The thermal stabilizers, lubricant, and plasticizers are three crucial additives for processing poly (vinyl chloride) (PVC). In this study, a new mannitol stearate ester-based aluminum alkoxides (MSE-Al) was designed and synthesized as a novel additive for PVC. The thermal stability and processing performance of PVC stabilized by MSE-Al were evaluated by Congo red test, conductivity measurement, thermal aging test, ultravioletevisible (UV-vis) spectroscopy test, and torque rheometer test. Results showed that the addition of MSE-Al can not only markedly improve the long-term thermal stability of PVC, but also greatly accelerate the plasticizing and decrease the balance torque which demonstrated that MSE-Al possesses the lubricating property. Thus, MSE-Al was demonstrated to be able to provide tri-functional additive roles, e.g., thermal stabilizer, plasticizer, and lubricant. The test results for the thermal stability of PVC indicated that the initial whiteness of PVC stabilized with MSE-Al was not good enough, thus the synergistic effect of MSE-Al with zinc stearates (ZnSt₂) on the thermal stability of PVC was also investigated. The results showed that there exhibited an appreciable synergistic effect between MSE-Al and ZnSt₂. The thermal stabilization mechanism and synergism effect of MSE-Al with ZnSt₂ were then discussed.

In this study, a high energy conversion efficient dye-sensitized solar cells (DSSC) was successfully fabricated by attaching a double anti-reflection (AR) layer which is composed of a subwavelength moth-eye structured polymethyl methacrylate (PMMA) film and a polydimethylsiloxane (PDMS) film. The efficiency is up to 6.79%. The moth-eye structured PMMA film was fabricated by using anodic aluminum oxide (AAO) template which is simple, low-cost and scalable. The nano-pattern of AAO template has been precisely reproduced onto PMMA film. The photoanode is composed of Titanium dioxide (TiO₂) nanoparticles (NPs) with diameter of 25 nm deposited on the fluorine-doped tin oxide (FTO) glass substrate and the sensitizer N3. The double AR layer can effectively improve the short-circuit current density (JSC) and conversion efficiency from 14.77 to 15.79 mA/cm² and from 6.26% to 6.79%, respectively.

This study develops into the application of a combined MFC unit with chemical coagulation for total treatment of inert contaminants in complex substrates. Microbial Fuel Cell (MFC) technology converts chemical energy in the form of organic matter, into bioelectricity in an environmentally friendly and effi-cient manner, reducing carbon emissions and increasing bioenergy production. An evaluation of a la-boratory scale chemical coagulation using an aluminum and poly-based coagulant on how effective it can remove bulk impurities such as particulate COD and turbidity to obtain the purest and most cost-effectively treated wastewater using a jar test is being conducted in this current study. This study aims to find the most effective treatment technologies for wastewater recovery in breweries in order to achieve zero liquid effluent discharge (ZLED). The preliminary results showed that adding a modest amount of poly and a 50 % alum alone treatment improved COD, color, and turbidity reduction. The turbidity removal efficiency achieved after chemical coagulation treatment was 90.50 % and 59.36 % COD removal, demonstrating the benefits of adopting an alum/poly based technique. To determine ZLED, this study clearly advised a combined treatment technique, specifically the MFC-flocculator unit for efficient organics and inorganics removal.

Friction Stir Welding is a suitable solid-state joining technology to connect dissimilar materials. To produce an effective joint, it requires a phase of optimization which leads to the definition of process parameters such as pin geometry, tool rotational speed, rotation direction, welding speed, thickness of the sheets or tool tilt angle. The aim of this review is to present a complete and detailed frame of the main process parameters and their effect on the final performance of a friction stir welded joint in terms of mechanical properties and microstructure. Particularly, the attention was focused on the connection between different aluminum alloys. Moreover, the experimental results were correlated to the development and the applications of tools, which can effectively use in the design of the manufacturing process, such as finite element analyses, artificial neural networks, statistical studies. The review wants to be also a point of reference to identify the best combinations of process parameters based on the dissimilar aluminum to be joined.

The present work aims to explain the aluminum hydrolysis reaction kinetics based on properly chosen theoretical model with machined aluminum waste chips and alkali solutions up to 1M as a promoter, and to estimate overall reaction profit. In order to obtain results of better accuracy, we work with flat Al waste chips because a flat surface is preferable to maximally increase the time for created hydrogen bubbles to reach the critical gas pressure. At describing the reaction kinetics, flat shape allows using a planar one-dimensional shrinking core model instead of much complicated polydisperse spheric shrinking core model. We analyze the surface chemical reaction and mass transfer rate steps to obtain the first order rate constant for surface reaction and the diffusion coefficient of aqueous reactant in the byproduct layer, respectively. With our reactor we achieved H2 yield of 1145 mL per 1 g Al with 1M NaOH, which is 92% of the theoretical maximum. At estimation of the profit, we pay much attention to the loss of alkaline and find a crucial dependence on its price. Nevertheless, in terms of consumed and originated materials for sale, conversion of the aluminum waste material into green hydrogen by properly chosen reaction parameters has a positive profit even by consuming alkali of chemical grade.

Heat-treated aluminum-silicon (Al-Si)-based alloys have dominated the cast lightweight alloy industry for several decades. However, in the last decade, Al-Ce-based alloys have shown promise in replacing Al-Si alloys due to their ability to remove the need for costly heat treatments. Since the properties of Al-Ce alloys depend on the as-cast microstructure, it is important to characterize the solidification kinetics of these alloys. Therefore, this study focused on characterizing the solidification of a near eutectic Al-Ce alloy with additions of Ni and Mn. The alloy was cast in a wedge mold configuration, resulting in cooling rates between 0.18 and 14.27 °C/s. SEM coupled with EDS and DSC techniques characterized the evolution rate of solid phases. The SEM/EDS data revealed that an Al10CeMn2 phase is present at higher cooling rates. At lower cooling rates, near the center of the casting, a proeutectic Al23Ce4Ni6 phase was more present. It was observed that up to 2.6 at. % of Mn was dissolved in this proeutectic Al23Ce4Ni6 phase, thereby removing a large portion of the available Mn for forming the Al10CeMn2 phase. DSC analysis showed differences in the samples' liquidus temperatures which is indicative of compositional variations. Inductively coupled plasma atomic emission spectroscopy (ICP-OES) and Scheil solidification simulations correlated the compositional differences to phase formation, which agreed with the SEM and DSC results. This experimentation provides insight into novel Al-Ce-Ni-Mn alloys and where their potential lies in industrial applications.

A method for accurately determining the chemical composition of deposits at the bottom of pores during the electrocoloring (e-coloring) of aluminum anodic oxide (AAO) layers in tin-based solutions is developed. The aluminum samples were AC e-colored after DC sulfuric anodization. Free-standing, tin e-colored aluminum oxide film was obtained by selective dissolution of the metallic aluminum from the AAO in copper chloride solution to access the deposit directly at the bottom of the pore. This allowed us to take XPS analysis directly from the deposits at pore bottoms without any interference from the base material or insulating barrier layer. The results revealed the presence of a mixture of tin oxide and metal in the deposits, which were richer in oxide content. Furthermore, a cyclic voltammetry experiment mimicking real polarization conditions during AC conditions was optimized and used to gain a deeper understanding of the electrochemical reactions that occur during AC electrocoloring. The comparison of CV results in tin-free and tin-containing electrolytes indicated that the tin deposited during a cathodic cycle is oxidized in the anodic cycle. The formation of tin based deposits radically changed the CV behavior. The XPS and cyclic voltammetry results consistently show that the deposits formed during e-coloring comprised a mixture of metallic and oxidic tin species richer in oxide content.

Impure and pure casts have collected reasonable attentions over all the world. In this paper, Aluminum (Al) and Copper (Cu) cast alloys are considered to be studied. Multiple impure and pure Al-Cu cast alloys are established under the condition of very high temperatures. Then, all of the established alloys are examined by applying mechanical tests. More specifically, tests of hardness are exploited. Moreover, different quenching conditions are employed and analyzed. These are the water, air and oil. Consistent results are separately obtained for the impure and pure materials.

We used atomistic molecular dynamics (MD) simulations to study polyelectrolyte brushes based on anionic α-L-glutamic acid and α-L-aspartic acid grafted on cellulose in the presence of divalent CaCl2 salt at different concentrations. The motivation is the search of the ways to control properties such as sorption capacity and the structural response of the brush to multivalent salts. For this detailed understanding of the role of side chain length, chemical structure and their interplay is required. It was found that in the case of glutamic acid oligomers, the longer side chains facilitate attractive interactions with the cellulose surface, which forces the grafted chains to lie down on the surface. The additional methylene group in the side chain enables side chain rotation enhancing this effect. On the other hand, the shorter and more restricted side chains of aspartic acid oligomers prevent attractive interactions to a large degree and push the grafted chains away from the surface. The difference in side chain length also leads to differences in other properties of the brush in divalent salt solutions. At a low grafting density, the longer side chains of glutamic acid allow the adsorbed cations to be spatially distributed inside the brush resulting in a charge inversion. With an increase in grafting density, the difference in the total charge of the aspartic and glutamine brushes disappears, but new structural features appear. The longer sides allow for ion bridging between the grafted chains and the cellulose surface without a significant change in main chain conformation. This leads to the brush structure being less sensitive to changes in salt concentration.

This paper presents a new method of preparing a coating on the Ti65 titanium alloy by a two-step procedure comprising hot-dipped aluminum and solid carburization. The effects of the carburization in the presence of NaCl deposit at 810oC have been systematically studied. In this article, the microstructure, morphology, phase composition of the coating, and the corrosion products were investigated by SEM, EDS, and X-ray diffraction. Results indicated that the corrosion resistance of hot dip aluminum/carburizing composite coating was not significantly enhanced by hot dip aluminum coating. This can be attributed to the formation of TiC and Ti3AlC after carburization, which promoted the formation of loose and unprotected TiO2 in the coating during molten salt corrosion. In addition, the oxidation of the carbon atom into CO2 /CO leaded to a high concentration of vacancy in the coating, creating channels for NaCl to penetrate the coating and accelerated the corrosion rate.

The analysis of high-temperature physicochemical properties of theK₃AlF₆-Na₃AlF₆-AlF₃ molten salt system is crucial for practical production of electrolytic aluminum. In this paper, the physicochemical properties of the K₃AlF₆-Na₃AlF₆-AlF₃ molten salt electrolyte system at 1173 K and standard atmospheric pressure were simulated using molecular dynamics calculations. The effects of Zr、B、C、W、Ti、Hf、Nb、and Ta on the radial distribution function, coordination number, viscosity and conductivity of the electrolyte system are discussed in detail. The simulation results show that the coordination number between Al-F and the conductivity is decreasing as the content of B²- increases. And the coordination number between Al-F and the viscosity is decreasing as the content of Zr⁴⁺ increases. With the addition of impurity elements such as C, W, Ti, Hf, Nb, and Ta, the data show that C has no significant effect on this electrolyte system, while the presence of W will decrease the coordination number between Al-F in the system. The presence of Ti, Hf, Nb, and Ta may intensify the decomposition reaction between one of the Al-F ligands, which increases the coordination number between Al-F and the number of ions in the electrolyte. This work provides theoretical support for the subsequent study of inert anodes containing Zr, B, Ti, Hf, Nb, and Ta.

This study utilized electron back scattered diffraction (EBSD) and X-ray diffraction (XRD) to investigate the impact of inter-annealing temperature and heating rate of final annealing on the microstructure of high-voltage anode aluminum foils. The findings indicate that the formation of cube texture in the final products is significantly influenced by the inter-annealing temperature, as low inter-annealing temperatures retain a considerable amount of deformation stored energy, providing a strong driving force for nucleation. The cube texture is observed to deviate from the ideal position at lower inter-annealing temperatures. Additionally, an increase in heating rate during final annealing leads to a gradual decrease in the fraction and grain size of recrystallization. This is attributed to the fact that a higher heating rate (below the critical heating rate) reduces the time available for grain boundary migration, thereby slowing the recrystallization process.

Light alloys machining is a widely implemented process that have usually used in presence of cutting fluids to reduce the wear impact and increase tool life. However, current environmental protection policies require their elimination in order to improve process sustainability. This fact forces to work under aggressive cutting conditions, producing adhesion wear that affects the integrity of the part surface. This study describes cutting tool wear mechanisms in machining of UNS A92024 samples under dry cutting conditions. EDS analysis showed the different composition of the adhered layers, while roughness was also positively affected by the change of the cutting geometry produced in the tool.

In this study composite with alternate layers of 5056 and 1580 alloys was manufactured by wire arc additive manufacturing technology. It is shown that increased strength characteristics of composite material can be obtained due to deformation treatment by high-pressure torsion (HPT) technique. The microstructure and mechanical properties of the HPT-processed material in different structural states were investigated. The HPT-processed material exhibits high value of ultimate tensile strength (~ 770 MPa) but low ductility. Short-term annealing at 250 oС and additional deformation by HPT to 0.25 of revolution at room temperature resulted in a slight decrease in material’s strength to ~ 700 MPa but provided ductility ∼ 9%. Physical mechanisms to improve plasticity in correlation with microstructure evolution is discussed.

A new process is reported for the incorporation of a fluoropolymer into a solid perovskite film. Poly(trifluoroethyl methacrylate) [CH2C(CH3)(CO2CH2CF3)]n was delivered to methylammonium lead iodide (CH3NH3PbI3) perovskite films by crystallizing the film in supercritical carbon dioxide/ethanol containing the dissolved fluoropolymer. The surface was characterized before and after fluoropolymer exposure using scanning electron microscopy, Raman spectroscopy and contact angle measurements. The results indicate that the fluoropolymer was incorporated into the perovskite film during the supercritical fluid crystallization process.

Introduction: Young adults are the second largest segment of the immigrant population in the United States (US). Given recent trends in later age of initiation of tobacco use, we examined variation in use of tobacco products by nativity status for this population group. Methods: Our study included young adults 18-30 years of age sampled in the National Health Interview Survey (2015-2019), a nationally representative sample of the US population. We calculated prevalence of use of any and 2 or more tobacco products (cigarettes, cigars, pipes, e-cigarettes, and smokeless tobacco) for foreign-born (n=3,096) and US-born (n=6,811) young adults. Logistic regression models adjusted for age, sex, race-ethnicity, education, and poverty, while accounting for the complex survey design. Results: Foreign-born young adults were significantly less likely to use any tobacco product (Cigarette = 7.3% vs 10.7%; Cigar= 1.8% vs 4.8%; E-cigarette= 2.3% vs 4.5%, respectively; p<0.01) or poly tobacco use (1.9% vs. 4.2%; p<0.01) than US-born young adults. Adjusted regression models showed lower odds of poly tobacco use among the foreign-born than their US-born counterparts (Odds Ratio = 0.41, (95% Confidence Interval: 0.26-0.63)). Conclusion: Findings highlight the importance of targeted interventions by nativity status and further tobacco prevention efforts needed for the US-born.

A bridged 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) derivative (PN-DOPO) in combination with aluminum phosphates coated sepiolite (Sep@AlPO4) was used to improve the flame retardancy, thermal stability and mechanical properties of poly (ethylene oxide) (PEO)/poly (butylene adipate-co-terephthalate) (PBAT) blends. The synergistic effects of PN-DOPO and Sep@AlPO4 on the fire resistance, thermal decomposition behavior and mechanical properties of PEO/PBAT composites were investigated systematically. The results indicated that 5 wt % Sep@AlPO4 combined with 10 wt% PN-DOPO into PEO/PBAT achieved a V-1 rating in UL-94 test and the LOI value increased to 23.7%, meanwhile, the peak-heat release rate (p-HRR), av-HRR and total heat release (THR) values of PEO/PBAT/PN10%/Sep5% composites decreased by 35.6%, 11.0% and 23.0% compared with those of PEO/PBAT, respectively. The thermogravimetric analysis (TGA) results confirmed that PN-DOPO/Sep@AlPO4 could enhance the initial thermal stability and char yield of PEO/PBAT matrix, and TGA/Fourier transform infrared spectrometry (TGA-FTIR) results revealed that the composites exhibited the absorption peaks of phosphorous-containing groups and an increase in gas-phase volatiles during the thermal decomposition process. The digital photographs and morphological structures of char residues demonstrated that PN-DOPO and Sep@AlPO4 mixtures benefited to the formation of a more continuous and dense carbon layer on the composites surface during combustion. Rheological behavior revealed that a higher storage modulus, loss modulus and complex viscosity of PEO/PBAT/PN-DOPO/Sep@AlPO4 composites could also promote the cross-linking structure during burning. Furthermore, the PEO/PBAT/PN-DOPO/Sep@AlPO4 composites exhibited excellent mechanical properties in terms of elongation at break and flexural performance than the PEO/PBAT system. All the results demonstrated that PEO/PBAT system modified by the combination of PN-DOPO and Sep@AlPO4 not only exhibited excellent synergistic effect on the flame retardance, but also had good improvement on thermal stability and mechanical properties, indicating the potential application in areas requiring fire safety.

This study investigated the relationship between aluminum adjuvant vaccines and the prevalence of 4 childhood diseases (Autism, Allergies, Asthma, ADD/ADHD) using data from the 2020-2021 National Survey of Children's Health (NSCH) [1] and the Centers for Disease Control National Immunization Survey (CDC NIS) [2]. The study found an association with aluminum adjuvant dosage and the prevalence of each disease studied (Autism, Allergies, Asthma, ADD/ADHD) through a weighted regression analysis of disease prevalence against the summed likelihood of aluminum adjuvant vaccine uptake.

Although 7055 aluminum alloy is a deformed aluminum alloy and will show excellent mechanical properties after recrystallization after large deformation, it is a method to enrich its application range if rare earth is added and the rare earth phase dispersion is promoted by heat treatment. This article used optical microscopy, scanning electron microscopy energy dispersive spectroscopy (SEM-EDS), X-ray diffraction (XRD), micro Vickers hardness and room temperature stretching methods to study the as-cast 7055-xEr (x=0wt.%, 0.2wt.%, 0.4wt.%, 0.6wt.%, 0.8wt.%) aluminum alloy after being subjected to 460 oC×3h homogenization and 410 oC×1h solid solution+150 oC×12h aging treatment the changes in microstructure and properties. The results indicated that: when 0.2wt.%Er was added to 7055 aluminum alloy after solution at 410 oC×1h and aging at 150 oC×12h, the dendrite structure was significantly reduced, the grain thinning was obvious and the distribution was uniform, Al8Cu4Er phase appeared in the lamellar eutectic η-Mg(Zn,Al,Cu)2 structure at grain boundaries, and the hardness reached 168.8HV. The yield strength, tensile strength and elongation were 542.12Mpa, 577.67MPa and 8.36%, respectively.

A technology for obtaining nanosized aluminum nitride powder by plasma-chemical synthesis is presented. Nitrogen gas (N2), melamine (C3H6N6) and ammonia (NH3) were used as a source of nitrogen. Aluminum powder of different fractions was used as a source of aluminum. The influence of the nitrogen source, the height of the injector, and the input power of the plasma equipment on the synthesized aluminum nitride powder is shown. The resulting aluminum nitride powder has a size d90=60 nm. The parameters of aluminum nitride synthesis did not in any way affect the granulometric composition of the synthesized powder materials. It was found that, due to the high binding energy, the nitrogen molecule (N2) reacts poorly with aluminum powder particles, as a result a mixture of nitrogen and ammonia gases was used in a ratio of 70/30 (mol.%) for aluminum nitride synthesis.

In this study, a summary of the processes performed on the SPL for recycling, reduction in toxicity and treatment were examined on an industrial and laboratory scale. In writing this research, an attempt has been made to address the useful processes that have taken place in this field. Spent pot lining or SPL is a type of solid waste that is produced in the aluminum production process. After 3 to 8 years, the cathode blocks become problematic and can no longer be used, and need to be replaced due to adverse effects on cell function. SPL is known to be a hazardous waste to nature due to its fluoride and cyanide content. Research has shown that SPL ingredients have destructive and very dangerous effects on human DNA, which is why they are so important to maintain and recycle.

Sugarcane is an important sugar-source crop. As any other plant, it can be exposed to several abiotic stress conditions. Though some metals contribute to critical physiological processes in plants, the presence of aluminum ions (Al3+) can be very toxic. In order to develop plants that flourish in acidic soils, it is critical to gain insights into the molecular mechanisms of sugarcane response to aluminum stress. To determine the genes involved in sugarcane response to aluminum stress we generated 372 million paired-end RNA sequencing reads, from roots of CTC-2 and RB855453 two contrasting cultivars. Data normalization resulted in 162,161 contigs and 97,335 trinity genes. After the read cutoff, the differentially expressed genes were 4,858 in CTC-2 and 1,307 in the RB855453, Treatment Vs Control, respectively. The differentially expressed genes were annotated into 34 functional categories. The majority of the genes were upregulated in the CTC-2 (tolerant cultivar) and down regulated in RB855453 (sensitive cultivar). Here, we present the first root-transcriptome of sugarcane under aluminum stress. The results and conclusions of this study provide a valuable resource for future genetic and genomic studies in sugarcane. This transcriptome analysis points out that sugarcane tolerance to aluminum may be explained by an efficient detoxification mechanism combined with the lateral root formation and activation of redox enzymes. Following our results, we present here, a hypothetical model for the aluminum tolerance in CTC-2 cultivar.

Strain induced melt activation process (SIMA) creates a globular microstructure which improves the hardness and ultimate tensile stress (UTS) of 7075 aluminum alloys. But, at the grain boundaries of SIMA processed 7075 aluminum alloy, presence of continuous and brittle intermetallic compounds and the eutectic structure result in decreasing mechanical properties, such as elongation, formability and etc. Hence, in order to improve microstructure and formability of 7075 aluminum alloy respect to SIMA process, a new process was done that is called two-step strain induced melt activation (TSSIMA). This process, which has been mentioned in the experimental procedure section, both organized globular structure and significantly modified the microstructure of the alloy compared to that of the SIMA method. It promoted discontinuity and more homogeneity in distribution of the precipitates and, approximately removed the eutectic mixture. Performing the rolling process on the alloy also revealed that it is more effective in formability enhancement in comparison with SIMA process. Also, it increased the hardness of 7075 aluminum alloy respect to that of SIMA process.

Poly(dA:dT) tracts cause nucleosome depletion in many species, e.g., at promoters and replication origins. Their intrinsic biophysical sequence properties make them stiff and unfavorable for nucleosome assembly, as probed by in vitro nucleosome reconstitution. The mere correlation between nucleosome depletion over poly(dA:dT) tracts in vitro and in vivo inspired an intrinsic nucleosome exclusion mechanism in vivo. However, we compile here published and new evidence that this correlation does not reflect mechanistic causation. 1) Nucleosome depletion over poly(dA:dT) in vivo is not universal, e.g., very weak in S. pombe. 2) The energy penalty for incorporating poly(dA:dT) tracts into nucleosomes is modest (<10%) relative to ATP hydrolysis energy abundantly invested by chromatin remodelers. 3) Nucleosome depletion over poly(dA:dT) is much stronger in vivo than in vitro if monitored without MNase and 4) actively maintained in vivo. 5) S. cerevisiae promoters evolved a biased poly(dA) versus poly(dT) distribution. 6) Nucleosome depletion over poly(dA) is directional in vivo. 7) The ATP dependent chromatin remodeler RSC preferentially and directionally displaces nucleosomes towards 5’ of poly(dA). Especially bias and directionality would not be expected for an intrinsic mechanism. Together, this argues for a mechanism where active and species-specific read out of intrinsic sequence properties, e.g., by remodelers, shapes nucleosome occupancy.

The Bacillus megaterium LVN01 species native to Colombia has demonstrated the ability to metabolize different co-products or industrial waste (such as fique juice, cane molasses, residual glycerol) and accumulate polyhydroxybutyrate (PHB), giving it potential in the bioplastics industry. In this research, the potential of liquid digestate as a carbon source for the production of PHA in fermentation processes with this bacterial strain was evaluated. Favorably, it was found that B. megaterium utilizes the nutrients from this residual substrate to multiply appropriately and efficiently synthesize poly(hydroxybutyrate-co-hydroxyvalerate) (PHBV). Bench scale aerobic batch fermentation, under the operational conditions of this research [Volume: 3L; Temperature: 30.8°C; Agitation: 400 rpm; pH: 7.0 ± 0.2; Disolved Oxygen: 100% saturation; Antifoam 10% (v/v)], generated maximum values of DCW (0.56 g cell L-1) at 60 h, while the maximum PHB yield (360 mg PHB L-1) occurred at 16 h, which is very favorable for sustainable degradable bioplastics production. Additionally, GC-MS and NMR analyses confirmed that the PHBV copolymer synthesized by B. megaterium is made up of the monomers 3-hydroxybutyrate (3HB) and 3-hydroxyvalerate (3HV). Furthermore, the thermal properties determined by TGA (Tonset=283.1 ºC, Tendset= 296.98 ºC. Td =290.114 °C) and DSC (Tm= ºC155.7 °C, ΔHf= 19.80 J g-1, Xcr = 18.17%), indicate that it is a thermally stable biopolymer with low percentages of crystallinity, providing flexibility that facilitates molding, adaptation, and application in various industrial sectors.

Aluminum, a contentious trace element found in the environment, has been demonstrated to have harmful effects on both humans and animals. In contrast, Sempervivum tectorum, an evergreen plant, has been found to offer numerous beneficial effects for both humans and animals. Therefore, this study aims to assess the protective effect of S. tectorum on certain reproductive biomarkers in male rats exposed to aluminum. Thirty-five Wistar rats were randomly divided into five groups: NTC (no-treatment control) received distilled water; NC (negative control) received drinking water containing 1 mg/L aluminum sulfate (AS); E1 received 1 mg/L AS along with an 8% S. tectorum extract; PC (positive control) received only 8% S. tectorum extract; E2 received 1 mg/L AS for three months followed by 8% extract for one month. The study analyzed testosterone, LH, FSH, body weight, and the histological structure of the testis, epididymis, and prostate, as well as the levels of zinc, manganese, copper, and iron in these organs. Significant decreases in body weight, testis, and epididymis size were observed in the aluminum-exposed groups compared to the control, whereas these decreases were not significant in the S. tectorum-treated groups compared to the control. Aluminum exposure led to significant decreases in testosterone and LH levels, with FSH levels showing a non-significant decrease in males, which were mitigated significantly by the administration of the plant extract. Histological analysis revealed alterations in the testis, epididymis, and prostate of the AS-exposed groups, including necrosis of seminiferous tubule epithelium and Leydig cells in the testis, and basal epithelial necrosis in the epididymis and prostate. Aluminum levels increased in all organs studied, while levels of zinc, copper, iron, and manganese decreased, showing a negative and significant correlation with aluminum levels. The aqueous extract of S. tectorum demonstrated a protective effect on certain studied biomarkers in male rats affected by aluminum exposure.

Hypoeutectic Al-Si-Cu-Mg alloys are promising candidates for use in automobile parts. Therefore, various attempts have been made to develop alternative casting technologies to improve the mechanical properties of cast alloys. In this study, the effects of modification with different levels of strontium (Sr) on primary and eutectic silicon (Si) in hypoeutectic Al-Si-Cu-Mg alloys were investigated. Using a gravity cast process, the Sr-modified samples were prepared from melts with four levels (100, 200, 300, and 400 ppm) of Sr. In addition, the wear properties of the cast samples were studied using a block-on-ring wear-testing machine. The sizes of the primary Si phases increased with increasing Sr content in the alloys. Moreover, more finely dispersed eutectic Si was observed with higher Sr content. In frictional wear tests, the specific wear rates of the test specimens decreased as the Sr content increased from 200 to 400 ppm. Coarse Si phases are considered to act as solid lubricants in the contact region during sliding.

Modified aluminum slag (MAS) was applied as an adsorbent for Congo red (CR) prepared by the hydrothermal treatment of Ca (OH) 2. At 25 ℃, with a MAS dosage of 0.3g, initial CR concentration of 100 mg/L and initial pH=5, and the adsorption time was 40 min, the CR removal efficiency was 98.41%. The adsorption trend of CR conformed to the second-order kinetics, and the adsorption isotherm follows the Freundlich isotherm model. Compared with RAS, MAS has a larger pore volume and specific surface area. The mechanism of action of MAS on CR was the interaction between membrane diffusion and internal diffusion, and the adsorption rate during the membrane diffusion was the fastest.

The current study aimed to evaluate the influence of different sintering temperatures on the properties of copper aluminum oxide (CuAlO₂) pellets synthesized from copper oxide (CuO) and aluminum hydroxide (Al(OH)₃) for application in smart infrastructure systems. The pellets were sintered at 400 K, 1000 K, and 1300 K, in the presence of nitrogen gas flow to reduce the amount of oxygen availability. The CuAlO₂ sintered nanoparticles were chemically analyzed by X-ray diffractometry, and the nanostructure of the materials was studied by scanning electron microscopy. The transmittance of the sintered materials was examined by ultraviolet/visible (UV/Vis) spectrophotometry, and 88% transparency was observed for the pellets sintered at 1300 K. Electrical conductivity was measured at 0.905 mS/cm, indicating a semiconducting behavior.

Transient liquid phase (TLP) bonding of Al-6063 and UNS S32304 was performed using copper foil as an interlayer between the base metals. A compression load was applied normal to the specimens. Metallurgical examination of the produced joints showed three distinct regions including a reaction zone, diffusion affected zone and the base metals. The diffusion of copper into aluminum resulted in an Al-Cu eutectic structure. However, the oxide layer on the aluminum surface controlled the dissolution behavior of copper and the extent of its wettability with the base metals. Although voids and intermetallic compounds were detected at the interfaces of the processed joints, a defect free joint was produced at 570°C. In addition, the results from corrosion tests showed that the use of copper as an interlayer decreased the corrosion resistance of the joints. However, increase in thickness of the joining reaction zone with increasing bonding temperature was observed to increase corrosion resistance.

Aluminum is a strategic mineral resource, and China’s aluminum production and consumption is fairly large. However, its supply guarantee is uncertain because of a high dependency on external raw materials. This uncertainty may expand, so finding a way to reduce the uncertainty of aluminum resource supply is especially important. This paper applies the SFA method to analyze the aluminum flows in mainland China from 1996 to 2014, and establishes a supply structure model to measure its supply guarantee degree. The results claim that: (1) China’s aluminum production can satisfy demand and even create a surplus; (2) Domestic self-productive primary and secondary aluminum increased at an annual rate of 12% and 24%; (3) The proportion of self-productive secondary aluminum in the supply structure increased from 7.7% in 1996 to 12.8% in 2014, while that of primary aluminum decreased from 79.6% to 42.8%; (4) The total supply guarantee degree decreased from 87.3% to 55.6% in this period. These results provide a feasible way to solve this plight: the proportion of secondary aluminum in the supply structure should be enhanced, and an efficient aluminum resource recycling system needs to be established as soon as possible to ensure its sustainable supply.

The wealth of data obtained during the past 20 years using Laser-Induced Breakdown Spectroscopy (LIBS) indicates that the technique is very promising to detect small chemical contents of alloying elements. The potential of LIBS was looked more seriously during the past two decades or so as more data were obtained on Aluminum and steel to study the phenomena in the condition of local thermodynamic equilibrium and time-delay between a Q-switch laser and an intensified CCD camera. Since the past decade, some data on compounds were also shown to be useful in determining small concentrations of harmful elements. This manuscript is intended to show that the technique of LIBS performance is very promising in fields such as micro-machining, in alloying element analysis, surface cleaning and environmental applications even with lightweight spectrometers having a relatively low resolution, which can potentially be air-borne.

Organic compounds that contain poly-triazole are very important intermediates in pharmaceutical and chemical industry. Click chemistry is one of essential reactions that can form C-N bond with high atom economy. The research progress in metals catalyzed Click chemistry of azides and alkynes from the perspective of reaction mechanism is categorized and summarized.

Malignant melanoma is a highly aggressive type of cancer that requires radical treatment strategies to inhibit the cancer cell progression and metastasis. In recent years, preclinical research and clinical trials on melanoma treatment are considerably focused on the adjuvant-based immunotherapy for enhancing the immune response of innate immune cells against cancer cells. However, the clinical outcome of these adjuvant-based treatments are inadequate due to improper delivery system for these immune activators to reach the target site. Hence, we developed a vaccine formulation containing tumor lysate protein (TL) and poly I:C (PIC) complexed with positively charged poly (sorbitol-co- polyethylenimine (PEI)(PSPEI). The resulting ionic PSPEI-polyplexed antigen/adjuvant (PAA) (PSPEI-PAA) nanocomplexes were stable at the physiological condition, non-toxic and enhanced intracellular uptake in immature dendritic cells. In murine B16F10 tumor xenograft model, PSPEI-PAA nanocomplexes significantly suppressed tumor growth and did not exhibit any noticeable sign of toxicity. Additionally, the cytotoxic T lymphocytes (CTLs) assay involving co-culturing of splenocytes isolated from the PSPEI-PAA-treated mice with that of B16F10 cells significantly revealed enhanced cancer killing by the TL-reactivated CTLs compared to untreated control mice bearing tumor. Therefore, we strongly believe that PSPEI-PAA nanocomplexes could be an efficient antigen/adjuvant delivery system and also enhance the antitumor immune response against melanoma tumor in the future clinical trials.

Poly(acrylic acid) (PAAc) hydrogels possess good bioadhesive properties and allow enhanced penetration of drugs. In addition, it is possible to localize the absorption site of the drug in the hydrogel and increase the drug residence time. As opposed to other cross-linking processes radiation-induced polymer cross-linking can be easily and rapidly carried out without the use of cross-linking agents and other chemical additives. In this study, we fabricated metronidazole (MD) containing PAAc hydrogel (MD/PAAc) with different MD contents (0.1, 0.25, 0.5 wt%) using varying radiation doses (25, 50, 75 kGy) by gamma-irradiation. The physical and thermal properties were determined by gel content analysis, swelling ratio measurements, compressive strength measurements, differential scanning calorimetery, and thermogravimetric analysis. The properties of the hydrogel degraded due to the crystalline nature of MD. The properties of the hydrogel degraded due to the crystalline nature of MD. Cumulative release observed after 50 min in the case of 0.5MD/PAAc and 0.1MD/PAAc was 50% and 10%, respectively. Our findings suggest that MD/PAAc could be a suitable drug delivery carrier for use with radiation-based techniques.

Beyond factors such as smoking and obesity, the risk of getting gastrointestinal cancer is passed down from parents to offspring, inherited by a gene mutation, predisposing them to develop cancer in their lifetime. Here we describe the clinical history of family members affected by gastrointestinal pathologies often leading to cancer. In the epidemiological study, the cohort of members of this family shared a high risk of developing gastrointestinal diseases. The subjects were monitored from May 2006 to December 2017 by collecting periodically clinical and endoscopic data, and determining both auto-modification of lymphocyte Poly(ADP-ribose)Polymerase as early signal of DNA damage, and erythrocyte membrane lipid composition (Fat Profile). Both biomarkers were demonstrated to be non invasive and easy tools, to monitor over time family members, first the oldest members (nine siblings), and thereafter their offspring, whose cell status evolved from physiological even to cancerous one. All subjects developed gastrointestinal pathologies of different kind and seriousness. Some diseases evolved to cancer, sometimes as a sudden and lethal event. The results of the two molecular approaches, agreed and even predicted the clinical and imaging paths. This cohort study supported the hypothesis that both noninvasive molecular analyses can predict altered cell states and support clinical and imaging tests.

Fluorophores with a tetraphenylethylene (TPE) core are attracting increasing interest because of their aggregation-induced emission (AIE) behaviour, which makes them particularly suitable when dispersed in thin-layer films. We propose the synthesis and use of a novel TPE fluorophore (hereafter called TPE-BPAN) decorated with two dimethylamino push groups and a 4-biphenylacetonitrile pull moiety. In tetrahydrofuran solutions, TPE-BPAN showed a broad absorption spectrum, and an intense emission is observed when a non-solvent as water is added in amounts of 70% and above. We selected and synthetized five different polymer matrices for TPE-BPAN with decreasing polarity: a) poly(methylmetacrylate) homopolymer (PMMA); b), c), and d) three copolymers of methyl methacrylate and cyclohexyl methacrylate at different compositions (P(MMA-co-CHMA) 75:25, 50:50, 25:75 mol%); e) poly(cyclohexyl methacrylate) homopolymer (PCHMA). The presence of a less polar comonomer as cyclohexyl methacrylate appeared to enhance the emission behaviour of TPE-BPAN, which displayed the highest quantum yield (QY) in P(MMA-co-CHMA) 75:25 in all the range of concentration studied from 0.4 wt.% to 2.0 wt.%. Further reduction in polarity lowered QY to the values of PMMA films; also, lower adhesion to the glass and a marked fragility of the films were observed. Referring to the P(MMA-co-CHMA) 75:25 films, QY values decreased from over 40% at 0.4 wt.% to about 30% at 2.0 wt.%, which is still helpful for energy harvesting applications such as luminescent solar concentrators (LSC). LSC performances were not significantly affected by the matrix's lower polarity and resulted in around one-third of the state-of-the-art due to the lower QY of TPE-BPAN. The theoretical investigation on density functional theory (DFT) clarified the origin of the observed AIE and the role played by the environment in modulating the photophysical behaviour.

Additive Friction Extrusion Deposition (AFED) is a recently developed additive manufacturing technique that promises high deposition rates at low forces. Due to the novelty of the process, the underlying phenomena and their interactions are not fully understood, and in particular the processing strategy and tool design are still in their infancy. This work contributes to the state of the art of AFED through a comprehensive analysis of its working principles and an experimental program including a representative sample component. The working principle and process mechanics of AFED are broken down into their individual components. Forces, their origins and effects on the process are described, and measures of process efficiency and theoretical minimum energy consumption are derived. Three geometrical features of the extrusion die are identified as most relevant to the active material flow, process forces and deposition quality: the topography of the inner and outer circular surfaces and the geometry of its extrusion channels. Based on this, the experimental program investigates seven different tool designs in terms of efficiency, force reduction and throughput. The experiments using AA 6061-T6 as feedstock show that AFED is capable of both high material throughput (close to 550 mm³/s) and reduced substrate forces: For example, the forces for a run at 100 mm³/s remained continuously below 500 N, and for a run at 400 mm³/s below 3500 N. Material flow and microstructure of the AFED are assessed from the macrosections. Significant differences are found between the advancing and retracting sides for both process effects and material flow. Banded structures show strong similarities to other solid state processes. The fabrication of the sample components demonstrates that AFED is already capable of producing industrial grade components. In mechanical testing, interlayer bonding defects result in a more brittle failure behavior in the direction of the structure, in the microstructure show strong similarities to other solid-state processes. The manufacturing of the sample components demonstrates that AFED is already capable of producing industrial grade components. In mechanical tests, interlayer bonding defects result in a more brittle failure behavior in the direction of the structure, while in the horizontal direction of the structure mechanical properties corresponding to a T4 temper have been achieved.

This study aims to investigate a friction stir welded joint between steel and aluminum alloy. Friction stir welding is nowadays one of the most interesting joining technique due to the possibility to connect materials and thicknesses that are difficult or impossible to weld with traditional techniques. The main advantage is that Materials are not affected by thermal cycle problems during solidification and cooling and the absence of fumes and pollution during the process favors the quality of the welded joint. The life of metal joints could be greatly reduced in a corrosive environment, since the less noble material will tend to increase its corrosion rate while the nobler one will reduce its electrochemical dissolution. Accelerated ageing tests (i.e. salt fog test) are used to estimate the lifetime of metal joints in highly aggressive environments. The aim of the present work is to evaluate the durability at long ageing time in salt spray test (according to ASTM B117) of carbon steel/aluminum alloy joints, obtained by FSW. In this first part, mechanical tests results are reported. A deep metallographic and chemical investigation are going to be reported in the part 2.

Sr4Al6O12SO4 samples were obtained from the compound mixture formed by a solid–state reaction of Al2O3, SrSO4, and SrCO3. Samples were compacted at 100MPa to form pellets of 1 and 4cm in diameter and were sintered at 1400°C for 4 hours. The compound was analyzed by X–ray diffraction. Static immersion and wettability tests were performed to evaluate corrosion resistance in contact with Al–Si. Corrosion tests were carried out by immersion at 800, 900, and 1000°C for 24, 50, and 100 hours, while wettability was carried out at 900, 1000, and 1100°C for 2 hours. Subsequently, the samples were prepared metallographically. Samples were analyzed by optical microscopy, scanning electron microscopy, and image analysis. In general, reaction products consisting of alumina, spinel, oxides, and sulfates were found. The contact angles obtained were 124° to 135°. It is concluded that ceramic substrate Sr4Al6O12SO4 is resistant to corrosion by Al–Si alloy, since the slight thickness of the reaction products found in the samples (100μm) considering the severe conditions of the experiment: 1000°C and 100 hours of isothermal temperature. Furthermore, it can be said that Sr4Al6O12SO4 is not wettable by Al–Si alloys.

Sodium-potassium (NaK) liquid alloy is a promising candidate for use as anode material in sodium batteries because of its fluidity, which effectively suppresses the growth of sodium or potassium dendrites. However, the poor wettability of the NaK liquid alloy on conventional metal substrates is unfavorable for cell fabrication due to its strong surface tension. In this paper, low-density and low-cost fluorinated aluminum foam is used as a substrate support material for NaK liquid alloy. By combining low surface tension NaK@C with fluorinated aluminum foam, we obtain a uniformly distributed and structurally stable electrode material. The composite electrode has a cycling stability of more than 3000 hours in a symmetrical cell. Furthermore, when coupled with a sulfurized polyacrylonitrile cathode in carbonate electrolyte, it maintains excellent stability even after 800 cycles, with 72% of capacity retention.

Epoxy was blended with benzoxazine resin and aluminum trihydrate (ATH) additive to render flame retardancy while maintaining mechanical properties. The ATH was modified using three different silane coupling agents and then added to 60/40 epoxy/benzoxazine mixtures. The effect of blend compositions and surface modification on flame retardant and mechanical properties of the composites was investigated by UL94, tensile, and shear tests. Resin mixtures containing more than 40 wt% benzoxazine revealed a UL94 V-1 rating with enhanced tensile and shear strength. Upon addition of 20 wt% ATH to 60/40 epoxy/benzoxazine, a V-0 rating was achieved. The lowered tensile and adhesive properties of the composites in the presence of ATH were improved by modifying the ATH surface using silane coupling agents.

Background: Aluminum phosphide (AlP), also known as “rice tablet,” is widely used as an effective pesticide. However, AlP poisoning is a common cause of mortality in many countries, such as Iran. Unfortunately, there is no specific antidote for AlP toxicity to date. AlP releases phosphine gas when it is exposed to moisture and acid. Phosphine is a robust mitochondrial toxin that could significantly inhibit cellular energy metabolism. AlP poisoning is an emergency condition that needs instant and effective intervention. Dihydroxyacetone (DHA) is a simple saccharide used for several pharmacological as well as cosmetic purposes. Previously, we found that DHA could significantly prevent mitochondrial impairment induced by toxic agents such as cyanide and phosphine in various in vitro and in vivo experimental models.Methods: Hospitalized patients (n = 111) were evaluated for eligibility criteria. Among these patients, n = 35 cases were excluded due to incomplete data (n = 11) and suspicion of poisoning rather than AlP (n = 24). Meanwhile, n = 76 cases with confirmed AlP poisoning were included in the study. AlP-poisoned patients who did not receive DHA (n =18) were used as the control group.Patients (n = 58) received at least one dose of DHA (500 ml of 5% DHA solution w/v, i.v.) in addition to routine treatment of AlP poisoning. Arterial blood gas (ABG), blood pH, bicarbonate levels, and other vital signs and biochemical measurements were monitored. Moreover, the mortality rate and time of hospitalization were evaluated in both DHA-treated (n = 58) and AlP-poisoned patients without DHA administration (n = 18). Several biomarkers were assessed before (upon hospitalization) and after DHA treatment. The routine tests for AlP-poisoned patients in this study were the measurement of electrolytes (K+ and Na+), WBC, RBC, hemoglobin, INR, carbonate (HCO3), blood pH, PaCO2, and PaO2 and SGPT, SGOT, BUN, Cr. Results: Upon patients' admission, significant decreases in blood pH (acidosis), blood PaO₂, and HCO₃ levels were the hallmarks of AlP poisoning. It was found that DHA significantly alleviated biomarkers of AlP poisoning and tremendously enhanced patients’ survival rate compared to patients treated based on hospital routine AlP poisoning protocols (no DHA). No significant adverse effects were evident in DHA-treated patients in the current study.Interpretation: These data suggest that parenteral DHA is a novel and effective antidote against AlP poisoning.Trial registration: IR.SUMS.REC.1394.102

The conductor aluminum alloys Al-0.25wt.%Zr doped additionally with Х = Er, Si, Hf, and Nb were the objects of investigations. The fine-grained microstructure in the alloys was formed by Equal Channel Angular Pressing and Rotary Swaging. The thermal stability of the microstructure, specific electrical resistivity, and microhardness of the novel conductor aluminum alloys was investigated. The mechanisms of nucleation of the Al3(Zr,X) secondary particles during annealing the fine-grained aluminum alloys were determined using Jones-Mehl-Avrami-Kolmogorov equation. Using Zener equation, the dependencies of the mean secondary particle sizes on the annealing time were obtained on the base of analysis of the data on the grain growth in the aluminum alloys. The secondary particle nucleation during long-time low-temperature annealing (300 оC, 1000 hrs) was shown to go preferentially at the cores of the lattice dislocations. The Al-0.25%Zr-0.25%Er-0.20%Hf-0.15%Si alloy subjected to long-time annealing at 300 оC has the optimal combination of the microhardness and electrical conductivity (59.8%IACS, Hv = 480 ± 15 MPa).

The research was undertaken to study the way deformation behaves in ultrafine-grained (UFG) conducting Al-Zr alloys doped with Sc, Hf, and Yb. All in all, 8 alloys were studied with zirconium partially replaced by Sc, Hf, and/or Yb. Doping elements (X = Zr, Sc, Hf, Yb) in the alloys total 0.4 wt.%. The choice of doping elements is conditioned by possible precipitation of Al3X particles with L12 structure while annealing these alloys. Such particles provide higher thermal stability of a nonequilibrium UFG microstructure. Initial coarse-grained samples were obtained by induction casting. The UFG microstructure in the alloys was formed by Equal Channel Angular Pressing (ECAP) at 225°C. Superplasticity tests were carried out at temperatures ranging from 300 to 500 °C and strain rates varying between 3.310-4 and 3.310-1 s-1. The highest values of elongation to failure are observed in Sc-doped alloys. A UFG Al-0.2%Zr-0.1%Sc-0.1%Hf alloy has maximum ductility: at 450 °C and a strain rate of 3.310-3 s-1, relative elongation to failure reaches 765%. At the onset of superplasticity, stress–strain curves are characterized by a stage of homogeneous strain and a long stage of localized plastic flow. The dependence of homogeneous strain (eq) on test temperature in UFG Sc-doped alloys is increasing uniformly, which is not the case for other UFG alloys with eq(T) dependence peaking at 350-400 оС. Strain rate sensitivity coefficient of flow stress m is small and does not exceed 0.26-0.3 at 400-500 °C. In UFG alloys containing no scandium, m coefficient is observed to go down to 0.12-0.18 at 500 оС. It has been suggested that lower m values are driven by intensive grain growth and pore formation in large Al3X particles, which develop specifically at the ingot crystallization stage.

The solid-state welding method known as friction stir welding (FSW) bonds two metallic work parts, whether the same or different, by plastically deforming the base metal. The frictional resistance between both metallic work pieces causes them to produce heat, which produces plastic deformation and welds them. However, the weldability and strength of FSW joints mainly depend on the FSW parameters. This review work highlights the previous research work on the FSW parameters and their effects on the weldability and quality of the aluminum alloys joined with similar and dissimilar metals through the FSW method. About 150 research studies were systematically reviewed, and the articles included data from peer-reviewed journals. It has been concluded that the key parameters, including welding speed, “rotational speed”, “plunge depth”, “spindle torque”, “shoulder design”, “base material”, “pin profile” and “tool type", significantly affect the weldability of the aluminum joint through the FSW method. Also, the selection of these parameters is important and fundamental as they directly affect the joint. It is recommended that future work focus on FSW for aluminum. Among these, the most essential is the application of artificial intelligence (AI) techniques to select the optimum FSW parameters for aluminum welding.

Microalgal harvesting is one of the most challenging processes in the development of algal research and development. Several methods, such as centrifugation, flocculation, and filtration, are available at the laboratory scale. However, the requirement of expensive pieces of equipment and the possibility of biomass contamination are recurring gaps that hinder the development of microalgae I+D in different parts of the world. Recently, the electroflotation has been proved as a suitable method for the harvesting of different species of microalgae and cyanobacteria. To this day, there are no companies that sell laboratory-scale electroflotation equipment; this is mainly due to the gap in the knowledge on which factors (time, mixing rate, number of electrodes, and others) will affect the efficiency of concentration without reducing the biomass quality. This paper aims to build an innovative low-cost electroflotation system under 300 USD with cheap and resistant materials. To achieve our goal, we test the interaction of three variables (time, mixing rate, and amount of electrodes) were evaluated. Results showed that an efficiency closer to 100% could be achieved under 20 minutes using >10 electrodes and 150 rpm. We hope this innovative approach can be used by different researchers to improve our knowledge of the concentration and harvesting of algae and cyanobacteria.

In this paper, the effect of preheating on the mechanical properties and micro structure of similar friction stir welded AA6061 aluminum alloys sheets was investigated. Aluminum alloy 6061 sheets with a thickness of 5 mm and threaded cylindrical pins were used. Rotation and traverse speeds were 1200 rpm and 75 mm/min, respectively. The results of tensile tests performed on the welded samples showed that compared to the non-preheated samples, preheating had increased the strength and elongation of the joints by 58% and 46%, respectively. In the present study, during the welding process preheating cause emerged heat with lower slope from stir zone. This phenomenon may result in Increase the deformation resistance of material and consequently decrease of grain size. This grain refinement can improve the mechanical properties of welds. Accordingly, hardness and strength of the material will be increased.

This paper seeks to model the crack propagation in of AAs (aluminum-alloys) 2524-T3 and 7050-T7452 subjected to fatigue loading at low temperature. Fatigue crack growth tests were performed on AAs 2524-T3 and 7050-T7452 subjected to constant-amplitude and actual random-spectra loading histories at room temperature of about 25 °C and at cryogenic temperature of -70 °C, respectively, to determine their crack growth properties and residual lives. The interaction mechanisms between cryogenic temperature and the fatigue load were deduced on the basis of the results of fractographic analysis. Temperature-dependent residual lives under actual random-spectrum load history were modeled based on a modified accumulation damage rule by accounting for the load interaction. Good correlation was achieved between the predictions and actual experiments, demonstrating the practical and effective use of the proposed method.

In this paper we report a new development on the numerical model for aluminum-steam combustion. This model is based on diffusion flame of continuum regime and the thermal equilibrium between the particle and the flow field, which can be used to calculate the aluminum particle combustion model for two phase calculation conditions. The model prediction is in good agreement with the experimental data. A new type of vortex combustor was proposed for the combustion of aluminum and steam, and the mathematical model of the two phase reacting flow with in this combustor was established. The turbulence effects are modeled using the Reynolds Stress Model (RSM) with Linear Pressure-Strain approach, and the Eddy-Dissipation model is used to simulate the gas phase combustion. Aluminum particles are injected into the vortex combustor and form a swirling flow around the chamber and their trajectories are traced using the Discrete Phase Model (DPM). The simulation results show that the vortex combustor can achieve high efficient combustion of aluminum and steam. The influencing factors, such as the eccentric distance of the inlet of aluminum particles, particle size and steam inlet diameter, etc., are studied. The work described in this paper represents an attempt to the design of a vortex combustor in order to increase aluminum combustion efficiency.

Base excision repair (BER) is the predominant pathway to remove most forms of hydrolytic, oxidative and alkylative DNA damage. The precise functioning of BER is achieving by the regulation of each step by regulatory/accessory proteins, with the most important of which being poly(ADP-ribose) polymerase 1 (PARP1). The PARP1 regulatory functions extend to many cellular processes including regulation of mRNA stability and decay. PARP1 can therefore affect BER both at the level of the BER proteins and at the level of their mRNAs. Systematic data on how the PARP1 content affects the activities of key BER proteins and the levels of their mRNAs in human cells are extremely limited. In this study the CRISPR/Cas9 based technique has been used to knocked out the PARP1 gene in the human HEK 293FT line. The obtained cell clones with putative PARP1 deletion were characterized by several approaches including: PCR analysis of deletions in genomic DNA, Sanger sequencing of genomic DNA, qPCR analysis of PARP1 mRNA, western-blot analysis of whole-cell-extract proteins with anti-PARP1 antibodies, and the PAR synthesis in the whole-cell-extracts. qPCR analysis of mRNAs coding the BER related proteins: PARP2, uracil DNA glycosylase 2, AP endonuclease 1, DNA polymerase β, DNA ligase III and XRCC1 did not reveal crucial influence of PARP1 knockout. The corresponding catalytic activities in the whole-cell extracts (WCEs) evaluated in parallel did not differ significantly between mutant and parental cell lines. No considerable influence of poly(ADP-ribose) synthesis on the activity of the above WCE enzymes was revealed.

Curcumin attracts a huge attention because of its biological properties: antiproliferative, antioxidant, anti-inflammatory, immunomodulatory and so on. However, its usage has been limited by poor water solubility and low bioavailability. Herein, to solve these problems we developed curcumin-loaded nanoparticles based on end-capped amphiphilic poly(N-vinylpyrrolidone). Nanoparticles were obtained using the suspension method and were characterized by dynamic and electrophoretic light scattering, transmission electron microscopy and atomic force microscopy. The average particle size was 200 nm, and ζ-potential was -4 mV. Curcumin release studies showed that nanoparticles are stable in water solution. In vitro release study showed prolonged action in gastric, intestinal and colonic fluids, consistently and in PBS. In vitro studies on epidermoid carcinoma and human embryonic kidney cells showed that the cells absorbed more curcumin in nanoparticles compared to pure curcumin. Nanoparticles are safe for healthy cells and show high cytotoxicity for glioblastoma cells in cytotoxicity studies in vitro. Median lethal dose was determined in acute toxicity assay on Zebrafish and was 23 μM. Overall, the curcumin-loaded nanoparticles seem promising for cancer treatment.

Water-soluble nonionic surfactant, pentaethylene glycol monododecyl ether, C12E5, spontaneously blooms to the surface of spin-cast hydrophobic polyiso-prenes, generating hydrophilic surfaces. This system represents a simple model for hydrophilic chemical modification of rubbery polymers yet demonstrates surprisingly rich, complex and unexpected behaviour. The ver-tical depth profiles were quantified using neutron reflectometry (NR) and deuterated surfactant, and the surface properties were characterized using con-tact angle analysis and atomic force microscopy (AFM). Despite the low surface tension of the toluene solvent used in film preparation and the low surface en-ergy of the PI matrix, NR depth profiles revealed clear evidence of surfactant segregation. This surface layer was typically thicker than a monolayer, but incomplete, yet was remarkably stable with respect to dissolution, even when exposed to hundreds of thousands of times the volume of water required to dissolve all the surfactant on the surface. Despite the apparent resistance to removal from the surface, water exposure does alter the subsequent wettabil-ity of the surface, with a hydrophilic-to-hydrophobic transition occurring after rinsing. Complementary AFM images of these C12E5 / cis-PI films showed unexpected strand-like features on the surface of the film, which we attribute to a non-uniform lateral distribution of some of the surfactant. This surface structure becomes more evident after rinsing, and it appears that there are two distinct populations of surfactant on the PI film surface. We conclude that some of the bloomed surfactant exists as layers, which are relatively inert with respect to rinsing or surface modification, and some is laterally inhomogene-ous. This latter population is primarily responsible for surface wetting be-havior, but is not detected by specular NR.

Here, we present a series of novel block copolymers (BCP) from bio-derived monomers, poly(lactic acid)-block-poly(2,5-furandimethylene succinate) (PLA-b-PFS), in which the furan groups from PFS block can be crosslinked with bis(maleimido) triethylene glycol (M2) through a Diels-Alder reaction. This dynamic crosslinking reaction leads to a network structure for enhancing the mechanical properties compared to their linear BCP analogous. Decreasing the crosslinking density leads to a decrease of glass transition temperature of BCPs and a transition from glassy to rubbery-like behavior at room temperature. This allows a wide tunablity of both elastic moduli and yields of the materials. For the lowest crosslinking density. the material exhibits an over 50% self-healing efficiency at room temperature after five days, attributed to the low Tg (15.2 C) from the introduction of PFS block, allowing sufficient chain mobility for structure re-organization. Moreover, with the appropriate selection of crosslinking density (PLA-b-PFS/M2 (6/1)), it also shows an excellent shape memory property with a high recovery rate of 96.3% and a fixity rate of 97.3%. The permanent shape can be rewriteable due to the reversibility of Diels-Alder reaction. With these advanced functionalities and ease in large-scale fabrication, the PLA-b-PFS/M2 shows great promises for self-healing coatings or films with shape memory properties in a wide variety of applications such as packaging materials

Delivery systems of the biologically active substance such as proanthocyanidins (PCAN) produced through the electrospinning method were designed using a blend of poly(L-lactide-co-glycolide) and poly[(R,S)-3-hydroxybutyrate]. The research involved the structural and thermal characteristics of the developed electrospun three-dimensional fiber matrix, as well as hydrolytic degradation tests performed on them. Additionally, the release profile of PCAN from the electrospun nonwoven was determined using UV–VIS spectroscopy. Approximately 30% of PCAN was released from the tested electrospun nonwoven during the initial 15-20 days of incubation. The chemical structure of water-soluble oligomers that were formed after the hydrolytic degradation of the developed delivery system was identified through electrospray ionization mass spectrometry. Oligomers of lactic acid and OLAGA oligocopolyester, as well as oligo-3-hydroxybutyrate terminated with hydroxyl and carboxyl end groups, were recognized as degradation products released into the water during the incubation time. It was also demonstrated that variations in the degradation rate of individual mat components influenced the degradation pattern, and the number of formed oligomers. The obtained results suggest that the incorporation of proanthocyanidins into the system slowed down the hydrolytic degradation process of the poly(L-lactide-co-glycolide)/poly[(R,S)-3-hydroxybutyrate] three-dimensional fiber matrix. In addition, in vitro cytotoxicity and antimicrobial studies advocate the use of PCAN for biomedical applications with promising antimicrobial activity.

: The paper presents the results of uniaxial tensile tests of samples of hypoeutectic aluminum-silicon alloy A319. According to the results of which the influence of surface treatment by a pulsed electron beam on the mechanical properties of the material was determined. The peculiarities of localization of deformation in the material, caused by grinding of the surface layer material structure due to rapid crystallization during electron beam treatment were revealed. The surface treatment up to 100 µm depth leads to the formation of a fine dendritic columnar structure of silumin and to an increase in the plasticity of the samples. The influence of surface treatment affects the increase of deformation localization in the region of stable concentrator before failure. The largest increase in ductility and localization of deformation occurs during processing with energy density of 15 J/cm2. In the process of specimen deformation, unstable, metastable, and stable areas of plastic deformation localization are formed and replaced, and the formation of stable areas of localized plastic deformation, in which the specimen fails at the end of the test, can be detected at the initial stages of testing. In specimens, during testing in the zone of localized plastic deformation, bands are formed that pass through the entire surface of the specimen at an angle from 35 to 55 degrees to the axis of tension, their evolution leads to the formation of stable zones of localized plastic deformation and to the failure of the specimen.

The results of the study of the influence of the size of cylindrical samples of A5N aluminum on the time and rate of their cooling are presented. According to experimental data, the temperature dependence of the heat transfer coefficient for pure metals is calculated. It revealed that the process of cooling of the aluminium and its alloys has a relaxation behavior. It has found that the main mechanisms of natural air cooling are convection heat transfer and radiation. The characteristic cooling time due to radiation is less than due to convection. The contribution of thermal radiation is noticeable at high temperatures. It was found that the characteristic times of cooling due to radiation and convection increase with increase in volume to area ratio of the sample.

Magnesium and Aluminum alloys continue to be important in the context of modern and lightweight technologies. With the advancement of additive manufacturing (AM), components can be produced directly in a net shape, widen up the usage of magnesium and aluminum alloys as well as holding new ideas for the application of unique physical structures made feasible by 3D printing. Laser-based approach, one of the metal additive manufacturing (AM) methods, enables the formation of arbitrary 3D structures. With promising findings, research in this area is advancing quickly, bringing up a variety of potential applications in both the scientific and industrial sectors. Complex structures can now be manufactured easily utilizing AM technologies to meet the pre-requisite objectives like reduced part numbers, greater functionality, and lightweight, among others. AM has the ability to meet demands by lowering costs and speeding up the manufacturing process. Due to their popularity in numerous high-value applications, aluminum, and magnesium alloys are one of the key material systems being researched in the laser-based additive manufacturing approaches. The review here aims to comprehensively examine the additive manufacturing of magnesium and aluminum alloys, highlighting the influence of the laser-based additive manufacturing approach on the mechanical characteristics, microstructure, and tribological performance of magnesium and aluminum alloys.

Since the first generation of 7xxx superhard aluminum alloy was investigated in 1930, hitherto the fifth generation aluminum alloy materials with high comprehensive properties such as high static strength, high strength, heat resistance, high toughness, damage resistance, low density and low quenching sensitivity have been improved and developed. This paper reviews the progress of 7xxx aluminum alloy materials in composition, microstructure, properties, preparation methods, heat treatment strengthening and applications from 2014 to 2021. The effect of adding trace elements on microstructure and properties of 7xxx series alloy and the problems existing in aging precipitation characteristics and reinforcement mechanism are discussed. The future development direction of 7xxx superhard aluminum alloy is prospected by optimizing heat treatment technological, adding appropriate trace elements to alloy and controlling alloy microstructure.

The 8Nb isopleth section of a Ti-Al-Nb system is experimentally determined based on thermal analysis and thermodynamic calculation methods to obtain the phase transformation and equilibrium relations required for material design and fabrication. The phase transus and relations for the 8Nb-TiAl system show some deviations from the calculated thermodynamic results. The ordered βo phase transforms from the disordered β/α phases at 1200–1400 °C over a large Al concentration range, and this transformation is considered to be an intermediate type between the first- and second-order phase transitions. Moreover, the βo phases are retained at the ambient temperature in the 8Nb-TiAl microstructures. The ωo phase transforms from the highly ordered βo phase, rather than from α2 or βo with low degree of atom ordering B2 (LOB2) structure, with Al concentration of 32–43 at.% at approximately 850 °C. From the experimental detection, the transition of the ωo phase from the βo phase is considered to be a further ordering process.

This study aims to identify an optimal heat-treatment parameter set for an additively manufactured AlSi10Mg alloy in terms of increasing the hardness and eliminating the anisotropic microstructural characteristics of the alloy in as-built condition. Furthermore, the influence of these optimized parameters on the fatigue properties of the alloy investigated. In this respect, microstructural characteristics of an AlSi10Mg alloy manufactured by Laser-Based Powder Bed Fusion in non-heat-treated and heat-treated conditions were investigated. Their static and dynamic mechanical properties were evaluated, and fatigue behavior was explained by a detailed examination of fracture surfaces. Much of the microstructure in the non-heat-treated condition was composed of columnar grains oriented parallel to the build direction. Further analysis revealed a high fraction of pro-eutectic α-Al. Through heat-treatment, the alloy was successfully brought to its peak-hardened condition, while eliminating the anisotropic microstructural features. Yield strength and ductility increased simultaneously after heat-treatment, which is due to the relief of residual stresses, preservation of refined grains, and introduction of precipitation strengthening. The fatigue strength, calculated at 10^7 cycles, improved as well after heat-treatment and finally detailed fractography reviled that a more ductile fracture mechanism has happened in the heat-treated condition compared to the non-heat-treated condition.

Several challenges stand in the way of production of Metal Matrix Composites (MMCs) such as higher processing temperatures, particulate mixing, particulate-matrix interface bonding issues and ability to process into desired geometrical shapes. Although there are many literatures showing composites with single particulate reinforcements, the studies on composites with multiple reinforcing agents (hybrid composites) are found to be limited. Development of a hybrid particulate composite with optimized mechanical and tribological properties is very significant to suit modern engineering applications. In this study, Al-Si hypereutectic alloy (A390) is used as the matrix and Silicon Carbide (SiC) and Graphite (Gr) and Molybdenum di-Sulphide (MoS₂) are used as particulates. Particulate volume (wt%) is varied and sample test castings are made using squeeze casting process through stir casting processing route. The evaluation of mechanical properties indicates that presence of both the hard phase (SiC) and the soft phase has distinct effect on the properties of Hybrid Composite. Composite samples were characterized to understand the performance and to meet the tribological applications. Fractography study indicated an intra-granular brittle fracture for hybrid composites. Wear study shows that Hybrid MMCs has better tribological performance compared to that of A390 alloy.

Iron powders having average particle sizes of ~40µm are mechanically mixed thoroughly with aluminum powders ranging from 1 to 10 in wt.% with an average particle size of ~10µm. Two different powder metallurgical techniques cold and hot pressing are used to study the effect of the additive element powder on the mechanical properties, wear properties and the microstructure of the iron based alloys. The hot pressing technique was performed at a temperature up to 500°C at 445.6 MPa. The cold pressing technique was performed at 909 MPa in room temperature. By increasing the Al content to 10 wt. % in the base Fe-based matrix, the hardness was decreased from 780 to 690 MPa and the radial strength was decreased from 380 to 202 MPa with reductions of 11.5% and 40%, respectively. Improvement of the wear resistance with the increase addition of the Al powder to the Fe matrix up to 5 times was achieved compared to the alloy without Al addition for different wear parameters namely; wear time and sliding speed.

Aluminum alloy Al 2024-T3 were successfully joined using friction stir spot jwelding joining (FSSW). Satisfactory joint strengths were obtained at different welding parameters (tool rotational speed, tool plunge depth, dwell time) and tool pin profile (straight cylindrical, triangular and tapered cylindrical). Resulting joints were welded with welded zone. The different tools significantly influenced the evolution on the stir zone in the welds. Lap-shear tests were carried out to find the weld strength. Weld cross section appearance observations were also done. The macrostructure shows that the welding parameters have a determinant effect on the weld strength (x: the nugget thickness, y: the thickness of the upper sheet and SZ: stir zone). The main fracture mode was pull out fracture modes in the tensile shear test of joints. The results of tensile shear tests showed that the tensile-shear load increased with increasing rotational speed in the shoulder penetration depth of 0.2 mm. Failure joints were obrerved in the weld high shoulder penetration depth and insufficient tool rotation.

In this work, we investigated for the first time the complexation of sepiapterin (SP), the natural precursor of the natural essential cofactor tetrahydrobiopterin, that displays mild water-solubility and short biological half-life, with the hydrophobic triacetyl-β-cyclodextrin (TAβCD) to improve its encapsulation within methoxy-poly(ethylene-glycol)-poly(epsilon-caprolactone) (mPEG-PCL) nanoparticles. First, TAβCD-SP complexes were produced by spray-drying of TAβCD/SP binary solutions by utilizing the Nano Spray Dryer B-90 HP. Then, dry powders were characterized by differential scanning calorimetry (DSC), Fourier-transform infrared spectroscopy (FTIR) and transmission and scanning electron microscopy (SEM and TEM, respectively) and compared to the complex components and physical mixtures (PMs). Next, SP was encapsulated within methoxy-poly(ethylene-glycol)-poly(epsilon-caprolactone) (mPEG-PCL) nanoparticles by nanoprecipitation of a SP/TAβCD complex/mPEG-PCL solution. In addition to complex nanoencapsulation, we assessed encapsulation of pure SP by nanoprecipitation with an intermediate step, which comprised the co-drying of SP, TAβCD and mPEG-PCL copolymer solution in organic solvent; this step aimed to promote the formation of molecular interactions between SP, TAβCD and the PCL blocks in the copolymer. SP-loaded mPEG-PCL nanoparticles were characterized by dynamic light scattering (DLS) and SEM. Nanoparticles with size of 74-75 nm and small polydispersity index (PDI <0.1) were obtained when SP-TAβCD equimolar spray-dried complex was used for nanoencapsulation, and SEM analysis indicated the absence of free SP crystals. Moreover, the encapsulation efficiency (%EE) and drug loading (DL) were 85% and 2.6%, respectively, as opposed to those achieved with pure SP encapsulation (14% and 0.6%, respectively). Overall, our results confirm that spray-drying of SP/TAβCD solutions at the appropriate molar ratio leads to the hydrophobization of the relatively hydrophilic SP molecule, enabling its encapsulation within mPEG-PCL nanoparticles.

This study aimed to investigate the effect of potassium poly-γ-glutamate (PGA-K) on mice fed a high-fat diet consisting of 60% of total calories for a duration of 12 weeks. PGA-K administration reduced the increase in body weight, epididymal fat, and liver weight caused by a high-fat diet compared to the obese group. The triglyceride, low-density lipoprotein cholesterol and high-density lipoprotein cholesterol levels, which are blood lipid indicators, were significantly increased in the obese group but were significantly decreased in the PGA-K-treated group. The administration of PGA-K resulted in a significant inhibition of pro-inflammatory cytokines, including tumor necrosis factor α and interleukin 6. Moreover, the levels of leptin and insulin, which are insulin resistance indicators, significantly increased in the obese group but were significantly decreased in the PGA-K-treated group. These results suggest that PGA-K exhibits a protective effect against obesity induced by a high-fat diet, underscoring its potential as a candidate for obesity treatment.

Nanofibers are one of the most attractive materials that can modify functionalities for developing new kinds of specific applications, mainly used as a biomedical material. Herein, we designed and prepared the antibacterial nonwoven fiber mats of PLA and PLA composited with Ag nanoparticles by electrospinning. The effects of varying filler contents on their chemical, surface morphology, thermal, water absorbency, and antibacterial properties were investigated using FTIR, SEM/EDS, DSC, swelling ratio, and qualitative and quantitative antibacterial tests. FTIR and EDS spectra indicated that Ag nanoparticles were incorporated in the PLA without chemical bonding. SEM revealed that the average diameter of the PLA nanofibers containing the Ag nanoparticles was more significant than those without those particles. Besides, fiber diameters are proportionally the amount of Ag nanoparticle contents. DSC indicated that the Ag nanoparticles can be incorporated within the PLA-matrix without strongly affecting their thermal properties. Moreover, the crystallinity of the composite nonwoven fiber mats was higher than those of fiber mats in the neat PLA. Accordingly, the antibacterial activities revealed that all the composite nanofiber mats exhibited excellent against S. aureus and E. coli bacterial strains. In addition, in the cell toxicity study, all produced hybrids nonwoven fiber mats induced a reduction in cell viability for the L929 fibroblast cells. Our results suggest that the designed and prepared nonwoven fiber mats may have good potential for use in the biomedical field, particularly in wound dressing applications

Due to the growing interest in biopolymers, biosynthesizable and biodegradable polymers currently occupy a special place. Unfortunately, the properties of native biopolymers are not satisfactory, which explain that attempts are being made to modify them. The work attempts to improve the properties of poly(3-hydroxybutyrate) (P3HB) using linear aliphatic polyurethane (PU) based on 1,4-butanediol and hexamethylene 1,6-diisocyanate. The conducted studies on the effect of the amount of PU used (5, 10, 15 and 20 wt.%) showed an improvement in the thermal properties of the prepared polymer blends. There was an increase in the degradation temperature of the ob-tained blends in relation to the native P3HB by 12-57C, and the difference between the melting point and the degradation point was above 100°C for most of the obtained blends. As part of the tested mechanical properties of the new polymer blends, we noted the desired increase in the tensile strength, in the relative elongation at break and in the impact strength with a decrease in hardness, in particular with the presence of 5 wt.% PU. Therefore, for further improvement, hybrid nanobiocomposites with 5 wt.% PU and organically modified montmorillonite (MMT – Cloisite 30B) were produced. The nanoadditive was used in typical amount of 1-3 wt.%. The nanostructure of the biocomposites produced by extrusion was examined by small-angle X-ray scattering (SAXS) and transmission electron microscopy (TEM), the morphology by scanning electron microscopy (SEM), and compatibility by infrared spectroscopy (FT IR). In addition, selected mechanical properties were determined and thermal properties were tested by the thermogravimetric analysis (TGA) and the standard differential scanning calorimetry (DSC). The polyester and polyurethane chains penetrated into the interlayer spaces of organically modi-fied nanoclay – Cloisite30B and the complete delamination occurred during direct mixing in the extrusion process. FT IR spectral analysis showed the compatibility of the polymer biocomposite components by the coexistence of intermolecular interactions in the form of hydrogen bonds. The morphology studies of the produced hybrid nanobiocomposites showed an interaction of the bi-opolymer matrix with PU and Cloisite30B and the formation of easily migrating polyester-polyurethane-montmorillonite adducts, which resulted in improved mechanical properties com-pared to the properties of the native P3HB and P3HB-PU compositions. The influence of the presence of a nanofiller on the properties of the prepared nanobiocomposites was tested and it was found that, as expected, the smallest amount of nanofiller provides the best results.It was found that the obtained nanobiocomposites containing the smallest amount of nano-fillers, i.e. 1 wt.% Cloisite30B exhibited the best mechanical and thermal properties. The desired decrease in hardness by 15% and a higher value of impact strength by 15%, an increase in elonga-tion at break by 60% and an increase in thermal stability of the newly produced biocomposites compared to to the native P3HB were observed. The prepared nanobiocomposites combined the best features caused by the elasticizing effect of polyurethane and the formation of P3HB-PU-MMT adducts.

Poly-DADMAC (PD) is a common organic polymer used as an effective coagulant in water treatment. yet its residue in water raises several concerns regarding membrane fouling and the production of carcinogenic compounds. Therefore, fast and simple quantification is necessary to control and monitor the optimal poly-DADMAC concentration dose with minimal negative effects. This study introduces a new colorimetric quantification method for poly-DADMAC, based on complexation with a cationic dye (fast green- FG). The method was examined through varying conditions that included different analytical and commercial poly-DADMAC formulations and concentrations. The experiments confirm its effectiveness in quantifying poly-DADMAC with a detection limit of 3.22 µg L-1 (0.02 µM based on monomers' molecular weight), which is one order of magnitude lower than regulatory requirements (50 µg L-1). To validate the method, the effect of pH was examined, and implementation demonstrations were conducted on cyanobacteria and cowshed polluted water samples. This research presents a new, fast, easy to apply, and cost-effective method to accurately quantify poly-DADMAC, improving water treatment strategies and allowing high quality purification and water reuse.

Nanomaterials such as pH-responsive polymers are promising for targeted drug delivery systems, due to the difference in pH between tumor and healthy regions. However, there is a significant concern about the application of these materials in this field due to their low mechanical resistance, which can be mitigated by combining these polymers with mechanically resistant inorganic materials such as mesoporous silica nanoparticles (MSN) and hydroxyapatite (HA). Mesoporous silica has interesting properties such as high surface area and hydroxyapatite has been widely studied to aid in bone regeneration, providing special properties adding multifunctionality to the system. Furthermore, fields of medicine involving luminescent elements such as rare earth are an interesting option in cancer treatment. The present work aims to obtain a pH-sensitive hybrid system based on silica and hydroxyapatite with photoluminescent and magnetic properties. The nanocomposites were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), nitrogen adsorption methods, CHN elemental analysis, Zeta Potential, scanning electron microscopy (SEM), and transmission electron microscopy (TEM), vibrational sample magnetometry (VSM), and photoluminescence analysis. Incorporation and release studies of the antitumor drug doxorubicin were performed to evaluate the potential use of these systems in targeted drug delivery. The results showed the luminescent and magnetic properties of the materials and showed suitable characteristics for application in the release of pH-sensitive drugs.

.Functionalization of multi-walled carbon nanotubes (MWNTs) surface with sulfonated poly(ether ether ketone) SPEEK chains using hexane diamine (HAD) as the interlinking molecule was investigated. MWNTs were first oxidized by nitric acid to generate carboxyl groups on their surface. Grafting of SPEEK chains on the MWNTs surface was achieved using hexane diamine as a cross-linking molecule. The attachment took place after the reaction of amine groups with carboxyl groups of oxidized MWNTs and sulfonate groups of SPEEK as confirmed by infrared (FTIR) analysis. Scanning electron microscopy (SEM) showed that MWNTs were packed into a dense and compact structure. Transmission electron microscopy (TEM) showed that the nanotubes were wrapped by polymer chains and arranged in a bundle like structure. These observations reveal that some of MWNTs were interconnected by SPEEK chains.

Poly (Lactic Acid) (PLA) / Ground Tire Rubber (GTR) blends using Dicumyl peroxide (DCP) as a crosslinking agent were prepared as a route to recycle wastes rubber from the automotive industry. The GTR were exposed to grinding and exhibited mechanical damage, traduced at the rubber network scale by chains scission and/or chemical cross-links breakage. Such damage is accompanied by a decrease of 80% of the rubber chains network density of the initial tire buffing but found independent on the type of grinding (cryogenic, dry ambient) or on the GTR size (from <400 µm to <63 µm). Moreover, the finest sieved GTR contain the largest the amount of reinforcing elements (carbon black, clay) that can be advantageously used in PLA/GTR blends. The melt-blending of these finest GTR particles obtained by cryo-grinding at an amount of 15 wt.% and in presence of the crosslinking agent (DCP), resulted in an optimum improvement of the ductility, energy at break and impact strength of the PLA/GTR blends as compared to neat PLA, while maintaining its stiffness. The results were attributed to (i) the good dispersion of the fine GTR particles into the PLA matrix, (ii) the partial re-crosslinking of the GTR particles and co-crosslinking at PLA/GTR interface and (iii) the presence of reinforcing carbon black into the GTR particles and clay particles dispersed into the PLA matrix.

Motivation by the definition of the type 2 poly-Bernoulli polynomials introduced by Kim-Kim [9], in the present paper, we consider a new class of new generating function for the Fubini polynomials, called the type 2 poly-Fubini polynomials by means of the polyexponential function. Then, we derive some useful relations and properties. We show that the type 2 poly-Fubini polynomials equal a linear combination of the classical of the Fubini polynomials and Stirling numbers of the first kind. In a special case, we give a relation between the type 2 poly-Fubini polynomials and Bernoulli polynomials of order r. Moreover, inspired by the definition of the unipoly-Bernoulli polynomials introduced by Kim-Kim [9]. We introduce the type 2 unipoly-Fubini polynomials by means of unipoly function and give multifarious properties including derivative and integral properties. Furthermore, we provide a correlation between the unipoly-Fubini polynomials and the classical Fubini polynomials.

Poly lactic acid (PLA) has made inroads for commercial market segment with lot many unique characteristics such as tenacity, low flame rate, moisture regain percentage, loss of ignition percentage, heat of combustion, UV resistance, Elastic recovery and higher melting point allowed it to be the fastest moving material in today's commercial market. An attempt has been made to test the feasibility and biocompatibility aspect of PLA with cement mix. The basic strength and physical test results were carried out and published in an article, to the continuation of the work, micro-structural study was conducted to evaluate the elemental characteristics. Thermo gravimetric analysis revealed that PLA either in granular form or filament will hold good for the inclusion into construction applications, provided degradation aspects are to be looked out for improvisation. From DSC it was found that PLA in filament form is the best inclusion material for construction application, however the tenacity of fibers has to checked, as currently available filaments in market does not have high tenacity value. From EDX reports, 30% inclusion of PLA as replacement for fine aggregate has constituent members as Calcium carbonate(CaCO3), Silica(SiO2) and Wollastonite (CaK) resulted in best composition among the rest. FESEM images revealed that, proper gradation in size, rough surface of PLA granular form or filament form will definitely enhance the mechanical/physical or even chemical behavior of PLA.

Synthesis of poly(o-phenylenediamine) (PoPD) and poly(o-phenylenediamine)-ZnO (PoPD-ZnO) nanocomposites on carbon steel by in-situ polymerization with HCl acid as doping acid Material coating. The composition and structure of PoPD-ZnO nanocomposites were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The corrosion protection ability of polymer coatings in 3.5% NaCl was studied by potentiodynamic polarization curves and electrochemical impedance spectroscopy. It can be seen from the electrochemical corrosion experimental data that PoPD-WPU coating (PWC) and PoPD-ZnO-WPU coating (PZWC) can effectively improve the corrosion resistance of the carbon steel substrate, and the corrosion rate is reduced by 2-3 orders of magnitude compared with carbon steel. The conclusion demontrates that PoPD can effectively extend the service life of carbon steel substrates. In addition, it is advantageous to form a compact and low-defect coating when added nano-particle ZnO, which is advantageous for the POPD film to develop its good barrier property and corrosion resistance.

Polymer-based piezoelectric biomaterials have already proven their relevance for tissue engineering applications. Further, the morphology of the scaffolds plays also an important role in cell proliferation and differentiation. The present work reports on poly(hydroxybutyrate-co-hydroxyvalerate) (PHBV), a biocompatible, biodegradable and piezoelectric biopolymer that has been processed in different morphologies, including films, fibres, microspheres and 3D scaffolds. Further, the corresponding magnetically active PHBV-based composites were also produced. The effect of the morphology on physico-chemical, thermal, magnetic and mechanical properties of pristine and composites samples was evaluated, as well as their cytotoxicity. It was observed that the morphology does not strongly affect the properties of the pristine samples but the introduction of cobalt ferrites induces changes in the degree of crystallinity that could affect the applicability of prepared biomaterials. Young modulus is dependent of the morphology and also increases with the addition of cobalt ferrites. Both, pristine and PHBV/cobalt ferrite composite samples are no cytotoxic, indicating their suitability for tissue engineering applications.

Limonene epoxide (1,2 limonene oxide) readily reacts with carbon dioxide in a ring opening copolymerization reaction with insertion of CO₂ and formation of polycarbonates of exceptional chemical and physical properties. Both poly(limonene carbonate) and poly(limonene dicarbonate) can be synthesized using low cost Zn or Al homogeneous catalysts. This study addresses selected relevant questions concerning the technical and economic feasibility of limonene and carbon dioxide polymers en route to the bioeconomy.

A new approach for the preparation of polymer brush was developed via the union of controlled/“living” radical polymerization and click chemistry. The application of the approach realized the more quickly and accurate design and synthesis of the polymer brushes. A novel functional polymer brush of poly(acrylonitrile-g-glycidyl methacrylate) with tremendous application potential in the field of biology has been successfully synthesized via the new approach. The reaction conditions of click chemistry were optimized with the reaction time and the reactant ratio and judged from UV-vis spectra. Under the optimum of click chemistry, the novel functional polymer brushes were prepared. The GPC, FTIR analyses, 1H NMR spectrum and TGA were employed to ensure the successful synthesis of poly(acrylonitrile-g-glycidyl methacrylate) polymer brushes.

A new and easy-to-make polymer film sensor was prepared by dip-coating technique and this film used as fluorescent chemosensor for the detection of metal ions in aqueous solution. The proposed film sensor exhibited dual emissions at 540 and 582 nm under a single excitation wavelength. The fluorescence behavior of this film sensor toward metal ions has been investigated using these two wavelengths. The proposed sensor was found to show selectivity and sensitive to Fe³⁺ ion when compared the other metal ions in deionized water with excellent photostability. Detection limit of the polymeric film sensor was calculated as 86.15 and 28.90 μM. The results showed that the sensor can be successfully applied to the determination of Fe³⁺ ions in aqueous media. Contact angle measurement of PAZU film probe was also investigated and the result showed that the proposed film probe has hydrophobic property.

Electrospinning is the versatile technique to generate large quantities of micro- or nano-fibers from a wide variety of shapes and sizes of polymer. Natural bone is a hierarchically composites with the dispersion of inorganic ceramic along organic polymer. The aim of this study, the electrospun poly (lactic acid) (PLA) mats coated with chitosan (CH) and calcium silicate (CS) powder were fabricated. The morphology, chemical composition, and surface properties of CS/CH-PLA composites were characterized by scanning electron microscopy, X-ray diffraction, and Fourier transform infrared spectroscopy. In vitro, the CS/CH-coated PLA mats increased the formation of apatite on the surface when soaking in cell cultured medium. During culture, the adhesion and proliferation of the human mesenchymal stem cells (hMSCs) cultured on CS/CH-PLA were significantly promoted relative to those on PLA. Collagen I and fibronectin levels and promoted cell adhesion were observed upon an increase in CS content. Further, compared to PLA mats without CS/CH, CS10 and CS15 mats markedly enhanced the proliferation of hMSCs as well as their osteogenesis properties, which was characterized by bone-related gene expression. Our results demonstrated that the biodegradable and electroactive CS/CH-PLA mats had potential application as an ideal candidate for bone tissue engineering. Together, findings from this study clearly demonstrated that PLLA-C2S composite scaffold may function as an ideal candidate for bone tissue engineering.

We report the synthesis and characterization of Poly Methyl-Meth-Acrylate (PMMA)/Poly vinylalcohol (PVA) polymeric blend doped with different concentrations of Copper oxide (CuO) nanoparticles (NPs). The (PMMA-PVA)/CuO nanocomposite hybrid thin films (wt. % = 0%, 2%, 4%, 8%, and 16%) of CuO NPs are deposited on glass substrates via dip-coating technique. The transmittance (T%), reflectance (R%), the absorption coefficient (α), the optical constants [refractive index (n), extinction coefficient (k)], optical dielectric functions [ɛ',ɛ''] are investigated and interpreted. Tauc, Urbach, Spitzer-Fan, and Drude models are employed to calculate the optical bandgap energy (Eg) and the optoelectronic parameters of the nanocomposite thin films. The refractive index and optical bandgap energy of of (PMMA-PVA) polymeric thin film are found to be (1.5 to 1.85) and 4.101 eV, respectively. Incorporation of specific concentrations of CuO-NPs in (PMMA-PVA) polymeric thin films leads to a noticeable decrease in the optical bandgap energy and to an increase of the refractive index. Moreover, Fourier Transform Infrared Spectroscopy (FTIR) transmittance spectra are measured and analyzed for undoped and doped polymeric thin films to pinpoint the major vibrational modes in the spectral range (500 and 4000 cm-1), as well as, the nature of network bonding in both systems. Thermal stability of thin films is investigated by performing thermogravimetric analysis (TGA). The TGA thermograms confirm that both doped polymeric thin films are thermally stable at temperatures below 110°C which enables them to be attractive for a wide range of optical and optoelectronic applications. Our results indicate that optical, vibrational and thermal properties of both polymeric thin films can be tuned for specific applications by the appropriate corporation of particular concentrations of CuO-NPs.

Translation is spatiotemporally regulated and ER-associated mRNAs are generally in efficient translation. It is unclear whether the ER-associated mRNAs are deadenylated or degraded on the ER surface in situ or in the cytosol. Here, we showed that ER possessed active deadenylases, particularly the poly(A)-specific ribonuclease (PARN), in common cell lines and mouse tissues. Consistently, purified recombinant PARN exhibited a strong ability to insert into the Langmuir monolayer and liposome. ER-anchored PARN was found to be able to reshape the poly(A) length profile of the ER-associated RNAs by suppressing long poly(A) tails without significantly influencing the cytosolic RNAs. The shortening of long poly(A) tails did not affect global translation efficiency, suggesting that the non-specific action of PARN towards long poly(A) tails was beyond the scope of translation regulation on the ER surface. Transcriptome sequencing analysis indicated that the ER-anchored PARN trigged the degradation of a small subset of ER-enriched transcripts. The ER-anchored PARN modulated the translation of its targets by redistributing ribosomes to heavy polysomes, suggesting that PARN may play a role in dynamic ribosome reallocation. During DNA damage response, MK2 phosphorylated PARN-Ser557 to modulate PARN translocation from the ER to cytosol. By promoting the decay of ER-associated MDM2 transcripts with low ribosome occupancy, the ER-anchored PARN modulated DNA damage response and thereby cell viability. These findings revealed that a highly regulated communication between mRNA degradation rate and translation efficiency is present on the ER surface in situ and that PARN may contribute to this communication by modulating the dynamic ribosome reallocation between transcripts with low and high ribosome occupancies.

The effects of different pulse frequencies on the microstructure grain size and solid solubility of Al-9Si alloy were systematically investigated using OM, SEM, and EDS. The effects on the mechanical properties of the alloy were analyzed using micro-Vickers hardness tester and multifunctional friction tester. During the solidification process, the Al-9Si alloy is exposed to high-frequency electric current pulses with a current density of 300A/cm2 and frequencies of 0Hz, 500Hz, 1 000Hz, and 2 000Hz. The experimental results show that as the high-frequency pulse frequency increases, the Lorentz force also increases. The intense electromagnetic stirring leads to grain refinement. However, as the pulse frequency continues to increase, the combined effect of Joule heating and Lorentz force results in an enlargement of the melt zone and an increase in grain size. At a pulse frequency of 1 000Hz, the eutectic structure size of the Al-9Si alloy is optimal, with the average size reduced to 13.87μm and a dense distribution, effectively eliminating primary Si. The EDS results revealed that the high-frequency pulse led to a more uniform distribution of Si elements within the matrix, and the solid solubility of Si in the α-Al matrix increased to a maximum value of 1.99%, representing a 39.2% increase. At a pulse frequency of 1 000Hz, the sample demonstrates the most favorable mechanical properties, with the friction coefficient reaching a minimum value of 0.302, representing a 37.7% decrease in the average friction coefficient. The results demonstrate that high-frequency pulsing is an effective method for enhancing the mechanical properties of Al-9Si alloy.

Structural evolution, mechanical and tribological properties of Al-Mg alloy admixed with 5, 10 and 15 vol.% of iron powder using multi-pass friction stir processing (FSP) have been studied. Homogeneous distribution of intermetallic compound (IMC) particles were achieved after 4 FSP passes what resulted in increasing the stir zone hardness and ultimate tensile stress with simultaneous loss in the ductility. The reinforcement of the aluminum alloy matrix with IMCs allowed reducing wear at the same magnitude of friction. Subsurface composite tribological layer was formed on the FSPed samples as a result of rubbing against a steel counterbody.

Statistical analysis of mechanical properties of thin-walled samples (~500 microns) obtained by selective laser melting from AlSi10Mg material and subjected to heat treatment for 1 hour at temperatures from 260 °C to 440 °C (step of aging temperature change 30 °C) has shown that the maximum strain hardening in the stretching diagram section from yield strength to tensile strength is achieved at the heat treatment temperature equal to 290 °C. At carrying out of correlation analysis statistically significant positive correlation between deformation corresponding to yield strength and the sum of heights of the largest protrusions and depths of the largest depressions of the surface roughness profile within the basic length of the sample (Rz) and the full height of the surface roughness profile (Rmax) was established. It was found that the reason for the correlation is the presence of cohesive states between the extreme values of the surface roughness profile that persist along the entire length of the specimen.

Precipitates are the primary source of strength for the Al-Mg-Si alloy. Aluminum alloy in the peak-aged state mainly contain β'' and β' precipitates. In the past, most of the literature only considered the strengthening effect of β''. Here we develop a single crystal intensity model including both precipitate enhancement effects for the first time. This model was subsequently implemented into a crystal plastic finite element method to model the uniaxial tensile process of a polycrystalline aggregate model of Al-Mg-Si alloy. The simulation results for uniaxial stretching are in good agreement with the experimental results, confirming that the constitutive parameters used for the single crystal strength model with two precipitates are based on realistic physical implications. Furthermore, by comparing the uniaxial tensile simulation results of a peak-aged alloy considering the actual precipitated phase composition of the alloy with those assuming that the precipitated phase is only the β'' phase, the predicted tensile strength of the former is around 5.65% lower than that of the latter, suggesting that the two kinds of precipitation should be considered separately when simulating the mechanical response of Al-Mg-Si alloy. It is highly expected that the present simulation strategy is not limited to the Al-Mg-Si alloys, and it can be equally applied to the other age-enhanced alloys.

The cast grains of the 7055 aluminum alloy were refined by adding Sm + Er, and the proper heat treatment procedure was utilized to further precipitate the rare earth phase in order to increase the alloy's strength and toughness. The grain size, microstructure and phase were characterized by optical microscopes (OM), Scanning electron microscopy - energy spectrum (SEM-EDS), XRD diffractometer (XRD). The macroscopic hardness, yield strength and tensile strength of alloy materials were measured by hardness meter and universal electronic tensile machine. The results shown that the as-cast sample and the heat treatment sample all exist Al10Cu7Sm2 and Al8Cu4Er rare earth phase; But after heat treatment, the volume percentage of the rare earth phase dramatically increased and the dispersion was more unified. When 0.3wt.%Sm and 0.1wt.%Er were added, the grain size could be refined to 53μm. With the increase of the total content of rare earth elements, the refining effect first increased and then decreased. Under 410 oC solid solution for 2h + 150oC aging for 12h, the macroscopic hardness, yield strength, tensile strength and elongation of 0.3wt.%Sm + 0.1wt.%Er+7055 as-cast sample were 155.8HV, 620.5Mpa, 658.1Mpa, and 11.90%, respectively.

In this paper, in order to provide proper parameters for the preparation of semi-solid billets, the semi-solid annealing of hot-rolled 2A14 Al alloy was investigated. The microstructure was characterized by X-ray diffraction (XRD), scanning electron microscope (SEM) with X-ray energy dispersive spectrometer (EDS) and electron backscattered diffraction (EBSD), scanning transmission electron microscope (STEM). XRD results show that with the increase of temperature, equilibrium θ-Al2Cu gradually dissolved in the matrix. The EDS results of SEM and STEM show that there were coarse θ-Al2Cu phase, ultra-fine precipitate Al(MnFeSi) or (Mn, Fe)Al6 phase and atomic clusters in the microstructure. EBSD results show that the recrystallization mechanism was dominated by continuous static recrystallization (CSRX), the homogeneous nucleation occurred when the sample was heated to near solidus temperature, and CSRX happened in the semi-solid temperature. In the process of recrystallization, the micro-texture changed from preferred orientation to random orientation. A variety of experimental results show that static recrystallization (SRX) occurred at semi-solid temperature due to the blocking effect of atomic clusters on dislocation slip and the Zener drag effect of fine precipitates on low angle grain boundaries (LAGBs) disappeared with melting at semi-solid temperature.

Al-6%Mg-Sc-Zr alloys with the total ratio of Sc + Zr = 0.32 wt.% make up the target of this research. The content of scandium and zirconium varied with an increment of 0.02%. The alloys were produced by induction casting. Their ultrafine-grained (UFG) microstructure was formed with Equal Channel Angular Pressing (ECAP). Such cast alloys have a homogeneous macrostructure formed by small equiaxed grains in the central part of the ingot and columnar crystals along the edges of the cross section. After ECAP, the average grain size in the alloy specimens is 0.5–1 µm. The average grain size does not depend on the ratio of Sc and Zr in these alloys. Superplasticity tests were performed at temperatures ranging from 300 to 500 °C and at a strain rate varying between 3.3·10-3 and 3.3·10-1 s-1. UFG Al-6%Mg-0.20%Sc-0.12%Zr and Al-6%Mg-0.18%Sc-0.14%Zr alloys exhibit the highest superplasticity. It was suggested that changes in Sc:Zr ratio affect spatial distribution and composition of the following precipitating particles: Al3Sc, Al3Zr, Al3(ScxZr1-x). An increase in Zr concentration is shown to reduce the susceptibility of UFG alloys to cavitation fracture.

The supramolecular aggregation processes occurring on metallic (aluminum and gold) surfaces in aqueous solutions of bovine serum albumin (BSA) during drying were studied using advanced scanning electron microscopy (SEM). The possible mechanism for the formation of amazing intricate fractal structures on metallic surfaces was proposed based on the analysis of SEM images, size distribution diagrams and EDX-scanning elements distribution maps.

In this article, it is proposed to use aluminum breakage scraps to obtain Green Hydrogen through the aluminum-water reaction with caustic soda as a catalyst. From this exothermic reaction, both hydrogen and the heat generated can be used. Due to the low price of aluminum chips, this allows us to produce Green hydrogen below the current price that is obtained using renewable energy sources and electrolyzers. On the other hand, we have developed a process that is sustainable since it is obtained as alumina and caustic soda waste that can be reused. This alumina obtained, once filtered, has high purity which allows us to produce high-quality primary aluminum without the need to use bauxite and reducing the production of red sludge. A comparative study-analysis has been carried out of two of the types of forms in which the most common aluminum is presented in the industry to analyze which one performs better by studying key factors such as the hydrogen produced, and the waste generated during the process. Finally, the mathematical model has been defined to be able to control the flow based on different key parameters such as temperature, molarity, and geometry. Undoubtedly, the study that we present represents a milestone for the recovery of metallic aluminum waste and may be of great interest to industries that use aluminum in their processes, such as recuperators, but also the vehicle or aerospace industry.

This article discuss the effects of heat treatment and lubrication modes on the machinability of an A356 alloy (Al-Si-Mg); the alloy is studied as-received, with solution heat-treated alloy (SHT) as well as with an alloy that is solution heat-treated and then aged at 155, 180 and 220 °C. In the course of machinability evaluation, several criteria including cutting force, surface roughness, tool wears and burr analysis (chip) were studied. The results and analysis in this work indicated that the selected machinability criteria are important and necessary to effectively evaluate the machinability of A356 alloys. The machinability of both materials and tools were estimated in terms of cutting force, chip thickness ratio and burr formation, flank wear and roughness. The effects of different cutting parameters (cutting speed and feed rate) and lubrication modes (dry, mist and wet) on the machinability of the A356 cast alloy were also examined. The influence of heat treatments on the burr formation and surface quality was clearly revealed by the experimental results. Experimental work revealed that cutting forces were influenced significantly by aging and cutting speed. However, the different aging at 155, 180, and 220 °C and the cutting speed significantly affected the machinability of the A356 cast alloy. The results obtained show that a better drilling performance in terms of surface quality occurs at a high feed rate, with dry drilling and artificial aging at T6.

Owing to the reduction of rupture instability and the avoidance of wrinkle defect, hydrodynamic deep drawing (HDD) process is gradually becoming attractive for fabricating lightweight and complicated products. Meanwhile, since metallic material presents anisotropic deformation behavior, it is necessary to select an appropriate constitutive model for the prediction of plastic deformation behavior of applied material with high precision. In the present research, several anisotropic yield criteria namely, Hill’48, Yld2000-2d and BBC2005 are implemented to investigate the effect of yield functions on the prediction accuracy of the critical process window and deformation behavior for HDD process of 2024 and 5754 aluminum alloys. Material constants in the yield criteria are determined by applying uniaxial and equi-biaxial tension tests and optimizing an error-function by using the Levenberg-Marquardt algorithm. Furthermore, the process window diagram is computed utilizing the stress analytical model combined material properties with workpiece geometrical features. Numerical simulation results of predicted material anisotropic parameters, process window and HDD deformation for aluminum alloys are compared with the experimental data. Through the comparison of diverse yield criteria based on materials anisotropic coefficients, critical process window prediction, earing profile, and thickness distribution, it is revealed that the Yld2000-2d and the BBC2005 yield criteria can offer more precise models of material behavior in planar anisotropy properties for HDD process of 2024 and 5754 aluminum alloys.

Many strategies have been developed for the synthesis of silicon carbide (SiC) thin films on silicon (Si) substrates by plasma-based deposition techniques, especially plasma enhanced chemical vapor deposition (PECVD) and magnetron sputtering, due to importance of these materials for microelectronics and related fields. A drawback is the large lattice mismatch between SiC and Si. The insertion of a thin aluminum nitride (AlN) buffer layer between them has been shown useful to overcome this problem. Herein, the high-power impulse magnetron sputtering (HiPIMS) technique was used to grow SiC thin films on AlN/Si substrates. Furthermore, the SiC films were also grown on Si substrates. Comparisons of the structural and chemical properties of SiC thin films grown on the two types of substrates allowed us to evaluate the influence of AlN buffer layer on such properties. The chemical composition and stoichiometry of the samples were investigated by Rutherford backscattering spectrometry (RBS) and Raman spectroscopy, while the crystallinity was characterized by grazing incidence X-ray diffraction (GIXRD). Our set of results evidenced the versatility of HiPIMS technique to produce polycrystalline SiC thin films at near room temperature only varying the discharge power. In addition, this study opens up a feasible route for the deposition of crystalline SiC films with a good structural quality using AlN buffer layer.

Lightweight composite sandwich structures are laminated composite structures that are composed of thin stiff face sheets bonded to a thicker lightweight core in between. These structures have high potential to be used in marine, aerospace, defense and civil engineering applications due to their high strength to weight ratios and energy absorption capacity.In this study, composite sandwich structures were developed with carbon fiber reinforced polymer composite face sheets and aluminum honeycomb core materials with various thicknesses. Carbon fiber/epoxy composite face sheets were fabricated with lamination of [0/90]_s carbon fabrics by vacuum infusion technique. Al honeycomb layers were sandwiched together with the face sheets using a thermosetting adhesive. Mechanical tests were carried out to determine the mechanical behavior of face sheets, Al cores and the composite structure. Effect of core thickness on the mechanical properties of the sandwich was investigated.

Among all the processing technologies of heat-treatable aluminum alloys like 2219 aluminum alloy, using friction stir welding (FSW) as the joining technology and using electromagnetic forming (EMF) for plastic forming technology both have obvious advantages and successful applications. Therefore, there is a broad prospect for the compound technologies which can be used on the 2219 aluminum alloy to manufacture the large-scale thin-wall parts in the astronautic industry. The microstructure and mechanical properties of 2219 aluminum alloy under the process compounded of FSW, heat treatment, and EMF were investigated by means of tensile test, optical microscope (OM), and scanning electron microscope (SEM). The results show that the reduction of strength, which was caused during the FSW process, can be recovered effectively by the post-welding heat treatment composed of solid solution and aging, while the ductility was still reduced after heat treatment. Under the compound technology of FSW, heat treatment, and EMF, the forming limit of 2219 aluminum alloy decreased distinctly due to the poor ductility of the welding joint. A ribbon-pattern, which was formed due to the banded structure caused by FSW process, was found on the fracture surface of welded 2219 aluminum alloy after EMF treatment. During the EMF process, because of the effects of induced eddy current, a unique structure, which was manifested as a molted-surface appearance under the SEM observation, was formed as the material fractured.

Shot peening is an attractive technique for fatigue enhanced performance of metallic components, because it promotes crack initiation retardation and later crack growth. Engineering design based on fatigue crack propagation predictions applying the principles of fracture mechanics is commonly used in aluminum structures for aerospace engineering. The main purpose of present work was to analyze the effect of shot peening on the fatigue crack propagation of the 7475 aluminum alloy, under both constant amplitude loading and periodical overload blocks. The tests were performed on 4 and 8 mm thickness specimen's with stress ratios of 0.05 and 0.4. The analysis of the shot-peened surface showed a small increase of the micro-hardness values, due to the plastic deformations imposed by shot peening. The beneficial effect of surface peening on fatigue crack growth rates is quite limited to an increasing near the threshold. The specimens’ thickness has only marginal influence on the crack propagation, in opposite to the stress ratio. Periodic overload blocks of 300 cycles promotes a reduction of the fatigue crack growth rate for both intervals of 7,500 and 15,000 cycles.

Isothermal interrupted hot compression tests of 5754 aluminum were conducted on Gleeble-3500 thermo-mechanical simulator at temperature 350 °C and 450 °C, strain rate 0.1 s-1 and 1s−1. These tests simulated flat rolling to investigate how softening behaviors respond to controlled parameters, such as deformation temperature, strain rate and delay times. This data allowed the parameters for the hot rolling process to be optimized. The delay times during interrupted compression vary between 5s and 60s. The dynamic softening at each pass and metadynamic recrystallization at the intervals of deformation passes were analyzed in detail. 0.2% offset yield strength is applied to calculate the softening fraction undergoing metadynamic recrystallization. A kinetic model was developed to describe metadynamic recrystallization behaviors of the hot deformed 5754 aluminum alloy. Furthermore, the time constant for 50% recrystallization was expressed as functions related to the temperature and the strain rate. The experimental and calculated results were found to be in close agreement, which verified the developed model.

Biomimetic materials are substances that replicate natural structures. There are several methods for producing such materials with highly developed surfaces from a wide range of polymers, but electrospinning is of particular interest due to its simplicity of implementation and the ability to modify the produced fibrous materials resembling structures found in living organisms. This study explores new biomimetic materials based on polyhydroxyalkanoates, specifically poly-3-hydroxybutyrate, modified with chlorophyll derivatives. The research investigates the impact of chlorophyll derivatives on the morphology, supramolecular structure, and key properties of nonwoven materials. The obtained results are of interest for the development of new biomimetic environmentally friendly materials for biomedicine with special properties.

We present synthetic experiments of lactic acid (LA) polycondensation to produce poly(lactic acid) (PLA), as well as kinetic modeling calculations that capture the polymer molecular weight increase with time, given the initial concentrations. Tin-octoate-catalyzed polycondensation of (D,L)- or L-lactic acid, was carried out in pre-dried toluene after azeotropic dehydration for 48-120 hours at 130-137 °C. The polymerization was optimized by varying lactic acid and catalyst concentrations as well as the temperature. Gel Permeation Chromatography was used to experimentally follow the evolution of molecular weights and the products were characterized by NMR, TGA, DSC and IR. Under optimal conditions, PLLA with weight-average molecular weight (Mw) of 161 kDa could be obtained. The rate equations that describe polycondensation kinetics were recast in a condensed form that allowed very fast numerical solution and calculation of the number-average molecular weight with time. Deviations with respect to the experiment were minimized in a least-squares fashion, to determine rate constants. The optimized kinetics parameters are shown to reproduce the experimental data accurately