The purpose of this study is to propose a consecutive manufacturing process system to secure the productivity of excellent STKN540B steel tube in the respect of economy and safety as the supporting material for mega structures such as building, bridge and ship. The components of consecutive manufacturing are press-bending, orbital auto welding and steel tube correction. By using STKN540B a high-strength steel material with low yield point that requires a special manufacturing process unlike other steel materials, an actual tube manufacturing is carried out at each stage in this experimental study. With this, the quality of steel tube and the efficiency of the manufacturing process are analyzed to draw out some points to improve in the future.

In view of the limitations of the existing optimization method of suspender cable force, in order to improve the stress of suspender under completion state and avoid frequent adjustment of cable force and grid beam elevation during construction, a new method of cable force optimization is proposed. The article takes the longest large span arch bridge in the world, Pingnan Third Bridge, a Concrete-filled steel tube (CFST) arch bridge with a span of 575m as the engineering background combined with the finite element analysis and multi-objective optimization method. One cable force optimization method that suspender “Real-time correction during construction, in the process variable optimal and results reliable” during panel girder lifting of long span CFST arch bridges is clarified. Taking the panel girder weight and displacement during the construction as parameter variables, the displacement and unevenness of the panel girder under completion state as constraint conditions, the displacement and cable force during the hoisting construction as the objective equation, through the optimization of the objective equation, the suspender cable force and dis-placement of each hoisting section are calculated. The results show that it is feasible to introduce the optimization theory into the cable force optimization when lifting the panel girder. the segment displacement variation is minimized to meet the destination. The cable force distributed evenly under completion state of the bridge that further making sure the completion state satisfies the requirements. No repeating iteration is needed, thus avoiding cumberso me calculation, getting cable force once. With higher optimization efficiency and better effects, the method provides high value for the cable force calculation of same type bridge suspender construction and for guiding construction.

Plate fin-tube heat exchangers are widely used in air conditioning and refrigeration systems and other industry fields. Various errors made in the manufacturing process can result in the formation of an air gap between the tube and fin. Several numerical simulations were carried out for a symmetric section of plate fin-tube heat exchanger to study the influence of air gap on heat transfer under periodic flow conditions. Different locations and sizes of an air gap spanning 1/2 circumference of the tube were considered for the range of airflow velocities. Velocity and temperature fields for cases with air gap were compared with ideal thermal contact cases. Blocking of heat flow by the gap leads to the reduction of heat transfer rate. Fin discontinuity in the front of the tube causes the smallest reduction of the heat transfer rate in comparison to the ideal tube-fin contact, especially for thin slits. The rear gap position is the worst in the smallest gap range. Therefore, reversing the flow direction can lead to up to a 15% heat transfer increase, if mainly the rear gaps are present. The introduction of a thin slit in the front of the tube leads to convective heat transfer enhancement, which should be further investigated.

Steam boiler has a significant role in the industrial sector. The failure in boiler tubes significantly reduces the availability of the plant. Furthermore, deposits on the inner tube wall contribute to such failure by changing the thermal resistance of the wall, which causes a significant increase in the tube wall's temperature and, consequently, lower allowable stress. The presented thermal-fluid model is developed for the water tube. The model is implemented using ANSYS FLUENT to estimate the wall maximum water tube wall temperature considering the deposits layer and then determine the minimum thickness of the tube wall via ASME standards to assure safe operation. The model is verified via a mesh independence test. The minimum tube thickness is recommended and justified given the thermo-mechanical performance of the water tubes at several operating loads of 50, 75, and 100 %. These loads are implemented by different convective heat transfer coefficients of flue gases under different deposit thicknesses, thermal conductivity, and flue gas temperature. The present work contributes to the literature by recommending the minimum thickness of the water wall tubes and highlighting the thermo-mechanical effect of the deposits on water tube resilience under different operating conditions.

Primary spontaneous pneumothorax (PSP) is a pleural disease that abruptly affects healthy adolescents and young adults, representing a common thoracic disorder in this age group. This study aimed to investigate the necessity of preoperative chest tube insertion in patients with PSP and to re-evaluate current clinical treatment approaches. A retrospective review of medical records was conducted for children and young adults aged 14–30 years, diagnosed with PSP and who underwent Video-assisted thoracoscopic surgery (VATS) between January 2016 and December 2022 at Wonju Severance Christian Hospital. Patients were retrospectively divided into two groups based on their initial treatment: chest tube insertion and non-chest tube insertion. Clinical data including demographics, treatment details, and outcomes were collected and compared. Total 128 cases of PSP were included in the study. The total length of hospital stay was significantly shorter in the non-chest tube group (p=0.000), which was attributed to the omission of pre-operative chest tube insertions. No significant differences were observed between the two groups in terms of postoperative complications or recurrence rates. In cases of young patients with PSP, omitting pre-operative chest tube insertion may be a viable option if the patient is scheduled for VATS.

Eustachian Tube Dysfunction is considered a common condition among ENT patients and requires careful history, clinical examination and appropriate investigations to obtain a diagnosis. The ETDQ-7 questionnaire is a useful tool to subjectively score severity of symptoms that are related to this pathology (Appendix A). This study aimed to adapt and validate the ETDQ-7 questionnaire in Greece to ensure correct and efficient use in the outpatient setting (Appendix B). The ETDQ-7 was translated into the Greek language following appropriate methodology. Data for the main study were collected from a sample of 75 Greek patients diagnosed with ETD as well as 25 patients that did not have ETD and who served as a control group. The participants completed the adapted ETDQ-7 questionnaire and underwent a clinical examination that was statistically correlated with their ETDQ-7 answers. Face and content validity were confirmed and the questionnaire was found easy to administer and to be completed by our patients. Test-retest reliability revealed similar internal consistency for the questions and good correlation between individual items and total score. Discriminative validity confirmed statistically significant difference between the two patient groups to ensure that the Greek version of ETDQ-7 is useful to confirm the diagnosis. The Greek version of the ETDQ-7 is safe and efficient to use among a variety of investigation methods for the diagnosis of ETD in the Greek speaking population.

Accurately monitoring insecticide resistance in target mosquito populations is important to combating malaria and other vector-borne diseases, and robust methods are key. The “WHO susceptibility bioassay” has been used for +60 years: mosquitoes of known physiological status are exposed to a discriminating concentration of insecticide. Several changes to the test procedures have been made historically which may seem minor but could impact bioassay results. The published test procedures and literature for this method were reviewed for methodological details. Areas where there was room for interpretation in the test procedures or where the test procedures were not being followed were assessed experimentally for impact on bioassay results: covering or uncovering of the tube end during exposure, number of mosquitoes per test unit, and mosquito age. Many publications do not cite the most recent test procedures, methodological details are reported which contradict the test procedures referenced or methodological details are not fully reported. As a result, the precise methodology is unclear. Experimental testing showed that using fewer than the recommended 15-30 mosquitoes per test unit significantly reduced mortality, covering the exposure tube had no effect, and using mosquitoes older than 2-5 days old increased mortality, particularly in the resistant strain. Recommendations are made for better reporting of experimental parameters.

The high environmental impact of conventional methods of cooling and heating has increased the need for renewable energy deployment for covering thermal loads. Towards that direction, the proposed system aims at offering an efficient solar powered alternative, coupling a zeolite-water adsorption chiller with a conventional vapor compression cycle. The system is designed to operate under intermittent heat supply of low-temperature solar thermal energy (<90 °C) provided by evacuated tube collectors. A prototype was developed and tested in cooling mode operation. The results of separate components testing showed that the adsorption chiller was operating efficiently, achieving a maximum coefficient of performance (COP) of 0.65. With respect to the combined performance of the system, evaluated on a typical week of summer in Athens, the maximum reported COP was approximately 0.575, mainly due to the lower driving temperatures at a range of 75 °C. The corresponding mean energy efficiency ratio (EER) obtained was 5.8.

Beginning with the discovery of the BRCA ovarian cancer susceptibility genes and subsequent detailed examination of risk reduction salpingo-oophorectomy (RRSO) specimens, a new paradigm of ovarian carcinogenesis has unfolded with attention to the distal fallopian tube. The primary focus has been an early cancer in the fallopian tube which is seen in virtually all incidentally discovered high-grade serous cancers in asymptomatic women. This high-frequency of tubal involvement in early serous cancer - serous tubal intraepithelial carcinoma or STIC - has galvanized attention to this organ as a primary source of this disease. However, an enduring mystery has been the relatively low frequency of STIC in fallopian tubes of women with advanced malignancy. This paradox, a high-frequency of tubal involvement early and a low-frequency late in the disease process has spurred interest in other potential sources, such as the ovarian surface or secondary Mullerian system. However, because essentially all high-grade serous carcinomas are linked by TP53 mutations, and because fallopian tubes frequently contain early serous proliferations (ESPs) with these mutations, attention has turned to the possibility that nonmalignant but TP53 mutated tubal epithelium could be responsible for an eventual malignancy. Recent data have shown evidence of lineage continuity between ESPs and concurrent serous carcinomas prompting the concept of "precursor escape". This creates a 2nd component of the paradigm by which cells from early lesions can escape the fallopian tube and undergo future malignant transformation later, emerging suddenly as widespread malignancy. This dualistic model thus explains the paradox and opens new questions pertaining to the challenge of both early detection and prevention of this lethal malignancy.

TiC–high Mn steel-bonded carbide with a cellular structure was designed and fabricated by powder metallurgy techniques using coarse and fine TiC particles as the hard phase. This preparation process was carefully investigated and optimized. The microstructure of the TiC steel-bonded carbide was observed using a scanning electron microscope. Results showed that there are two types of microstructures in the TiC steel-bonded carbide: the coarse-grained TiC and fine-grained TiC. The transverse rupture strength and impact toughness of the alloy reach maximum values 2231 MPa and 12.87 J/cm2, respectively when the starting weight ratio of MP-A (containing coarse TiC particles) to MP-B (containing fine TiC particles) is 60:40. Hence, this study serves as a feasible example of how to prepare a high-strength and high-toughness TiC–high Mn steel-bonded carbide.

Experimental quantification of retention factors related to post-fire strength as well as post-fire ductility of intentionally selected stainless steel grades applied in construction is the objective of research presented here. These steel grades are characterized by a two-phase austenitic-ferritic microstructure of the duplex type. In this context two mutually corresponding chromium-nickel-molybdenum steel grades have been subjected to analysis, namely X2CrNiMoN22-5-3 steel belonging to the standard duplex group (DSS 22% Cr) and X2CrMnNiN21-5-1 steel belonging to the lean duplex group (LDSS). The similarities and differences in the mechanical properties exhibited by these steel grades after effective cooling, following more or less prolonged simulated fire action conforming to several development scenarios, have been identified and indicated. The resistance of given steel grade to permanent structural changes induced by the heating program proved to be the critical factor determining these properties and resulting in many cases in increased susceptibility to brittle fracture.

In this paper is proposed an analytical technique which can be used to obtain the forced response of a cantilevered tube conveying fluid. Considering the pipe subjected to an arbitrary harmonic force either distributed or concentrated, an analytical solution is found using Green’s function method. The solution obtained of the closed form satisfies the differential equations in a classical sense. The presented method giving the exact solutions is more precise than the classical eigenfunction expansion or Galerkin’s method with no need to the eigenfunctions or eigenvalues.

. The impedance change of an induction coil surrounding a metal tube adapter is investigated by the truncated region eigenfunction expansion (TREE) method. Conventional TREE method is inapplicable to this problem as a consequence of the numerical overflow of eigenfunctions of the air-metal multi-subdomain regions. The difficulty is surmounted by a normalization procedure for the numerical eigenfunctions obtained from the finite element method (FEM). Efficient algorithm is devised by the Clenshaw-Curtis quadrature rule for integrals involving the numerical eigenfunctions. Numerical results of the TREE and FEM simulation coincide very well in all cases, and the efficiency of the proposed method is also confirmed.

The sugar company Valdez S.A. Entity located within the geographical limits of the city of Milagro, needs to reduce its emissions to the environment and does not always comply with the air emissions standards for stationary combustion sources, which indicates that for equipment installed before 2003 they have a maximum limit of 300 mg / m³. A mist eliminator was designed to work inside the original wet gas scrubber of the water-tube cauldron #10, which uses Bagasse as fuel, for the generation of steam for industrial use. The research is documentary and field. The methodology used was mixed. focusing on the comparison of three types of technologies to meet the objectives, the fog eliminators types: Demister, Cyclone and Chevron. To find the appropriate complement, a comparison sheet was made, which is a table of contents evaluated quantitatively, analyzing indicators formulated in each of the contents. The results, supported by the Multiple Criteria Decision Analysis methodology, select the Chevron type fog eliminator, with the best efficiency for capture. Using AutoCAD, allows to visualize in 3D, the structural design in the gas scrubber.

Among the best-known capillarity phenomena is a capillary rise, the understanding of which is essential in fluidics. Some capillary flows rise monotonically whereas others oscillate, but until now no criteria have been formulated for this scenario. In this paper, the Levine's capillary rise modelling is computed numerically, then the critical radius of the capillary tube is formulated by using the dimensional method and data fitting for identification of exponent index. The phase space diagram of capillary velocity versus height is obtained for the first time and shows that the phase transition from oscillating to monotonic rising happens when the phase trajectory decreases exponentially to somewhere other than the "attractor." Two general Maple codes of the problem are provided as an essential part of this paper.

Raindrop erosion is a significant materials limiting issue. It can affect materials for transportation and renewable energy converters such as wind turbines as well as all external structures used in the construction industries. In such cases, the raindrop effects can occur over a wide range of impact velocities and particles sizes. In understanding tribological variable effects, it is useful to study using reference materials. This is because the reference material is well characterized, from previous knowledge of the tribological and corrosion patterns. Further, the well established chemical composition and stochiometry of the corrosion products provide some background understanding of how effectively, during tribological action, the surface scale adheres to the substrate. In this study, a carbon steel was used as a reference to study the effects of velocity and drop diameter in a whirling arm erosion test rig. The results were used to establish the conditions where corrosion was accelerated and the environments where aerodynamic effects may have resulted in droplets being deflected the surfaces. Erosion maps were generated to illustrate such mechanisms based on the results.

Balance requires constant adjustments in muscle activation to attain force steadiness. Creating appropriate training can be challenging. The purpose of this study was to examine the effects of two weeks front squat instability training using a water-filled training tube on force steadiness during an instability challenge. Control (CON, n= 13) and experimental (EXP, n=17) subjects completed pre and post testing for EMG variability by completing one set of 10 repetitions with a stable and unstable training tube. Electrodes were placed bilaterally on the anterior deltoid, paraspinal and vastus lateralis muscles. CON subjects completed 2 weeks of training using a stable training tube, while EXP subjects trained with a water-filled instability tube. EMG data were integrated for each contraction and force steadiness computed using the natural log of coefficient of variation. CON results showed no changes in force steadiness for any condition. EXP showed significant reductions in EMG activation variability across all muscles. These results indicate a significant training effect in reducing muscle activation variability in subjects training with a water-filled instability training device. Improvements seen in these healthy subjects supports development of training implements for a more clinical population to help improve force steadiness.

This study demonstrates the orientation and the ‘shape factor’ have pronounced effects on the development of the localized pressure fields inside of the helmet. We used anatomically accurate headform to evaluate four modern combat helmets under blast loading conditions in the shock tube. The Advanced Combat Helmet (ACH) is used to capture the effect of the orientation on pressure under the helmet. The three modern combat helmets: ECH, Ops-Core, and Airframe, were tested in frontal orientation to determine the effect of helmet geometry. Using the unhelmeted headform data as a reference, we characterized pressure distribution inside each helmet and identified pressure focal points. The nature of these localized “hot spots” is different than the elevated pressure in the parietal region of the headform under the helmet widely recognized as the under-wash effect also observed in our tests. It is the first experimental study which indicates that the helmet presence increased the pressure experienced by the eyes (as evidenced by the pressure sensors in the H8 and H9 locations), and the forehead (denoted as H1 location). Pressure fingerprinting using an array of sensors combined with the application of principle component analysis (PCA) helped elucidate the subtle differences between helmets.

The overall cost of a hydropower plant is mainly due to the expenses for civil works, mechanical equipment (turbine and control units) and electrical components. The goal of a new draft tube design is to obtain a geometry that reduces investment costs, especially the excavation ones, but the primary driver is to increase the overall machine efficiency allowing for reduced payback time. In the present study, an optimization study of the elbow-draft tube assembly of a Kaplan turbine was conducted. A CFD model for the complete turbine has been developed and validated; next, an optimization of the draft tube alone was performed using a Design of Experiments technique; finally, several optimum solutions for the draft tube were obtained using a Response Surface technique aiming at maximizing pressure recovery and minimizing flow losses. A selection of optimized geometries was subsequently post-checked using the validated model of the entire turbine and a detailed flow analysis on the obtained results could make it possible to provide insight into the improved designs. It was observed that efficiency could be improved by 1% (in relative terms), and the mechanical power increased by 1,8% (in relative terms) with respect to the baseline turbine.

The value of QuantiFERON in the diagnosis of tuberculosis and in the monitoring of the response to anti-tuberculosis treatment is unclear. The aims of this study were to evaluate the accuracy of the QuantiFERON-TB Gold In-Tube (QFT-GIT) test in the diagnosis of tuberculosis and in the monitoring of the response to anti-tuberculosis treatment in patients with active pulmonary tuberculosis (PTB). Between January 2013 and December 2015, 128 cases with active PTB and 128 controls with no mycobacterial infection, matched by age (within 3 years) and by the week that they visited Tainan Chest Hospital, were enrolled in the study. Serial testing by QFT-GIT at baseline and after 2 and 6 months of treatment was performed. At these time points, a comparison of the performance of QFT-GIT with that of sputum culture status among study subjects was conducted. Compared to baseline, 116 (87.2%) cases showed a decreased response, whereas 17 (12.8%) showed persistent or stronger interferon-gamma (IFN-γ) responses at 2 months. Their IFN-γ responses declined significantly from baseline to 2 months (median, 6.32 vs. 4.12; P < 0.005). The sensitivity values of the QFT-GIT test for the detection of pulmonary tuberculosis at cut-off points of 0.35 IU/ml, 0.20 IU/ml, and 0.10 IU/ml were 74.4%, 78.2%, and 80.5%, respectively. The specificity values at cut-off points of 0.35 IU/ml, 0.20 IU/ml, and 0.10 IU/ml were 66.2%, 63.9%, and 57.1%, respectively. Our results support the QFT-GIT assay as a potential tool for diagnosing tuberculosis and for monitoring the efficacy of anti-tuberculosis treatment.

In order to tackle the issue of severe rocking phenomenon under seismic conditions in structures equipped with steel spring isolation bearings, this paper investigates a novel type of anti-rocking bearing. Firstly, the structural configuration and working principle of the novel anti-rocking bearing are introduced, and a design method for bearing parameters is proposed. Secondly, a finite element analysis model is established using SAP2000 software to conduct nonlinear dynamic time history analysis under seismic loading. The analysis results show that the structural arrangement of the novel anti-rocking bearing reduces both the vertical displacement difference and the rocking angle of the isolation layer. The bearing exhibits a certain level of anti-rocking effect, but it may cause significant tensile forces in some bearings, necessitating the installation of anti-tensile reinforcement. The effectiveness of the anti-rocking effect improves as the stiffness of the steel tension rod in the bearing increases; however, it also leads to higher maximum tension in individual bearings as well as the total tension in all bearings. For structures equipped with the novel anti-rocking bearing, the acceleration amplifies under most cases, with amplification coefficients ranging from 0.82 to 1.55. The performance of the novel anti-rocking bearing varies significantly for different seismic waves. The stiffness of the steel tension rod should be determined considering the reference pressure of the bearing and the maximum designed tension of the bearing. Through the finite element simulation of the bearing, the mechanical properties of the bearing are basically the same as the theoretical analysis results. For the cylinder and the joint bearing, certain structural measures need to be taken to ensure its strength and stiffness.

In this paper, through high-temperature tensile tests of 55NiCrMoV7 steel, the high-temperature fracture behavior, microstructure evolution and carbide distribution characteristics of both thermal-mechanical coupling zone (fracture zone) and thermal stress zone (clamping zone) at different temperatures were studied. Intrinsic relationship between high temperature fracture and carbides types, distribution and size were revealed and evolution mechanism of microstructure near cracks in 55NiCrMoV7 hot-working die steel during high temperature deformation was clarified. Samples were stretched at different temperatures from 25 °C to 700 °C, and microscopic examinations were carried out by using SEM and TEM. The results showed that: With the increase of temperature, tensile strength and yield strength decreased, elongation and reduction of area increased, and fracture mode changed from brittle fracture to ductile fracture by transition temperature at about 400℃. During high temperature deformation, the grain dislocation density decreased, the tempered martensite decomposed, recovered, recrystallized, and then grain grew. M7C3 and M23C6 carbides precipitated and grew along the grain boundary, and a small amount of fine granular MC carbides were dispersed in the grain. The work done by the external force on the deformation zone would cause the temperature of it to be higher than tensile temperature, which provides thermodynamic conditions for the re-dissolution of small carbides near the fracture zone and the grain growth of large carbides, resulting in the decrease of small carbides and increase of large carbides in thermal-mechanical coupling zone.

Corrosion is considered as one of the main factors in the structural performance deterioration of steel members. In this study, experimental and numerical methods were used to assess the reduction in compressive strength of short tubular steel columns with local corrosion damage. The corrosion damage was varied with different depths (0, 1.5, 2, 3, 4, 4.5, and 6 mm), height (0, 20, 40, 60, 80, 100, 120, 140, 160, and 180 mm), circumference (0, 90, 180, 270, and 360°), and location along the column. A parametric numerical study was performed to establish a correlation between the residual compressive strength and the severity of corrosion damage. The results showed that as the corrosion depth, height and circumference increased, the compressive strength decreased linearly. As for the corrosion height, the residual compressive strength became constant after decreasing linearly when the corrosion height was greater than the half-wavelength of buckling of the short columns. An equation is presented to evaluate the residual compressive strength of short columns with local corrosion wherein the volume of the corrosion damage was used as a reduction factor in calculating the compressive strength. The percentage error using the presented equation was found to be within 11.4%.

The object of this work is to determine the correlation on the Nusselt number on the individual rows of a four-row tubular finned heat exchanger with continuous fins with a staggered tube arrangement using CFD modelling. Correlations for calculating Darcy-Weisbach friction factors on individual tube rows were also determined. Relationships for the Nusselt number and friction factor derived for the entire exchanger based on CFD modelling were compared with those available in the literature determined using experimental data. The maximum relative differences between the Nusselt number for a four-row exchanger determined experimentally and by CFD modelling are in the range from 22% for a Reynolds number based on a tube's outside diameter of 1,000 to 30% for a Reynolds number of 13,000. The maximum relative differences between the friction factor for a four-row exchanger determined experimentally and by CFD modelling are in the range of 50% for a Reynolds number based on a tube outer diameter of 1,000 to 10% for a Reynolds number of 13,000. The CFD modeling performed shows that in the range of Reynolds numbers based on hydraulic diameters from 150 to 1,400, the Nusselt number for the first row in a four-row finned heat exchanger is about 22% to 15% higher than the average Nusselt number for the entire exchanger. In the range of Reynolds number changes based on hydraulic diameter from 2,800 to 6,000, the Nusselt numbers on the first and second rows of tubes are close to each other. Correlations on Nusselt numbers and friction factors derived for individual tube rows can be used in the design of plate-fin and tube heat exchangers used in equipment such as air-source heat pumps, automotive radiators, air-conditioning systems and in air hot-liquid coolers. In particular, the correlations can be used to select the optimum number of tube rows in the exchanger.

The article presents results of research consisting in an attempt to assess the influence of temperature, heating time and cooling method on microstructure and residual strength properties of steel previously tempered during the production process. Simulated environmental conditions to which high-strength bolts, commonly used in steel construction, were subjected, were intended to reflect conditions of a natural fire that may occur in public facilities where the obligation to ensure safety of users and rescue teams is of key importance, also required by law. Furthermore, the tests carried out also comprised a simulated effect of a rescue and firefighting operation using shock, rapid cooling of some of the heated bolts. Samples cut out from the tested bolts, after they were properly prepared, were subjected to microstructural tests using light microscopy, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), phase analysis with the use of an X-ray diffractometer (XRD) and quantitative analysis of the microstructure involving, inter alia, measuring the surface area of grains, their equivalent diameter and mean diameter. As a result of the tests, considerable microstructure changes were identified occurring in the bolt material as a result of exposing it to fire conditions, leading to a change in key, from the point of view of structural safety, mechanical properties. The results of the microstructure tests were compared with the results of previous strength tests, including hardness of the material after the heat treatment and the residual tensile strength of the material Rm. A conducted comparative analysis showed a significant effect of all such factors as the temperature level of the simulated fire, its duration and the fire-fighting method on the mechanical properties of bolts. Results obtained were provided with required comments and the concept of using the microstructure for the post-fire assessment of steel structures was referred to.

Density is a crucial parameter for quantitatively describing the physical properties of liquids. It serves as an important indicator for scientific research, production process control, pipeline transportation, and other aspects. In oil pipeline transportation and raw material processing, real-time online measurement of liquid density is of great significance. This paper analyzes the working principle of an on-line vibrating tube densitometer and derives the fitting equation for temperature, pressure, and density；it also conducts experiments with an on-line vibrating tube liquid densitometer and establishes a traceability chain for the experimental device. The experimental setup includes a desktop densitometer system, a multi-temperature field constant temperature stirring system, a walk-in constant temperature box, an automatic blowing system, and a frequency acquisition and calculation system. The uncertainty of the device's evaluation is U= 0.08kg/m3, k=2.The experimental research on the on-line vibrating tube liquid densitometer can be carried out within the range of (650~1400) kg/m3, (10~70)℃, (0~50)bar the metrological performance of the vibrating tube densitometer can be researched by utilizing the straight tube type and the elbow type on-line vibrating tube densitometer. A preliminary study was conducted on the effects of different densities, temperatures, and pressures on the vibrating tube system's vibration cycle. The fit coefficient and error were calculated, and the experimental results were compared to the theoretical analysis to confirm the device's conformity. The study verified the device's scientific and reasonable design, and demonstrated that it is feasible to use the device for follow-up research.

Axial compression tests were carried out on 6 square steel tube confined concrete short columns and 6 BFRP square pipe confined concrete axial compression tests. The concrete strength grades were C30, C40, and C50. The test results show that the failure modes of steel pipe and BFRP pipe are obviously different, and the BFRP pipe undergoes brittle failure. Compared with the short columns of concrete confined by BFRP pipes, the ultimate bearing capacity of axial compression is increased by -76.46%, -76.01%, and -73.06%, and the ultimate displacements are -79.20%, -80.78%, -71.71%.

Axial compression tests were carried out on 6 square steel tube confined concrete short columns and 6 BFRP square pipe confined concrete axial compression tests. The concrete strength grades were C30, C40, and C50. The test results show that the failure modes of steel pipe and BFRP pipe are obviously different, and the BFRP pipe undergoes brittle failure. Compared with the short columns of concrete confined by BFRP pipes, the ultimate bearing capacity of axial compression is increased by -76.46%, -76.01%, and -73.06%, and the ultimate displacements are -79.20%, -80.78%, -71.71%.

Expansion tube is ideal energy absorber which dissipates kinetic energy through plastic deformation and friction. There is an urgent need to understand the influence of key parameter, e.g. semi angle, tube material, and friction coefficient, on the mechanical response and energy absorption characteristics of expansion tube. In the present work, the material properties of the tubes were tested under quasi-static loading condition, and the numerical simulations were carried out by using commercial software ABAQUS. Based on the validated finite element simulation, all the semi angle, tube material, and friction have significant effects on the energy absorption capacity of expansion tube. The expansion tube with high tensile stress of parent material have high energy absorption capacity, while the specific energy absorption is linear with the tensile stress/density of tube material. This work would give a guidance to the structural design and parent materials selection for expansion tubes.

Isolated fallopian tube torsions presenting to the emergency department are a very rare cause of childhood acute abdominal pain. Since the diagnosis to be made in the early period is of importance in terms of affecting tubal damage and fertility, it was aimed to evaluate the cases in the light of literature. Materials and Methods: This study included 10 patients under 18 years of age presented to the emergency department with abdominal pain between January 2003 and December 2018. The mean age was 14.5±1.43 years (range: 12-17years). The demographic characteristics, surgical findings, and methods, concomitant pathology results of these patients were retrospectively evaluated. Results: The reason for admitting to the emergency department of 10 patients included in the study was abdominal pain. The mean duration of hospital admission with pain was 4.97 days. The onset of pain was less than 24 hours in 7 patients (70%) and was more than 24 hours in three patients (30%). Of the patients, 9 (90%) had tenderness in the lower abdominal quadrant, 5 (5%) had the defense, and 3 (30%) had a rebound. Nausea, vomiting, and leucocytosis were present in 50% of the cases. Right and left tubal involvement of the cases was equal. Seven (70%) of the isolated tubal torsions were accompanied by paraovarian cysts. Of the patients, 8 (80%) underwent open surgery and 2 (20%) underwent laparoscopic intervention. Detorsion was performed in 5 (50%) and salpingectomy was performed in 5 (50%) cases. Conclusion: Isolated tubal torsion should be considered in children presenting with acute abdominal pain in early adolescence. Early diagnosis is important for the maintenance of fertility.

This paper proposes the configuration of an Organic Rankine Cycle (ORC) coupled to a solar domestic hot water system (SDHWS), with the purpose of analyzing the cogeneration capacity of the system. A simulation of the SDHWS was conducted at different temperatures, observing its performance to determine the amounts of useable heat generated by the solar collector; thus, from an energy balance, the amount of heat that may be used by the ORC could be determined. The working fluid that would be suitable for the temperatures and pressures given in the system were selected. The best fluid for the given conditions of superheated vapor at 120 °C and 604 kPa and a condensation temperature of 60 °C and 115 kPa was acetone. The main parameters for the expander thermodynamic design that may be used in such ORC were obtained with the possibility of generating 443 kWh of annual electric energy, with 6.65 % global efficiency of solar to electric power, or an overall efficiency of the cogeneration system of 56.35 % with a solar collector of 2.84 m².

The co-circulation of duck hepatitis A virus subtypes 1 (DHAV-1) and 3 (DHAV-3) in ducklings has resulted in significant economic losses. Because ducklings infected with DHAV-1 or DHAV-3 show similar clinical signs and gross lesions, it is important to discriminate these subtypes as early as possible for better clinical management. On the basis of multiple alignments of the 5′-noncoding region sequences of strains DHAV-1 and DHAV-3, universal and type-specific primers were designed and synthesized. Using the primers in a one-tube reverse transcription-PCR (RT-PCR) assay, reference strains of DHAV-1 and DHAV-3 (isolated over a span of 60 years and covering many different countries) were successfully amplified, indicating that the primer sequences were completely conserved. The amplicon sequences results and the sizes of amplicons from reference DHAV-1 and DHAV-3 isolates correlated completely with their genotypes. Moreover, with this one-tube RT-PCR system, the amplicon sizes of liver samples of reference DHAV-1- or DHAV-3-infected birds matched perfectly with their respective genotypes, as determined by virus isolation and neutralization tests. No other RNA viruses of duck origin were detected with the synthesized primers. The sensitivity of viral RNA detection was 10 pg. With this system, 20% genotype 1, 45% genotype 3, and 9% co-infection of the two genotypes were detected in 55 clinical samples. This novel approach could be used for the rapid genotyping DHAV-1 and/or DHAV-3 infection in routine clinical surveillance or epidemiologic screening.

This study presents the comparison of heat transfer capacity and pressure drop characteristics between a basic fin-tube heat exchanger and a modified heat exchanger with the structural change of branch tubes and coiled turbulators. All experiments were carried out using an air-enthalpy type calorimeter based on the method described in ASHRAE standards, under heat exchanger experimental conditions. 14 different kinds of heat exchangers were used for the experiment. Cooling and heating capacities of the turbulator heat exchanger were excellent, compared to the basic one. As the insertion ratio of the coiled turbulator and the number of row increased, the heat transfer performance increased. However, the capacity per unit area was more effective in 4 rows than 6 rows, and the cooling performance of the 6 row turbulator heat exchanger (100% turbulator insert ratio) was down to about 6% than that of 4 row one. As the water flow rate and the turbulator insertion ratio increased, the pressure drop of the water side increased. This trend was more pronounced in 6 rows. In the cooling condition, the pressure drop on the air side was slightly increased due to the generation of condensed water, but was insignificant under the heating condition. The power consumption of the pump was more affected by the water flow rate than the coiled turbulator. The equivalent hydraulic diameter of a tube by the turbulator was reduced and then the heat transfer performance was improved. Thus, the tube diameter was smaller, the heat flux was better.

To weaken the harm of Al-Si coating and increase the strength of welded joint, variable thickness of Ni foil (Ni, an austenitic formation element) was added into the lap laser welding Al-Si coated 22MnB5 hot stamping steel/galvanized steel joints. The joints' weld appearance, microstructure, and mechanical properties were explored. The weld altered from X-shape to Y-shape with the increased thickness of Ni foil. During welding, Al-Si coating was melted and diluted into the welding pool, forming δ-ferrite (a rich-Al phase with low toughness and strength) in FZ and FB. This phase deteriorated the strength of the joints. After adding Ni, the amount and size of the δ-ferrite phase decreased. With a significant thickness of Ni foil, δ-ferrite would disappear. However, a new phase (FM, rich-Ni phase) probably formed except PM(a no or negligible Ni phase). The heat-affected zone (HAZ) on the side of 22MnB5 comprised a coarse martensite zone, refined martensite zone, martensite+ferrite zone, and tempered martensite zone from the FZ to the basic material. HAZ on the side of galvanized steel mainly contained ferrite and pearlite. After adding Ni foil, the strength of the joint was more than that without Ni. The maximum strength of the joint can be up to 679MPa because of the disappearance of δ-ferrite. Meanwhile, the toughness of the joint increased. The fracture mode was from three mixed fractures(cleavage, quasi-cleavage, and dimple) to one fracture(dimple).

CO₂ emissions have been identified as the main driver for climate change, with devastating consequences for the global natural environment. The steel industry is responsible for ca. 8%-11% of global CO₂ emissions, due to high fossil-fuel and energy consumption. The onus is therefore on industry to remedy the environmental damage caused and to decarbonise production. This desk research report follows a two-tiered route: 1) exploring the Bio Steel Cycle; 2) proposing a seven-step strategy to overcome the challenges within the iron and steel industry. The true levels of CO₂ emissions in the steelmaking process, during the blast-furnace/basic-oxygen-furnace operation, will be detailed first, at 4.61t of CO₂ emissions/t of steel produced. The manuscript proposes a solution for reduced carbon emissions steelmaking with the Bio Steel Cycle components and detail on how to reach net-zero carbon emissions steel production. The 7-step-implementation-strategy as a potential solution to achieve net and true zero carbon emissions steel production in the short to medium-term. The findings of this are pointing towards the conclusion that CO₂ emissions seem to have been under-reported and under-estimated in the past, but the emission can be addressed if the correct scenarios for net-zero steel manufacturing are implemented by 2050.

The cold-formed steel sections are becoming popular for different steel structures because it has a high resistance against the different straining actions with minimum weight compared with hard steel sections. Recently, the perforated cold-formed steel (PCFS) sections are used in many applications such as storage perforated uprights racks. Experimental research into the behaviour of steel storage rack uprights subjected to axial compression is presented in this paper. The material qualities of cold-formed steel uprights were determined by tensile tests. The seventeen perforated specimens were examined under axial compression, with five different cross-sections, three different web heights and thicknesses, and varying lengths. The study's goals are to find out how perforations affect the performance and failure mode of steel storage rack uprights, discuss the interaction of distortional and global buckling, and verify the accuracy of using the Direct Strength Method (DSM) for predicting the ultimate strength of uprights failing in buckling interactions for perforated uprights. It is found that the failure modes of perforated specimens with stiffeners generally cannot be well predicted by the Direct Strength Method. But when the modifications proposed by Xianzhong Zhao etc. al. are used, their accuracy is acceptable.

Whole blood viscosity, a hemorheological factor, is currently used for diagnosis, as it is correlated with various vascular diseases that are difficult to diagnose early with a general blood test. It was determined that it was necessary to set reference intervals for further studies and utilization of whole blood viscosity in cats, a representative companion animal, and this study was conducted. 50 healthy cats were recruited for the study and whole blood viscosity, complete blood count, and serum chemistry tests were performed. The reference intervals of whole blood viscosity were 15.169 to 43.684 cP at a shear rate of 1 s-1 reflecting diastole, and 3.524 to 5.544 cP at a shear rate of 300 s-1 reflecting systole. Red blood cells, hematocrit, hemoglobin, white blood cells, and neutrophils in the complete blood count, and total protein, albumin, globulin, and cholesterol in the serum chemistry were significantly correlated with whole blood viscosity. The results of this study set reference intervals of whole blood viscosity for healthy cats in a wide shear rate range that has not yet been fully established and investigated its correlation with other blood indicators.

The pulsating flow is one of the techniques which can enhance heat transfer, therefore leading to energy saving in tubular heat exchangers. This paper investigates the heat transfer and flow characteristics in a two-dimensional in-line tube bundle with the pulsating flow by a numerical method using the Ansys Fluent. Numerical simulation is performed for Reynolds number Re = 500 with different frequencies and amplitude of pulsation. Heat transfer enhancement was estimated from the central tube of the tube bundle. Pulsation velocity had an asymmetrical character with a reciprocating flow. The technique developed by the authors to obtain asymmetric pulsations was used. This technique allows simulating an asymmetric flow in heat exchangers equipped with a pulsation generation system. Increase in both the amplitude and the frequency of the pulsations has a significant effect on heat transfer enhancement. Heat transfer enhancement is mainly observed in the front and back of the cylinder. At a steady flow in these areas, heat transfer is minimal due to the weak circulation of the flow. The increase in heat transfer in the front and back of the cylinder is associated with increased velocity and additional flow mixing in these areas.

In mammals, the oviduct (or the Fallopian tube in humans) can be divided into the infundibulum (responsible for oocyte pick-up), ampulla (site of fertilization), isthmus (where preimplantation embryos develop), and uterotubal junction (where embryos transit to the uterus). The oviductal fluid, as well as extracellular vesicles produced from the oviductal epithelial cells, referred to as oEVs, have been shown to improve the fertilization process, prevent polyspermy, and aid in embryo development. oEVs contain molecular cargos (such as miRNAs, mRNAs, proteins, and lipids) that can be delivered and fuse to recipient cells. oEVs produced from the ampulla appear to be functionally distinct from those produced from the isthmus. In multiple species including mice, cats, dogs, pigs, and cows, oEVs can be incorporated into the oocytes, sperm, and embryos. In this review, we show the positive impact of oEVs on gamete function as well as blastocyst development and how they may improve embryo quality in in vitro conditions in an assisted reproductive technology setting for rodents, domestic animals, farm animals, and humans.

Angiogenesis is a complex process that involves interactions between endothelial cells and various other cell types as well as the tissue microenvironment. Several previous studies have demonstrated that mast cells accumulate at angiogenic sites. In spite of the evidence suggesting a relationship between mast cells and angiogenesis, the association of mast cells and endothelial cells remains poorly understood. The present study aims to investigate the relationship between mast cells and endothelial cells during in vitro angiogenesis. When endothelial cells were co-cultured with mast cells, angiogenesis was stimulated. Furthermore, there was direct intercellular communication via gap junctions between the two cell types. In addition, the presence of mast cells stimulated endothelial cells to release angiogenic factors. Moreover, conditioned medium from the co-cultures also stimulated in vitro angiogenesis. The results from this investigation demonstrate that mast cells have both direct and indirect proangiogenic effects and provide new insights into the role of mast cells in angiogenesis.

JIS SUJ2 is most widely used in bearing steels. The advantages are good hardenability, excellent fatigue, wear resistance and comprehensive mechanical properties. For wear resistance and fatigue resistance of the steel are getting more and more attention, the residual stress state and its distribution on the surface of the heat affect zone are critical factors affecting the fatigue life and wear resistance of the parts. In this study, using the SUJ2 as the material to talk about the surface residual stress and retained austenite distribution. Doing the quenching and tempering treatment to obtain different microstructures, using the induction method to re-quench the case region. After the heat treatment, measuring the residual stress and retained austenite volume on the surface by X-ray diffraction, observing the microstructure and comparing the hardness. The results show that the microstructure after heat treatment contains unsolidified carbides, tempered martensite and retained austenite. The residual stress on the surface is the tensile state. In the re-hardened area after induction quenching, the residual stress is all compressive, and the values are more than -800 MPa. In conclusion, in the same output power condition can be observed that the microstructure of the specimens before induction hardening has a significant impact on the effective case depth. The surface residual stress has changed from a tensile to a compressive state. In the re-hardened area, the maximum of the residual compressive stress increased with the austenitized temperature increase.

Energy market price volatility and an upward trajectory of prices per unit of electricity have sent all industrial sectors and many economies to the brink of recession. Alongside the urgent need for decarbonisation of all industries, achieving a higher level of energy independence across all sectors seems imperative. A multi-disciplinary approach with a proposed system of CO₂ emissions reduction and capture technologies has the potential for short-term emissions reduction to near-zero in absolute terms. The findings of this research showed CO₂ emissions reduction of ~30% from 977t of CO_2e to 684t in one single blast furnace production cycle, by switching the energy provider generating energy exclusively from renewable sources. Replacing coal with biomass (BECCS), resulted in an additional reduction of ~30%, to CO_2e to 479t CO_2e. Installing solar PV panels for energy generation on site resulted in a further ~30% reduction, to 335 tonnes CO_2e. Finally, the installation of CO₂ filters reduced the CO₂ emissions to near-zero. Simultaneously, energy-saving and process improvement measures implementation (up to 60% efficiency increase), excess heat recovery (&lt;30% of energy savings), and retrofitting renewable energy technology resulted in an energy independence of 88%. Short-term engineering solutions, partly subsidised in the UK, are readily available.

In this study, the Bohler K 190 steel was used. The steel was manufactured by the powder metallurgy (PM) process. The boronizing process was carried out in the range of 1173 to 1323 K, for 1-10 h. The samples were boronized in solid medium, called the Durborid powder mixture. For the microstructural observations, the scanning electron microscopy was utilized for determining the morphology of interfaces and measuring the layers’ thicknesses. The phase composition of boride layers was also determined with X-ray diffraction analysis. To investigate the redistribution of chemical elements redistribution during the boronizing process, the EDS mapping and EDS point analysis were used. The boride layers were constituted by FeB and Fe2B phases except for 1173 K for 1 h. The values of Vickers microhardness of Fe2B, FeB and transition zone were estimated. Finally, to assess the boron activation energies in FeB and Fe2B, the so-called integral method was applied and the results in terms of activation energies were confronted with the literature data.

: The effect that the microstructure exerts on the TRIP phenomenon and on the mechanical properties in a multiphase steel was studied. Samples of an initially cold-rolled ferrite-pearlite steel underwent different intercritical annealing treatments at 750 °C until an equal fractions of austenite/ferrite was reached; the intercritical treatment was followed by isothermal bainitic treatments before cooling the samples to room temperature. Samples in the first treatment were heated directly to the intercritical temperature, whereas other samples were heated to either 900 or 1100 °C to obtain a fully homogenized, single phase austenitic microstructure prior to the conducting the intercritical treatment. The high temperature homogenization of austenite resulted in the decrease in its stability, so a considerable austenite fraction transformed into martensite by cooling to room temperature after the bainitic heat treatment. Most of the retained austenite transformed during the tensile tests, and as a consequence, the previously homogenized steels showed the highest UTS. In turn, the steel with a ferritic-pearlitic initial microstructure, exhibited higher ductility than the other steels and texture components that favor forming processes.

Enhancement in the strength of austenitic steels with a small content of carbon can be achieved by a limited number of methods, among which is the ultrafine-grained (UFG) structure formation, especially efficient with the use of severe plastic deformation (SPD) processing that enables increasing significantly the contribution of grain-boundary strengthening, and also involves a combination of other strengthening factors (work hardening, twins, etc.). In this paper, we demonstrate that the use of SPD processing combined with conventional methods of deformation treatment of metals, such as rolling, may lead to an additional strengthening of UFG steel. Analysis of the results of the study on the change of the microstructure and mechanical properties of the Cr-Ni stainless austenitic steel after a combined deformation reveals a substantial increase in the strength properties of this steel, resulting from a consecutive application of SPD processing via equal-channel angular pressing and rolling at a temperature of 400 С, yielding a strength more than 1.5 times higher that that produced by any of these two methods used separately.

Here we propose a simple way in which one can considerably improve performance of the gas stripper setup at the GSI UNILAC. To do so, it will be enough to replace inside the main GSI stripper chamber the present nozzle and the short windowless storage gas cell (for pulsed gas-jet operation mode) by a simple conical diverging nozzle combined with a gas catcher tube placed on the axis of gas-jet at some distance downstream the nozzle exit. As a result, the background pressure in the main and differentially pumped adjacent vacuum chambers of the gas stripper at the GSI UNILAC will dramatically reduce, and it will make possible to achieve the required optimal thickness of gas targets. The pulsed gas stripper operation is simply realized by implementing a commercially available fast gas valve connected to the nozzle entrance. Moreover, the ion beam pulses repetition rate can be increased and it will allow for the considerably higher average intensity of the ion beams extracted from the GSI UNILAC. Performance of the proposed GSI UNILAC gas stripper modification we explored by means of detailed computer experiments, which give a realistic description of supersonic gas jets flowing out the nozzle into vacuum. Results of these computer experiments have presented and discussed.

Four groups (sugar, lipid, protein and waste based) of bait materials combined with boric acid were evaluated in laboratory and field conditions. When compared to all the sugar-based bait materials, a mixture of honey with boric acid registered to be the most effective in attracting the maximum number (83.00) of red ants followed by a mixture of molasses with boric acid (55.00). Likewise, among the oils tested, the highest number (47.33) of red ants registered was in the mixture of rice bran oil with boric acid followed by mustard oil with boric acid mixture (37.00). Similarly, from the protein-based bait materials, the maximum number of red ants (35.00) attraction was found in the mixture of gram flour with boric acid which was followed by dog biscuits with boric acid mixture (27.67). When all the waste-based bait materials were tested, sugarcane trash with boric acid mixture attracted most of the red ants (96.67) followed by banana peel with boric acid mixture (36.67). Based on the laboratory performance, the two best bait materials in each group were assessed against red ant, Dorylus orientalis in potato crops. Of the 8 bait materials tested, the use of rice bran oil with boric acid was found to be more attractive against red ants (1564.66, 1972.33 and 2636.33 during tuber formation, tuber maturity and harvesting stages, respectively) in potato crop when compared to other bait materials. Additionally, the attraction of D. orientalis was tested separately against rice bran oil, boric acid and rice bran oil in combination with boric acid using Y-tube olfactometer under laboratory conditions. Results indicated that rice bran oil in combination with boric acid had the highest attractiveness ratio of 86.66 per cent followed by boric acid and rice bran at 76.66 and 73.33 per cent, respectively. The outcome of the current investigation can be explored for the management of red ant menace in potato and other field crops, particularly grown under organic cultivation approach.

Purpose: To evaluate the efficacy and survival rates of trabectome-mediated ab interno trabeculectomy combined with non-fenestrated Baerveldt glaucoma implants (BT) in comparison to Baerveldt glaucoma implant alone (B).Method: A total of 175 eyes undergoing primary glaucoma surgery (60 eyes BT and 115 B) were enrolled in this retrospective comparative case series. Participants were identified using the procedural terminology codes. Groups were then matched using Coarsened Exact Matching (51 eyes in each group). The primary outcome measure was surgical success, defined as 5 mmHg < IOP ≤ 21 mmHg, and IOP reduction ≥ 20% from baseline, and no reoperation for glaucoma. Secondary outcome measures were intraocular pressure, the number of glaucoma medications, and best corrected visual acuity (BCVA).Results: The cumulative probability of success at one year was 61% in BT, and 50% in B. IOP decreased significantly from 23.5±2.4 mmHg at baseline to 14.1±2.7 mmHg at the final follow up in BT (P= 0.001). The corresponding numbers for B were 23.2± 2.0 and 13.9± 1.6, respectively (P= 0.001). There was no significant difference in IOP at the final follow-up (P=0.56). The number of medications at baseline was 2.3±0.3 in both groups. However, BT needed significantly fewer drops at all postoperative time intervals and used 1.1±0.3 (BT) and 2.0±0.4 eye drops (B) at the final follow-up visit (P= 0.004). No dangerous hypotony or hypertension occurred in BT.Conclusion: Similar rates of success and IOP reduction were observed in BT and B. BT needed significantly fewer glaucoma medications. Tube fenestration was not necessary in BT resulting in less postoperative hypotony and hypertension.

A proposed low-temperature forging method aims to enhance stainless steel bearings by creating a martensitic subsurface layer, significantly boosting bearing fatigue life due to increased surface hardness. This technique induces beneficial residual stresses, particularly in axial bearings, streamlining their construction and improving machine elements. Challenges persist, especially with radial bearings, but simplicity in axial bearing forging promotes compact, resource-efficient facility construction. Future research will focus on applying this technique to axial bearing washers, potentially replicating success in other bearing components. Despite the energy ex-penditure for cooling during forging, the substantial increase in bearing fatigue life offsets this, enhancing overall longevity and reliability of critical machine components. Integration of this forging technique into bearing fabrication appears seamless, offering a promising trade-off be-tween energy use and enhanced performance.

The effect of current density of electrodeposition on the morphology, hardness, and corrosion resistance of the Ni coatings and Ni-Al2O3 coatings on Q345 steels were investigated. The surface of Ni coatings exhibited the cellular structure, while the surface of Ni-Al2O3 composite coatings showed the finer protrusions structure. The thickness of all coatings increased as the current density of electrodeposition increased from 1.5 A/dm2 to 3.0 A/dm2. After coating, the hardness and corrosion resistance of the Q345 steels were significantly enhanced. Furthermore, for the Ni coatings and Ni-Al2O3 coatings, the highest hardness and best anticorrosion property were obtained at 2.5 A/dm2 of electrodeposition current density. Compared with the Ni coatings, the co-deposition of Al2O3 nanoparticles improved the hardness of Ni-Al2O3 coating due to the second phase strengthen, but reduced the thickness and corrosion resistance due to more defects caused by the coelectrodeposition of the Al2O3 particles.

The forming mechanism of clinch joints, for various materials arrangement, using a punch and a rigid die, is well known. The basic technological parameter of the process is the parameter X – the minimal thickness of the embossment. Usually, the lower the X parameter, the greater the joint interlock. This paper presents the possibility of forming a pressed joint for two 1.5 [mm] thick sheets made of HX340 steel. The joint was formed using an additional deformable steel rivet with a hardness of 400HV1. Different values of rivet pressing below the initial surface of the upper sheet were chosen: 0, 0.15, 0.30, 0.45 and 0.60 (in [mm]). The punch positioning accuracy was 0.01 [mm]. For the mentioned rivet pressing distances, forming tests were performed using an ‘‘SKB’’ die with three die depths: 1.45, 1.60 and 1.75 (in [mm]). Observations and measurements of the characteristic geometric dimensions of the interlock were made. Furthermore, the strength of the clinch-riveted joints was analysed. The greater the rivet pressing distance, the larger the interlock parameters. Furthermore, depending on the size of the rivet pressing distance, different failure mechanisms of the lap joint were observed in the tensile shear tests.

To investigate the structural behavior of simply supported concrete beams with steel and polypropylene fiber under low velocity impact loading. In all twenty-four beams (150X200X1800 mm) with simply supported boundary condition were modeled and analyzed using ABAQUS software. Steel and polypropylene fibers of aspect ratio of 60 and 231 respectively are used. The total volumes of fibers are maintained at 1% by volume of specimen. A 100 kg hammer with tip diameter 16 mm (hemispherical contact area = 201 mm2) with four different velocities (3.13 m/s, 4.42 m/s, 5.43 m/s and 6.11 m/s) were used in the analysis. It is observed that with the addition of hybrid fibers the deflection in beams was reduced. The beams with 1% PP and 0% steel fiber shows the maximum deflection values due to low modulus of elasticity. Beams with 0.9% steel and 0.1% polypropylene fibers was less affected in terms of deflection as compared to all other beams, it is due to presence of high tensile strength fibers.

This paper describes the formulations for viscoplasticity of metals based on the Chaboche and Delobelle model. The implementations of the viscoplastic models were detailed herein and then implemented via user subroutines for material models (UMAT) in ABAQUS. Two typical metals, i.e., 316 Stainless Steel and Zircaloy-4, were chosen as examples and their viscoplastic behaviors were captured. Numerical simulations are compared to reported experiments to validate the models and the UMAT codes. Typical viscoplastic behaviors of both metals, such as stress relaxation and creep, were captured well against available experiments. We publicize all the data and codes via: https://github.com/XJTU-Zhou-group/ABAQUS_UMAT_316ss_Zr4.

In this work a solution-annealed AISI 316H grade austenitic stainless steel was studied in terms of investigating the electrolytic hydrogen charging effects on the resulting Charpy impact toughness and dry sliding tribological behavior. Conventional Charpy impact bending tests were employed to study the mechanical response of the investigated material to dynamic loading conditions, whereas dry linear sliding tribological tests were used to study the material friction and wear behavior. The obtained mechanical and tribological properties were correlated with corresponding fracture and tribological mechanisms determined from morphological observations of fracture surfaces and tribological tracks. The applied testing procedures were individually carried out for the non-hydrogenated, hydrogen-charged, and dehydrogenated material conditions. The observed changes of individual properties due to applied hydrogen charging were rather small which indicated good resistance of the solution-annealed AISI 316H steel against material degradation in currently used electrolytic hydrogenation conditions.

Cold gas dynamic spray (CS) is a unique technique to deposit material using high strain rate solid state deformation. A major challenge for this technique is its dependence on the powder properties and lack of standards to assess them between lots and manufacturers. The motivation of this research was to understand the variability in powder atomization techniques for stainless steel powders and their subsequent properties for their corresponding impact on CS. A drastic difference (~30%) was observed in deposition efficiencies (DE) of unaltered, spherical, and similar sized stainless steel (316) powders produced using centrifugal (C.A) and traditional gas atomization (G.A) techniques. The study highlights more on differences on precursor level. Using recent advancements in large scale statistical measurements like laser diffraction shape analysis, µCT scanning, traditional methods like EBSD, nano-indentation, an attempt is made to understand the powder property. Insights on powder size and shape are documented. Significant differences were observed between C.A and G.A powders in terms of grain size, fraction of higher angle grain boundaries (HAGB) and nano hardness. The outcomes of this study would be helpful to understand the commercialization of the cold-spray process for bulk manufacturing of powder precursors

As the coproduct of steelmaking, steelmaking slag, volumetrically expansive-prone without treatment, has been satisfactorily used as an aggregate base course material in highway construction. Although numerous technical reports and papers have revealed that steel slag aggreged using in rigid matrixes, the end product, paving block, non-structural concrete, for example, possesses superb strength and durability properties, the application of steel slag aggregate as a concrete aggregate is currently prohibited in highway construction. Naturally, researchers explore the practicality of use of steel slag, how to connect the laboratory experiment results to the end-product behavior, and further convert the research results into real construction? For all nontraditional or secondary materials utilization, the procedure of laboratory material examination, lab and field trial test are critical. To generalize the utilization, usability criteria establishment is necessary. This paper tries to use step-by-step method and plain language to explain how the volumetrically expansion can be simulated in lab testing apparatus, and based on the model, the mathematical deduction can result in a numerical usability criterion for steel slag use as a coarse aggregate in concrete (a rigid material). Therefore the paper is composed four main parts, laboratory test methods to examine the expansion force resulted from steel slag; converting the measured expansion force in a given volume of mass aggregate to the expansion (body) force of a single particle; modeling of slag and end material disruption; and a usability criterion from numerical deduction for the use of expansive-prone coarse slag in concrete or other rigid matrices. The paper provides the solutions to answer the above questions. Through the mathematical and mechanical modeling, provides the potential criteria that could result in specifications and guidance establishment for broad volumetric expansive-prone slags.

The study presents the effect of annealing process parameters on the microstructure, hardness and strain hardening coefficients i.e., the strength coefficient c and the strain hardening exponent n, of 42CrMo4 steel. Seven selected annealing time-temperature schemes are examined for superior steel formability in cold metal forming conditions. The c and n coefficients are first determined in experimental upsetting of annealed samples and then used in FEM simulations of the upsetting process. The results demonstrate that the strain hardening coefficients (c and n) depend on the employed annealing scheme. Compared to the as-received sample, the annealing process reduces the true stress and effectively decrease the hardness of 42CrMo4 steel, improves microstructural spheroidization and, consequently, facilitates deformability of this material. The annealing schemes relying on heating the material to 750 °C and its subsequent slow cooling lead to the highest decrease in hardness ranging from 162 to 168HV. Results obtained with the SEM-EDS, LOM and XRD methods lead to the conclusion that the employed heat treatment schemes cause the initial ferritic-pearlitic microstructure to develop granular and semi-lamellar precipitation of cementite enriched with Mo and Cr in the ferrite matrix. In addition, the annealing process affects the growth of α-Fe grains. The highest cold hardening rate, and thus formability, is obtained for the annealing scheme producing the lowest hardness. The results of FEM simulations are positively validated by experimental results. Obtained results are crucial for further numerical simulations and experimental research connected with developing new cold metal forming methods for producing parts made of 42CrMo4 steel.

In this investigation steel P355NH has been successfully cladded with Inconel 625 through the method of explosive welding. Explosively welded bimetal clad-plate was subjected to the two separated post weld heat treatment processes: stress relief annealing (at 620oC for 90 minutes) and normalizing (at 910oC for 30 minutes). In order to analyze the microstructure of the joint in the as-welded state and to investigate the influence of the post weld heat treatment on it, the light and scanning electron microscope observations and microhardness analysis have been performed. The examination of the diffusion zone microstructure has been performed by using the scanning transmission electron microscope. It was stated that obtained joint has characteristic wavy-shape geometry with the presence of the melted zones and severe deformed grains of both joined materials. Strain hardening of the materials in joint zone was established with microhardness analysis. In both of the heat treatments the changes in the grain structure have been observed. The normalizing heat treatment has the most significant impact on the microstructure of the joint as well as the concentration of the chemical elements in the joint zone. It was reported that due to normalizing the diffusion zone has been formed together with precipitates in the joint zone. The analysis of the diffusion zone images leads to the conclusion that the diffusion of alloying elements from Inconel 625 to steel P355NH takes place along the grain boundaries with additional formation of the voids in this area. The precipitates in Inconel 625 in the joint zone are two type of carbides – chromium-rich and molybdenum-rich. Scanning transmission electron microscope observation of the grain microstructure in the diffusion zone shows that this area consists of equiaxed grains (from the side of Inconel 625 alloy) and columnar grains (from the side of steel P355NH).

The fatigue strength of the hot work steel depends on various factors, including the mechanical, properties and behavior and bulk and the surface under layer, the microstructural features as well as heat treatments. The influence of a series of heat treatments on the fatigue strength of H13 hot work steel was investigated. Different preheating, quenching and tempering treatments were applied to four sets of specimens and fatigue tests were conducted at room temperature using a rotating bending test machine. All heat treatments resulted in a certain improvement of the fatigue strength. Highest fatigue strength obtained by applying a double tempering heat treatment (first tempering at 550 °C for two hours and second tempering at 610 °C for two hours) after initial preheating and quenching. One tempering treatment (550 °C for two hours after preheating and quenching) did not significantly improve the fatigue strength.

Additive manufacturing (AM) is today’s buzzword—and not only in commercial production. One of the AM techniques produces 3D objects with complex geometry using a laser beam. The relationship between the morphology of individual powder particles and the printing process has not been adequately documented yet. This article presents a detailed microscopic analysis of virgin and reused powder particles of maraging steel. Metallographic observation was performed using a scanning electron microscope (SEM). Detailed analyses of individual particles were carried out using SEM with a focused ion beam (FIB) milling capability. Analyses of elemental distribution and phase distribution were performed using EDS and EBSD, respectively. The findings have led to a better understanding and prediction of defects in additive-manufactured products.

Construction involves the use of significant quantities of raw materials and entails high-energy consumption. For the sake of choosing the most appropriate solution that considers environmental and sustainable concepts, tools such as the integrated value model for sustainable assessment (Modelo Integrado de Valor para una Evaluación Sostenible, MIVES) used in Spain, plays a key role in obtaining the best solution. MIVES is a multi-criteria decision-making method based on the value function concept and the seminars delivered by experts. Such tools, in order to show how they may work, require application to case studies. In this paper, two concrete slabs manufactured with differing reinforcement during the construction of the La Canda Tunnels are compared by means of MIVES. The two concrete slabs were reinforced with a conventional steel-mesh and with polyolefin fibres. The results showed that from the point of view of sustainability, the use of polyolefin fibres provided a significant advantage mainly due to the lower maintenance required.

Laser Cladding is one of the leading processes within Additive Manufacturing technologies, a fact which has concentrated an important amount of effort on its development. In regard to the latter, the current study aims to summarize the influence of the most relevant process parameters in the laser cladding processing of single and compound volumes (solid forms) made from AISI 316L stainless steel powders and using a coaxial nozzle for deposition. Process speed, applied laser power and powder flow are considered to be the main variables affecting laser cladding in single clads, meanwhile overlap percentage and overlapping strategy become also relevant when dealing with multiple clads. By means of setting appropriate values of each process parameter, the main goal of this paper is to develop a processing window in which a good metallurgical bond between the delivered powder and substrate is obtained, trying simultaneously to maintain processing times in their lowest value possible. Conventional metallography techniques were performed on the cross sections of the laser tracks to measure the effective dimensions of clads for dilution analysis, height and width for the values of overlap between contiguous clads and layers, and also to analyze them for physical defects such as porosity and cracks. The resulting solid piece was 8 mm high at 800 mm/min.

The article presents tests aimed to verify the possibility of making T-joints in TMCP steel using laser. The tests involved the use of 10 mm thick high yield point steel S700MC obtained in an industrial manufacturing process. The joints made in the tests were single and double-sided. Subsequent non-destructive tests revealed that the joints obtained in the tests represented quality level B in accordance with PN-EN ISO 13919-1. Single-sided welding performed using the laser beam having a power of 11 kW enabled the obtainment of 8 mm deep penetration without visibly deforming the web of the joint. The double-sided welded joints were characterised by proper geometry and the presence of gas pores in the welds not compromising the requirements of quality level B (strict requirements). The weld structure was bainitic-ferritic. The weld hardness was by approximately 60 HV1 higher than that of the base material (280 HV1). The HAZ area was slightly softer than the base material. The tests of thin foils performed using a high-resolution scanning transmission electron microscope revealed that, during welding, an increase in the content of the base material in the weld was accompanied by an increase in contents of alloying microagents Ti and Nb, particularly near the fusion line. The above-named alloying microagents, in the form of fine-dispersive (Ti,Nb)(C,N) type precipitates, could reduce plastic properties of joints.

The precipitate phases often play an important influence on the corrosion resistance of 2205 Duplex stainless steel (DSS). In the presented paper, the microstructure and corrosion resistance in the hot-rolled and cold-rolled 2205 DSS aging for different time at 850 °C was investigated by XRD, SEM and potentiodynamic polarization. It has been found that the Chi(χ) phase and Sigm(σ) phase were precipitated in turn after aging treatment of hot-rolled and cold-rolled materials, but the precipitate amount in cold-rolled material is much more than that of hot-rolled samples. The corrosion resistance of the solution-annealed cold-rolled material is similar to the hot-rolled material, but the corrosion resistance of cold-rolled material with precipitate is weaker than that of hot-rolled material after aging treatment. Pitting initiates preferentially in the Cr-depleted region from σ phase in aged hot-rolled 2205, and severe selective corrosion occurs on sigma/ferrite interfaces aged for a long aged lime. However, the initiation of pitting corrosion may take place at the phase boundary, defect and martensite in the aged cold-rolled 2205. The σ phase is further selectively dissolved by electrochemical method to investigate the difference of microstructure and corrosion behavior in hot-rolled and cold-rolled 2205 duplex stainless steel.

The reconstruction of traffic accidents has grown as an interdisciplinary field since the first accident occurred. Various methods have been developed over time, starting with primary data collected at the scene of the accident. In this work, I proposed a method by which the value of the force in the safety belt buckle can be determined when it is equipped with a pretensioning system with pyrotechnic trigger in the tube, PBP or PLP type. The anti-return system of the pretensioner mechanism, which prevents the passenger's body from moving forward, contains a set of balls that block the movement of the piston in the pretensioner tube after its activation. When limiting the movement, the force the human body exerts on the safety belt webbing is transformed into the deformation of the pretensioner tube by the balls of the anti-return system. Depending on the magnitude of the force, the marks left by the balls differ. I propose a relationship of dependence between the acting force and the deformation of the tube. An experimental test bench was created to perform shock traction tests on the pre-tensioning system, under similar conditions to those of the human body acting on the belt in case of a frontal collision. Following the tests, the force value of the seat belt buckle cable and the diameter of the spherical indentations that the balls left in the pretensioner tube were measured. A mathematical model was proposed to determine the normal force with which a ball from the anti-return system deforms the tube. The normal force was also determined by two other methods specific to contact mechanics and used in the specialized literature. By comparing the normal forces obtained by the three methods, a good correlation between the proposed mathematical model and the Komvopoulos-Ye method resulted, the "Hardness" method not being suitable for this study. The determined polynomial regression curve allows finding out the force in the cable of the closer depending on the size of the deformations produced by the balls in the tube. The forces in the belt webbing can be thus determined and biomechanics specialists can evaluate the injuries to the chest and abdomen of the occupants of a vehicle.

In this study, divalent Yb2+-doped silica fiber was fabricated using rod-in-tube technology. The fiber core of Yb2+-doped silica glass was prepared by high-temperature melting technology under vacuum conditions. The spectroscopic properties of the Yb2+-doped glass and fiber were studied. The experiments indicate that divalent Yb2+-doped glass has a high quantum efficiency and superbroadband fluorescence in the visible region with an excitation wavelength of 405 nm. In additionally, the results suggest that Yb2+-doped fiber has a potential for application in visible fiber laser and fiber amplification.

Micro channel tube (MCT) is widely employed in industry due to its excellent efficiency in heat transfer. An MCT is commonly produced through extrusion within a porthole die, where severe plastic deformation is inevitably involved. Moreover, the plastic deformation, which dramatically affects the final property of the MCT, varies significantly from location to location. In order to understand the development of the microstructure and its effect on the final property of the MCT, the viscoplastic self-consistent (VPSC) model, together with the finite element analysis and the flow line model, is employed in the current study. The flow line model is used to reproduce the local velocity gradient within the complex porthole die, while VPSC model is employed to predict the evolution of the microstructure accordingly. In addition, electron backscatter diffraction (EBSD) measurement and mechanical tests are used to characterize the evolution of the microstructure and the property of the MCT. The simulation results agree well with the corresponding experimental ones. The influence of the material’s flow line on the evolution of the orientation and morphology of the grains, and the property of the produced MCT are discussed in detail.

Discovery of inhibitors for endothelial-related transcription factors can contribute to the development of angiogenic therapies that treat diseases ranging from cardiovascular to cancer. The role of transcription factor Vezf1 in vascular development and regulation of angiogenesis has been defined by several earlier studies. Through construction of a computational model for Vezf1, work here has identified a novel small molecule drug capable of inhibiting Vezf1 from binding to its cognate DNA binding site. Using structure-based design and virtual screening of the NCI Diversity Compound Library, 12 shortlisted compounds were tested for their ability to interfere with the binding of Vezf1 to DNA using electrophoretic gel mobility shift assays. We identified one compound, T4, which has an IC50 of 20uM. Using murine endothelial cells, MSS31, we tested the effect of T4 on endothelial cell viability and angiogenesis by using tube formation assay. Our data show that addition of T4 in cell culture medium does not affect cell viability at concentrations lower or equal to its IC 50 but strongly inhibits the network formation by MSS31 in the tube formation assays. Given its potential efficacy, this inhibitor has significant therapeutic potential in several human diseases raging from wound healing to cancer.

In order to improve the performance of the draft tube in hydraulic turbine, a multi–objective optimization method for the draft tube is developed by combining the design of experiment (DOE), the radial basis function (RBF) and the non–dominated sorting genetic algorithm (NSGA–II) in this paper. The geometrical design variables of the median section in the draft tube and the cross section in its exit diffuser are considered as design parameters in this optimization, which objective function is to maximize the pressure recovery factor (Cp) and minimize the energy loss coefficient (ζ). The limited numbers of design matrix required for the shape optimization of the draft tube is generated by optimal Latin hypercube (OLH) method of the DOE technique, of which performances are evaluated through computational fluid dynamic (CFD) numerical simulation. For reducing of the computational consumption, the approximate model is used based on the RBF. The Pareto optimal solutions are finally performed using the NSGA–II for obtaining the best geometrical parameters of the draft tube. The optimization result of the draft tube shows a marked performance improvement over the original, which verifies the theoretical validity and feasibility of the proposed method in this paper.

Laser powder bed fusion (LPBF) is an additive manufacturing process employed in many industries, for example for aerospace, automotive and medical applications. In these sectors, mainly nickel-, aluminum- and titanium-based alloys are used. In contrast, the mechanical engineering industry is interested in more wear-resistant steel alloys with higher hardness, both of which can be achieved with a higher carbon content, like in high-speed steels. Since these steels are susceptible to cracking, preheating needs to be applied during processing by LPBF. In a previous study, we applied a base plate preheating temperature of 500 °C for HS6-5-3-8 with 1.3 % carbon content. We were able to manufacture dense (p > 99.9 %) and crack-free parts from HS6-5-3-8 with a hardness > 62 HRC (as built) by LPBF. In this study, we investigate the influence of preheating temperatures up to 600 °C on hardness and microstructure dependent on part height for HS6-5-3-8. The microstructure was studied by light optical microscopy (LOM), scanning electron microscopy (SEM) and electron backscatter diffraction (EBSD). The analysis of hardness and microstructure at different part heights is necessary because state-of-the-art preheating systems induce heat only into the base plate. Consequently, parts are subjected to temperature gradients and different heat treatment effects depending on part height during the LPBF process.

A new lateral force-resisting wall panel is presented for applications in mid-rise prefabricated lightweight steel construction in seismic prone regions. This panelised system is composed of a hot-rolled frame and cold-formed studs and tracks, which works as a lateral force resisting system in lightweight steel framing. The proposed hybrid panel system exhibits proper ductility and energy dissipation behaviour. The hysteretic responses of full-scale panel experiments demonstrate that the system can safely resist high cyclic loads. The hot-rolled steel part, on the other hand, can significantly improve the initial lateral stiffness of the total system that will control the maximum allowable drift of multi-story buildings. Finally, in a case study, by applying the proposed system to the design of a mid-rise building in a high seismic area, the performance of the hybrid panels, are compared with those of fully hot-rolled systems (moment resisting frames) and fully cold formed systems. The findings indicate that applying hybrid panels will result in lower weights and better performance in seismic prone regions.

Steel slag and GBFS are wastes generated during the steel and iron smelting process, characterized by their considerable production rates and extensive storage capacities. After grinding, they are often used as supplementary cementitious materials. However, the intrinsic slow hydration kinetics of steel slag-GBFS cementitious material (SGM) when exposed to a pure water environment result in prolonged setting times and diminished early-age strength development. The incorporation of modifiers such as gypsum, clinker, or alkaline activators can effectively improve the various properties of SGM. This comprehensive review delves into existing research on the utilization of SGM, examining their hydration mechanisms, workability, setting time, mechanical strengths, durability, and shrinkage. Critical parameters including the performance of base materials (water-to-cement ratio, fineness, and composition) and modifiers (type, alkali content, and dosage) are scrutinized to understand their influence on the final properties of the cementitious materials. The improvement mechanisms of various modifiers on properties are discussed. This the promotes resource utilization of industrial solid wastes and provides theoretical and technical support for the application of SGM.

The microstructure evolution of SCM435 cold heading steel at different cooling rates was investigated by means of scanning electron microscopy, TEM, XRD, and electron backscatter diffraction. The results show that the cooling rate has a significant effect on the microstructure of the experimental steel. With an acceleration of the cooling, the microstructure of the steel gradually changed from ferrite and pearlite to ferrite, pearlite, and granular bainite; finally, the pearlite disappeared, and the microstructure changed to acicular ferrite, bainite, and martensite. With an increase in the cooling rate, the morphology of the carbide underwent an evolution from sheet carbide to short-rod carbide, granular carbide, and ultimately thin-strip carbide. With the acceleration of cooling, the proportion of large-angle grain boundaries gradually decreased, and the area of small-angle grain boundaries gradually increased. When the cooling rate was 0.1℃/s, the proportion of large-angle grain boundaries was as high as 52.8%, and the dislocation density was only 1.91 × 1012 cm−2. When the cooling rate was 2.0℃/s, the proportion of large-angle grain boundaries was only 27.1%, and dislocation density increased to 5.38 × 1012 cm−2. With the increase in the cooling rate, the depth of the decarbonization layer and the thickness of the scale oxide gradually decreased, the proportion of FeO phase in the scale phase gradually decreased, and the proportion of Fe3O4 phase and Fe2O3 phase gradually increased. The tensile strength increased monotonously with the increase in cooling rate, whereas the elongation and shrinkage first decreased, then increased, and then decreased. When the cooling rate was 1.0 m/s, the short rod and granular bainite in the material structure endowed the SCM435 steel with excellent strength and toughness matching, and the tensile strength and elongation of the steel reached 895 MPa and 24%, respectively.

The guided ultrasonic wave (GUW) is extensively employed in non-destructive testing (NDT) for the purpose of detecting defects in aerospace vehicles, oil pipelines and mechanical equipment. The filtration of GUW signals, which often contain substantial environmental noise, is a crucial procedure in signal processing. This paper presents a novel denoising approach that combines Variational Mode Decomposition (VMD) with an enhanced Singular Value Decomposition (SVD). The VMD method is employed to preprocess the initial signal, thereby segregating the signal component from the noise component. Subsequently, the SampEn-SVD (Sample Entropy-SVD) method is utilized to extract the effective component from the VMD-preprocessed noise component. Finally, the VMD-preprocessed signal component and the SampEn-SVD-processed effective component are combined to yield the resultant signal, which effectively filters out the noise. The efficacy of this integrated denoising approach is substantiated through the examination of experimental signals. Furthermore, a comparative analysis is conducted to evaluate the efficacy of this method in relation to other denoising techniques. The results indicate that the SampEn-SVD method yields a superior signal-to-noise ratio (SNR) when processing the GUW signal transmitted through the steel strand. Moreover, the denoising procedure significantly reduces the discretization of characteristic parameters in the signal waveform, thereby addressing the issue of inadequate reproducibility in testing outcomes. Consequently, the denoised signal exhibits high fidelity and demonstrates a strong correlation between its combined eigenvector and strand stress.

Shape Memory Alloy (SMA) have emerged as a revolutionary material that holds the potential to change the design and construction methods of buildings and other structures. One of the most promising applications of SMAs in civil engineering is their use as reinforcements for steel structures. This paper presents the latest research progress, opportunities and challenges of SMA in the field of steel structural reinforcement, both in terms of basic components and applications. In terms of components, the construction forms and working mechanisms of Fe-SMA strips, SMA/CFRP composite patches and SMA dampers are introduced. On this basis, the application of SMA in steel structures reinforcement is introduced, and its effect is analyzed from three aspects: crack restoration, seismic retrofitting and structural strengthening. Finally, the results of the current research are summarized and the shortcomings are analyzed, hoping to provide a reference for the research of SMA in the field of steel structures reinforcement.

This study deals with two different aspects of the high-strength low-alloyed 1100 MC steel. The first is associated with the remarkable heterogeneity in the surface state produced during sheet rolling with respect to the sheet width. The variable-thickness surface layer exhibits a microstructure different from that of the deeper bulk. Variation of the thickness of the thermally softened near-surface region strongly affects Barkhausen noise, as well. This technique can be considered a reliable tool for monitoring the aforementioned heterogeneity. It can also be reported that the opposite sides of the sheet are different with respect to the surface state, heterogeneity distribution, and corresponding Barkhausen noise. These aspects indicate the different conditions during hot rolling followed by rapid quenching on the upper and lower rollers. The second aspect is related to the remarkable asymmetry of Barkhausen noise emission with respect to two consecutive bursts. This asymmetry is due to the presence of remnant magnetisation in the sheet produced during manufacturing. The remnant magnetisation is coupled to the magnetic field produced by the excitation coil of the Barkhausen noise sensor and strongly contributes to the aforementioned asymmetry. As soon as sufficient removal of this remnant magnetisation is carried out in the vanishing magnetic field (demagnetisation), the aforementioned remarkable asymmetry is fully lost.

We present functionalization of AISI 316L surfaces by nanosecond Nd:YAG laser texturing in order to modify the surface morphology with crosshatch and dimple patterns. We performed tribological analysis under lubrication with sunflower and jojoba oil with and without addition of solid lubricant, MoS2 nanotubes. In connection to friction/wear response we analysed laser-textured surface wettability, oil spreadability and oil retention capacity. We have shown, that the crosshatch pattern generally exhibited lower friction than the dimples pattern, with the addition of MoS2 nanotubes not having any significant effect on the coefficient of friction under the investigated contact conditions. This was additionally with better oil spreadability and oil retention capacity results of crosshatch textured surface. Furthermore, texturing reduced wear of the stainless steel surfaces but led to approximately one order of magnitude larger wear rate of the steel counter-body, primarily due to the presence of hard bulges around the textured patterns. Overall, the crosshatch pattern showed better oil retention capacity and lower friction in combination with different vegetable oils, thus making it a promising choice for improving tribological performance in various environmentally friendly applications.

Nitriding has long been used to engineer the surfaces of engineering steels to improve their surface and subsurface properties. The role of the surface compound layer (’-Fe4N and/or -Fe2-3N) in improving the tribological and corrosion resistant properties of nitrided steels has been established. However, there have been very few studies on the response of the compound layer to tribocorrosion in corrosive environments. In this work, the tribocorrosion behaviour of a 5 m thick ’-Fe4N nitride layer produced on mild steel (MS) by plasma nitriding has been studied in a NaCl containing solution under various electrochemical conditions. The results show that at a cathodic potential, where mechanical wear is predominant, the total material removal (TMR) from the ’-Fe4N layer is 37% smaller than that from the untreated MS, and at open circuit potential, TMR from the layer is 35% smaller than that from the untreated MS, while at an anodic potential, the ’-Fe4N layer can reduce TMR from mild steel by 87%. The beneficial effect of the ’-Fe4N nitride layer in improving the tribocorrosion behaviour of mild steel is derived from its high hardness and good corrosion resistance in the test solution and its ability to resist both mechanical wear and chemical wear.

A large amount of steel slag (SS) and CO2 are generated in the steelmaking process. The indirect CO2 capture using SS is a promising way for co-treatment of the wastes. Ammonium salt solution is widely used to extract Ca2+ from the SS since it is recyclable. Several works have focus on improving the carbonation rate by adjusting various parameters (e.g., temperature and pH). However, there is little detail information about the associating behaviors and interaction strength between the various ions in the ammonia solution during the carbonation process. In this work, the Ca2+–CO32-–NH4+–Cl-–H2O system was established by using Material studio software. The effects of temperature and concentration of CO32- on CaCO3 growth were explored at the atomic scale by calculating the binding energy, mean square displacement, and diffusion coefficient between particles. Furthermore, the microstructure, bonding characteristics, and occurrence behavior of each particle were studied though molecular dynamics simulation methods. The results showed that with the increase of temperature (20–80 ℃), the binding ability and diffusion coefficients of Ca2+ and CO32- increase in the system, which is beneficial to the formation of CaCO3 clusters. With the increase of the concentration of CO32- (15–25 vol.%), the binding ability and diffusion coefficient of Ca2+ and CO32- in the system are enhanced, which is beneficial to the formation of CaCO3 clusters.

Steel slag is a co-product of the steelmaking industry, this material is rarely used as a binder due to its low cementitious properties. Thus, it´s believed that the alkaline activation of steel slag can enable its use as a cementitious material. This work has the objective of making a systematic bibliographic review on the theme "slag melt as a precursor in activated alkali binders". To this end, the ProKnow-C method was used for the selection and analysis of relevant research on the topic. The portfolio resulted in 71 texts, mostly journals paper. Bibliometrics showed that the country with the most publications is China and the journal with the most publications is Construction and Building Materials. The critical analysis concluded that the XRD, XRF, and compressive strength tests are the most used for the characterization of the material. It is possible to establish that there are some knowledge gaps on the subject, such as better mechanical characterization and greater production of works with dosing by the one-part method.

This study is follow-up of the steel shot transformation under the influence of environmental factors research (Lisin et al., 2022) and is the initial stage of investigating the iron behavior in soils during steel shot corrosion under a number of factors: the metallic lead in soils, atmospheric precipitation, excess organic matter. The results obtained show that corrosion of steel ammunition is a continuous process, including the formation of a poorly soluble rust crust on the surface of the steel and the mineralization of the metal until it is destroyed. As a result, the metal transformed into rust form, is a constant source of iron ions and dispersed rust particles migrating in soil waters and accumulating in soils. In addition, the aggregation of corrosion products of steel ammunition is the cause of a change in physical and mechanical properties of soils, which leads to a violation of the air and water migration regime of soils and an increase in surface runoff from the territories of shooting activity. The highest environmental risks are observed when steel ammunition is used on shooting areas where metallic lead intensifies steel shot corrosion rate, while the deposited steel shot activates the deterioration of previously encapsulated metal and — if steel and lead ammunition are used at the same time — slows down the encapsulation of newly deposited metallic lead, which catalyses the accumulation and migration of lead in environmental components.

The article presents a modified finite element (FE) based algorithm for nonlinear analysis of 2D beam structures, which takes into account the influence of the shear forces. The method proposed enables using complex materials with nonlinearities without the need of implementing advanced constitutive models in FE routines. It can be directly integrated with commonly available FE software for linear analysis of beam structures, so its functionality can be easily extended also with material nonlinearities. The presented approach adopts the generalized constitutive law algorithm to iteratively modify the stiffness of beam element. To address an influence of a shear stiffness, a Timoshenko beam element was used. The methodology was implemented and its performance was verified on several numerical examples. For validation, the displacements and the ultimate loads were compared with the values from a commercial FE software. The results shown a good correlation between the reference model and the method proposed.

A phosphate/molybdate and cerium-modified phosphate/molybdate conversion coatings were deposited on a carbon steel surface and their protective and self-healing abilities were evaluated. Surface morphology and inner structure of the coatings were examined using FE-SEM-FIB and TEM techniques, chemical composition and element distribution depth profiles in conversion layers were determined using EDX measurements, whereas XPS was applied for the analysis of Mo and Ce oxidation states. Voltammetric measurements and EIS were performed to assess the corrosion behavior of the samples. The higher protective and stronger self-healing abilities were found for phosphate/molybdate/cerium conversion coating deposited in a sulphate-containing solution. This was attributed to higher values of both: total cerium and Ce(IV) content in the conversion layer as well as to lower number of structural defects in the coating. It was demonstrated that the micro-structural characteristics of protective coatings are also important in determining self-healing abilities.

Metal 3D printing technology is a promising manufacturing method, especially in the case of complex shapes. The quality of the printed product is still a challenging issue for mechanical applications. The anisotropy of the microstructure, imperfections, and residual stress are some of the issues that diminish the mechanical properties of the printed sample. The simulation could be used to investigate some technical details, and this research has tried to computationally study the metal 3D printing of austenitic stainless steel to address austenite microstructure and local yield strength. Two computational codes were developed in Visual basics 2015 to simulate the local heating/cooling curve and subsequent austenite microstructure. A stochastic computational code was developed to simulate austenite grain morphology based on calculated thermal history. Then Hall-Pitch equation was used to estimate the yield strength of the printed sample. These codes were used to simulate the effect of temperature of the printer’s chamber on microstructure and subsequent yield strength. The austenite grain topology is more columnar at a lower temperature. The percentage of the equiaxed zone will be increased at a higher chamber’s temperature. Almost a fully equiaxed austenite microstructure will be achieved at 800 C chamber’s temperature, but the last printed layer, which is columnar and can be removed by cutting then. The estimated local austenite grain size and the local yield strength in the equiaxed regions are in the range of 15 to 30 μm and 270 to 330 MPa at 800 C temperature of printer’s chamber, respectively.

This paper analyses the evolution of the internal damage in two types of steel that show different fracture behaviours, with one of them being the initial material used for manufacturing prestressing steel wires, which shows a flat fracture surface perpendicular to the loading direction, and the other one being a standard steel used in reinforced concrete structures, which shows the typical cup-cone surface. 3mm-diameter cylindrical specimens are tested with a tensile test carried out in several loading stages and, after each of them, unloaded and analysed with X-ray tomography, which allows detection of internal damage throughout the tensile test. In the steel used for reinforcement, damage is developed progressively in the whole specimen, as predicted by Gurson-type models, while in the steel used for manufacturing prestressing steel-wire damage is developed only in the very last part of the test. In addition to the experimental study, a numerical analysis is carried out by means of the finite element method by using a Gurson model to reproduce the material behaviour.

Transient liquid phase (TLP) bonding of Al-6063 and UNS S32304 was performed using copper foil as an interlayer between the base metals. A compression load was applied normal to the specimens. Metallurgical examination of the produced joints showed three distinct regions including a reaction zone, diffusion affected zone and the base metals. The diffusion of copper into aluminum resulted in an Al-Cu eutectic structure. However, the oxide layer on the aluminum surface controlled the dissolution behavior of copper and the extent of its wettability with the base metals. Although voids and intermetallic compounds were detected at the interfaces of the processed joints, a defect free joint was produced at 570°C. In addition, the results from corrosion tests showed that the use of copper as an interlayer decreased the corrosion resistance of the joints. However, increase in thickness of the joining reaction zone with increasing bonding temperature was observed to increase corrosion resistance.

Carbon fiber reinforced polymer (CFRP) has been used widely in strengthening of steel structures. Steel/CFRP systems subjected to elevated temperatures is realistic in a summer climate event in many countries where the temperature in steel may approach 50 °C or even higher, which will lead to the degradation of the bond performance between CFRP and steel. Therefore, predicting the bond behavior of the CFRP/steel system under elevated temperature is critical. This paper investigated the mechanical performance of CFRP/steel adhesively-bonded double strap joints at elevated temperatures. Thirty CFRP-steel double strap joints were tested to failure under temperatures between 10 °C and 90 °C. It was found that the joint failure mode changed from adherend failure to debonding failure as the temperature approached T_g. In addition, the ultimate load and joint stiffness decreased significantly at temperatures near to and greater than T_g. Based on the experimental results, a model is proposed to predict the bond stress of the CFRP/steel at different temperatures.

1-[(4-ethyl-2-phenyl-4,5-dihydro-1,3-oxazol-4-yl)methyl]-4-phenyl-1H-1,2,3-triazole (Ph4) and1-[(4-ethyl-2-phenyl-4,5-dihydro-1,3-oxazol-4-yl)methyl]-5-phenyl-1H-1,2,3-triazole (Ph5) are new isomers of the triazole derivative family, were synthesized and tested on the corrosion of mild steel in molar hydrochloric acid molar media using weight loss, electrochemical polarization and impedance spectroscopy. Then the experimental results were confirmed by quantum chemical calculations using DFT at B3LYP /6-31G (d,p). The compound Ph4 is the best inhibitor and its inhibitory efficiency increased with increasing concentration and reaching 95% at 10⁻³ M. Polarization curves studies show that both compounds tested are mixed-type inhibitors. Nyquist curves presented a single capacitive loop, their diameter increases progressively with both inhibitors concentration. The change of the substitution phenyl from position 5 to position 4 in the triazole ring increases the inhibitory effect of the triazole compounds. The effect of temperature on the corrosion behavior of iron indicates that the inhibitory efficiency of the two inhibitors decreases with increasing temperature in the range of 308 to 338K. DFT study is in good correlationwith the experimental results.

Medium-carbon steel is commonly used for the rail, wire ropes, tire cord, cold heading, forging steels, cold finished steel bars, machinable steel and so on. Its fatigue behavior analysis and fatigue life estimation play an important role in the machinery industry. In this paper, the estimation of fatigue life of medium-carbon steel with different surface roughness using established S-N and P-S-N curves is presented. To estimate the fatigue life, the effect of the average surface roughness on the fatigue life of medium-carbon steel has been investigated using 75 fatigue tests in three groups with average surface roughness (Ra): 0.4μm, 0.8μm, and 1.6μm respectively. S-N curves and P-S-N curves have been established based on the fatigue tests. The fatigue life of medium-carbon steel is then estimated based on Tanaka-Mura crack initiation life model, the crack propagation life model using Paris law, and material constants of the S-N curves. 6 more fatigue tests have been conducted to validate the presented fatigue life estimation formulation. The experimental results have shown that the presented model could estimate well the mean fatigue life of medium-carbon steel with different surface roughness

Epoxy asphalt (EA) concrete is widely used in constructing long-span steel bridge pavements (SBDPs). This study aims to derive a fatigue damage evolution law, conducting an experimental investigation of SBDP. First, a general theoretical form of the fatigue damage evolution law of materials is established based on the thermal motion of atoms. Then, fatigue experiments demonstrate that this evolution law well represents the known damage–life relationships of SBDP. Taking into account the experimental relationships between damage and fatigue life under symmetrical cyclic loadings with different overload amplitudes and temperature variations, a detailed damage evolution law is deduced. Finally, the role of damage accumulation is discussed on the basis of the proposed damage evolution law for the extreme situation of heavy overload and severe environments. The results show that both heavy loading and falling temperatures increase the fatigue damage of SBDP considerably; therefore, SBDP should avoid heavy loading combined with winter temperatures. EA shows a fatigue life two to three times longer than that of modified matrix asphalt (SMA) or guss asphalt (GA). For the same thickness, EA pavement is demonstrated to be more suitable for an anti-fatigue design of large-span SBDP under high traffic flows and low temperatures.

This study aimed to investigate the efficacy of probiotics in elderly hospitalized tube-fed patients undergoing antibiotic therapy for Clostridium difficile-associated diarrhea (CDAD). Probiotics were administered to 29 patients, with twice-daily doses for 7 days following the completion of antibiotic treatment. In the probiotic group, while stool form showed no significant change, there was a significant decrease in stool frequency. Conversely, the control group exhibited improved stool form but not frequency. The probiotic group maintained a significant difference in stool form during the follow-up period. Additionally, the control group showed a positive correlation between stool form, frequency, antibiotic therapy, and intensive care unit admission, which was not observed in the probiotic group. These findings suggest that supplementing with probiotics can effectively normalize stool form in elderly hospitalized tube-fed patients undergoing antibiotic treatment for CDAD, highlighting the potential benefits of probiotic intervention in this specific population.

The thoracic surgery has increased drastically in recent years, especially in the light of the severe outbreak of 2019 novel coronavirus disease (COVID-19). Routine “passive” chest computed tomography (CT) screening of inpatients detects some pulmonary diseases requiring thoracic surgeries timely. As an essential device for thoracic anesthesia, the double-lumen tube (DLT) is particularly important for anesthesia and surgery. With the continuous upgrading of the DLTs and the widespread use of the fiberoptic bronchoscopy (FOB), the position of DLT in thoracic surgery is gradually becoming more stable and easier to observe or adjust. However, the DLT malposition still occurs during transferring patients from supine to lateral position in thoracic surgery, which leads to lung isolation failure and hypoxemia during one-lung ventilation (OLV). Recently some innovative DLTs or improved intervention methods have shown good results in reducing the incidence of DLT malposition. This review aims to summarize the recent studies of the incidence of left-sided DLT malposition, the reasons and effects of malposition, and summarize current methods for reducing DLT malposition and prospects for possible approaches. Meanwhile, we use bibliometric analysis to summarize the research trends and hot spots of the DLT research.

The VisionCube is a 2-unit CubeSat developed in-house, of which the primary mission is aimed at detecting the occurrence of transient luminous events in the upper atmosphere and obtaining corresponding images from the low Earth orbit. An on-board TLE observation system of the VisionCube cubesat is designed and developed by incorporating a photon-sensitive MaPMT and a CMOS image sensor. Also, a distinctive TLE observation software which enables detecting the TLEs and capturing images in a timely manner is devised. By taking into account the limited resources of a small CubeSat in size and power, the on-board observation system is developed employing a system-on-chip design architecture by which both hardware and software can be integrated seamlessly. The purpose of this study is to investigate the functionality of the hardware and the validity of the software algorithm to show the on-board system will operate properly with no human intervention during the space operation. To this end, a ground simulation facility is constructed to emulate the space environment of the TLE occurrence using a set of UV LEDs inside a darkbox. Based on the analysis of the spectral and temporal properties of the TLEs, the randomly generated UV LED pulses are opted for verification scenarios for the TLE observation system. The validation results show that the hardware and the software algorithm of the on-board observation system can effectively detect the TLEs and obtain the images during the on-orbit operation.

Purpose: To compare the efficacy and safety of graft-free short tunnel small flap (STSF) technique with that of scleral patch graft (SPG) in Ahmed glaucoma valve (AGV) implantation. Design: Randomized clinical trial. Participants: Eighty-eyes of eighty patients with medically uncontrolled glaucoma including 41 in STSF and 39 eyes in SPG. Methods: Patients were enrolled and assigned randomly to STSF or SPG. Main Outcome Measures: tube exposure, Intraocular pressure (IOP), number of glaucoma medications, best corrected visual acuity (BCVA), surgical complications, and success rate ( defined as intraocular pressure (IOP) >5 mmHg, ≤21 mmHg, and IOP reduction ≥20% from baseline at two consecutive visits after three months, no reoperation for glaucoma). Results: only one case in SPG developed tube exposure at 1-year follow-up. The cumulative probability of success during the first year of follow-up was 70% in the STSF and 65% in SPG (P = 0.36). IOP decreased significantly from 29.6 ± 8.6 mmHg at baseline to 16.4 ± 3.6 mmHg at the final follow-up in STSF (p = 0.001). The corresponding numbers for SPG were 30.9 ± 11.2 and 15.8 ± 4.7, respectively (p = 0.001). The final IOP was comparable between both groups (p = 0.65). Mean ± standard deviation of the number of glaucoma medications was 1.8 ± 0.9 in STSF and 1.6 ± 0.9 in SPG at final follow-up (P = 0.32). Postoperative complications developed in 8 patients (19%) in STSF and 9 patients (23%) in SPG (P = 0.81). Conclusions: STSF and SPG techniques had comparable complication rate at one-year follow-up. Both techniques were comparable in terms of success rate, postoperative IOP, and glaucoma medications.

China is facing the development requirements of the dual carbon goal and the construction needs of resilient cities. Currently, high-strength composite structural systems are a feasible solution, but their research and application in the construction field are insufficient, especially for the combination forms of concrete above C100 and steel above Q550. In response to this issue, this paper proposes a new high-performance structural system, namely the composite frame - high-strength steel plate wall core tube resilient structure system, which includes high-strength steel plate (Q550) - ultra-high strength concrete (C100) shear walls, replaceable energy dissipation coupling beams, and composite frames. Taking a 200 meter building as an example, this paper designs and establishes calculation models for a conventional reinforced concrete frame-core tube structure and a high-performance structure based on PKPM software, and establishes elastoplastic analysis models for both based on SAUSAGE software, and then conducts dynamic elastoplastic time history analysis and seismic resilience assessment of structures under design basis earthquakes (DBEs), maximum considered earthquake (MCEs) and extremely rare earthquakes (EREs). Research has shown that compared to conventional structures, new high-performance structures can effectively reduce the size of shear walls, reduce the self-weight of the structure, and enhance the space for building use; The story drift ratio has higher redundancy than specification limits, lower plastic damage and overall stiffness degradation of the structure, and better seismic performance; The seismic resilience has significantly improved, especially in the case of casualties, which can better ensure the safety of people's lives and property.

The corrosion inhibition behavior of cetyl pyridinium chloride (CPC) on mild steel in 0.5 M H2SO4 solution was examined using measurement techniques such as Fourier Transform Infra-red Spectroscopy (FTIR), Field Emission Scanning Electron Microscopy (FESEM), and Atomic Force Microscopy (AFM). The studies were carried out within a 25°C temperature range. The surface morphology of the corroded steel samples was investigated using FESEM and AFM. The results show that cetyl pyridinium chloride (CPC), a mild steel corrosion inhibitor, effectively prevents corrosion in 0.5 M H2SO4 and, when present, increases corrosion resistance. CPC has a stronger inhibitory effect on mild steel. The FESEM and AFM images clearly show how surface morphology changes when additives are present. The weight loss results were confirmed by en-ergy dispersive X-ray (EDX) spectroscopy analysis, and a value of 98.54% was obtained from potentiodynamic polarization studies at 0.0077M CPC. CPC acts as an important corrosion in-hibitor.

This study aims to investigate a friction stir welded joint between steel and aluminum alloy. Friction stir welding is nowadays one of the most interesting joining technique due to the possibility to connect materials and thicknesses that are difficult or impossible to weld with traditional techniques. The main advantage is that Materials are not affected by thermal cycle problems during solidification and cooling and the absence of fumes and pollution during the process favors the quality of the welded joint. The life of metal joints could be greatly reduced in a corrosive environment, since the less noble material will tend to increase its corrosion rate while the nobler one will reduce its electrochemical dissolution. Accelerated ageing tests (i.e. salt fog test) are used to estimate the lifetime of metal joints in highly aggressive environments. The aim of the present work is to evaluate the durability at long ageing time in salt spray test (according to ASTM B117) of carbon steel/aluminum alloy joints, obtained by FSW. In this first part, mechanical tests results are reported. A deep metallographic and chemical investigation are going to be reported in the part 2.

The investigation aims to analyze the effect of homogenization heat treatment on the quantity, distribution, morphology, and chemical composition of δ ferrite and sigma phase in the 316L austenitic stainless steel cast billet. Microstructures of the cast billet at different locations, center, 0.5 R, R, and the subsequent 2/6-hour homogenization heat treatment at 1240 oC were examined. The microstructure at the radius R was much more uniform and expected a better performance in the following hot/cold forging processes due to the highest cooling rate compared with those at 0.5R and center. The δ ferrite often accompanies the generation of the sigma phase, and the transformation of δ ferrite into the sigma/(austenite) and retained δ ferrite is strongly related to the cooling rate after homogenization heat treatment. The sigma phase is hard and detrimental to the subsequent hot/cold forgings. It must be removed from the homogenization heat treatment before forging. Fast air cooling from 850 oC to room temperature after homogenization heat treatment cannot prohibit the sigma phase formation. Rapid cooling between 850 and 1240 oC after homogenization treatment is required to avoid the sigma phase formation in the 316L stainless steel cast billet.

The effect of plasma electrolytic nitrocarburizing on the wear resistance of carbon tool steel in friction couples with hardened steel and lead-tin bronze is considered. The microgeometry of friction tracks and its change with increasing duration of friction tests are analyzed. The equilibrium roughness is determined, which is optimal for the friction couple and ensures minimal wear. The type and mechanism of wear of carbon tool steel after plasma electrolytic nitrocarburizing has been determined. The optimal values of the plasma electrolytic nitrocarburizing parameters, which provide the lowest values of the friction coefficient and weight wear, have been determined. The phase and elemental composition of the surface layer was studied using X-ray diffraction analysis and EDX analysis. The relationship of the microstructure of the nitrocarburized layer of tool steel with the friction coefficient and weight wear is established.

In the current industrial revolution, advanced technologies and methods can be effectively utilized for the detection and verification of defects in high-speed steel filament production. This paper introduces an innovative methodology for the precise detection and verification of micro surface defects found in steel filaments through the application of the Eddy current principle. Permanent magnets are employed to generates a magnetic field with high frequency surrounding a coil of sensor positioned at the filament's output end. The sensor's capacity to detect defects is validated through a meticulous rewinding process, followed by a thorough analysis involving scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS). Artificial defects were intentionally introduced into a sample, and their amplitudes were monitored to establish a threshold value. The amplitude signal of these created defect was identified at approximately 10% FSH, which corresponds to a crack depth of about 20 µm. In the experimental production of 182 samples covering 38 km, the defect ratio was notably high, standing at 26.37%. These defects appeared randomly along the length of the samples. The verification results underscore the exceptional precision achieved in the detection of micro surface defects within steel filaments. These defects were primarily characterized by longitudinal scratches and inclusions containing physical tungsten carbide.