristics, where decreased the lightness and whiteness index of native arrowroot starch. Single OSA modification increased swelling volume higher than dual modification. Both single HMT and dual modifications increase water absorption capacity and decrease the oil absorption capacity of native arrowroot starch.

Iron-containing nickel sulfides, selenides, and sulfoselenides were synthesized via a simple two-step hydrothermal reaction (temperature 160 °C) for their application as electrocatalysts in the oxygen evolution reaction (OER) in an alkaline solution (1 mol L–1 KOH). The study demonstrated that iron-containing nickel cobalt sulfides and selenides exhibit superior OER performance with lower overpotentials compared to iron-free nickel cobalt sulfide and selenide, which highlights the significant role of iron in enhancing OER nickel cobalt electrocatalysts: Fe0.1Ni1.4Co2.9(S0.87O0.13)4, η50 = 318 mV; Fe0.2Ni1.5Co2.8(S0.9O0.1)4, η50 = 310 mV; Fe0.3Ni1.2Co2.5(S0.9O0.1)4, η50 = 294 mV; Fe0.6Ni1.2Co2.5(S0.83O0.17)4, η50 = 294 mV, Fe0.4Ni0.7Co1.6(Se0.81O0.19)4, η50 = 306 mV compared to Ni1.0Co2.1(S0.9O0.1)4, η50 = 346 mV and Ni0.7Co1.4(Se0.85O0.15)4, η50 = 355 mV (all values at current densities η50 of 50 mA cm–2). Furthermore, the iron-containing nickel cobalt sulfoselenide Fe0.5Ni1.0Co2.0(S0.57Se0.25O0.18)4 displayed exceptional OER performance with η50 = 277 mV, surpassing the benchmark RuO2 electrode with η50 = 299 mV. The superior performance of the sulfoselenide was attributed to its low charge transfer resistance (Rct) of 0.8 Ω at 1.5 V vs. the reversible hydrogen electrode (RHE). Moreover, the sulfoselenide demonstrated remarkable stability, with only a minimal increase in overpotential (η50) from 277 mV to 279 mV after a 20 h chronopotentiometry test. These findings suggest that trimetallic iron, nickel and cobalt sulfide, selenide and especially sulfoselenide materials hold promise as high-performance, cost-effective, and durable electrocatalysts for sustainable OER reactions. This study provides a valuable approach for the development of efficient electrocatalytic materials, contributing to the advancement of renewable energy technologies.

Photoluminescent (PL) layers and electroluminescent (EL) systems have been extensively explored for constructing flat panels, screen monitors, and lighting systems. Due to their optical properties, our group is interested in the relationship between optical properties and dielectric constant is converted due to thermal change. In this study, we prepared a zinc sulfide (ZnS) fluorescent film on barium-calcium zirconium titanate ceramics. BCZT0.85 (Ba0.85Ca0.15Zr0.1Ti0.9O3) and BCZT0.9 (Ba0.9Ca0.1Zr0.1Ti0.9O3) were prepared using the solid-state reaction method for the dielectric layer. The BCZT powders were calcined at 1200 and 1250 °C and dwell times of 2 and 4h. The phase formation and microstructure characteristics were then determined using X-ray diffraction and scanning electron microscopy, respectively. The dielectric behavior and optical properties rela-tionship was then studied to determine the composition and optimal conditions for further use as thermal detectors in electric vehicle battery packs. All BCZT powders exhibited the tetragonal phase, which was confirmed by JCPDS No. 01-079-2265. The dielectric constant increased with increasing calcining temperature or dwell time. The dielectric properties showed the BCZT0.85 ceramic sintered had the maximum dielectric constant of 15342 at calcine temperature of 1250 °C for 4h. Therefore, in this study, this condition was optimal for preparing the dielectric film. The maximum dielectric constant film is 42. The electroluminescence intensity of the samples increased in a temperature-dependent manner, with the highest EL intensity at 80 °C. Moreover, the electroluminescence intensity value was enhanced with the increase of the dielectric constant. Our results show promise for developing applications for Opto-thermal sensors.

In this work, a novel silane coupled cationic precursor (SAGS) was synthesized by 3-glycidyloxypropyltrimethoxysilane and sodium 2-((2-aminorthyl)amino) ethanesulfonate. A series of cation exchange membranes were prepared with poly(vinyl alcohol) (PVA) and SAGS by sol-gel process. The structure of the prepared membranes were characterized by fourier transform infrared spectrum (FTIR) and scanning electron microscopy (SEM), and its properties were studied by water uptake (WR), cation exchange capacity (CEC), linear expansion ratio (LER), alkali stability, thermogravimetric analysis (TGA), mechanical properties and diffusion dialysis performance. FTIR and X-ray photoelectron spectroscopy (XPS）confirmed the successful preparation of SAGS membranes, and SEM images showed that the prepared membranes were dense and uniform. The WR values of the SAGS membranes were in the range of 91.49-122.39 %, and the LER values were 17.65-28.21 %. In addition, the SAGS membranes had suitable CEC value, good alkali resistance and thermal stability which ensured the application of membranes in the field of diffusion dialysis (DD) for alkali recovery. In DD test, the dialysis coefficients of NaOH (UOH) ranged from 0.012 mm/h to 0.023 mm/h, and the separation factors (S) was in the range of 30.77-16.43. In summary, the prepared membrane had good performance and simple preparation process, which had great application potential in textile industrial wastewater recovery.

Much attention has been attracted by aqueous zinc zinc-ion batteries (AZIBs) due to the features of inherent safety, environmental compatibility, low cost and fantastic energy density. Nevertheless, chemical corrosion and dendrite growth occurring on Zn anode during the charge/discharge process usually cause the surface passivation and short circuit of cells, seriously hindering the development of AZIBs. To settle these problems, a Cu(II)/polydopamine modified glass fiber (Cu-PDA/GF) is designed as separator. Due to the enhanced ionic conductivity of Cu(II) and PDA modified glass fiber separator, reversible zinc plating/striping is achieved in symmetric cells, which display long cycle life of over 1800 h at the current density of 1 mA cm−2 with the fixed capacity of 1 mAh cm−2. Moreover, the assembled Zn//V2O5 cells using Cu-PDA/GF separator also demonstrate improved capacity retention. The present study provides a simple separator modification strategy for high-performance and reliable AZIBs, which are conducive to energy storage devices.

Reducing the costs of repairing concrete structures damaged due to the appearance of cracks and reducing the number of people involved in the process of their repair is the subject of a multitude of experimental studies. Special emphasis should be placed on research involving industrial by-products, the disposal of which has a negative environmental impact, as is the case in the research presented in this paper. The basic idea was to prepare a mortar with added granulated blast furnace slag from Smederevo Steel Mill and then treat artificialy produced cracks with a Sporosarcina pasteurii DSM 33 suspension under the conditions of sterile demineralized and water from Danube river in order to simulate natural conditions. The results show a bio-stimulated healing efficiency of 32.02% in sterile demineralized water and 42.74% in Danube water already after 14 days. The SEM images clearly show calcium carbonate crystals as the main compound that has started to fill the crack, and the crystals are much more developed under the Danube water conditions. As a special type of research, microscopic images of cracks were classified into those with and without the presence of bacterial culture. By applying convolutional neural networks (ResNet 50), the classification success rate was 91.55%.

Advanced coatings are essential to modern technologies, as they optimise surface characteristics for different application scenarios. Transparent and self-cleaning coatings are increasingly used as protective coatings for various applications, such as foldable touchscreens, windows, and solar panels. Moreover, incorporating other functionalities such as high hardness, wear resistance, and flexibility into transparent and self-cleaning coatings is important for broadening the use cases. Although many kinds of multifunctional coatings have been developed, it is still difficult to embody several properties in one coating adequately, as some properties, such as hardness and flexibility, are inherently contrastive. This review first describes basic principles, including wetting ability, photocatalytic reactions, photo-induced hydrophilic phenomena, and the implication of self-cleaning. The desired properties of multifunctional coatings are then listed, and methods for evaluating different properties are used. Recent progress in various preparation methods for multifunctional coatings, including the sol-gel, dip/spin, and chemical vapour deposition (CVD) methods, are also presented. Magnetron sputtering (MS) technology is widely used in coating preparation. Compared with chemosynthesis and CVD, MS is time-saving, suitable for industrial production, and environmentally friendly. Coatings prepared by MS usually possess excellent mechanical properties. Thus, we highlight the current research status of MS technology in multifunctional coating preparation. Moreover, according to the multilayer design structure of coatings, their optical and mechanical properties and self-cleaning ability can be controlled by combining the characteristics of different materials. Finally, combining photocatalytic materials such as TiO2 with other materials through a multilayer structure to obtain a multifunctional coating with excellent overall properties is discussed.

Benign design of alkali-activated slag/FA geopolymer paste has intriguing increasing attention for optimizing its service performance. Therefore, the replacement of fly ash (FA) with 10 wt% silica fume (SF) is investigated by mechanical strength after freeze-thawing cycles and microstructure characterization. The results show that an appropriate dosage (30 wt%) of slag is necessary to attain alkali-activated slag/FA geopolymer paste with excellent mechanical performance, and the SF/slag/FA (SF: slag: FA= 10:30:60, wt%) geopolymer paste exerts the compressive and flexural strength of 95.2 and 3.2 MPa, respectively. Meanwhile, the doped 10 wt% SF facilitates the propagation of (N, C)-A–S–H chains, rather than the formation of C-S-H gels, evidenced by the absent exothermic peak at about 861oC from the differential scanning calorimetry (DSC) curves, leading to the increases in the pores volume with a pore diameter<20 nm and tortuosity by mercury intrusion porosimeter (MIP) results, corresponding to an improved freezing-thawing resistance with the residual compressive strength of 52.8 MPa and the weight loss of 10.5% after 300 freeze-thawing cycles. It explores a cost-effective and benign facile approach to designing heating curing-free alkali-activated slag/FA geopolymer paste with good freezing-thawing resistance.

In this paper, Fe-Cr-C-N-Al-Y wear-resistant surfacing alloy was prepared by open arc surfacing with self-shielded flux-cored wire. The wear properties of the surfacing alloy were analyzed by MLS-23 rubber wheel wet sand wear tester. The phase composition and microstructure of the surfacing alloy were analyzed by XRD, SEM, EBSD and TEM, and the strengthening mechanism and wear mechanism of the alloy were discussed. The results show that the microstructure of Fe-Cr-C-N-Al-Y surfacing alloy is composed of M + γ-Fe + M7C3 + AlN. When the content of nano-Y2O3 is 0.456wt. %, the formability of the surfacing alloy is the best and the wetting angle is the smallest, which is 50.8°, AlN and M7C3 precipitate the most, and the microstructure grain is the smallest. At this time, the hardness value of the surfacing alloy is up to 62.3 HRC, which is 11.8 % higher than that of the unmodified surfacing alloy. The minimum wear weight loss is 0.125 g, and the wear resistance is increased by 41.86 %. The wear mechanism of surfacing alloy is mainly plastic deformation mechanism, and the material removal process is micro cutting and furrow wear.

In this work, nitrite intercalated CaAl-LDH was firstly prepared in this work. Scanning electronic microscopy (SEM) coupled with the energy dispersive spectrometer (EDS) was used to characterize the morphology and element composition of the synthesized powder. Fourier transform infrared spectroscopy (FTIR) was used to characterize the chemical composition and X-ray diffraction (XRD) was used to analyze the structure. The nitrite release curve and the chloride concentration change curve were obtained to study the anion-exchange reaction. The corrosion protection effect of the CaAl-LDH loaded with nitrites towards the carbon steel was evaluated in 0.02 M NaCl solution by electrochemical impedance spectroscopy (EIS). Then the powder was added in the epoxy coating with a percentage of 2% (vs. epoxy resin). The coating morphology and roughness was evaluated by SEM and laser microscopy, and the corrosion protection effect was investigated by EIS in an immersion period of 21 d. Local electrochemical impedance spectra (LEIS) was used to characterize the corrosion development process in micro-corrosion sites. The corrosion product of the scratched area after salt spray exposure was analyzed by EDS and Raman spectroscopy. The corrosion protection mechanism of the CaAl-LDH loaded with nitrites was proposed based on the above experimental results.

The use of analytical techniques is important and critical in all areas of REE research such as exploration, mining, extraction, and metallurgical activities at different stages. At every stage of these activities, rock, ore, mineral, and other related materials have to be analysed for their REE contents in terms of elemental, isotopic, and mineralogical concentrations using different analytical techniques. Spectacular developments have taken place in the area of analytical instrumentations during the last four decades, with some of them having shrunk in size and become hand-held. Among laboratory-based techniques, F-AAS, GF-AAS, ICP-OES, and MP-AES have become very popular. Because of high sensitivity, less interference effects, and ease of use. ICP-MS techniques such as quadrupole-ICP-MS, ICP-MS/MS, ICP-TOF-MS, MH-ICP-MS, HR-ICP-MS, and MC-ICP-MS, with both solution nebulisation as well as direct solid analysis using laser ablation sample introduction methods, have become extremely popular for REE analysis. For direct analysis of solids INAA, XRF, and LIBS techniques besides LA-based ICP-MS techniques are being extensively utilised. LIBS technique in particular requires little to no sample preparation. TIMS, SIMS, and SHRIMP techniques are being used for isotopic as well as dating REE depots. Portable analytical techniques such as pXRF, pLIBS, and Raman spectrometers are able to do in situ analysis even in the field helping to take fast decisions during exploration studies. At present hyperspectral remote sensing techniques including hand-held, drone, and satellite-based techniques have become very popular in REE exploration studies because of their ability to cover larger areas in a limited time and thus became very cost-effective. Deployment of microanalytical devices/sensors mounted in remotely operated vehicles (ROV) is being successfully utilized in detecting REE-rich deposits in the deep oceans. Providing updated in-depth information on all these important aspects with suitable examples, especially from the point of view of REE research studies is the focal point of this review article.

Two-dimensional MXene synthesized from MAX phase ceramic has the good electrical conductivity, promising to be used as electrodes. In this study, Nb4C3Tx MXene and low-entropy (Nb0.8Ti0.05V0.05Zr0.05Ta0.05)4C3Tx MXene were prepared by etching Nb4AlC3 and (Nb0.8Ti0.05V0.05Zr0.05Ta0.05)4AlC3 ceramics in the HF acid at 60 oC. By investigating the electrochemical properties of lithium batteries, it was found that the Nb4C3Tx and (Nb0.8Ti0.05V0.05Zr0.05Ta0.05)4C3Tx could provide the specific capacities of 163.7 mAh·g-1 and 130 mAh·g-1 after 50 cycles at a current density of 0.1 A·g-1, respectively, and maintain the coulombic efficiency close to 100%, good for the utilization of electrodes in the lithium batteries.

The sepiolite/ZrO2 composites were prepared by sepiolite (Sep) modification with zirconium propoxide in toluene, at room temperature for 24 h (Sep –ZrI) or 95 °C for 4h (sample Sep –ZrII). The efficiency of the obtained adsorbents for the removal of phosphate from aqueous solutions at initial pH = 4 and pH = 8, was investigated. Characterization of the samples showed that higher temperature of synthesis for shorter time provided slightly higher content of amorphous Zr-phase, which was deposited on sepiolite fibers as a thin layer and agglomerated nanoparticles. Compared to Sep, the composites had lower point of zero charge and higher specific surface area and pore volume. The adsorption kinetics follows the pseudo second-order model. The adsorption capacities of the composites were approximately the same at both initial pH and higher at initial pH = 4 than at pH = 8. The XPS and ATR-FTIR of Sep-ZrI before and after adsorption identified the formation of inner-sphere complexes as the mechanism of phosphate adsorption. The slow release during desorption with NaOH solution confirmed strong bonds of phosphates with the surface of the composites.

Detecting low concentrations of thyroxine hormone (T4) is of utmost importance to prevent diseases and medical issues caused by hypothyroidism. In this work, we propose the use of a simple technique for T4 sensing, the well-known surface-enhanced Raman spectroscopy (SERS). Spherical Au and Ag nanoparticles (NPs) and functionalized with ascorbic acid and tannic acid, respectively. They synthesized by a seed-mediated growth method, were used as SERS substrates to quantify T4 at different concentrations. The NPs were characterized by UV-VIS spectroscopy and scanning electron microscopy. Both, Au and Ag NPs, have an average diameter of 50 nm, the first ones have a surface plasmon resonance at 537 nm, while the latter have it at 421 nm. It was noticed the SERS substrates are composed of isolated and agglomerated NPs. From theoreti-cal-numerical calculations, we identified the hot spots |E| of the agglomerate NPs is at least 7 times more intense than that of the isolated NPs. We show the substrates can detect up to 0.01 mM and, for the range of concentration studied, the Ag substrate is more sensitive than Au. Thus, the proposed substrates and the SERS technique constitute a potential prospect for sensing hormones and organic molecules at low concentrations.

A novel fluorescent probe (C460@Tb-MOFs) was designed and synthesized through encapsulating the fluorescent dye 7-diethylamino-4-methyl coumarin into terbium-based metal-organic framework by a simple ultrasonic impregnation method. It is impressive that this dye-modified metal-organic framework can specifically detect styrene and temperature upon luminescence quenching. The sensing platform of this material exhibit great selectivity, fast response and good cyclability toward styrene detection. It is worth mentioning that the sensing process undergoes a distinct color change from blue to colourless, providing conditions for accurate visual detection of styrene liquid and gas. The significant fluorescence quenching mechanism of styrene toward C460@Tb-MOFs is explored in detail. Moreover, the dye-modified metal-organic framework can also achieve temperature sensing from 298 to 498 K with high relative sensitivity at 498 K. The preparation of functionalized MOFs composites by fluorescent dyes provides an effective strategy for the construction of sensors for multifunctional applications.

Tackling global warming and the consequent climate change in our planet is of urgent importance to our society. Renewable biomass derived carbons have been studied as promising adsorbents, but marine biomass derived carbons have not been explored extensively. S and N double-doped porous carbons were obtained from a marine biomass related precursor. Adding carbon nanoparticles (CNP) graphene oxide (GO), or carbon nanotubes (CNTs), in an early stage of the synthesis leads to a modified porous texture and surface chemistry. The carbons retained 2-4.5 at% nitrogen and 1.1 at% sulfur. The best GO and CNT added carbons had an apparent surface area 1780 m2/g and 1170 m2/g, respectively, compared to 1070 m2/g of the CNP-free matrix. The Dubinin-Radushkevich (DR) and Henry models were used to assess the strength of the interactions between various gases and the surface. The N2/H2 and CO2/CH4 selectivities were estimated with ideal adsorbed solution theory (IAST). While the CNPs, particularly GO, had a remarkable effect both on the porous texture and the surface chemistry, their influence on selectivity is more modest.

An attempt to investigate the effect of binary composite activators on the microstructure of fly ash-based geopolymers is conducted through the comparison of 24 experiments, which consisted of Na2SiO3•9H2O, Na2CO3, K2CO3, NaOH, and KOH through a facile preparation technique. The results show that the activator of Na2SiO3•9H2O+KOH presents the highest mechanical strength, due to the synergy activation between the inherent ≡Si-O-Si≡ chains derived from Na2SiO3 and K+’s catalysis. It reveals that the K+ plays a crucial role in Na2SiO3-activated fly ash geopolymer, which is the rate-determining step of the enhanced crosslinking and propagation of N-(C)-A-S-H chains, leading to an increase in weight loss temperatures of specimens from TG/DTG results. Furthermore, the adding silica fume facilitates as-formed amorphous silicates, which also could fill into the pores of N-(C)-A-S-H amorphous gels and present a uniform and compact morphology, leading to an increase in the pore volume of the pore diameter less than 100 nm. It explores an efficient and cost-effective preparation of fly ash-based geopolymer for developing solid-waste recycling techniques.

The article focuses on the galvanic replacement synthesis of Ti-Ni and Zr-Ni metal systems with the "core-shell" structure which are potential precursors for intermetallics. The authors defined the effective synthesis parameters and the formation features of polymetallic systems character-ized by granulometric, phase and elemental composition. The X-ray fluorescence and X-ray phase analysis methods showed that the deposition of nickel on dispersed titanium and zirconium leads to the production of test samples with phase composition representing a mechanical mixture of Ni and Ti, Ni and Zr. The method of X-ray fluorescence analysis showed that the presence of hy-drofluoric acid with a 0.5-1.5 M concentration results in the formation of fixed quantitative ratios of elements in the precipitate, which allows the quantitative composition of dispersed systems "titanium - nickel", "zirconium - nickel" to be regulated within a relatively wide range. Scanning electron microscopy proved that all synthesized systems are characterized by a highly porous structure that follows the titanium and zirconium particle surface contour and the presence of spherical nanoscale subunits on the formed particle surface.

To date, zinc ion batteries (ZIBs) have been attracting extensive attention due to their outstanding properties and the potential to be the solution for next-generation energy storage systems. However, the uncontrollable growth of zinc dendrites and water-splitting issues seriously restrict the further scalable application. Over the past few years, solid polymer electrolytes (SPEs) have been regarded as a promising alternative to address these challenges and facilitate the practical advancement of zinc batteries. In this review, we revisited the research progress of SPEs applied in zinc batteries in the past few years and focus on introducing cutting-edge polymer science and technologies that can be utilized to prepare advanced SPEs for high-performance zinc batteries. The operating mechanism of SPEs and the functions of polymers will be summarized. To highlight the polymer functions, SPEs are categorized into three types, respectively, homogenous polymer SPEs, hybrids polymer SPEs, and nanocomposites SPEs, which are expected to reveal the roles and principles of various polymers in zinc batteries. This review presents the current research progress and fundamental mechanisms of polymer-based SPEs in zinc batteries, outlines the challenging issues encountered, and meanwhile proposes potential solutions for future endeavours.

Vascular endothelial growth factor (VEGF) is a important biomarker with significant clinical importance. It plays a key role in angiogenesis, would healing, tumor growth, lung development, and in retinal diseases. Hence, detecting and quantifying VEGF is crucial in clinical diagnosis and prognosis of various diseases. In this work, a simple but highly cost-effective platform is developed for VEGF protein detection by using commercially available interdigitated sensors that are modified through surface chemistry tagged with DNA aptamer grafting. The dielectric characteristics between the fingers of sensor is modulated by the negatively charged aptamer-VEGF capture and the impedance is estimated using impedance analyzer. Impedance spectra tests was compared between pristine unmodified, functionalized monolayer surfaces and aptamer-grafted surfaces in order to evaluate the efficacy of VEGF detection. In our results, the sensitivity experiments as conducted had shown the ability of the interdigitated sensor to detect VEGF at a low concentration of 5 pM. The specificity of the functionalized sensor in detecting VEGF is further studied by comparing the impedance to platelet-derived growth factor (PDGF), and the results confirm the specificity of the sensor. Finally, an alternative illustration of impedance spectra is also proposed to improve the data visualization, and such presentation may be potential for intelligent VEGF detection.

The study investigates the effects of immobilizing the fungi on the straw's performance as an oil sorbent. The buoyancy of the straw with fungi was found to be unaffected by the immobilization process. Even when sorbed with oil, the straw floated on the water’s surface throughout the 14-day test period. The sorption kinetics of the oil appeared similar in straw with and without immobilized fungi, regardless of beaker shaking. However, the fraction of non-extractable oil was higher in the straw with fungi and shaking compared to the straw without shaking. This observation suggests the potential initiation of oil mining. Based on these results, it is suggested that instead of leaving the straw with fungi and oil in the water, removing it may be beneficial and allow for oil degradation and straw decomposition on land.

With the rapid development of electronic and communication technology in military radar, the demand for microwave absorbing materials in low-frequency with thin layer is growing increasingly. In this study, flexible Co3O4/CC (carbon cloth) composites derives from Co-MOFs (metal-organic frameworks)/CC are prepared by hydrothermal and thermal treatment processes. The flexible precursors of Co-MOFs/CC are calcined with different calcination temperatures, which the material structure, dielectric properties and microwave absorption performance are changed. With the increase of calcination temperature, the minimum reflection loss of the corresponding Co3O4/CC composites gradually moves to the lower frequency with thinner thickness. In addition, the Co3O4/CC composites with 25 wt% filler loading ratio exhibit the minimum reflection loss (RL) of -46.59 dB at 6.24 GHz with 4.2 mm thickness. When the thickness is 3.70 mm, the effective absorption bandwidth is 3.04 GHz from 5.84 to 8.88 GHz. This study not only proves that the composite Co3O4/CC is a kind of outstanding microwave absorbing material with better flexibility, but also provides a useful inspiration for the low frequency and broadband microwave absorbing material.

This paper describes the influence of the regeneration treatments on 4-chloro-2-methyl-phenoxyacetic acid (MCPA)-loaded activated carbons (ACs) on adsorption-desorption cycles with two commercial ACs, Merck and Norit 1240 X ( Norit 1240 X was used in a granular and powder form). The ACs were saturated with MCPA and then submitted to four regeneration cycles, by washing with ethanol, NaOH solutions and washed with NaOH solutions followed by a thermal treatment. The ACs regenerated with ethanol showed a better performance concerning the successive adsorption-desorption cycles. On the first cycle, the MCPA desorbed, from washing with ethanol, from all ACs was higher than 99%. After a fourth adsorption-desorption cycle, washing regeneration combined with thermal treatment allowed excellent regeneration results. The amount of MCPA adsorbed on Norit 1240 X AC was higher than the amount adsorbed in the first cycle. MCPA adsorption kinetic data were analyzed by applying pseudo-first-order, pseudo-second-order, and Weber-Morris models. The pseudo-second-order fit better fit to the data and the Weber-Morris representation allows confirming that on Norit 1240 X, in a granular form, the pore diffusion was the limiting factor concerning the MCPA adsorption.

This study demonstrates the successful synthesis of Ni/Y2O3 nanocomposite particles through the application of ultrasound-assisted precipitation using the Ultrasonic Spray Pyrolysis technique. The particle size was predicted accurately using a modified equation, and they were collected in a water suspension with Polyvinylpyrrolidone (PVP) as the stabiliser. The presence of the Y2O3 core and Ni shell was confirmed with Transmission Electron Microscopy (TEM) and with electron diffraction. The TEM observations revealed the formation of round particles with an average diameter of 466 nm, while the lattice parameter on the Ni particle’s surface was measured to be 0.343 nm. The Ni/Y2O3 nanocomposite particle suspensions were lyophilized, to obtain a dried material that was suitable for embedding into a Polylactic acid (PLA) matrix. The resulting PLA/Ni/Y2O3 composite material was successfully extruded successfully, so that a 3D printed technology Fused Filament Fabrication could be used further for the production of tensile test tubes. The tensile tests showed that the addition of lyophilised Ni/Y2O3 into the PLA matrix decreased the tensile strength by 21.8 %, while the tensile modulus was not influenced. Dynamic Mechanical Analysis (DMA) showed that the addition of the Ni/Y2O3 particles increased the glass transition temperature by 5 °C, and increased the storage modulus in the glass transition range significantly. These findings demonstrate the potential for utilising Ni/Y2O3 nanocomposite particles in 3D printing applications, and warrant further exploration of their mechanical properties and potential applications in various fields.

Dendritic Mesoporous Organosilica Nanoparticles (DMON) are a new class of biodegradable nanoparticles suitable for biomolecules delivery. In order to escape from the endosomes-lysosomes and to deliver biomolecules in the cytoplasm of cells, we studied photochemical internalization (PCI) and photodynamic therapy (PDT) of DMON. We added photosensitizers in the framework of DMON. DMON were also loaded with siRNA or FVIII factor protein. We made four formulations with four different photosensitizers, The photosensitizers allowed to perform imaging of DMON in cancer cells, but the presence of the tetrasulfide bond in the framework of DMON quenched the formation of singlet oxygen. Fortunately one formulation allowed to efficiently deliver proapoptotic siRNA in MCF-7 cancer cells leading to 31% of cancer cell death, without irradiation. For FVIII protein, it was loaded in two formulations with drug loading capacities (DLC) up to 25%. In conclusion DMON are versatile nanoparticles which allowed to load siRNA and to deliver it in cancer cells, and to load FVIII protein with good DLC. Due to the presence of tetrasulfide, it was not possible to perform PDT and PCI.

2,7-bis(pyridin-4-ylethynyl)-9H-carbazole (1) was synthesized by reacting 4-ethynylpyridine hydrochloride with 2,7-dibromo-9H-carbazole. The full characterization of compound 1 is presented, and the crystal structure of its monohydrate co-crystal was determined by single-crystal XRD analysis.

Brewers’ spent grain (BSG) is an important waste produced in beer companies with a high po-tential to be transformed into commercial by-products. The present paper reports a forecasting technology study with the aid of bibliographic review and patent analysis tools aiming to in-vestigate the maturity of certain technologies, considering the use of BSG on a closed-loop bio-refinery and circular bioeconomy concept integrated into a brewery. To evaluate the possibili-ties of production of high-added value products in Brazil, it was presented an overview of BSG’s scientific, technological, and marketing products and applications. The comparison between numbers of articles versus patents shows that the solutions proposed by research articles are not being transformed into maturated viable technologies. The results suggest that there is a gap between the scientific research in the institutions and their applications in industry, which lead to the destination of the BSG for more economically attractive investments when compared to research in Brazil. Ultimately, from the carried-out analysis, it was possible to propose a brew-ing process connected to the biorefinery system, showing the possibility to the newly arising brewery industries.

We have investigated the interfacial dislocations in InxGa1–xN/GaN (0 ≤ x ≤ 0.20) heterostructures using diffraction contrast analysis in a transmission electron microscopy. The analysis indicate that the structural properties of the interface dislocations depend on the indium composition. For lower indium composition up to x = 0.09, we observed that the screw-type dislocations and dislocation half loops occurred at the interface even though the former do not contributes toward elastic relaxation of the misfit strain in the InGaN layer. With the increase of indium composition (0.13 ≤ x ≤ 0.17), in addition to the network of screw-type dislocations, edge-type misfit dislocations were found generated with their density gradually increasing. For higher indium composition (0.18 ≤ x ≤ 0.20), all the interfacial dislocations are transformed into a network of straight misfit dislocations along the <10-10> directions leading to partially relaxation of the InGaN epilayer. The presence of dislocation half loops may be explained by slip on the basal plane, the formation of misfit dislocations are attributed to punch-out mechanism.

Oxygen evolution reaction is a momentous part of electrochemical energy storage and conversion devices such as rechargeable metal-air batteries. It is particularly urgent to develop low-cost and efficient electrocatalysts for oxygen evolution reactions. As a potential substitute for noble metal electrocatalysts, transition metal selenides are still challenging in improving the activity of oxygen evolution reaction and the research of reaction intermediates. In this study, a simple one-step solvothermal method was used to prepare a polymetallic compound carbon matrix composite (Co9Se8/Ni3Se4/Fe3O4@C) with a multilayered nanosheets structure. It exhibited good OER activity in an alkaline electrolyte solution with an overpotential of 268 mV at 10 mA/cm2 in an alkaline medium. Besides, this catalyst also showed excellent performance in the 24 hours stability test. The composite presents a multi-layer sheet structure, which effectively improves the contact between the active site and the electrolyte. The selenide formed by Ni and Co has a synergistic effect, Fe3O4 and Co9Se8 form a heterojunction structure, which can effectively improve the reaction activity by initiating the electronic coupling effect through the interface modification. In addition, carbon quantum dots have rich heteroatoms and electron transferability, which improves the electrochemical properties of the composites. This work provides a new strategy for the preparation of highly efficient OER electrocatalysts utilizing the multimetal synergistic effect.

In this work, a series of compounds in the CaO-½Er2O3-CoOz ternary oxide system were synthesized in air at 885℃ using high temperature solid-phase synthesis method. Phase boundary of each solid solution region in the CaO-½Er2O3-CoOz system was determined by X-ray powder diffraction technique. The phase diagram of the CaO-½Er2O3-CoOz system at 885℃ includes three series of ternary oxide solid solutions : (Ca3-xErx)Co4O9-z (0≤x≤0.9), (Ca3-xErx)Co2O6-z (0≤x≤1.25) and (Er1-xCax)CoO3-z (0≤x≤0.33). Four three-phase regions and five solid solution tie-line regions were obtained. The structure of perovskite solid solution (Ca3-xErx)Co2O6-z has been analyzed by Rietveld refinements. With the increase of Er content, the cell parameters of (Ca3-xErx)Co2O6-z exhibit an decreasing trend in a and b directions and an increasing trend in c direction.

Improving the quality of natural water purification is one of the priority areas in the research of scientific communities in the field of ecology. At the same time, the task is to achieve optimal efficiency at a low cost of the technological process. The solution in this case is the use of materials necessary for cleaning, in particular, sorbents from natural raw materials, including agricultural waste. At present, a sufficient number of research results have been published confirming the effectiveness of the sorbent from biochar of various agricultural wastes, as well as from rice straw biochar. This article proposes an innovative method for modifying biochar from rice straw, which allows the use of the material as a sorbent with a disinfecting effect. The method consists in processing biochar in a process activation apparatus (PAP) in a solution of silver nitrate with the release in the form of a carbon nanomaterial with attached metallic silver ions on the surface of biochar particles. Rice straw biochar was mixed in distilled water with silver nitrate AgNO3 and placed in the AAP in a replaceable insert with ferromagnetic particles that have a magnetostrictive effect under the influence of an electromagnetic field. Next, the contact of biochar impregnated with a solution of silver nitrate and ferromagnetic particles was carried out for 2 minutes under electromagnetic influence, after which the treated sample was dried in an oven for 4 hours at t=105ºС, followed by calcination in a muffle furnace at 450ºС for 3 hours. The resulting silver-containing sorbent was subjected to a physicochemical analysis of its properties, photographs of electron microscopy were also obtained, and a bacteriological analysis of the effectiveness of the sorbent on natural water was carried out. According to the results of the analyzes, the silver-containing sorbent is a mesoporous nanomaterial with an average mesopore diameter for desorption of 196 Å, a relative volume of pores with a diameter of up to 900 Å 0.034 cm³/g,, specific surface 7.45 m²/g and a content of metallic silver ions on the surface of the sorbent particles of (Ag) 16.7%, oxygen (O) 54.9%, unexpectedly (С) 13.7%, silicon (Si) 8.1%. Laboratory studies for the bacteriological analysis of natural water consisted in the sorption processing of the selected samples in the carbonization mode, followed by sedimentation after the introduction of the reagent (a mixture of coagulant and flocculant). The analysis was carried out on three indicators - total microbial count (TMC), total coliform bacteria (TCB) and thermotolerant coliform bacteria (TCB). According to the research results, the sorbent showed its disinfecting properties and confirmed its high efficiency (90,48%-100%).

Photocatalytic technology based on specific band structure of semiconductors offers a promising way to solve the urgent energy and environmental issues in modern society. In particular, hydrogen production from water splitting over semiconductor photocatalysts attracts great attention owing to the clean source and application of energy, which highly depends on the performance of photocatalysts. Among the various photocatalysts, TiO2 has been intensively investigated and used extensively due to its outstanding photocatalytic activity, high chemical stability, non-toxicity and low cost. However, pure TiO2 has a wide band gap of approximately 3.2 eV, which limits its photocatalytic activity for water splitting to generate hydrogen only under ultraviolet light, excluding most of the inexhaustible sunlight for human beings. Fortunately, the band gap of semiconductors can be manipulated, in which introducing oxygen defects is one of the most effective measures to narrow the band gap of titanium oxides. This review starts out by the fundamentals of photocatalytic water splitting for hydrogen production over TiO2, discusses the latest progress in this field, and summarizes the various methods and strategies to induce oxygen defects in TiO2 crystals. Then, the next section outlines the modification approaches of oxygen-deficient titanium oxide (TiO2-δ) to further improve its photocatalytic performance. Finally, a brief summary and outlook of the researches on TiO2-δ photocatalysts for water splitting to produce hydrogen were presented.

In this paper, through high-temperature tensile tests of 55NiCrMoV7 steel, the high-temperature fracture behavior, microstructure evolution and carbide distribution characteristics of both thermal-mechanical coupling zone (fracture zone) and thermal stress zone (clamping zone) at different temperatures were studied. Intrinsic relationship between high temperature fracture and carbides types, distribution and size were revealed and evolution mechanism of microstructure near cracks in 55NiCrMoV7 hot-working die steel during high temperature deformation was clarified. Samples were stretched at different temperatures from 25 °C to 700 °C, and microscopic examinations were carried out by using SEM and TEM. The results showed that: With the increase of temperature, tensile strength and yield strength decreased, elongation and reduction of area increased, and fracture mode changed from brittle fracture to ductile fracture by transition temperature at about 400℃. During high temperature deformation, the grain dislocation density decreased, the tempered martensite decomposed, recovered, recrystallized, and then grain grew. M7C3 and M23C6 carbides precipitated and grew along the grain boundary, and a small amount of fine granular MC carbides were dispersed in the grain. The work done by the external force on the deformation zone would cause the temperature of it to be higher than tensile temperature, which provides thermodynamic conditions for the re-dissolution of small carbides near the fracture zone and the grain growth of large carbides, resulting in the decrease of small carbides and increase of large carbides in thermal-mechanical coupling zone.

In this study various samples were fabricated by increasing the amount of CNT from 0% to 5%. The bulk mechanical properties of the samples were measured using DMA. Alternatively, the local mechanical properties were assessed using nanoindentation technique. There is a clear trend that the behavior of the material is dependent of carbon fillers before, during and after percolation threshold. The bulk mechanical properties were reduced after the percolation threshold due to CNT agglomeration. Then the samples were exposed to acid solution for one week and one month. Regardless the amount of CNT in the matrix, there is always a gradient of properties from the skin to the core of the sample. There is a net reduction of in physical properties. However, the level of degradation was a dependent of the amount of CNT in the host polymer. At higher concentration the CNTs behave as a barrier. However due to the formation of porosity around the CNT agglomerates, the acid diffusion encounters preferential path ways. . Both techniques lead to the same observation..

Considering the current energy environment, both efficient and environmentally friendly solutions have to be developed for building construction. Bio-based building materials offer new perspectives through their insulating and natural humidity regulation capacities. Nevertheless, these materials are as complex as they are promising and grey areas still remain regarding their behavior. Their water sorption and desorption curves recorded in experimental work demonstrate a hysteresis phenomenon and, although plausible hypotheses have been formulated in the literature, there is currently no consensus on its causes. Furthermore, it is important to emphasize that no reference considers the hydrophilic nature of the resource. Yet this is a specificity of raw material coming from the plant world. In this context, this paper explores the microstructure and chemical composition of plant aggregates to propose a new explanation for the hysteresis. It is based on recent work demonstrating the existence of differentiated hydrogen bonds between the water sorption and desorption phase in cellulose. Obviously, hysteresis also has an origin at the molecular scale. Lastly, the hypothesis put forward here is supported by the swelling of bio-based materials that has been observed at high relative humidity and this study aims to identify a link between the mechanical (swelling/shrinking) of bio-based materials and their hygroscopic behavior. This leads to a better understanding of the hydro-mechanical coupling of these materials.

Synthesis of ZSM-5 zeolite from OSDA-free systems has been a very interesting alternative method because it can avoid the usage of organic templates and consequent calcination step. However, in opened reports, organic substance such as alcohol is more or less involved. In the present work, a calcined commercial ZSM-5 zeolite was used as a seed, sodium aluminate as an aluminum source, silica sol as a silicon source, which ensures that there is no any organics (template) in the synthesis system, and polycrystalline ZSM-5 aggregates consisting of rod-like nanocrystals are successfully prepared in a completely OSDA-free system. The effects of seed (chemical component, dosage) and crystallization conditions on the synthesis of ZSM-5 were systematically investigated. The results show that highly crystallinity ZSM-5 aggregate consisting of primary nano-sized crystals with a size of less than 100 nm can be yielded from a gel precursor with 5.6 wt.% seed after hydrothermal treatment for 48 h. The results also shows that the chemical composition of the seeds had little effect on the topological structure and pore structure of the synthesized samples, but the seed with a low Si/Al ratio is more conducive to the rapid crystallization of zeolite and to the improvement of the acid, especially the strong acid centers of the catalyst.

The modern material design aims to achieve multifunctionality by integrating structures in a diverse range, resulting in simple materials with embedded functions. Biological materials and organisms are typical examples of this concept, where complex functionalities are achieved through a limited material base. This review highlights the inspiration from multifunctional organisms and materials in nature, emphasizing their structural and functional integration. In particular, we discuss complex hierarchical architectures ranging from the nanoscale to the macroscale, to achieve multifunctional properties such as extreme pressure, impact and wear resistance, shape memory and self-healing, adhesiveness and anti-fouling, sensing-actuating and sensing-camouflage, and extreme environmental survival. These strategies of integrating structure and function are critical for promoting innovations and breakthroughs in the modern engineering materials and applications.

In nowadays, the synthesis of new composite nanomaterials based on graphene oxide (GO) modified with cellulose and its derivatives, as well as nanocellulose, is an important direction and contributes to solve many problems in various fields such as: nanotechnology, information technology, medicine, high-dielectric materials and nanoelectronics. In this work, for the first time, for the production of GO and its membrane with carboxymethylcellulose (CMC), local Kazakhstan “Ognevsky” graphite was used as the initial raw material. In this regard, the preparation of nanocomposites of GO modified with cellulose derivatives, including CMC, attracts great interest from scientists and expands its field of practical application due to the amazing changes of physicochemical properties. In the work, the GO obtained by the Hummers method was modified by CMC, with following study of its physicochemical, structural and electrical characteristics. The GO/CMC membrane was synthesized by mixing 1% GO with crushed solid mass of CMC (0.03 g; 0.06 g; 0.15 g) and then was processed by ultrasound. The surface morphology of the GO/CMC membrane were studied using Scanning electron microscopy (SEM). It has been established that with an increasing in the mass of CMC (0.03 g; 0.06 g; 0.15 g), polymerization of CMC occurs on the surface of GO nanosheets. Cross-sectional micrographs of GO/CMC show the formation of sandwich-like layered structures.

: The stability of semiconductor catalysts is a very important property in the field of catalytic reactions. Materials necessitate resistance to mechanical abrasion and chemical erosion for better overall performance. In this work, high crystallinity BiOCl nanosheets were prepared by a simple hydrothermal method. The photocatalysts demonstrate full UV light absorption ability and excellent photocatalytic norfloxacin degradation performance. 84 % of highly toxic norfloxacin were photocatalytically eliminated within 180 min. The internal structure and surface chemical state of BiOCl were analyzed by SEM, TEM, Raman, FTIR, UV-vis, XPS, and other techniques. Such high crystallinity makes BiOCl molecules closely arranged and the molecular chains strongly connected, thus exhibiting a high level of photocatalytic stability and recyclability.

A developing energy-saving approach of cold sintering in a pure aqueous medium was applied to the preparation of α-Al2O3 ceramics and performed on spark plasma sintering equipment. The initial γ-Al(OH)3 and γ-AlOOH powders and the cold-sintered ceramics were studied by X-ray diffraction analysis, infrared spectroscopy, thermal analysis, and scanning electron microscopy to reveal the chemical and structural transformations they experienced during the cold sintering. At 450°C and 70 MPa, initial γ-AlOOH transformed into a fragile α-Al2O3 material. Porous α-Al2O3 ceramics with about 60% porosity was obtained after cold sintering of γ-Al(OH)3 in the same conditions combined with subsequent annealing at 1250°C for 3 h. The role of water molecules in the studied processes was considered as the enhancement of structural mobility in the cold-sintered material due to its reversible hydroxylation similar to earlier investigated supercritical water action on the precursors during α-Al2O3 formation. Further improvement of the cold sintering setup and regimens would open prospects in α-Al2O3 ceramics manufacturing by an ecologically benign route.

Abstract: Bulgaria is famous for its oil-bearing rose. R. damascena Mill. and R. alba L. are mainly cultivated in the country, but a recent survey of industrial plantations in 2020 revealed that R. centifolia L. and hybrids of R. damascena Mill. x R. gallica L. are also common in the rose valley. Although their essential oil cannot be compared in quality with the classic, they are preferred by farmers with high yields of flowers and resistance to diseases and pests. All these roses are also used to produce rose water and extracts. The aim of this investigation was to compare the yield and chromatographic fingerprints of seven rose oils and hydrosols produced in Bulgaria. The quantitative composition of the main components of the oils was compared with the norms of the world standard. Our study showed that the yield of essential oil from these roses was in the range of 0.015 - 0.048%. The main group in the chemical composition is terpene alcohols, which vary in the range: geraniol (17.60 - 34.02 %), citronellol (8.38 - 28.7 %), and nerol (4.8 - 11.90 %), but with a different ratio. Hydrocarbons are represented by saturated aliphatic homologs with an odd number of carbon atoms, the main ones being: nonadecane (8.10 - 22.67 %), heneicosane (4.37 - 10.21 %), heptadecane (1.07 - 2.98 %) and triclosan (0.81 - 5.90 %). In contrast, the chemical profile of the hydrosols was performed by phenyl ethyl alcohol (27.45 - 69.88 %), geraniol (13.72 - 28.67 %), and citronelol+nerol (4.56 - 17.37 %). The results show that the presence of plantations with a genotype different from that of R. damascena implies differences in the quality of rose oils and hydrosols. This predetermines their properties of use.

Demand for development of the convergence industry, research studies on electrical conductivity, thermal characteristics, semiconductors, motors, and batteries using special materials have come to the fore. Meanwhile, molybdenum (Mo) exhibits relatively small inorganic qualities, and the thermal conductivity rate is applied to various fields. In this study, in-depth characteristics were considered regarding the concentration of thermal characteristics, IR car terminal characteristics, and IR ve-hicles. This study calculated each phase temperature of the molybdenum sputtered specimens in the steady state according to the heat transfer theory. When the molybdenum-sputtered fabric’s metal layer pointed to the outside air, the heat transfer rate (Q) was high at 5748.3W, In contrast, if the molybdenum sputtered film’s metal layer of the pointed toward the heat source, the heat transfer rate (Q) was low at 187.1W. As a result of measuring the IR transmittance, the infrared transmit-tance of the molybdenum sputtering-treated sample was significantly reduced compared to the untreated sample. In the case of untreated samples, the transmittance ranged from 92.7 to 42.0%. When only the cross part was treated with molybdenum sputtering and the molybdenum surface was directed toward the IR irradiator, the IR transmittance was 66.8~0.7%. It is believed that the molybdenum sputtering polyamide samples produced in this study can be applied to multifunc-tional military wear, biosignal detection sensors, semiconductor products, batteries, etc., by utilizing excellent electrical properties, stealth functions, IR blocking properties, and lightness for infrared thermal imaging detectors.

In this study the formation of thin-film barrier coatings based on a highly-conducting Bi1.60Er0.4O3 (EDB) solid electrolyte on supporting Ce0.8Sm0.2O1.9 (SDC) electrolyte substrates is implemented for the first time using electrophoretic deposition (EPD). Electrokinetic properties of EDB-based suspensions in a non-aqueous dispersion medium of isopropanol modified with small additions of polyethyleneimine (PEI, 0.26 g/L) and acetylacetone (0.15 g/L), as well as in a mixed isopropanol/acetylacetone (70/30 vol.%) medium are studied. The dependences of the thickness of EDB coatings on voltage and deposition time are obtained using deposition on a model Ni-foil electrode. Preliminary synthesis of a conductive polypyrrole (PPy) polymer film is used to create surface conductivity of non-conductive SDC substrates. The efficiency of using a modified dispersion medium based on isopropanol to obtain a continuous EDB coating 12 μm thick, sintered at a temperature of 850 °C for 5 h, is shown. The microstructure and morphology of the surface of the EDB coating are studied. Pt/SDC/EDB/Pt cell is used to characterize the coating conductivity. The EPD method is shown to be promising for the formation of barrier coatings based on doped bismuth oxide. The developed method can be used for creating cathode barrier layers in SOFC technology.

This work presents an LC resonant passive wireless gas sensor with a novel structure designed to mitigate the negative impact of substrate. The LC sensor antenna with the new structure and the reader antenna were designed and optimized utilizing HFSS software to improve the transfer efficiency. The superiority of the designed structure compared with the general ones is highlighted and verified. The change in the substrate capacitance has essentially no interference with the parameters to be measured of the LC sensor. The sensor with the new structure was prepared by combining etching and sputtering methods. The structure of the ZnO nanowires (NWs) was characterized to confirm their high purity and wurtzite crystal structure. The LC gas sensors demonstrated excellent wireless sensing performance including a low detection limit of 0.5 ppm NO2, high response of 1.058 and outstanding stability at 180 °C. The developed new sensor structure not only prevented interference from the substrate during gas sensing testing, but also expanded the choice of sensor substrates, playing a critical role in the development of sensors based on LC resonance principle.

This study investigates the Hagen–Poiseuille pipe flow of viscoplastic fluids, focusing on analytical predictions of concrete pumping using the shear-stress-dependent parabolic model. Research highlights encompass solving the steady laminar pipe flow for viscoplastic fluids described by the parabolic model, extending analytical studies to a nonlinear rheological model with easily accessible experimental parameters, presenting detailed results for the two-fluid parabolic model, and introducing computational apps implementing theoretical findings. The parabolic model outperforms linear models, such as the Bingham model, in accuracy by accounting for the nonlinearity in the shear stress and shear rate relations. The influence of rheological parameters on these relations is analyzed, and their versatility is demonstrated by a Wolfram Mathematica-based application program. This approach is adaptable for other models with shear stress as the independent variable, offering valuable insights into viscoplastic fluid flows.

Cyclic olefin copolymer (COC) is a novel type of thermoplastic polymer gaining the attention of the scientific community in electronic, optoelectronic, biomedicine and packaging applications. Despite the benefits in the use of COC like undoubted optical transparency, chemical stability, good water-vapor barrier and biocompatibility, its original hydrophobicity restricts its wider applicability and optimization of its performances. Presently, we report on the optical, and morphological properties of the films of COC covered with Ti in selected areas. The layer of Ti on COC was deposited by pulsed lased deposition processing. The Ti/COC film was characterized by UV-Vis spectroscopy indicating that its transmittance in the visible region decreased by about 20% with respect to the pristine polymer. The quality of the deposited Ti was assessed with the morphology by scanning electron (SEM) and atomic force microscopies (AFM). The modification of the wettability was observed by the sessile drop method indicating a reduction of the native hydrophilicity.

Organic light-emitting diodes (OLEDs) are energy-efficient; however, the coordinating ligand can affect their stability. Sky-blue phosphorescent Pt(II) complexes with a C^N chelate, fluorinated-dbi (dbi = [1-(2,4-diisopropyldibenzo[b,d]furan-3-yl)-2-phenyl-1H-imidazole]), and acetylactonate (acac)(1)/picolinate (pic)(2) ancillary ligands were synthesized. The molecular structures were characterized using various spectroscopic methods. The Pt(II) coordination sphere in 2 exhibited a distorted square-planar geometry, with several intra- and inter-molecular interactions involving Cπ⋯H/Cπ⋯Cπ stacking. Complex 1 emitted bright sky-blue light (λmax = 485 nm) with a moderate photoluminescent quantum efficiency of 0.37 and short decay time (6.1 µs) compared to those of 2. Time-dependent density functional theory calculations suggested that the electronic transition of 1 arose from ligand(C^N)-centered π–π* transitions combined with metal-to-ligand charge transfer transitions (MLCT), whereas that of 2 arose from MLCT and ligand(C^N)-to-ligand(pic) charge transfer (LLCT), with minimal contribution from the C^N chelate to the lowest unoccupied molecular orbital. Multi-layered phosphorescent OLEDs using 1 as a dopant and a mixed host, 3,3-di(9H-carbazol-9-yl)-1,1-biphenyl:3-di(9H-carbazol-9-yl)-1,1-biphenyl (mCBP)/9-(3’-carbazol-9-yl-5-cyano-biphenyl-3-yl)-9H-carbazole-3-carbonitrile (CNmCBPCN) were successfully fabricated. At a 10% doping of 1, a current efficiency of 13.6 cd A−1 and external quantum efficiency of 8.4 % at 100 cd m−2 were achieved. These results show that the ancillary ligand in phosphorescent Pt(II) complexes must be considered.

In this paper we propose a simple procedure to obtain multi-walled carbon nanotubes (MWCNT) decorated with TiO₂-Ag nanoparticles (MWCNT-TiO₂-Ag). MWCNT were decorated with TiO2-Ag via combined functionalisation with -OH and –COOH groups and polymer wrapping technique using poly(allylamine hydrochloride) (PAH). TiO₂ modified Ag nanoparticles were synthesized through Pechini method using mixture of acetylacetonate-modified titanium (IV) isopropoxide with silver nitrate (the Ag+/Ti4+ atomic ratio, is 0.5, 1,0, 1.5, 2.0 and 2.5 %, respectively) and the L(+)-ascorbic acid, as reducing agents. XRD analysis revealed the formation of nanocomposite containing CNT, TiO₂ (anatase and rutile) and Ag. By SEM was evidenced the presence of the nanoparticles on MWCNT surface. The increases of the ratio between Ag⁺ and Ti⁴⁺ decrease the band gap energy of the samples. In Raman spectra the characteristic vibration of the TiO₂, Ag and C atoms of graphite are identified. The photocatalytic activity of the MWCNT-TiO₂-Ag nanocomposite was assessed by examining the degradation of Allura red (E129) aqueous solution under UV irradiation. The dye photodegradation process follows a pseudo – first – order kinetic with respect to the Langmuir – Hinshelwood reaction mechanism.

The use of interleaving material with viscoelastic properties is one of the most effective solutions to improve the damping capacity of CFRP laminates. Improving composite damping without threatening mechanical performance is challenging and the use of nanomaterials should lead to the target. In this paper, the effect of a nanostructured interlayer based on Graphite Nanoplatelets (GNPs) on the damping capacity and fracture toughness of CFRP laminates has been investigated. High-content GNP/Epoxy (70wt/30wt) coating was sprayed on the surface of CF/Epoxy prepregs at two different areal weight (10 and 40 g/m2) and incorporated at the middle-plane of a CFRP laminate. The effect of the GNP areal weight on viscoelastic and the mechanical behaviour of the laminates was investigated. Coupons with low-areal weight GNP interlayer showed a 25% increase in damping capacity with a trivial reduction of the elastic modulus. Moreover, a reduction in interlaminar shear strength (ILSS) and fracture toughness (both mode I and mode II) was observed in the composites with GNPs interlayer. GNPs alignment and degree of compaction reached during process were found as key parameters on material performances. By increasing the areal weight a mitigation on the mechanical performances drop was achieved (-15%).

Rapid, accurate, and convenient diagnosis is essential for effective disease management. Various detection methods, such as enzyme-linked immunosorbent assay, have been extensively used, with lateral flow immunoassay (LFIA) recently emerging as a major diagnostic tool. Nanoparticles (NPs) with characteristic optical properties are used as probes for LFIA, and researchers have presented various types of optical NPs with modified optical properties. Herein, we review literature on LFIA with optical NPs for the detection of specific targets in the context of diagnostics.

The present work is focused on functionalizing Montmorillonite (Mt) with poly dimethyl siloxane (PDMS) to develop a hybrid membrane reactor for the removal of Co (II) and Ni (II) ions from model wastewater samples. The specific surface area of the novel material was found to be 444 m2 /g. X-Ray Diffraction (XRD) and Fourier Transform Infra-Red (FTIR) spectra reveal the formation of exfoliated composite material. The efficiency of this membrane material was determined by subjecting it to continuous filtration experiments. It was able to remove 50% of Co (II) and 75% of Ni (II) ions, respectively, in one cycle of filtration in less than three minutes of operation with a permeate flux rate of 675 L/m2/H and 975 L/m2/H respectively, for both the ions.

In this study, we investigated the inhibiting effect of Dioscorea spp leaf extracts on the corrosion of mild steel in selected media using the weight loss method. The mild steel samples were pre-weighed and immersed in NaOH, NaCl and H₂SO₄ solutions respectively containing the leaf extracts, with the control samples immersed in solutions of the media containing no extract. The samples were allowed to stand for 672 hours, with a set of samples from each environment withdrawn at intervals of 168 hours for corrosion characterization. The results obtained from all the environments indicate that the corrosion rate increased as concentrations of Dioscorea spp increased. Results also confirmed that the extract was an effective and excellent inhibitor in the alkaline, salt, and acidic media. Conclusively it was proven that the higher concentration of Dioscorea spp leaf extracts in the media had the best inhibition characteristic on the mild steel in the selected environments. The results show good potential for application in manufacturing industries. The microstructure analysis of the various test coupons in the test media should be carried out to reveal the influence of adding the leaf extracts to the stimulated media on the grain structure distribution of the mild steel.

Lead-based ternary chalcogenide thin films of the (PbTe)1-x(PbS)x system were obtained by plasma-enhanced chemical vapor deposition technique (PECVD) under conditions of a nonequilibrium low-temperature argon plasma of an RF discharge (40.68 MHz) at a reduced pressure (0.01 Torr). High-purity elements were directly used as starting materials – Pb, S and Te. Plasma-chemical synthesis was carried out on the surface of of c-sapphire and silicon substrate. The physicochemical properties of the films were studied by various analytical methods. The dependence of the Seebeck coefficient, resistivity, and power factor on the structural properties and composition has been studied. The thermoelectric characteristics were found to be dependent on the film composition. Upon the selection of optimal sulfur concentration one can increase the power factor as compared to single phase PbS ot PbTe films.

β-Ga2O3 is a well-known semiconductor material for power devices and other applications. Recently, β-Ga2O3 has also been reported as a scintillator material with a light yield of approximately 8400 ph./MeV, scintillation decay time of &lt;1 μs, and density of 6.44 g/cm3. In this study, 2-inch diameter β-Ga2O3 single crystals were prepared by oxide crystal growth using the cold crucible (OCCC) method under various oxygen partial pressures. In the OCCC method, as in the cold crucible method, a high frequency is applied directly to the oxide materials, which are heated and melted, and the melt is held by the outermost solid material itself that is cooled by water using a copper hearth. In the OCCC method, crystal growth is performed while rotating the seed crystal, as in the Czochralski method, to increase the crystal diameter. The optical properties and radiation responses of the crystals grown under various oxygen partial pressures were evaluated.

Liquid crystal elastomers (LCEs) are shape morphing materials whose large and reversible shape transformation results from the coupling between the mobile anisotropic properties of liquid crystal (LC) units and the rubber elastic of polymer networks. Their shape changing behaviors under the stimuli are largely directed by LC orientations, and therefore various strategies have been developed to spatially modulate the LC alignments. But most of the methods suffer from complex fabrication technologies or intrinsic limitations in applicability. To address this issue, programmable complex shape changes in some types of LCEs, such as polysiloxane side-chain LCEs or thiol-acrylate main-chain LCEs, etc, have been achieved by using a mechanical alignment programming process coupled with two-step crosslinking. Here, we report a polysiloxane main-chain LCE with programmable 2D and 3D shape changing performances achieved by mechanically programming the polydomain LCE between the two crosslinking steps. The resulting LCEs exhibited reversible thermal induced shape transformation between the initial and programmed shapes due to the two-way memory between the first network structure and the second network structure. Our work would be potential for expanding the applications of LCE materials in actuators, soft robotics and smart structures where arbitrary and easily programmed shape morphings are needed.

In contemporary science and technology, photonic sensors are essential. They may be made to be extremely resistant to some physical parameters while also being extremely sensitive to other physical variables. Most photonic sensors may be incorporated on chips and operate with CMOS technology, making them suitable for use as extremely sensitive, compact, and affordable sensors. Photonic sensors can detect electromagnetic (EM) wave changes and convert them into an electric signal due to the photoelectric effect. Depending on the requirements, scientists have found ways to develop photonic sensors based on several interesting platforms. In this work, we extensively reviewed the most generally utilized photonic sensors for detecting vital environmental parameters and personal healthcare. These sensing systems include optical waveguides, optical fibers, plasmonics, metasurfaces, and photonic crystals. Various aspects of light are used to investigate photonic sensors' transmission or reflection spectra. In general, resonant cavity or grating-based sensor configurations that work on wavelength interrogation methods are preferred, so these sensor types are mostly presented. We believe this paper will provide insight into the novel types of available photonic sensors.

The aim of the study was to find the effect of polyethylene (PE) coatings on the short-circuit current of silicon photovoltaic cells covered with glass, in order to improve the short-circuit current of the cells. Various combinations of PE films (thicknesses ranging from 9 to 23 µm, number of layers ranging from 2 to 6) with glasses (greenhouse, float, optiwhite and acrylic glass) were investigated. The best current gain of 4.05% was achieved for the coating combining a 1.5 mm-thick acrylic glass with 2 × 12 µm-thick PE films. This effect can be related to the formation of an array of micro-wrinkles and micrometer-sized air bubbles with a diameter of 50 to 600 µm in the films, which serve as micro-lenses and enhance light trapping.

Mn-promoted bulk iron catalysts with high specific surface area (82-211 m2.g-1) were synthesized by coprecipitation followed by drying under supercritical conditions. The catalysts were tested in the CO2 hydrogenation reaction. The Mn-promoted iron catalysts showed better textural properties than the bare Fe2O3 catalyst, allowing better dispersion of the active phase, easier reduction of iron oxide, better carburization of iron oxides and higher catalytic activity than the bare Fe2O3 catalyst. The best activity results were obtained by catalyst promotion with a very low amount of Mn (Mn/Fe ratio of 0.05). Upon steady-state conditions (T=340 ºC, total pressure of 20 bar and H2/CO2=3), this catalyst showed high CO2 conversion (44.2%) and selectivity to C2-C4 hydrocarbons (68%, olefin to paraffin ratio of 0.54), while the selectivity to C5+ hydrocarbons, CH4 and CO was about 3.2, 38.5 and 5%, respectively. A close correlation was found between catalyst textural properties and CO2 conversion. The most active MnFe-0.05 catalyst shows high stability during 72 h of reaction related to low amount of soft coke formation and catalyst activation through the formation of χ-Fe5C2 phase during the on-stream reaction.

Recent advances in synthetic membranes allow their use in fields as diverse as food and agriculture, biotechnology, industrial wastewater treatment, and potable water production. Among the newly developed technologies, nanofiltration for liquids and more particularly for desalination of seawater or saline aquifers are actively pursued. However, current solid-state membranes performance is limited, which calls for the development of novel formulations for membranes offering both high permeability (ion and water flux) and ion differentiation (selectivity), usually considered antagonist features. We report the development of hybrid nanoporous membranes made of solid-state polymeric carbonate track-etched (PCTE) thin films in which biological ion channels such as Gramicidin A (GA), alpha-hemolysin (α-HL), and outer-membrane protein F (OmpF) aquaporin are confined and graphene oxide (GO) conjugated cobalt ion selective binding peptide motifs (Copep) are adsorbed, referring as bioinspired and biomimetic approaches, respectively. These solid-state nanoporous membranes are attracting widespread attention since they offer scalability, mechanical robustness, selectivity, controlled pore dimension and shape, for water sustainability. The ion permeability, ion diffusion coefficient and selective ion recognition are evaluated via nanofiltration, cell diffusion kinetics, and UV-Visible absorption spectroscopy to gain insights into the role of key performance parameters including effective ion confinement in track-etched pores, rich surface chemistry, and peptide-induced channel for selective ion transport. These findings provide new avenues for artificial ion channels by synergistic combination of eco-friendly material design such as GO enabled by bio-molecular recognition chemistry.

Wearable thermoelectric generators (w-TEGs) convert thermal energy into electrical energy to realize self-powering of intelligent electronic devices, thus reducing the burden of battery replacement and charging, and improving the usage time and efficiency of electronic devices. Through finite element simulation, this study successfully designed high-performance thermoelectric generator and made it into wearable thermoelectric module by adopting “rigid device - flexible connection” method. It was found that higher convective heat transfer coefficient on cold-end leads to larger effective temperature difference and better power generation performance of device in typical wearable scenario. Meanwhile, at same convective heat transfer coefficient on the cold-end, longer TE leg length leads to larger temperature difference established at both ends of device, larger device output power and open-circuit voltage. However, when the convective heat transfer coefficient increases to a certain level, optimization effect of increasing TE leg length on device power generation performance will gradually diminish. For devices with fixed temperature difference between two ends, longer TE leg length leads to higher resistance of TEG, resulting in lower device output power but slight increase in open-circuit voltage. Finally, sixteen 16×4×2 mm2 TEGs (L=1.38 mm, W=0.6 mm) and two modules were fabricated and tested. At hot end temperature Th=33 ℃ and cold end temperature Tc=30 ℃, the actual maximum output power Pout of TEG is about 0.2 mW, and the actual maximum output power Pout of TEG module is about 1.602 mW, which is highly consistent with the simulated value. This work brings great convenience to research and development of wearable thermoelectric modules and provides new, environmentally friendly and efficient power solution for wearable devices.

Luminescent properties of epitaxial Cu2O thin films were studied in 10-300 K temperature range and compared with luminescent properties of Cu2O single crystals. Cu2O thin films were deposited epitaxially by the electrodeposition method on either Cu or Ag substrates at different processing parameters, which determined the epitaxial orientation relationships and encapsulated surface. Cu2O (100) and (111) single crystal samples were cut from a crystal rod grown by the floating zone method. Luminescence spectra of thin films contain the same emission bands as single crystals around 720, 810 and 910 nm, characterizing VO2+, VO+ and VCu defects, correspondingly. Additional emission bands, whose origin is under discussion, are observed around 650-680 nm, while the exciton features are negligibly small. The relative mutual contribution of the emission bands varies depending on the particular thin film sample. Existence of the domains of crystallites with different orientation determines the polarization of luminescence. PL of both Cu2O thin films and single crystals is characterized with negative thermal quenching in the low temperature region, the reason of this phenomenon is discussed.