In this study, the Bohler K 190 steel was used. The steel was manufactured by the powder metallurgy (PM) process. The boronizing process was carried out in the range of 1173 to 1323 K, for 1-10 h. The samples were boronized in solid medium, called the Durborid powder mixture. For the microstructural observations, the scanning electron microscopy was utilized for determining the morphology of interfaces and measuring the layers’ thicknesses. The phase composition of boride layers was also determined with X-ray diffraction analysis. To investigate the redistribution of chemical elements redistribution during the boronizing process, the EDS mapping and EDS point analysis were used. The boride layers were constituted by FeB and Fe2B phases except for 1173 K for 1 h. The values of Vickers microhardness of Fe2B, FeB and transition zone were estimated. Finally, to assess the boron activation energies in FeB and Fe2B, the so-called integral method was applied and the results in terms of activation energies were confronted with the literature data.

boronizing; K190 steel; microstructure; properties; simulation

Engineering, Metallurgy and Metallurgical Engineering

* All users must log in before leaving a comment