The influences of doped hole transporting layer (HTL) on the performances of perovskite solar cells were studied. The influences of electrostatic and surface roughness effect by solvent additive doping were compared. The electrostatic effect of solvent additive doping was compared by addition of 1,8-diiodooctane and 1,8-dichlorooctane to the HTL layer. The surface roughness effect of solvent additive doping was examined using atomic force microscopy. The perovskite crystallinity by doping HTL was studied by X-ray diffraction. The conductivity of HTL was measured using four probe methods and was higher for doped devices. Enhanced conductivity of PEDOT:PSS film was also proved using fluorescence emission quenching. Long-term stability of the device was enhanced by doping HTL. The device with solvent additive exhibited much enhanced stability, retained over 80% of the initial PCE for 400 hours, while PCE of the device without solvent additive decreased to less than 80% after 200 hours. A very weak power microwave treatment was used for post-annealing of the fully fabricated devices. Post-annealing enhanced the lifetime of the device. Comparing different size of cells, the device lifetime was decreased as the cell area increased and as the size of the cell increased, the extent of lifetime enhancement by doping was increased.

Ethylene is an ideal CO2 product in an electrocatalytic CO2 reduction reaction (CO2RR), which has high economic value. In this paper, Al–doped octahedral Cu2O (Al–Cu2O) catalyst was synthesized by a simple wet chemical method. The selectivity of CO2RR products was improved by doping Al onto the surface of octahedral Cu2O by regulating the Al content. The Al–Cu2O was used as an efficient electrocatalyst for CO2RR with selective ethylene production. The Al–Cu2O exhibited a high Faradic efficiency (FEC2H4) of 44.9% at -1.23 V (vs. RHE) in CO2 saturated 0.1 M KHCO3 electrolyte. Charge transferring from Al atom to Cu atom take place after Al doping in Cu2O, thereby optimizing the electronic structure, which facilitates CO2RR to ethylene production. The DFT calculation showed that the Al–Cu2O catalyst can effectively reduce the adsorption energy of the *CHCOH intermediate and promote the mass transfer of charges, thus improving the FEC2H4. After Al doping into Cu2O, the center of d orbitals shift positively, which makes the d–band closer to the Fermi level. Furthermore, the density of electronic states increases, which was conducted to the interaction between Cu atoms and intermediates, thus accelerating the electrochemical CO2 reduction process. This work proved that the metal doping strategy can effectively improve the catalytic properties of Cu2O, thus providing a useful way for CO2 cycling and green production of C2H4.

Zeolite Y with microporous and hierarchical structure containing Ti–Ni and Ti–Co oxides were obtained as active photocatalysts. Different Ti amounts (5, 10% TiO2) were supported, followed by loading of Ni or Co oxides (5 %). The X-ray diffraction evidenced the presence of TiO2 as anatase. N2 adsorption-desorption results showed type IV isotherms, for hierarchical zeolite Y samples, and a combination of type IV and I isotherms, for zeolite Y samples. UV–Vis diffuse reflectance spectra showed shift of absorption band to visible with increasing of Ti loading and especially after Co and Ni addition. A significant effect of the support was evidenced for Ti and interaction with Co/Ni species. The zeolite Y support stabilizes Ti in the 4+ oxidation state while hierarchical zeolite Y support favored the formation of Ti 3+ species and oxidation of Co and especially of Ni to 3+. Photocatalytic activity, under UV and visible light, was evaluated in degradation of amoxicillin, used as a model test. The photocatalytic mechanism was investigated using ethanol, p-benzoquinone and KI as ·OH, ·O2- radicals and hole (h+) scavengers. The best results were obtained for the immobilized Ni-Ti species on hierarchical zeolite Y support.

This work presents first time successfully fabricated silica few-mode microstructured optical fiber (MOF) with hollow GeO2-doped ring core and strongly induced twisting up to 790 revolutions per meter. Some technological issues for manufacturing of GeO2-doped supporting elements for large hollow cores as well as described above complicated spun MOFs are discussed. We introduce some results of tests, performed for pilot samples of designed and manufactured described above untwisted and twisted MOFs with outer diameter 65 µm and hollow ring core inner diameter 30.5 µm under wall thickness 1.7 µm and refractive index difference n=0.030, including their geometrical parameters, basic transmission characteristics and measurements of far-field laser beam profile patterns.

Herein, we report on a giant thermoelectric figure of merit of a non-degenerate fluorine-doped single-walled carbon nanotube (FSWCNT) using a tractable analytical approach and the phonon lattice Boltzmann model (LBM). We investigate the influence of the doping concentration, and the overlapping integrals on the ZT. The ZT and the temperature range of operation can be tuned using the doping (impurity) concentration and the overlapping integrals, respectively. The lattice thermal conductivity obtained using the phonon LBM was calculated to be 107.2 W/mK which yielded a ZT greater than 20. Interestingly, the ZT obtained is higher than what has been reported in superlattices, (ZT~1.4) and superlattice nanowire, (ZT~ 4) at 300 K, making FSWCNT a potential candidate for thermoelectric applications.

Abstract: This work for the first time investigated the densification of multi-doping zirconia ceramic body with organic coating powders for solid electrolyte of solid oxide fuel cells via online imaging technology. The densification results show the initial stage plays a key role in the sintering. It can be found the covered organic PVA (polyvinyl acetate) supplies a potential kinetics to the initial densification during sintering. As a result, a kinetic function of densification in the initial stage was suggested. Furthermore, a novel sintering model with six sub-stages is developed for polycrystalline zirconia ceramics. The findings would be a valuable reference for predicting final temperature of sintering, the equivalent strain during the sintering process, as well as optimizing the densification behavior.

A series of Eu³⁺ doped CaSiO₃/SiO₂ nano-phosphor powder of controlled grain size, crystalline structure, and chemical composition were synthesized using the microemulsion technique. XRD profiles of samples sintered over 600 of suggested phase shift from amorphous powder grain to more ordered polycrystalline powder of triclinic type wollastonite, CaSiO₃, with preferred crystal phase orientation of (112) and tetragonal type cristobalites of SiO₂. The grain size, crystallinity, and chemical composition of the host matrix, activator and sensitizer strongly affected both the absorption and emission bands of these samples. The amplitude of both the orange and red emission bands significantly increased with sintering temperature. The emission band is red-shifted with decreasing grain sizes. These bands displayed good sensitivity to ionic concentration of the Si⁴⁺, Ca²⁺, and Eu³⁺. With increasing Ca²⁺ ion concentration both the intensity of the red photoluminescence (PL) band increased and a concentration quenching observed. Increase in Si⁴⁺ ion concentration led to quenching in PL intensity of both the orange and red bands whereas the amplitude of the blue-band slightly increased. With increasing Eu³⁺ ion concentration the red-band initially increased whereas it started decreasing at higher sample concentration. In the presence of Ca²⁺ ion as a sensitizer, the sample showed a remarkable PL property—including—about 100% photon conversion efficiency and a two-fold increase in excitation and emission photons.

The nitrogen-doped amorphous oxide semiconductor (AOS) thin film transistors (TFTs) with double-stacked channel layers (DSCL) were prepared and characterized. The DSCL structure composed of nitrogen-doped amorphous InGaZnO and InZnO films (a-IGZO:N/a-IZO:N or a-IZO:N/a-IGZO:N) made the corresponding TFT devices exhibit quite large field-effect mobility due to the existence of double conduction channels. Especially, the a-IZO:N/a-IGZO:N TFTs showed even better electrical performance (μ_FE = 15.0 cm²·V^-1·s^-1, SS = 0.5 V/dec, V_TH = 1.5 V, I_ON/I_OFF = 1.1×10⁸) and stability (V_TH shift of 1.5, -0.5, and -2.5 V for positive bias-stress, negative bias-stress and thermal stress tests, respectively) than the a-IGZO:N/a-IZO:N TFTs. Based on the X-ray photoemission spectroscopy measurements and energy band analysis, it was assumed that the optimized interface trap states, the less ambient gas adsorption, and the better suppression of oxygen vacancies in the a-IZO:N/a-IGZO:N hetero-structures might be responsible for the better behaviors of the corresponding TFTs.

Postmenopausal osteoporosis, a metabolic bone disease associated with aging and that affects bones throughout the body, is emerging as an urgent public health concern and imposes a substantial healthcare burden on society. The clinical application of bisphosphonate, the primary treatment for osteoporosis, is limited owing to the drug’s severe complications. Herein, we investigate the synthesis and utilization of strontium-doped mesoporous bioactive glass loaded with alendronate (ALN@Sr-MBG) as a novel therapeutic agent for osteoporosis, to explore its potential as an alternative to alendronate (ALN). Strontium-doped mesoporous bioactive glass (Sr-MBG) was synthesized using the sol-gel method, while ALN@Sr-MBG was obtained by incorporating Sr-MBG into an alendronate saturated solution. The bioactivities of ALN@Sr-MBG, including biotoxicity, inflammation inhibition, and anti-osteoclast differentiation, were investigated in vitro using CCK-8, flow cytometry, tartrate-resistant acid phosphatase (TRAP) staining, and RT-PCR assays. Animal models were established by surgically removing the ovaries from non-pregnant female C57/BL mice, followed by weekly intraperitoneal injections of ALN@Sr-MBG, ALN, or excipients. After 8 weeks, the mice femurs were extracted and analyzed through Micro-CT scanning, and hematoxylin-eosi, osteoblastic, and osteogenic staining. The in vitro findings demonstrated that ALN@Sr-MBG displayed enhanced biological efficacy compared to ALN in terms of inflammation inhibition, osteogenesis promotion, and osteoclastogenesis inhibition. Furthermore, micro-CT analysis revealed that ALN@Sr-MBG significantly augmented bone mineral density (BMD), bone volume fraction (BV/TV), trabecular number (Tb.N), and trabecular thickness (Tb.Th), while reducing trabecular separation (Tb.Sp) and structural model index (SMI) in mice with ovariectomy-induced osteoporosis. The osteoblast and osteogenic staining results indicate the enhanced bioactivities of ALN@Sr-MBG in promoting bone formation and inhibiting bone resorption compared to ALN. In vitro and in vivo assessments further confirmed that ALN@Sr-MBG exhibits superior anti-osteoporotic bioactivity compared to ALN. The study findings confirm the potential of ALN@Sr-MBG as a novel alternative therapy to ALN and drug candidate for the treatment of osteoporosis.

Although 4Ce4YSZ has high corrosion resistance, it faces challenges concerning sinterability and ionic conductivity. Therefore, we studied destabilization behavior caused by corrosion and oxygen vacancy ordering according to ZnO doping. The powders of (4Ce4YSZ)1-x(ZnO)x (x=0.5, 1, 2, 4 mol%) were synthesized through the sol-gel method. With the addition of ZnO, the cubic phase increased, and secondary phases were not observed. The (111) peak showed a higher angle shift in ZnO-doped 4Ce4YSZ compared to 4Ce4YSZ, and TEM-SAED revealed a reduction in the spacing of the (011)t plane, suggesting lattice contraction due to the substitution of the smaller Zn2+ (60 Å) for Zr4+ (84 Å) in the lattice. The local atomic structure analysis was conducted using EXAFS to investigate the oxygen vacancy ordering behavior. Zr K-edge Fourier-transform data revealed a decrease in the Zr-O1 peak intensity with an increasing amount o ZnO doping, indicating an increase in oxygen vacancies. The Zr-O1 peak position shifted to the right, leading to an increase in the Zr-O1 interatomic distance. In the Y K-edge Fourier-transform data, the Y-O1 peak intensity did not decrease, and there was little variation in the Y-O1 interatomic distance. These results suggest that the oxygen vacancies formed due to ZnO doping are located in the neighboring oxygen shell of Zn, rather than in the neighboring oxygen shells of Y and Zr. Impedance measurements were conducted to measure the conductivity, and as the amount of ZnO doping increased, the total conductivity increased, while the activation energy decreased. The increase in oxygen vacancies by ZnO doping contributed to the enhancement of conductivity and it is considered that these created oxygen vacancies did not interact with Zn2+ and did not form defect associations. Fluoride-based molten salts were introduced to the specimens to assess corrosion behavior in a molten salt environment. Yttrium depletion layers (YDLs) were formed on the surfaces of all specimens due to the leaching of yttrium. However, Ce remained relatively stable at the interface according to EDS line scans, suggesting a reduction in the phase transformation (cubic, tetragonal to monoclinic) typically associated with yttrium leaching in YSZ.

In recent years, natural polymers have replaced synthetic polymers for antibacterial orthopedic applications owing to their excellent biocompatibility and biodegradability. Zein is a biopolymer found in corn. The lacking mechanical stability of zein is overcome by incorporating bioceramics e.g. mesoporous bioactive glass nanoparticles (MBGNs). In present study, pure zein and zein/Zn-Mn MBGNs composite coatings were deposited via electrophoretic deposition (EPD) on 316L stainless steel (SS). Zn and Mn were co-doped in MBGNs in order to make use of their antibacterial and osteogenic potential, respectively. A Taguchi design of experiment (DoE) study was established to evaluate the effect of various working parameters on the morphology of the coatings. It was observed that coatings deposited at 20 V for 5 min with 4 g/L concentration (conc.) of Zn-Mn MBGNs showed highest deposition yield. Uniform coatings with highly dispersed MBGNs were obtained adopting these optimized parameters. Scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), X-Ray diffraction (XRD), and fourier transform infrared spectroscopy (FTIR) were employed to investigate the morphology and elemental composition of zein/Zn-Mn MBGNs composite coating. Surface properties i.e. coating roughness and wettability analysis concluded that composite coatings were appropriate for cell attachment and proliferation. For adhesion strength various techniques including tape test, bend test, pencil hardness test, and tensile test were performed. Wear and corrosion analysis highlighted the mechanical and chemical stability of coatings. Colony forming unit (CFU) test showed that zein/Zn-Mn MBGNs composite coating was highly effective against Staphylococcus aureus (S. aureus) and Escherichia coli (E. coli) due to the presence of Zn. The formation of hydroxyapatite (HA) like structure upon immersion in simulated body fluid (SBF) validated the in vitro bioactivity of the coating. It was concluded that zein/Zn-Mn MBGNs coating synthesized in this work can be used for bioactive and antibacterial orthopedic applications.

The wide interest in developing green energy technologies stimulates the scientific community to seek, for devices, new substitute material platforms with low environmental impact, ease of production and processing and long-term stability. The synthesis of metal oxide (MO) semiconductors fulfils these requirements and efforts are addressed at optimizing their functional properties, through improvement of charge mobility or energy level alignment. Two MOs have rising perspectives for application in light harvesting devices, mainly for the role of charge selective layers but also as light absorbers, namely MoO3 (an electron blocking layer) and Co3O4 (a small band gap semiconductor). The need to achieve better charge transport has prompted us to attempt doping strategies with vanadium (V) ions that, when combined with oxygen in V2O5, produce a high work function MO. We report on subcritical hydrothermal synthesis of V-doped mesostructures of MoO3 and of Co3O4, in which a tight control of the doping is exerted by tuning the relative amounts of reactants. We accomplished a full analytical characterization of these V-doped MOs that unambiguously demonstrates incorporation of the vanadium ions in the MO crystal lattice, as well as effects on the optical properties and work function. We foresee a promising future use of these materials as charge selective materials in energy devices based on multilayer structures.

Partially stabilized zirconia (PSZ) is a promising material with superior combination properties in a wide range of industries. In this study, the effect of grain size on the mechanical properties such as hardness, bending strength and fracture toughness (named as ‘indentation toughness’ in this study) was investigated. The multi-doped zirconia ceramics were prepared by powder processing and pressure-less sintered following four sintering schedules. The measured mechanical properties results show that the polymorph structure sintered at a higher temperature has a lower bending strength and hardness. But 300% more indentation toughness (30.54 Kg/mm) of samples sintered at 1600 °C +1150 °C relative to others was estimated due to the grain size effect by our suggested equation. By contrast, the fracture toughness was calculated with an existing method. The results showed that similar trends were obtained. It appeared to be a novel method for evaluating the toughness of partially stabilized zirconia ceramics with micron grains based on the size effect.

Effective control of domain walls or magnetic textures in antiferromagnets promises to enable robust, fast, and non-volatile memories. The lack of net magnetic moment in antiferromagnets implies the need for creative ways to achieve such a manipulation. Here, we investigate changes in magnetic force microscopy (MFM) imaging and in magnon-related mode in Raman spectroscopy of virgin NiO films under a microwave pump. After the MFM and Raman studies, a combined action of broadband microwave (0.01-20 GHz, power scanned from −20 to 5 dBm) and magnetic field (up to 3 kOe) were applied to virgin epitaxial (111) NiO and (100) NiO films grown on (0001) Al2O3 and (100) MgO substrates, following which the MFM and Raman studies were repeated. We observed a suppression of the magnon-related Raman mode subsequent to the microwave exposure. Based on MFM imaging, this effect appears to be caused by the suppression of large antiferromagnetic domain walls due to the possible excitation of antiferromagnetic spin oscillations localized within the antiferromagnetic domain walls.

Photoluminescent (PL) layers and electroluminescent (EL) systems have been extensively explored for constructing flat panels, screen monitors, and lighting systems. Due to their optical properties, our group is interested in the relationship between optical properties and dielectric constant is converted due to thermal change. In this study, we prepared a zinc sulfide (ZnS) fluorescent film on barium-calcium zirconium titanate ceramics. BCZT0.85 (Ba0.85Ca0.15Zr0.1Ti0.9O3) and BCZT0.9 (Ba0.9Ca0.1Zr0.1Ti0.9O3) were prepared using the solid-state reaction method for the dielectric layer. The BCZT powders were calcined at 1200 and 1250 °C and dwell times of 2 and 4h. The phase formation and microstructure characteristics were then determined using X-ray diffraction and scanning electron microscopy, respectively. The dielectric behavior and optical properties rela-tionship was then studied to determine the composition and optimal conditions for further use as thermal detectors in electric vehicle battery packs. All BCZT powders exhibited the tetragonal phase, which was confirmed by JCPDS No. 01-079-2265. The dielectric constant increased with increasing calcining temperature or dwell time. The dielectric properties showed the BCZT0.85 ceramic sintered had the maximum dielectric constant of 15342 at calcine temperature of 1250 °C for 4h. Therefore, in this study, this condition was optimal for preparing the dielectric film. The maximum dielectric constant film is 42. The electroluminescence intensity of the samples increased in a temperature-dependent manner, with the highest EL intensity at 80 °C. Moreover, the electroluminescence intensity value was enhanced with the increase of the dielectric constant. Our results show promise for developing applications for Opto-thermal sensors.

Luminescent properties of epitaxial Cu2O thin films were studied in 10-300 K temperature range and compared with luminescent properties of Cu2O single crystals. Cu2O thin films were deposited epitaxially by the electrodeposition method on either Cu or Ag substrates at different processing parameters, which determined the epitaxial orientation relationships and encapsulated surface. Cu2O (100) and (111) single crystal samples were cut from a crystal rod grown by the floating zone method. Luminescence spectra of thin films contain the same emission bands as single crystals around 720, 810 and 910 nm, characterizing VO2+, VO+ and VCu defects, correspondingly. Additional emission bands, whose origin is under discussion, are observed around 650-680 nm, while the exciton features are negligibly small. The relative mutual contribution of the emission bands varies depending on the particular thin film sample. Existence of the domains of crystallites with different orientation determines the polarization of luminescence. PL of both Cu2O thin films and single crystals is characterized with negative thermal quenching in the low temperature region, the reason of this phenomenon is discussed.

In this work, we report manganese phthalocyanine (MnPc) films obtained by ultrasonic spray-pyrolysis technique at 40°C deposited on glass substrate subjected to thermal annealing at 100 °C and 120°C. The MnPc films were characterized by UV/Vis spectroscopy, Raman spectroscopy, X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM). The absorption spectra of the MnPc films were studied in a wavelength range from 200 to 850 nm, where the characteristic bands of a metallic phthalocyanine known as B and Q bands were observed in this range of the spectrum. The optical energy band (Eg) was calculated by the Tauc equation. It was found that for these MnPc films, the Eg has the values of 4.41, 4.46 and 3.58 eV corresponding to as deposited, annealing 100°C and 120°C, respectively. The Raman spectra of the films showed their characteristic vibrational modes of the MnPc films. In X-ray diffractograms of these films, the characteristic diffraction peaks of a metallic phthalocyanine are observed, presenting a monoclinic phase. SEM images of these films were studied in cross section obtaining thicknesses of 2, 1.2 and 0.3 μm to as deposited, annealing 100°C and 120°C, successively. Also, in the SEM images of these films, both the average particle sizes ranging from 4 to 0.041 µm and the average diameter from 4.8 to 0.091 μm were obtained. The results agree with those reported in the literature for MnPc films deposited with other techniques.

The concern about consuming eco-friendly products has motivated research in the development of new materials. Therefore, films based on natural polymers have been used to replace traditional polymers. This study consists of a production of films based on gelatin reinforced with black pepper essential oil-loaded nanoemulsions and Cloisite Na⁺. The films were characterized by water vapor permeability, mechanical and thermal properties, surface contact angle, X-ray diffraction and scanning electron microscopy. It was observed that the films containing the nanoemulsion have higher permeability values and an increase in their mechanical resistance. The addition of nanoclay contributed to an increase in the surface hydrophobicity of the film and an increase in the tensile strength at break by about 150%. The addition of essential oil nanoemulsions led to an increase in thermal stability. The presence of clay dispersion contributed to the formation of a surface that was slightly rougher and grainier. The addition of the black pepper essential oil nanoemulsion resulted in an increase in porosity of the gelatin matrix. Through X-ray diffraction analysis, it was possible to conclude that both the polymeric gelatin matrix and the essential oils nanoemulsion are intercalated with the clay dispersion.

By reactive DC magnetron sputtering from a pure Ta target onto silicon substrates, Ta(N) films were prepared with a different N₂ flow rate of 0, 12, 17, 25, 38, 58 sccm. The effects of N₂ flow rate on the electrical properties, crystal structure, elemental composition and optical properties of Ta(N) were studied. These properties were characterized by the four-probe method, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and spectroscopic ellipsometry (SE). Results show that the deposition rate decreases with an increase of the N₂ flows. On the other hand, the resistivity increases, the crystal size decreases, and the crystal structure transitions from β-Ta to TaN(111), and finally becomes the N-rich phase Ta₃N₅ (130,040). Studying the optical properties, it is found that there are differences in the refractive index (n) and extinction coefficient (k) of Ta(N) with different thicknesses and different N₂ flow rates, and dependent on the crystal size and crystal phase structure.

Active films based on carboxymethyl chitosan incorporated corn peptide were developed. Physicochemical properties of the films, including thickness, opacity, moisture content, color, mechanical properties, water vapor permeability, and oil resistance, were measured. Biological activities of the films, including the antioxidant and antibacterial activities, were characterized in terms of 2, 2-diphenyl-1-picrylhydrazyl free radical scavenging activity, reducing power, the total antioxidant activity, and the filter disc inhibition zone method. The results indicated that the incorporation of corn peptide caused interactions between carboxymethyl chitosan and corn peptide in Maillard reaction and gave rise to the films light yellow appearance. Compared with the Control, the degree of glycosylation, browning intensity, thickness, opacity, tensile strength, antioxidant activity, and antibacterial activity of films were increased, but the elongation, vapor permeability, and oil resistance of films were decreased. The films based on corn peptide and carboxymethyl chitosan can potentially be applied to food packaging.

The main aim of this work is to report an alternative energy efficient technique of fabricating flexible thermoelectric generators (TEGs) using printable ink. In this process, we have fabricated thermoelectric (TE) composite thick film and we are experimenting several ways to overcome the challenges of conventional and additive manufacturing methods. Two different mesh sizes of n-type bismuth particle, various binder to thermoelectric (TE) material weight ratio, and two different pressure (200 MPa and 300 MPa) were employed for optimizing the thermoelectric properties of TE composite films. We are also exploring naturally occurring chitosan as a binder. Dimethyl sulfoxide (DMSO) dissolved chitosan was used for the binder and less than 0.2 wt% of chitosan was sufficient for the fabrication of TE inks and composite films. Low energy intensive curing process was employed to evaporate the solvent from the drop casted inks. External uniaxial pressure not only eliminated high energy intensive curing processes but also increased the packing density of the film by removing pores and voids in the chitosan-bismuth composite film. The microstructure analysis reveals that bulk-like structure, which rarely has voids, pores and grain boundaries, was observed in the composite films pressed at sufficiently high pressures. The highest performing composite film was obtained with the conditions of 1:2000 binder to bismuth weight ratio, 100 mesh of particle size, and 300 MPa of pressure. The best performing bismuth chitosan composite film pressed at 300 MPa had the power factor as 4009 ± 391 μW/m·K² with high electrical conductivity value of 7337 ± 522 S/cm. The measured thermal conductivity of the best performing chitosan-bismuth composite film was 4.4 ± 0.7 W/m·K and the figure of merit calculated from the thermal conductivity was 0.27 at room temperature.

Titanium dioxide (TiO2) and aluminum oxide (Al2O3) coatings have been investigated in a wide range of bio-applications due to their biodegradation and biocompatibility properties, that are key parameters for their use in the food packaging and biomedical devices fields. The present study evaluates and compares the electrochemical behavior of the non-coated, commercial resin-coated, TiO2-coated and Al2O3-coated aluminum in commercial beer electrolyte. For this, TiO2 and Al2O3 thin films were deposited on aluminum (Al) substrates using atomic layer deposition (ALD). The evaluation of the corrosion barrier layer properties was performed by linear sweep voltammetry (LSV) and electrochemical impedance spectroscopy (EIS). In addition, profilometry, grazing incidence X-ray diffractometry (GIXRD), scanning electron microscopy (SEM) and Fourier-transform infrared spectroscopy (FT-IR) analyses were performed to investigate the physical and chemical properties of the pristine and / or corroded samples. TiO2 and Al2O3 films presented an amorphous structure, a morphology that follows Al substrate surface, and a thickness of around 100 nm. Analysis of LSV data showed that ALD coatings promoted a considerable increase in corrosion barrier efficiency being 86.3% for TiO2-coated Al and 80% for Al2O3-coated Al in comparison with 7.1% of commercial resin-coated Al. This is mainly due to the lower electrochemical porosity, 11.4% for TiO2-coated Al and 20.4% for Al2O3-coated Al in comparison with 96% of the resin-coated Al, i.e. an increase of up to twofold in the protection of Al when coated with TiO2 compared to Al2O3 coated. The EIS results allow us to complement the discussions about the reduced corrosion barrier efficiency of the Al2O3 film for beer electrolyte once SEM and FT-IR analyzes did not show drastic changes in both investigated ALD films after the corrosion assays. The above results indicate that ALD TiO2 and Al2O3 films may be a viable alternative to replace the synthetic resin coatings frequently used in aluminum cans of use in the food industry.

Enhancement of mechanical properties by using TiN/TiCN/TiC multilayer thin films deposited on commercially pure cast Titanium (CP-Ti), Ti6Al4V and silicon (Si) substrates via magnetron sputtering technique was investigated in this study. The structural, chemical and mechanical properties of the coatings were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), nanoindentation and scratch test. Results of the XRD analysis showed reflections corresponded to FCC (1 1 1) cubic and polycrystalline structure for TiN/TiCN/TiC films. XPS analysis revealed formation of titanium nitride, titanium carbonitride and titanium carbide in the coatings. According to SEM images, the coatings demonstrated dense cross-sectional morphology and columnar structure as well as good adhesion to the substrate with a thickness of 1.77 μm deposited on silicon (1 0 0). Scratch and nanoindentation test results showed the best mechanical behavior for the coated Ti6Al4V substrate material with the 19.96 GPa hardness and 25 N critical load values, because of its higher hardness and toughness of substrate in compared to Cp-Ti substrate.

Enhancement of mechanical properties by using TiN/TiCN/TiC multilayer thin films deposited on commercially pure cast Titanium (CP-Ti), Ti6Al4V and silicon (Si) substrates via magnetron sputtering technique was investigated in this study. The structural, chemical and mechanical properties of the coatings were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), nanoindentation and scratch test. Results of the XRD analysis showed reflections corresponded to FCC (1 1 1) cubic and polycrystalline structure for TiN/TiCN/TiC films. XPS analysis revealed formation of titanium nitride, titanium carbonitride and titanium carbide in the coatings. According to SEM images, the coatings demonstrated dense cross-sectional morphology and columnar structure as well as good adhesion to the substrate with a thickness of 1.77 μm deposited on silicon (1 0 0). Scratch and nanoindentation test results showed the best mechanical behavior for the coated Ti6Al4V substrate material with the 19.96 GPa hardness and 25 N critical load values, because of its higher hardness and toughness of substrate in compared to Cp-Ti substrate.

In biology molecules and macromolecules like sugars, proteins, DNA, and RNA are of utter importance. Detecting their presence as well as their conformation is still a challenge in many cases. It is well known that the vibrational states of such molecules lie from the infrared to the TeraHertz range. Spectroscopy can be used to detect such compounds and probe their conformation. Still, terahertz spectroscopy on biosample is a challenge for two main reasons: water absorption; and the small size of the samples. The sample volume is smaller than the cube of the TeraHertz wavelength; the light matter interactions are thus extremely reduced. In this paper, we present the design, fabrication, characterization and the first typical uses of a biophotonic device aiming at increasing light matter interaction to enable terahertz spectroscopy of minute samples on a broad band (0.2–2 THz). We demonstrate time domain spectroscopy experiments on few µl samples showing the validity of our approach.

Abstract: The expansion of global industries results in the release of harmful volatile acid vapors into the environment, posing a threat to various life forms. Hence, it's crucial to prioritize the development of swift sensing systems capable of monitoring these volatile acid vapors. This initiative holds great importance in safeguarding a clean and safe environment. This paper presents the synthesis and characterization of pyrene-based covalent organic frameworks (COFs) demonstrating exceptional crystallinity, thermal stability, and intense fluorescence. Three COFs—PP-COF, PT-COF, and PE-COF—were synthesized, showcasing large surface areas and robust thermal stability up to 400 °C. The fluorescence properties and intramolecular charge transfer within these COFs were significantly influenced by their Schiff base bonding types and π-stacking degrees between COF layers. Notably, PE-COF emerged as the most fluorescent among the three COFs and exhibited exceptional sensitivity and rapid response as a fluorescent chemosensor for detecting HCl in solution. The reversible protonation of imine bonds in these COFs allowed for the creation of highly sensitive acid vapor sensors, showcasing a shift in spectral absorption while maintaining structural integrity. This research highlights the potential of COFs as reliable and reusable sensors for detecting harmful acid vapors, addressing environmental concerns arising from industrial activities.

Polyvinyl Alcohol (PVA)/ Graphene Quantum Dots (GQDs) polymer nanocomposite films have been prepared, and the relationship between their structural, thermal and nanoscale morphologi-cal properties, and their photoluminescent response, has been investigated. Although according to X-ray Diffraction (XRD), Fourier-Transform Infrared Spectroscopy (FT-IR) and Differential Thermal Analysis (DTA) the incorporation of GQDs does not significantly affect the percentage crystallinity of the PVA matrix, for a range of added GQD concentrations, Atomic Force Micros-copy (AFM) showed the formation of islands with apparent crystalline morphology on the surface of the PVA/GQD films, with GQD presumably acting as a nucleating agent for island growth. The incorporation of GQD also led to the formation of characteristic surface pores with increased stiffness and frictional contrast, according to Ultrasonic Force Microscopy (UFM) and Frictional Force Microscopy (FFM) data. The photoluminescence (PL) spectra of the films were found to de-pend both on the amount of GQD incorporated and on the film morphology. For GQD loads > 1,2wt%, a GQD-related band was observed at ~ 1650 cm-1 in FT-IR, along with an increase in the PL band at lower energy. For a load of ~2wt% GQD, the surface morphology was characterized by extended cluster aggregates with lower stiffness and friction than the surrounding matrix, and the PL signal decreased.

Amorphous germanium films on non-refractory glass substrates were annealed by ultrashort near-infrared (1030 nm, 1.4 ps) and mid-infrared (1500 nm, 70 fs) laser pulses. Crystallization of germanium irradiated at a laser energy density (fluence) range from 25 to 400 mJ/cm2 under single-shot and multi-shot conditions was investigated using Raman spectroscopy. The dependence of the fraction of the crystalline phase on the fluence was obtained for picosecond and femtosecond laser annealings. The regimes of almost complete crystallization of germanium films over the entire thickness are obtained (from the analysis of Raman spectra with excitation of 785 nm laser). The possibility of scanning laser processing is shown, which can be used to create films of micro and nanocrystalline germanium on flexible substrates.

Plasma polymerized (PP) thin films deposited in a soft or intermediate plasma discharge from hexamethyldisiloxane (HMDSO) were developed as sensors for the detection of volatile organic compounds (VOCs) vapors. Energy dispersive X-ray spectroscopy (EDX) and X-ray reflectometry (XRR) were performed to determine the organosilicon films elemental composition and density. Spectroscopic ellipsometry measurements were carried out to determine the refractive index of the films. Quartz crystal microbalance (QCM) and ellipsometry coupled to vapor sorption were used to investigate the sorption mechanism of several VOCs vapors into the films as a function of the plasma deposition conditions. The density and the refractive index of the PP-HMDSO films increased with the plasma energy due to a different chemical composition and different proportion of free volumes in the material network. The PP-HMDSO films showed different affinities towards the VOCs vapors depending on the plasma discharge energy. The films elaborated in the lowest plasma energy revealed a good sensitivity towards the VOCs especially toluene (one of the BTEX vapors) compared to the other films deposited under higher plasma energy. In addition, the selectivity between toluene and other non-BTEX VOCs such as heptane and ethanol decreased to become zero while increasing the plasma energy.

Magnetic and morphological properties of equiatomic B2-ordered FeRh thin films irradiated with single high-intensity ultrashort laser pulses are investigated. The goal is to elucidate the effect of femtosecond laser ablation on the magnetic properties of FeRh. We employed Scanning Magneto-Optical Kerr Effect (S-MOKE) microscopy to examine the magnetic phase after laser processing, providing high spatial resolution and sensitivity. Our results revealed the appearance of a magneto-optical signal from the bottom of ablation craters, suggesting a transition from antiferromagnetic to ferromagnetic behavior. Fluence-resolved measurements clearly demonstrate that the ablation threshold coincides with the threshold of the antiferromagnet-to-ferromagnet phase transition. The existence of such magnetic phase transition was independently confirmed by temperature-dependent S-MOKE measurements using a CW laser as a localized heat source. Whereas the initial FeRh film displayed a reversible antiferromagnet-ferromagnet phase transition, the laser-ablated structures exhibited irreversible changes in their magnetic properties. This comprehensive analysis revealed the strong correlation between the femtosecond laser ablation process and the magnetic phase transformation in FeRh thin films.

Novel model of biodegradable PHA copolymer films preparation was applied to evaluate biodegradability of various PHA copolymers and discuss its biomedical applicability. In this study, we illustrate the potential biomaterial degradation rate affectability by manipulation of monomer composition via controlling biosynthetic strategies. Within the experimental investigation, we have prepared two different copolymers of 3-hydroxybutyrate and 4-hydroxybutyrate – P(3HB-co-36 mol.% 4HB) and P(3HB-co-66 mol.% 4HB), by cultivating thermophilic bacterial strain Aneurinibacillus sp. H1 and further investigated its degradability in simulated body fluids (SBFs). Both copolymers revealed faster weight reduction in synthetic gastric juice (SGJ) and artificial colonic fluid (ACF) than simple homopolymer P3HB. In addition, degradation mechanisms differed across tested polymers, according to SEM micrographs. While incubated in SGJ, samples were fragmented due to fast hydrolysis sourcing from substantially low pH, which suggest abiotic degradation as the major degradation mechanism. On the contrary, ACF incubation indicated obvious enzymatic hydrolysis. Further, no cytotoxicity of the waste fluids was observed on CaCO-2 cell line. Based on these results in combination with high production flexibility, we suggest P(3HB-co-4HB) copolymers produced by Aneurinibacillus sp. H1 as very auspicious polymers for intestinal in vivo treatments.

Ga doped ZnO thin films were formed by the Ultrasonic Chemical Spray Pyrolysis method onto substrates using zinc acetate and gallium (III) nitrate hydrate as precursors. The structural, optical, surface and electrical properties were studied as a function of increasing Ga doping concentration from 0 to 6 at %. Structural studies were shown polycrystalline with a hexagonal crystal structure. The transparency in the visible range was around 85% for thin film deposited using 6 at % Ga doping. With the aim of determining surface images and surface roughness of the films atomic force microscope images were taken. Ga doping of ZnO thin films could markedly decrease surface roughness. Electrical resistivity was determined by four point method. The resistivity 2.0% Ga doped ZnO film was the lowest resistivity of 1.7 cm. In the photoluminescence measurements of the films, existence of UV and defect emission band was observed. As a result, Ga doped ZnO films have advanced properties and promising materials for solar cells.

In order to improve the strength of PVA/xylan composite films and endow them with ultraviolet (UV) shielding ability, TiO2-KH550 nanoparticle was synthesized and added into the PVA/xylan matrix. The TiO2-KH550 nanoparticle dispersed well in the 0.04% sodium hexametaphosphate (SHMP) solution under ultrasonic and stirring treatments. Investigations on the properties of films showed that TiO2-KH550 had the positive impact on improving the strength, moisture and oxygen barrier properties of the composite films. The maximum tensile strength (27.3 MPa), the minimum water vapor permeability (2.75×10-11 g•m-1•s-1•Pa-1) and oxygen permeability (4.013 cm3•m-2•24h-1•0.1MPa-1) were obtained under the addition of 1.5% TiO2-KH550. The tensile strength of TiO2-KH550 reinforced composite film was increased by 70% than that of the pure PVA/xylan composite film, and the water vapor and oxygen permeability were decreased by 31% and 41%, respectively. Moreover, the UV transmittance of film at the wavelength of 400 nm was almost zero when adding 1.5~2.5% of TiO2-KH550, which indicated the PVA/xylan composite films were endowed with excellent UV light shielding ability.

A nanostructured electrochemical bi-sensor system for analysis of milks has been developed using the Layer by Layer technique. The non-enzymatic sensor [CHI+IL/CuPcS]2, is a layered material containing a negative film of the anionic sulfonated copper phthalocyanine (CuPcS) acting as electrocatalytic material, and a cationic layer containing a mixture of an ionic liquid (IL) (1-butyl-3-methylimidazolium tetrafluoroborate) that enhances the conductivity and chitosan (CHI) that facilitates the enzyme immobilization. The biosensor ([CHI+IL/CuPcS]2-GAO) results from the immobilization of galactose oxidase on the top of the LbL layers. FTIR, UV-vis and AFM have confirmed the proposed structure and cyclic voltammetry has demonstrated the amplification caused by the combination of materials in the film. Sensors have been combined to form an electronic tongue for milk analysis. Principal Component Analysis has revealed the ability of the sensor system to discriminate between milk samples with different lactose content. Using PLS-1 calibration models, correlations have been found between the voltammetric signals and chemical parameters measured by classical methods. PLS-1 models provide excellent correlations with lactose content. Additional information about other components such as fats, proteins and acidity can also be obtained. The method developed is simple and the short response time permits its use in assaying milk samples on-line.

In this study the formation of thin-film barrier coatings based on a highly-conducting Bi1.60Er0.4O3 (EDB) solid electrolyte on supporting Ce0.8Sm0.2O1.9 (SDC) electrolyte substrates is implemented for the first time using electrophoretic deposition (EPD). Electrokinetic properties of EDB-based suspensions in a non-aqueous dispersion medium of isopropanol modified with small additions of polyethyleneimine (PEI, 0.26 g/L) and acetylacetone (0.15 g/L), as well as in a mixed isopropanol/acetylacetone (70/30 vol.%) medium are studied. The dependences of the thickness of EDB coatings on voltage and deposition time are obtained using deposition on a model Ni-foil electrode. Preliminary synthesis of a conductive polypyrrole (PPy) polymer film is used to create surface conductivity of non-conductive SDC substrates. The efficiency of using a modified dispersion medium based on isopropanol to obtain a continuous EDB coating 12 μm thick, sintered at a temperature of 850 °C for 5 h, is shown. The microstructure and morphology of the surface of the EDB coating are studied. Pt/SDC/EDB/Pt cell is used to characterize the coating conductivity. The EPD method is shown to be promising for the formation of barrier coatings based on doped bismuth oxide. The developed method can be used for creating cathode barrier layers in SOFC technology.

The work reports a facile synthesis of high thermally-stable nanocrystalline anatase TiO2 nanoparticles (NPs) doped with different atomic concentrations (0.5, 1.0, 3.0, and 6.0%) of Gd3+ and Nd3+ ions by a template-free and one-step solvothermal process, using titanium(IV) butoxide as titanium precursor and dimethyl sulfoxide (DMSO) as solvent. The structure and morphology of the Gd3+, Nd3+, and 0.5%Gd3+-0.5%Nd3+/doped TiO2 NPs have been characterized by using various analytical techniques. The Gd3+/ and Nd3+/TiO2 molar ratios were found to have a pronounced impact on the crystalline structure, size, and morphology of TiO2 NPs. X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) studies revealed the proper substitution of Ti4+ by Gd3+ and Nd3+ ions in the TiO2 host lattice. The as-prepared Gdx/TiO2, Ndx/TiO2, and Gd1.0/Ndx/TiO2 bimetallic NPs, x = 0.5, 1.0, 3.0, and 6%, have been investigated as electrocatalysts for hydrogen evolution reaction (HER) in 1.0 M KOH solution using a variety of electrochemical techniques. At any doping percentage, the Gd1.0/Ndx/TiO2 bimetallic NPs showed higher HER catalytic performance than their corresponding counterparts i.e. Gdx/TiO2 and Ndx/TiO2. Upon increasing the Nd content from 0.5 to 6.0%, the HER catalytic performance of the Gd1.0/Ndx/TiO2 bimetallic NPs was generally enhanced. Among the studied materials, the bimetallic Gd1.0/Nd6.0/TiO2 NPs emerged as the most promising catalyst with an onset potential of -22 mV vs. RHE, a Tafel slope of 109 mV dec-1, and an exchange current density of 0.72 mA cm-2. Such HER electrochemical kinetic parameters are close to those recorded by the commercial Pt/C (onset potential: -15 mV, Tafel slope: 106 mV dec-1, and exchange current density: 0.80 mA cm-2), and also comparable with those measured by the most active electrocatalysts reported in the literature. The synergistic interaction of Gd and Nd is thought to be the major cause of the bimetallic catalyst's activity.

Lanthanide-doped upconversion nanoparticles (UCNPs) are promising bioimaging nanoprobes due to their excellent photostability. As one of the most commonly-used lanthanide activators, Tm3+ ions have perfect ladder-type electron configuration and can be directly excited by bio-friendly near-infrared-II (NIR-II) wavelengths. Here, the emission characteristics of Tm3+-doped nanoparticles under laser excitations of different near-infrared-II wavelengths were systematically investigated. The 1064 nm, 1150 nm and 1208 nm lasers are proposed to be three excitation strategies with different response spectra of Tm3+ ions. Particularly we found that 1150 nm laser excitation enables intense three-photon 475 nm emission, which is nearly 100 times stronger than that excited by 1064 nm excitation. We further optimized the luminescence brightness after investigating the luminescence quenching mechanism of bare NaYF4:Tm (1.75%) core. After growing inert shell, ten-fold increase of emission intensity was achieved. Combining the advantages of NIR-II wavelength and the higher-order nonlinear excitation, a promising facile excitation strategy was developed for the application of thulium-doped upconversion nanoparticles in single nanoparticle imaging and cancer cell microscopic imaging.

In this study, silver-strontium doped hydroxyapatite (AgSr-HA)/chitosan composite coatings were deposited on stainless steel (SS) substrate via electrophoretic deposition (EPD) technique. The EPD parameters such as the concentration of Ag Sr-HA particles in the suspension, applied voltage and deposition time were optimized on by the Taguchi Design of Experiment (DoE) approach. DOE approach elucidated that the “best” coating was obtained at; the deposition voltage of 20V, deposition time of 7 minutes, and at 5 g/L of Ag Sr-HA particles in the suspension. The optimum coatings were characterized by using scanning electron microscopy (SEM) and energy dispersive X-ray (EDX) spectroscopy. SEM images confirmed the deposition of chitosan/Ag Sr-HA on the SS substrate. The wettability studies indicated the hydrophilic nature of the chitosan/Ag Sr-HA coatings, which confirmed the suitability of the developed coatings for orthopedic applications. The average surface roughness of the chitosan/Ag Sr-HA coatings was in a suitable range for the attachment of bone marrow stromal cells. Chitosan/Ag Sr-HA coatings showed a potent antibacterial effect against the Gram-Positive and Gram-negative bacteria.

The electrical and optical properties of sol-gel derived aluminum-doped0 zinc oxide thin films containing 2 at.% Al were investigated considering the modifying effects of 1) increasing the sol H₂O content; and 2) thermal treatment procedure with high-temperature approach followed by an additional heat-treatment step under a reducing atmosphere. According to the results obtained via the TG-DTA analysis, FT-IR spectroscopy, X-ray diffraction technique and four-point probe resistivity measurement, it is argued that the sol hydrolysis, decomposition of the deposited gel and crystallization of grains result in grains of larger crystallite size and stronger c-axis preferred orientation with slightly less microstrain in the modified sample. The consequent morphology and grain-boundary characteristics turn out as improved conductivity, implying higher values of concentration and mobility of charge carriers. A detailed investigation on samples optical properties, in terms of analyzing their absorption and dispersion behaviors through the UV-Vis-NIR spectroscopy, support our reasoning for the increase of the mobility, and to a lesser extent, the concentration of charge carriers, while causing only a slight degradation of optical transmission. Hence, an enhanced performance as a transparent conducting film is claimed for the modified sample by comparing the figure-of-merit values.

Zinc oxide is one of the most important semiconductor metal oxides and one of the most promising n-type materials, but its practical use is limited because of both its high thermal conductivity and its low electrical conductivity. Numerous studies have shown that doping with metals in ZnO structures leads to the modification of the band gap energy. In this work, Al-doped ZnO, Ni-doped ZnO, and undoped ZnO nanocrystalline powders were prepared by sol-gel method coupled with ultrasound irradiation. The doping concentration in ZnO was 1.0 at.% of Al and Ni. Influence of Al³⁺ and Ni²⁺ ions in the ZnO network are explored in this paper. X-ray Diffraction (XRD), Raman Spectroscopy, Nitrogen Adsorption (BET method), X-Ray Fluorescence (XRF) and Field Emission Scanning Electron Microscopy (FESEM) analyses demonstrated the incorporation of metal ions (aluminum and nickel) into the ZnO wurtzite structure. The crystallite size of the sample was decreased from 24.5 nm (ZnO) to 22.0 nm (ZnO-Al) and 21 nm (ZnO-Ni).

The objective of this study was to assess the ability of producing laminated edible films manufactured using the following proteins; gelatin (G), whey protein isolate (WPI), and polysaccharide; sodium alginate (SA), and to evaluate their physical properties. Additionally, films’ preparation employing these ingredients was optimized through the addition of corn oil (O), Overall, 8-types of laminated films (G-SA, G-WPI, SA-WPI, SA-G-WPI, GO-SAO, GO-WPIO, SAO-WPIO, SAO-GO-WPIO were developed in this study. The properties of the prepared films were characterized through the measurement of; tensile strength (TS), elongation at break point (EB), puncture resistance (PR), tear strength (TT), water vapour permeability (WVP) and oxygen permeability (OP). The microstructure of cross-sections of laminated films was investigated by scanning electron microscopy (SEM). Mechanical properties of films were dramatically enhanced through the addition of film layers. GO-SAO laminate showed the best barrier properties to water vapour (22.6 ± 4.04 g mm/kPa d m2) and oxygen (18.2 ± 8.70 cm3 mm/kPa d m2). SAO-GO-WPIO laminate film was the strongest of all laminated films tested, having the highest TS of 55.77 MPa, PR of 41.36 N and TT of 27.32 N. SA-G-WPI film possessed the highest elasticity with an EB value of 17.4%.

The Sm3+/Gd3+ co-doped glasses in the B2O3–GeO2–PbO and B2O3–GeO2–Bi2O3 systems have been synthesized in the composition range of 40B2O3–40GeO2–(15-17)PbO(Bi2O3)–(3-2)Sm2O3–(2-1)Gd2O3 and 42.5B2O3–42.5GeO2–(11.25-12.75)PbO(Bi2O3)–(2.25-1.5)Sm2O3–(1.5-0.075)Gd2O3. The physical, structural, and spectral properties of the produced glasses have been studied. The fabricated glass samples demonstrated changes in temperature-sensitive luminescence parameters in 298-673 K temperature range. We found out several photoluminescence bands attributed with transitions from different Stark sublevels. By using a combination of two temperature sensitive and one non-sensitive transitions we calculated fluorescence intensities ratio (FIR). This procedure made it possible to increase the sensitivity of luminescence thermometry in several times. Such method could be very useful for the luminescent thermometry materials based on Ln3+ ions with multiplied f-f transitions.

In this study, we report a novel synthesis of hydrophobic silica aerogel powder composites, functionalized and binary-doped with [Tb(phen)₂](NO₃)₃ and [Eu(phen)₂](NO₃)₃ nanocrystals, employing a two-step sol-gel methodology. The investigation delves into the structural elucidation, optical properties and thermal conductivity of these functionalized Tb(III)-Eu(III) composites. Our analysis encompasses diffuse reflectance spectra, along with excitation and luminescence spectra, highlighting the quantum yields of composites with varying chemical composition. Remarkably, these samples exhibit a strong luminescence, with distinct hues of red or green color upon the specific doping type and level. The detailed examination of excitation spectra and quantum yields unequivocally establishes robust energy transfer mechanisms from the 1,10-phenanthroline molecule to the lanthanide ions. Notably, our study uncovers a Tb³⁺→Eu³⁺ energy transfer phenomenon within the binary functionalized samples, providing compelling evidence for a structural formation process occurring within the mesoporous framework of the aerogel powders.

A series of ZnO doped nitrogen-carbon materials (xZnO-N-C) with ZnO content of 5-40% are prepared by vacuum curing-carbonization strategy using polyamide-imide as N-C source and zinc nitrate as metal source for propane dehydrogenation (PDH). 20ZnO-N-C exhibits outstanding initial activity (propane conversion of 35.2% and propene yield of 24.6%) and relatively low deactivation rate (0.071 h-1) at 600 ◦C. The detailed characterization results show that small ZnO nanoparticles (5.5 nm) with high dispersion on the catalyst could be obtained by adjusting ZnO loading. Moreover, much more nitrogen-based species especially ZnNx species are formed on 20ZnO-N-C by comparison with 20ZnO-N-C-air prepared by curing-carbonization without vacuum, which may contribute for the higher product selectivity and catalytic stability of 20ZnO-N-C. The probable active sites for PDH reaction on the catalyst system are proposed to be C=O species and Zn2+ species. Moreover, the aggregation of ZnO nanoparticles is the primary reason for the activity loss on this catalyst system. The present finding not only provides the feasible construction strategy for the metal oxide doped nitrogen-carbon materials but also valuable guidance for the design of efficient catalyst in dehydrogenation of light alkane.

Water electrolysis is a highly efficient route to produce ideally clean H2 fuel with excellent energy conversion efficiency and high gravimetric energy density, without producing carbon trace unlike steam methane reforming, and resolves the issues of environmental contamination via replacing the conventional fossil fuel. Of special importance lies in the advancement of highly effective non-precious catalysts for the oxygen evolution reaction (OER). The electrocatalytic activity of an active catalyst mainly depends on the material conductivity, accessible catalytically active sites, and intrinsic OER reaction kinetics, which can be tuned via introducing heteroatom N in the catalyst stricture. Herein, an efficacious nitrogenation of CuS has been accomplished, which was synthesized using hydrothermal procedure, and characterized for their electrocatalytic activity towards OER. The nitrogen-doped CuO@CuS (N,CuO@CuS) electrocatalyst exhibits superior OER activity than pristine CuS (268 and 602 mV), achieving the low overpotential of 240 and 392 mV at a current density of 10 and 100 mA/cm2, respectively, ascribed to the favorable electronic structural modification triggered by nitrogen incorporation. The N,CuO@CuS also exhibits excellent endurance under varied current rates and a static potential response over 25 h stability measured at 10 and 100 mA/cm2.

The relaxation processes induced by an exposure of the Ar matrices doped with CH4 (0.1 – 10%) to an electron beam were studied with a focus on the dynamics of radiolysis products – H atoms, H2 molecules, CH radicals, and energy transfer processes. Three channels of energy transfer to dopant and radiolysis products were discussed: by free charge carriers, free excitons and photons from the “intrinsic source” provided by emission of the self-trapped excitons. Radiolysis products along with the total yield of desorbing particles were monitored in a correlated manner. Analysis of methane transformation reactions induced by free excitons showed that the CH radical can be considered as a marker of the CH3 species. The competition between exciton self-trapping and energy transfer to the dopant and radiolysis products has been demonstrated. A nonlinear concentration behavior of the H atoms in doped Ar matrices has been established. Real-time correlated monitoring of optical emissions (H atom and CH3 radicals), particle ejection, and temperature revealed a nonmonotonic behavior of optical yields with a strong luminescence flash after almost an hour of exposure, which correlated with explosive pulse of particle ejection and temperature. The connection of this phenomenon with the processes of energy transfer and radical-radical recombination is discussed.

Developing advanced carbon materials by utilizing biomass waste has attracted much attention. Herein, a N-doped carbon material (RSM-0.33-550) was prepared by directly pyrolyzing reed straw and melamine. The as-prepared RSM-0.33-550 possessed a N content of 6.02% and a specific surface area of 547.1 m2 g-1. As the anode for supercapacitors (SCs), in 6 M KOH, such RSM-0.33-550 exhibited a capacitance of 202.8 F g-1 at a current density of 1 A g-1. At a high current density of 20 A g-1, it still remained a capacitance of 158 F g-1. Notably, it delivered an excellent stability with capacity retention of 96.3% at 20 A g-1 after 5000 cycles. This work not only offer a new electrode material for SCs, but also gives a new insight for rationally utilizing the biomass waste for energy storage.

In this study, a new method for synthesizing Ag-NaYF4:Yb3+/Er3+ @ SiO2 nanocomposites was introduced. Using a hydrothermal method, the synthesized Yb3+- and Er3+-codoped NaYF4 upconversion luminescent materials and Ag nanoparticles were doped into upconversion nanomaterials and coated with SiO2 up-conversion nanomaterials. This material is known as Ag-UCNPs-SiO2’ it improves both the luminous intensity because of the doped Ag nanoparticles and has low cytotoxicity because of the SiO2 coating. The morphology of UCNPs was observed using scanning electron microscopy (SEM), and the mapping confirmed the successful doping of Ag nanoparticles. Successful coating of SiO2 was confirmed using transmission electron microscopy (TEM). Fluorescence spectra were used to compare changes in luminescence intensity before and after doping Ag nanoparticles. The reason for the increase in luminescence intensity after doping with Ag nanoparticles was simulated using first-principles calculations. The cytotoxicity of Ag-UCNPs-SiO2 was tested via the cell counting kit-8 (CCK-8) method, and its imaging ability was characterized using the micro-CT method.

This paper reports on the fabrication of alumina doped preforms using MCVD-vapor phase chelate delivery system with Al(acac)3 as the precursor. The objectives of the work are to study the deposition process, the efficiency of the fabrication process, and the quality of the fabricated fiber preforms. Two parameters are studied, Al(acac)3 sublimator temperature (TAl°C) and deposition direction (i.e. downstream and upstream). Other parameters such as oxygen flow and deposition temperature are fixed. The results showed that a high uniformity of refractive index difference (%RSD < 2%) and core size (%RSD < 2.4%) was obtained along the preform length using downstream deposition while for the combined upstream and downstream deposition the uniformity was deteriorated. The process efficiency was found to be about 21% for TAl°C of 185°C and downstream deposition. From the EDX elemental analysis, the refractive index was found to increase by 0.0025 per mole percent of alumina.

Metal oxide based electrodes play a crucial role in various as a transparent conductive oxide (TCO). One of the metal oxides, nickel oxide is a promising electrical conductive material. Here, we display that incorporation of vanadium in NiO lattice significantly improve both electrical conductivity and hole extraction. Also, vanadium doped nickel oxide exhibits a lower crystalline size compared to pristine nickel oxide, which maintains the reduction of surface roughness. These results indicating that the vanadium is an excellent dopant for NiO.

Phosphors based on magnesium titanate activated with Mn⁴⁺ ions are of great interest because, when excited with blue light, they display a strong red-emitting luminescence. They are characterized by a luminescence decay which is strongly temperature dependent in the range from 0 to 80 °C, making these materials very promising for temperature sensing in the biochemical field. In this work the optical and thermal properties of the luminescence of Mg₂TiO₄ are investigated for different Mn⁴⁺ doping concentrations. The potential of this material for temperature sensing is demonstrated by fabricating a fiber optic temperature microsensor and by comparing its performance against a standard resistance thermometer. The response of the fiber optic sensor is exceptionally fast, enabling monitoring of temperature fluctuation in subsecond time domain.

Highly photoluminescent C-Dots are prepared by hydrothermal reaction of citric acid and piperazine as dual reason in both hydrolysis and surface passivation agent along with the N-doping agent. The resulting C-Dots without external passivation showed PL enhancement by electron transfer from C-Dots-donor to piperazine-acceptor with the maximum emission yields of more than 84%. After mixing the prepared C-Dots with the mixture of EtOH and acetone (1:1 vol %), a novel washing process was performed by centrifugation to remove the precursors and by-products. The resulting C-Dots showed much better stability than dialysis. For evaluating the possible application of the C-Dots as a fluorescent biological probe which possess the wide dosing window and multicolor properties. The C-Dots were localized in perinuclear vacuole-like structures with granular pattern in cytoplasm sparing the nucleus. No signs of any morphological deterioration like nuclear shrinkage were observed.

In this paper, we investigate the structural, microstructural, dielectric, and energy storage properties of Nd and Mn co-doped Ba0.7Sr0.3TiO3 [(Ba0.7Sr0.3)1-xNdxTi1-yMnyO3 (BSNTM) ceramics (x = 0, 0.005, and y = 0, 0.0025, 0.005, and 0.01)] via a defect dipole engineering method. The complex defect dipoles (MnTi"-VO∙∙)∙ and (MnTi"-VO∙∙) between acceptor ions and oxygen vacancies capture electrons, enhancing the breakdown electric field and energy storage performances. XRD, Raman spectroscopy, and microscopic investigations of BSNTM ceramics revealed the formation of a tetragonal phase, increased oxygen vacancies, and reduced grain size with Mn dopant, respectively. The BSNTM ceramics with x=0.005 and y=0 exhibit a high dielectric constant of 2058 and a dielectric loss of 0.026 at 1 kHz. These values gradually decreased to 1876 and 0.019 for x=0.005 and y=0.01 due to the Mn2+ ions at Ti4+-site, which facilitates the formation of oxygen vacancies, and prevents the decrease of Ti4+. In addition, the defect dipoles act as a driving force for depolarization to tailor the domain formation energy and domain wall energy, which provides a high difference between the maximum polarization of Pmax and remnant polarization of Pr (ΔP=10.39 µC/cm2). Moreover, the complex defect dipoles with optimum oxygen vacancies in BSNTM ceramics can provide not only a high ΔP but also reduce grain size, which together improve the breakdown strength from 60.4 to 110.6 kV/cm, giving rise to a high energy storage density of 0.41 J/cm3 and high efficiency of 84.6% for x=0.005 and y=0.01. These findings demonstrate that defect dipoles engineering is an effective method to enhance the energy storage performance of dielectrics for capacitor applications.

The catalytic decomposition of methane (CDM) process produces hydrogen in a single stage and avoids the CO₂ emission thanks to the formation of high added value carbon nanofilaments as by-product. In this work, Ni monometallic and Ni-Co, Ni-Cu and Ni-Fe bimetallic catalysts are tested in the CDM reaction for the obtention of fishbone carbon nanofibers (CNF). Catalysts, in which Al₂O₃ is used as textural promoter in their formulation, are based on Ni as main active phase for the carbon formation and on Co, Cu or Fe as dopants in order to obtain alloys with an improved catalytic behaviour. Characterization of bimetallic catalysts showed the formation of particles of Ni alloys with a bimodal size distribution. For the doping content studied (5 mol. %), only Cu formed an alloy with a lattice constant high enough to be able to favor the carbon diffusion through the catalytic particle against surface diffusion, resulting in higher carbon formations, longer activity times and activity at 750 °C, where Ni, Ni-Co and Ni-Fe catalysts were inactive. On the other hand, Fe also improved the undoped catalyst performance presenting a higher carbon formation at 700 °C and the obtention of narrow carbon nanofilaments from active Ni₃Fe crystallites.

: Low-temperature growth of diamond films by chemical vapor deposition (CVD) method is not so widely reported and especially its initial periods of nucleation and growth phenomenon are of particular interest to the researchers. Four sets of substrates were selected for growing diamond films by linear antenna microwave plasma enhanced CVD (LA-MPCVD). Among them, silicon and sapphire substrates were pre-treated with detonation nanodiamond (DND) seeds before diamond growth for enhancement of its nucleation. On the other hand, carbon nanotube (CNT) films on Si substrates were also used as another template for LA-MPCVD diamond growth. In order to enhance the diamond nucleation during CVD growth, some of the CNT films were again pre-treated by electrophoretic deposition (EPD) of diamond nanoparticles. All these substrates were then put inside the LA-MPCVD chamber for growing diamond films under variable processing conditions. Microwave input powers (1100 – 2800 W), input power modes (pulse or continuous), antenna to stage distances (5 - 6.5 cm), process gas recipes (with or without CO2), methane gas percentages (3 - 5%), deposition times (11 – 120 minutes) were altered to investigate their effect on the growth of diamond film on the pre-treated substrates. The substrate temperatures were found to vary from as low as 170oC to a maximum of 307oC during the alteration of the different processing parameters. Contrary to the conventional MPCVD, it was observed that during the first hour of LA-MPCVD diamond growth, DND seeds or the nucleating structures, do not coalesce together to make a continuous film. Deposition time was the most critical factor in fully covering the substrate surfaces with diamond film, since the substrate temperature could not become stable during the first hour of LA-MPCVD. CNT was found to be oxidised rapidly under LA-MPCVD plasma conditions; therefore, a CO2-free process gas recipe was used to reduce CNT burning. Moreover, EPD-coated CNT was found to be less oxidised by the LACVD plasma during diamond growth.

Titanium oxynitride thin films are deposited by DC reactive magnetron sputtering. A pure titanium target is sputtered in a reactive atmosphere composed of argon, oxygen and nitrogen gases. The oxygen mass flow rate as well as that of the nitrogen gas are both pulsed during the deposition time using an independent and rectangular signal for each reactive gas. A constant pulsing period T = 45 s is applied for both reactive gases and a delay time  of 34 s between N2 and O2 injection times is set for all depositions. Oxygen and nitrogen duty cycles are systematically and independently changed from 0 to 100% of their pulsing period. From real time measurements of the Ti target potential and total sputtering pressure, it is shown that the reactive process alternates between oxidized, nitrided and elemental sputtering modes as a function of the oxygen and nitrogen injection times. The full poisoning of the Ti target surface by oxygen and/or nitrogen can be avoided for some given ranges of O2 and N2 duty cycles. Deposition rates of titanium oxynitride films are substantially enhanced and can be adjusted between that of pure Ti and TiN films with a gradual transition of their optical transmittance in the visible range. These results support that titanium oxynitride compounds exhibiting absorbent to transparent behaviors can be precisely sputter-deposited by means of a two reactive gases pulsing process.

Hydrotalcites (HTlc) represents a class of nanostructured layered materials that may be employed in a variety of applications, from green to bio technologies. In this paper, we report an investigation on HTlc made of Mg and Fe, recently employed to improve the growth in vitro of osteoblasts within a keratin sponge. We have carried out an analysis of powder materials and of HTlc dispersed in keratin and spin-coated on a Si/SiO2 substrate at different temperatures. A DC magnetic study of the powders has been carried out with a Quantum Design Physical Property Measurement System, equipped with a Vibrating Sample Magnetometer. The data gathered prove that these HTlc are fully paramagnetic, and keratin shows a very small magnetic response. Optical and Atomic Force Microscopy analyses of the thin films provide a detailed picture of clusters randomly dispersed in the films with various dimensions. The magnetic properties of these films have been characterized using the Nano Magneto Optical Kerr Effect (NanoMOKE) down to 7.5K. The data collected show that the local magnetic properties can be mapped with a micrometric resolution distinguishing HTlc regions from keratin ones. This approach opens new perspectives in the characterization of these composite materials.

Lead-based ternary chalcogenide thin films of the (PbTe)1-x(PbS)x system were obtained by plasma-enhanced chemical vapor deposition technique (PECVD) under conditions of a nonequilibrium low-temperature argon plasma of an RF discharge (40.68 MHz) at a reduced pressure (0.01 Torr). High-purity elements were directly used as starting materials – Pb, S and Te. Plasma-chemical synthesis was carried out on the surface of of c-sapphire and silicon substrate. The physicochemical properties of the films were studied by various analytical methods. The dependence of the Seebeck coefficient, resistivity, and power factor on the structural properties and composition has been studied. The thermoelectric characteristics were found to be dependent on the film composition. Upon the selection of optimal sulfur concentration one can increase the power factor as compared to single phase PbS ot PbTe films.

Mechanical robustness, biocompatibility, and antibacterial performances are key features for materials suitable to be used in tissue engineering applications. In this work, we investigated the link existing between structural and functional properties of TiCu(Ag) thin films deposited by physical vapor deposition magnetron sputtering on Si substrates. The thin films were characterized by X-ray diffraction (XRD), nanoindentation, atomic force microscopy (AFM), and X-ray photoelectron spectroscopy (XPS). The TiCu(Ag) thin films showed complete amorphous structure and improved mechanical properties in comparison with pure Ti films. However, for contents in excess of 20% Ag, we observed the appearance of nanometric Ag crystallite. The TiCu(Ag) thin films displayed excellent biocompatibility properties, allowing adhesion and proliferation of the human fibroblasts MRC-5 cell line. Moreover, all the investigated TiCu(Ag) alloy display bactericidal properties, preventing the growth of both Pseudomonas aeruginosa and Staphylococcus aureus. Results obtained from biological tests have been correlated to the surface structure and microstructure of films. The excellent biocompatibility and bactericidal properties of these multifunctional thin films opens to their use in tissue engineering applications.

Transparent conducting oxides (TCO) with high electrical conductivity and at the same time high transparency in the visible spectrum are an important class of materials widely used in many devices requiring a transparent contact such as light-emitting diodes, solar cells and display screens. Since the improvement of electrical conductivity usually leads to degradation of optical transparency, a fine-tuning sample preparation process and a better understanding of the correlation between structural and transport properties is necessary for optimizing the properties of TCO for use in such devices. Here we report a structural and magnetotransport study of tin oxide (SnO₂), a well-known and commonly used TCO, prepared by a simple and relatively cheap Atmospheric Pressure Chemical Vapour Deposition (APCVD) method in the form of thin films deposited on soda-lime glass substrates. The thin films were deposited at two different temperatures (which were previously found to be close to optimum for our setup), 590 °C and 610 °C, and with (doped) or without (undoped) the addition of fluorine dopants. Scanning Electron Microscopy (SEM) and Grazing Incidence X-ray Diffraction (GIXRD) revealed the presence of inhomogeneity in the samples, on a bigger scale in form of grains (80–200 nm), and on a smaller scale in form of crystallites (10–25 nm). Charge carrier density and mobility extracted from DC resistivity and Hall effect measurements were in the ranges 1–3 × 10²⁰ cm⁻³ and 10–20 cm²/Vs, which are typical values for SnO₂ films, and show a negligible temperature dependence from room temperature down to -269 °C. Such behaviour is ascribed to grain boundary scattering, with the interior of the grains degenerately doped (i.e., the Fermi level is situated well above the conduction band minimum) and with negligible electrostatic barriers at the grain boundaries (due to high dopant concentration). The observed difference for factor 2 in mobility among the thin-film SnO₂ samples most likely arises due to the difference in the preferred orientation of crystallites (texture coefficient).

Currently, petroleum-derived plastics are widely used. However, one of its main disadvantages is its low degradation time, which is not beneficial to the environment. Therefore, natural polymers are an alternative to overcome this obstacle. Among the natural polymers, starch can be highlighted. Thus, the objectives of our investigation were to obtain sisal nanofibers using low concentrations of acid solutions to produce and characterize corn starch nanocomposites reinforced with these nanofibers. The films were produced by a casting technique using commercial corn starch and glycerol as plasticizing agents; the nanofibers were obtained using acid hydrolysis. The films were subjected to tensile tests to evaluate their resulting mechanical behaviors. The results of X-ray diffraction and transmission electron microscopy analyses revealed the possibility of obtaining cellulose nanofibers using a sulfuric acid concentration lower than that previously reported in the literature. The nanocomposites reinforced with plant nanofibers showed lower tensile stress and elongation characteristics than the matrices without nanofibers.

ZnO thin films with a thickness of 300 nm were deposited on Si and Al2O3 substrates using electron beam evaporation technique with the aim to be tested as low cost and low power consumption gas sensors for ozone (O3). To characterize the surface roughness and the grain size, which are the main parameters recognized to enhance gas sensitivity since they directly influence the effective sensing area, surface morphology and roughness analyses of the films were performed using scanning electron microscopy and atomic force microscopy, respectively. The crystalline structure and elemental composition were studied through Raman spectroscopy and X-ray photoelectron spectroscopy. Gas tests were conducted at room temperature and zero-bias voltage to assess the sensitivity and response as a function of time of the films to O3 pollutant. The results indicate that the films deposited on Al2O3 exhibit promising characteristics, such as high sensitivity and a very short response time (< 2 s) to the gas concentration. Additionally, it was observed that the films display pronounced degradation effects after a significant exposure to O3.

On-chip integration of two-dimensional (2D) materials with unique structures and distinctive properties endow integrated devices with new functionalities and improved performance. With a high flexibility in modifying its properties and a strong compatibility with various integrated platforms, graphene oxide (GO) becomes an attractive 2D material for implementing functional hybrid integrated devices. Here, we demonstrate novel functionalities that go beyond the capabilities of conventional photonic integrated circuits, by harnessing the photo-thermal effects in 2D GO films integrated onto them. These include all-optical control and switching, optical power limiting, and non-reciprocal light transmission. The 2D layered GO films are on-chip integrated with precise control of their thicknesses and sizes. Benefitting from the broadband response of 2D GO films, all the three functionalities feature a very wide operational bandwidth. By fitting the experimental results with theory, we also extract the changes in material properties induced by the photo-thermal effects, which reveal interesting insights about 2D GO films. These results highlight the versatility of 2D GO films in implementing functional integrated photonic devices for a range of applications.

In the aerospace sector, structural and non-structural components are usually subjected to a wide range of environmental conditions. Although lightweight, the use of composite parts for these applications is restricted, due to their poor performance in severe environmental conditions. Specifically, moisture can seriously damage the materials' performance, reducing their mechan-ical, thermal, electrical, and physical properties as well as the service time. A strategy to improve the materials’ resistance in humid environments is the use of protective lightweight barrier coatings to reduce the diffusion of gases and/or liquids in composites. Nanolamellar nanocom-posite characterized by the high in-plane orientation of nanoplatelets effectively works as barrier structures by generating tortuous paths for molecule diffusion. In this work, the effectiveness of protection against water uptake of nanocomposites reinforced with Graphite NanoPlatelets (GNPs) at high filler content (70, 80 and 90%wt) for Kevlar sandwich panels of a nacelle engine of an ATR42 aircraft has been investigated. Moisture uptake and Ground Air Ground (GAG) tests were carried out in an environmental chamber to reproduce temperature and relative humidity profiles representative of a real-scale application for a regional aircraft composite part. The high filler content of the graphene films ensures a high level of tortuosity by delaying and reducing moisture absorption by –71% compared to the unprotected panel, showing good barrier properties.

Laser-induced functionalisation using excimer laser irradiation has been widely applied to transparent conductive oxide films. However, exploring suitable irradiation conditions is time-consuming and cost-ineffective as there are numerous routine film fabrication and analytical processes. Thus, we herein explored a real-time technique to monitor the laser-induced functionalisation of transparent conductive oxide films. We developed two types of monitoring apparatus, electrical and optical, and applied them to magnetron-sputtered Sn-doped In2O3 films grown on glass substrates and hydrogen-doped In2O3 films on glass or plastic substrates using a picosecond Nd:YAG pulsed laser. Both techniques could monitor the functionalisation from a change in properties of the films on glass substrates by laser irradiation, but electrical measurement was unsuitable for plastic samples because of a laser-induced degradation of the underlying plastic substrate, which harmed proper electrical contact. Instead, we demonstrated that the optical properties in the near-infrared region were suitable for the monitoring and the changes in the optical properties were visually detected in real-time by using a near-infrared camera.

A new process is reported for the incorporation of a fluoropolymer into a solid perovskite film. Poly(trifluoroethyl methacrylate) [CH2C(CH3)(CO2CH2CF3)]n was delivered to methylammonium lead iodide (CH3NH3PbI3) perovskite films by crystallizing the film in supercritical carbon dioxide/ethanol containing the dissolved fluoropolymer. The surface was characterized before and after fluoropolymer exposure using scanning electron microscopy, Raman spectroscopy and contact angle measurements. The results indicate that the fluoropolymer was incorporated into the perovskite film during the supercritical fluid crystallization process.

We investigated layered titanium nitride (TiN) and aluminum nitride (AlN) for color glasses in Building Integrated Photovoltaic (BIPV) systems. AlN and TiN are among suitable and cost-effective optical materials to be used as thin multilayer films, owing to the significant difference in their refractive index. To fabricate the structure, we used radio frequency magnetron deposition method to achieve the target thickness uniformly. A simple, fast, and cheap fabrication method is achieved by depositing the multilayer films in a single sputtering chamber. It is demonstrated that a multilayer stack that allows light to move from a low refractive index layer to a high refractive index layer or vice-versa can effectively create various distinct color reflections for different film thicknesses and multilayer structures. It is investigated from simulation based on wave optics that, TiN/AlN multilayer offers better color design freedom and cheaper fabrication process as compared to AlN/TiN multilayer films. Blue, green, and yellow color glasses with optical transmittance of more than 80% was achieved by ITO coated glass/TiN/AlN multilayer films. This technology exhibits good potential in commercial BIPV system applications.

We report the synthesis and characterization of Poly Methyl-Meth-Acrylate (PMMA)/Poly vinylalcohol (PVA) polymeric blend doped with different concentrations of Copper oxide (CuO) nanoparticles (NPs). The (PMMA-PVA)/CuO nanocomposite hybrid thin films (wt. % = 0%, 2%, 4%, 8%, and 16%) of CuO NPs are deposited on glass substrates via dip-coating technique. The transmittance (T%), reflectance (R%), the absorption coefficient (α), the optical constants [refractive index (n), extinction coefficient (k)], optical dielectric functions [ɛ',ɛ''] are investigated and interpreted. Tauc, Urbach, Spitzer-Fan, and Drude models are employed to calculate the optical bandgap energy (Eg) and the optoelectronic parameters of the nanocomposite thin films. The refractive index and optical bandgap energy of of (PMMA-PVA) polymeric thin film are found to be (1.5 to 1.85) and 4.101 eV, respectively. Incorporation of specific concentrations of CuO-NPs in (PMMA-PVA) polymeric thin films leads to a noticeable decrease in the optical bandgap energy and to an increase of the refractive index. Moreover, Fourier Transform Infrared Spectroscopy (FTIR) transmittance spectra are measured and analyzed for undoped and doped polymeric thin films to pinpoint the major vibrational modes in the spectral range (500 and 4000 cm-1), as well as, the nature of network bonding in both systems. Thermal stability of thin films is investigated by performing thermogravimetric analysis (TGA). The TGA thermograms confirm that both doped polymeric thin films are thermally stable at temperatures below 110°C which enables them to be attractive for a wide range of optical and optoelectronic applications. Our results indicate that optical, vibrational and thermal properties of both polymeric thin films can be tuned for specific applications by the appropriate corporation of particular concentrations of CuO-NPs.

We report on the effects of the film morphology on the fluorescence spectra for a thin film including a quinoxaline-based co-polymer (TQ1) and a fullerene derivative (PC₇₀BM). The ratio between the polymer and the fullerene derivative, as well as the processing solvent were varied. Beside the main emission peak at 700 nm in the fluorescence spectra of thin films of this phase-separated blend, a broad emission band is observed with a maximum at 520 - 550 nm. The intensity of this emission band decreases with an increasing degree of mixing in the film and becomes most prominent in thicker films, films with high PC₇₀BM content, and films that were spin-coated from solvents with lower PC₇₀BM solubility. We assign this emission band to aggregated PC₇₀BM.

Three-dimensional nanocomposite networks consisting of percolated Si nanowires in a SiO₂ matrix, Si:SiO₂, were studied. The structures were obtained by reactive ion beam sputter deposition of SiO_x (x ≈ 0.6) thin films at 450 °C and subsequent crystallization using conventional oven as well as millisecond line focus laser annealing. Rutherford backscattering spectrometry, Raman spectroscopy, X-ray diffraction, cross-sectional and energy-filtered transmission electron microscopy were applied for sample characterization. While oven annealing resulted in a mean Si wire diameter of 10 nm and a crystallinity of 72 % within the Si volume, almost single-domain Si structures with 30 nm in diameter and almost free of amorphous Si were obtained by millisecond laser application. The structural differences are attributed to the different crystallization processes: Conventional oven tempering proceeds via solid state, millisecond laser application via liquid phase crystallization of Si. The 5 orders of magnitude larger diffusion constant in the liquid phase is responsible for the three times larger Si nanostructure diameter. In conclusion, laser annealing offers not only significantly shorter process times but moreover a superior structural order of nano-Si compared to conventional heating.

The integration of clean energy generation with wastewater treatment holds promise for addressing both environmental and energy concerns. Focusing on photocatalytic hydrogen production and wastewater treatment, the study introduces PdIn/TiO2 catalysts for the simultaneous removal of the pharmaceutical contaminant paracetamol and hydrogen production. Physicochemical characterization showed a high distribution of Pd and In on the support as well as a high interaction with it. The Pd and In deposition enhances the light absorption capability and significantly improved HER in comparison to TiO2 not only in the electrolyte but also in presence of paracetamol. Regarding PTM oxidation, TiO2 and PdIn/TiO2 showed an irreversible behavior toward the PTM oxidation, limited by the adsorption of species on the electrode surface. Thus, PdIn-doped TiO2 stands out as a promising catalyst, showcasing enhanced physicochemical properties and superior catalytic performance. This underscores its potential for both environmental remediation and sustainable hydrogen production.

We used a metal-organic chemical vapor deposition technique to synthesize a boron-doped reduced graphene oxide (B-rGO) material with various electrical characteristics, dependent on simultaneous reduction and doping procedures. The effect of the doping level on the B bonding in the reduced graphene oxide (rGO) layer controlled by the annealing temperature was investigated using X-ray photoelectron spectroscopy (XPS). The XPS data indicated that the B-rGO layer had a higher B concentration and a considerable number of O-B bonds as a result of the appreciable annealing temperature, which resulted in a decreased work function and Schottky contact between B-rGO and n-type Si. Owing to the higher proportion of B-C and B-C3 bonding in the B-rGO device than that in the rGO/Si device, the lower Schottky barrier height of the B-rGO/n-Si vertical junction photodetector resulted in a higher responsivity. This work suggests a facile method of B doping to alter the electrical properties of graphene materials.

The development of high-performance sensing materials for detecting or removing SF₆ decomposition gases is crucial for gas-insulated switchgear (GIS). In this work, the adsorption characteristics of the pristine porphyrin (Pr) and Fe-doped porphyrin (FePr) monolayers towards SF₆ decomposition gases were investigated using the first-principles calculations. Additionally, the electronic properties and sensing-mechanism were also examined. The findings indicate that both Pr and FePr monolayers exhibit thermodynamic stability. The intrinsic Pr monolayer only exhibits a moderate affinity towards the SO₂ molecule, however, its poor sensitivity of the Pr monolayer renders it unsuitable as the sensing-material. In contrast, the FePr monolayer exhibits favorable adsorption strength towards all five toxic gases (H₂S, SO₂, SOF₂, SO₂F₂, HF). The FePr monolayer exhibits chemisorption towards SO₂/SOF₂ gases, Furthermore, the microscopic mechanism of gases-substrate interaction is elucidated through the analysis of charge density difference, charge transfer, and density of states. Moreover, the FePr has excellent sensitivity for H₂S, SO₂, SO₂F₂, SOF₂ and HF molecules owing to the significant variations of the band gap, electrical conductivity and work function. In addition, the τ of H₂S, SO₂, and SOF₂ is 12.6 μs, 18.5 s and 15.4 s at 298 K, respectively. Our calculated results can offer theoretical guidance for the practical application of FePr-based sensing materials to detect SF6 decompositions gases.

Nanomaterials such as pH-responsive polymers are promising for targeted drug delivery systems, due to the difference in pH between tumor and healthy regions. However, there is a significant concern about the application of these materials in this field due to their low mechanical resistance, which can be mitigated by combining these polymers with mechanically resistant inorganic materials such as mesoporous silica nanoparticles (MSN) and hydroxyapatite (HA). Mesoporous silica has interesting properties such as high surface area and hydroxyapatite has been widely studied to aid in bone regeneration, providing special properties adding multifunctionality to the system. Furthermore, fields of medicine involving luminescent elements such as rare earth are an interesting option in cancer treatment. The present work aims to obtain a pH-sensitive hybrid system based on silica and hydroxyapatite with photoluminescent and magnetic properties. The nanocomposites were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), nitrogen adsorption methods, CHN elemental analysis, Zeta Potential, scanning electron microscopy (SEM), and transmission electron microscopy (TEM), vibrational sample magnetometry (VSM), and photoluminescence analysis. Incorporation and release studies of the antitumor drug doxorubicin were performed to evaluate the potential use of these systems in targeted drug delivery. The results showed the luminescent and magnetic properties of the materials and showed suitable characteristics for application in the release of pH-sensitive drugs.

Mn-doped CeO2 and CeO2 with the same morphology (nanofiber and nanocube) were synthesized through hydrothermal method respectively. When applied to benzene oxidation, the catalytic properties of Mn-doped CeO2 were higher than those of CeO2, which was related with the concentration of O vacancy. Compared to CeO2 with the same morphology, more oxygen vacancies were formed on the surface of Mn-doped CeO2, due to Mn ion replacing Ce ion. The lattice replacement was analyzed through XRD, Raman, electron energy loss spectroscopy and electron paramagnetic resonance technology. The formation energies of oxygen vacancy on the different exposed crystal planes [(110) and (100)] for Mn-doped CeO2 were calculated by applying the density functional theory (DFT). The data showed that the oxygen vacancy was easier to be formed on the (110) plane. The factors influencing catalytic behavior were elaborated, which indicated that surface oxygen vacancy played an important part in catalytic reaction.

Vertically aligned Fe, S, and Fe-S doped anatase TiO₂ nanotube arrays are prepared by electrochemical anodization process using an organic electrolyte in which lactic acid is added as an additive. In the electrolyte, nanotube layers of greater length (12 μm) and high order with inner diameter of approx. 90 nm and outer diameter of approx. 170 nm are achieved. Doping of Fe, S, and Fe-S via simple wet impregnation method substituted Ti and O sites with Fe and S, which leads to enhance the rate performance at high discharge current densities. Discharge capacities of TiO₂ tubes increased from 82 mAh g-1 (bare) to 165 mAh g-1 for Fe-S doped TiO₂ at high current densities of 0.3 mAcm-2 after 100 cycles with exceptional capacity retention of 85% after 100 cycles. Owing to the enhancement of thermodynamic and kinetic properties by doping of Fe-S, Li-diffusion increas2ed resulting in remarkable discharge capacities of 143 mAh g-1 and 89 mAh g-1 at a current density of 7.4 mA cm-2 and 19 mA cm-2, respectively.

This study investigated dry reforming of methane with combined catalysts supported on γ-Al2O3 support doped with 3.0 wt. % TiO2. The physicochemical properties of all the catalysts were determined by inductively-coupled plasma/mass spectrometry metal analysis, nitrogen physisorption, X-ray diffraction, temperature programmed reduction/desorption, thermogravimetric analysis, and scanning electron microscopy. The addition of CeO2 and MgO to Ni strengthened the interaction between the Ni and the support. The catalytic activity results indicated that the CeO2 and MgO addition to Ni did not do much in retarding carbon deposition, but they improved the activity of the catalysts. Among the tested catalysts, it was found that the catalyst with the composition of 5.0 wt % NiO-10.0 wt % CeO2/3.0 wt %TiO2-γ-Al2O3 resulted in the highest CH4 and CO2 conversion with H2/CO mole ratio close to unity. The optimum reaction conditions in terms of reactant conversion and H2/CO mole ratio were achieved by varying space velocity and CO2/CH4 mole ratio.

Biodegradable and renewable plastic films have been regarded as promising alternative green materials to achieve the substitution polythene (PE)films to reduce plastic pollution. Poly (butylene adipate-co-terephthalate) (PBAT) is a kind of biodegradable polyester, which is widely used in the production of biodegradable mulching films. However, the high cost of PBAT limited it applications. Thus, lignin, one of the most abundant biomass resources was incorporated into PBAT matrix in the present work. A series of Lignin/PBAT biodegradable plastics films with different Lignin/PBAT weight ratios (0.00 %-5.00 %) were successfully fabricated using twin screw and twin roll extruders. The chemical compositions, morphologies, thermal stabilities, mechanical properties, and barrier properties of samples were characterized by XRD, FTIR, TG/DSC, mechanical testing machine, and WVTR, respectively. Results show that the corporation of lignin into PBAT matrix could lead to improved thermal stabilities, mechanical properties and barrier properties of films even after Xenon lamp aging process, especially when Lignin/PBAT weight ratio is 1.00 % in the present work. This work provides a very promising approach for fabrication of biodegradable plastics films with low cost, enhanced mechanical properties and barrier properties, the as-prepared samples may have potential applications in agricultural or food packaging materials.

In this article, the effect of substitution of Zr and Ga in Dy2Fe17 prepared by arc melting technique are studied. The substitution of Zr and Ga in Dy2Fe17 was found to have an important effect on their structure and magnetic properties. The Rietveld analysis conformed that the crystalline system wereTh2Ni17 structure. Lattice parameters a (Å) and c (Å), unit cell volume (Å3), bonding distance (Å) were calculated by using Rietveld analysis. The unit cell volume of Dy2Fe17-xZrx and Dy2Fe16Ga1-xZrx increase linearly with the Zr and Ga substitution. The substitution of Zr and Ga are limited up to x=1 in order to avoid the decrease in saturation magnetization. The Curie temperature (Tc) of Dy2Fe17-xZrx and Dy2Fe16Ga1-xZrx are found to be Zr content dependent. The Curie temperature is found to be increasing first and then decrease for higher Zr content. The maximum curie temperature was observed 510K at x = 0.75 for Dy2Fe17-xZrx and 505.1 K at x = 0.5 for Dy2Fe17-xZrx which are102 K and 97 K higher than Dy2Fe17. The room temperature Mössbauer analysis shows the decrease in average hyperfine field and increase in isomer shift with Zr doping.

Recently, electrocatalysts for oxygen reduction reactions (ORRs) as well as oxygen evolution reactions (OERs) hinged on electrospun nanofiber composites have attracted wide research attention. Transition metal elements and heteroatomic doping are important methods used to enhance their catalytic performances. Lately, the construction of electrocatalysts based on metal-organic framework (MOF) electrospun nanofibers has become a research hotspot. In this work, bimetallic NixCoy-ZIF nanocrystals were synthesized in an aqueous solution, followed by NixCoy-ZIF/PAN electrospun nanofiber precursors, which were prepared by a simple electrospinning method. Bimetal (Ni-Co) porous carbon nanofiber catalysts doped with nitrogen, oxygen, and sulfur elements were obtained at high-temperature carbonization treatment in different atmospheres (Ar, Air, and H2S), respectively. The morphological properties, structures, and composition were characterized by SEM, TEM, SAED, XRD, and XPS. Also, the specific surface area of materials and their pore size distribution was characterized by BET. Linear sweep voltammetry curves investigated catalyst performances towards oxygen reduction and evolution reactions. Importantly, Ni1Co2-ZIFs/PAN-Ar yielded the best ORR activity, whereas Ni1Co1-ZIFs/PAN-Air exhibited the best OER performance. This work provides significant guidance for the preparation and characterization of multi-doped porous carbon nanofibers carbonized in different atmospheres.

The effect of transition metal substitution for Fe and the structural and magnetic properties of Gd2Fe16Ga0.5TM0.5 (TM=Cr, Mn, Co, Ni, Cu, and Zn) compounds were investigated. Rietveld analysis of X-ray diffraction indicates that all the samples crystallize in the hexagonal Th2Ni17 structure. The lattice parameters: a, c and unit cell volume show TM ionic radii dependence. Both Ga and TM atoms show preferred site occupancy for 12j and 12k sites. The saturation magnetization at maximum room temperature was observed for Co, Ni, and Cu of 69, 73, and 77 emu/g, respectively while minimum value was observed for Zn (62emu/g) doping Gd2Fe16Ga0.5TM0.5. Highest Curie temperature of 590 K was observed for Cu doping which is 15% and 5% and thesehigher than Gd2Fe17 and Gd2Fe16Ga compounds, respectively. The hyperfine parameters viz. hyperfine field and isomer shift, show systematic dependence on the TM atomic number. The observed magnetic and Curie temperature behavior in Gd2Fe16Ga0.5TM0.5 is explained on the basis of Fe(3d)-TM(3d) hybridization. The superior Curie temperature and magnetization value of Co, Ni, and Cu doped Gd2Fe16Ga0.5TM0.5 compounds as compared to pure Gd2Fe17 or Gd2Fe16Ga makes Gd2Fe16Ga0.5TM0.5 a potential candidate for high-temperature industrial magnet applications.

The utilization of titanium dioxide (TiO2) as a photocatalyst for the treatment of wastewater has attracted significant attention in the environmental field. Herein, we have prepared a NH2-MIL-125-derived TiO2@N-doped C Visible Light Catalyst through an in-situ calcination method. The nitrogen element in the organic connector is released through calcination, simul-taneously doping into the sample, thereby enhancing its spectral response to cover the visible region. The as-prepared TiO2@N-doped C catalyst exhibited preserved cage structure even after calcination, thereby alleviating the optical shielding effect and further augmenting its photo-catalytic performance by increasing the reaction sites between the catalyst and pollutants. The calcination time of the TiO2@N-doped C-450 °C catalyst was optimized to achieve a balance be-tween the TiO2 content and nitrogen doping level, ensuring efficient degradation rates for basic fuchsin (99.7%), Rhodamine B (89.9%), and tetracycline hydrochloride (93%) within 90 minutes.

In recent years, genetic research has been developing rapidly and taking on a larger role in research and medicine. The synthesis of any particle that can be used in this research can pave the way for new developments in this field. This research aims to develop a chemical method to produce nitrogen-doped carbon quantum dots - economical and bio-sourced substances that bind to genomic DNA. Carbon quantum dots are produced by the green synthesis hydrothermal method from radish, which is abundant in nature, and economically affordable. Nitrogen is added to increase the fluorescence properties of the produced carbon quantum dots and to improve their binding to DNA. The synthesized nitrogen-doped carbon quantum dots (N-CQDs) were tested through chromosome imaging subsequently. It was shown that N-CQDs can bind to the chromosomes, and N-CQDs reflected green light better than DAPI under the FITC filter, a potential advantage of using N-CQDs over DAPI in chromosome imaging.

In this study, we created a series of N, S, and P-doped and co-doped carbon catalysts using a single graphene nanoribbon (GNR) matrix and thoroughly evaluated the impact of doping on ORR activity and selectivity in acidic, neutral, and alkaline conditions. The results obtained showed no significant changes in the GNR structure after the doping process, though changes were observed in the surface chemistry in view of the heteroatom insertion and oxygen depletion. Of all the dopants investigated, nitrogen (mainly in the form of pyrrolic-N and graphitic-N) was the most easily inserted and detected in the carbon matrix. The electrochemical analyses conducted showed that doping impacted the performance of the catalyst in ORR through changes in the chemical composition of the catalyst, as well as in the double-layer capacitance and electrochemically accessible surface area. In terms of selectivity, GNR doped with phosphorus and sulfur favored the 2e- ORR pathway, while nitrogen favored the 4e- ORR pathway. These findings can provide useful insights into the design of more efficient and versatile catalytic materials for ORR in different electrolyte solutions, based on functionalized carbon.

This work is devoted to the study of active and stable nickel catalysts for methane dry reforming based on Pr-doped ceria-zirconia obtained by solvothermal continuous method. The studies of physicochemical and catalytic properties of the 5%Ni\Ce0.75Zr0.25-xPrxO2 series showed that Pr introduction leads to an increase in the amount of highly reactive oxygen of the oxide lattice. Praseodymium-based catalysts showed significantly higher reactant conversions. In addition to the nature of support, the method of nickel introduction was also studied - Ni was added both by impregnation and one-pot with mixed oxide preparation. The method of Ni addition was shown to have significant effect on the morphology of the supported active component and, respectively, on the catalytic activity. The 5%Ni/Ce0.75Zr0.15Pr0.1O2 catalyst prepared by one-pot method showed stable operation in the MDR reaction for 30 hours at CO2 and CH4 conversions of ~40% and an H2 yield of ~18% (Т=700°С, τ=10ms).

In this study, a new method for synthesizing Au-NaYF4:Yb3+/Er3+-DSPE-PEG2K nanocomposites was introduced. Using a hydrothermal method, the synthesized Yb3+- and Er3+-codoped NaYF4 upconversion luminescent materials and Au nanoparticles were doped into upconversion nanomaterials and modified with DSPE-PEG2k up-conversion nanomaterials. This material is known as Ag-UCNPs-DSPE-PEG2k, it improves both the luminous intensity because of the doped Au nanoparticles and has low cytotoxicity because of the DSPE-PEG2k modified. Exciting UCNPs with a wavelength of 980nm near-infrared light will emit light with a wavelength of 520nm to further excite gold nanoparticles to convert light energy into heat. Successful synthesized gold nanoparticles was confirmed using transmission electron microscopy (TEM). The morphology of UCNPs was observed using scanning electron microscopy (SEM), and the mapping confirmed the successful doping of Au nanoparticles. Fluorescence spectra were used to compare changes in luminescence intensity before and after doping Au nanoparticles. The cytotoxicity of Au-UCNPs-DSPE-PEG2K was tested via the cell counting kit-8 (CCK-8) method, and its imaging ability was characterized using the Magnetic Resonance Imaging (MRI) and Computed Tomography (CT) method.

In the present work, doped ZnO (ZnO:Al) thin film has been grown on Silicon (Si) substrate by DC sputtering. The obtained thickness of the film is 230 ± 5 nm. The films were subjected to swift heavy ion (SHI) irradiation 120 MeV, Ag⁹⁺ with different fluences ranging from 3 × 10¹¹ to 3 × 10¹³ ions/cm². To study the impact of SHI, both pristine and irradiated samples were characterized to obtain the structural, surface morphological and electrical properties using X-ray diffractometry (XRD), atomic force microscopy (AFM) and hall effect measurement system respectively. From XRD results it is observed that there is change in crystallinity of the film with increase in irradiation fluence. The surface morphological studies through AFM shows the increase in surface roughness with increase in fluence. A significant change is also observed in electrical parameters viz conductivity, mobility and carrier concentration. Conductivity, mobility and carrier concentration decreases with increasing fluence.

The enormous potential of renewable bioresources is expected to play a key role in the development of the EU’s sustainable circular economy. In this context, inexhaustible, biodegradable, non-toxic and carbon-neutral forest-origin resources are very attractive for the development of novel sustainable products. The main structural component of wood is cellulose, which, in turn, is the feedstock of nanocellulose, one of the most explored nanomaterials. Different applications of nanocellulose have been proposed, including packaging, functional coatings, insulating materials, nanocomposite fields among others. However, the intrinsic flammability of nanocellulose restricts its use in some industries where fire risk is a concern. This paper overviews the most recent studies of the fire resistance of nanocellulose-based materials, focusing on thin films, coatings and aerogels. Along with effectiveness, increased attention to sustainable approaches is considered in developing novel fire-resistant coatings. The great potential of bio-based fire-resistant materials, combined with conventional non-halogenated fire retardants FRs, has been established. The formulation methods, types of fire retardants and their action modes, and methods used for analysing fire retardancy are discussed in the frame of this overview.

Rising consumer demand for more safety, healthy and fresh-like food has given new concepts for food packaging. Besides, the growing concern with environmental issues has increased the search for materials from non-petroleum sources and biodegradable ones. Thus, active films based on biopolymers loaded with natural active compounds have potential to be used as food packaging. However, there are a lot of lipophilic active compounds that are a problem to incorporate in hydrophilic matrices, such as polysaccharides and proteins. One way to overcome these challenges is adding these compounds encapsulated in O/W emulsions. The incorporation of emulsion in biopolymeric matrix has influence in the film properties, such as mechanical, barrier, optical, among other. In this way, this review aims to point out the main characteristics of the emulsions systems encapsulating active compounds and its influence in the film properties and to present and discus critically the recent advances in the area.

Magnetron sputtering was used for producing Titanium Vanadium Nitride (TiVN) coatings on a variety of substrates. In this research, we investigate how changing the sputtering power and nitrogen: argon (N2:Ar) gas ratio affects the structural and tribological properties of TiVN coatings. Scanning Electron Microscope (SEM) technique was used to examine TiVN coating surface morphology. Both variants showed a gradual increase in the intensity of the TiVN coating's (111) and (222) peaks. TiVN coating's tribological properties were examined using a pin-on-disc tribometer with varying loads, speeds, and sliding distances. The wear rates of TiVN-coated brass pins were in the range of 2.5×10-4 to 9.14×10-4 mm3/Nm depending on load, sliding distance, and gas ratio variation, when compared to the wear rates of TiVN-coated brass pins deposited at various power, which ranged from 1.76×10-3 to 5.87×10-3 mm3/Nm.

Neuromorphic computing, reconfigurable optical metamaterials operational over a wide spectral range, holographic and nonvolatile displays of extremely high resolution, integrated smart photonics and many other applications need phase-change materials (PCMs) of the next generation with better energy efficiency, wider temperature and spectral range for reliable operation compared to current flagship PCMs as Ge2Sb2Te5 or doped Sb2Te. Gallium tellurides are promising candidates to achieve the necessary requirements because of higher melting and crystallization temperatures, combined with a low switching power and fast switching rate. At the same time, Ga2Te3 and non-stoichiometric alloys appear to be atypical PCMs, characterized by regular tetrahedral structure and the absence of metavalent bonding. The sp3 gallium hybridization in cubic and amorphous Ga2Te3 is also different from conventional p-bonding in flagship PCMs, raising a question of the phase-change mechanism. Besides, gallium tellurides exhibit a number of unexpected and highly unusual phenomena as nanotectonic compression or viscosity anomaly just above melting. Using high-energy X-ray diffraction, supported by first-principles simulations, we will unravel the atomic structure of amorphous Ga2Te5 PLD films, compare it with the crystal structure of tetragonal gallium pentatelluride, and investigate electrical, optical and thermal properties of these two materials to estimate their potential for memory applications as well as for other fields.

Highly transparent thin films with the chemical formula BaSrMgWO6 were deposited by spin coating using a solution of nitrates of Ba, Sr and Mg and ammonium paratungstate in dimethylformamide with a ratio Ba:Sr:Mg;W=1:1:1:1. XRD, SEM, EDX and XPS investigations evidenced that an annealing at 800 ºC for 1h leaves the structure amorphous with a precipitate on the surface and that a supplementary annealing at 850 ºC for 45 min forms a nanocrystalline structure and dissolves a part of precipitates. It was evidenced a textured double perovskite cubic structure (61.9%) decorated with tetragonal and cubic impurity phases (12.7 %) like BaO2, SrO2 and MgO and an under-stoichiometric phase (24.4%) with the chemical formula Ba2-(x+y) SrxMgyWO5. From transmittance measurements the values of optical band gap were estimated for the amorphous (Eg= 5.15) and nanocrystalline (Eg=4.58 eV) phases. The presence of a lattice disorder was indicated by the high values of Urbach and weak absorption tail energies A decrease in their values was observed and attributed to the crystallization process and cation redistribution.

This work is devoted to consideration and analysis of the application of molecular dynamics simulation (MDS) methods to the study of nanosized polymer polyvinylidene fluoride (PVDF) thin ferroelectric films (two-dimensional ferroelectrics) and their composites with graphene layers: 1) to study and calculations of the polarization switching time depending on the electric field and PVDF film thickness; 2) to study and calculations of the polarization switching time depending changes of the PVDF on PVDF-TrFE film; 3) to study the polarization switching time in PVDF under influence of graphene layers. All calculations at each MDS step were carried out using quantum semi-empirical methods PM3. A comparison and analysis of the results of these calculations and the kinetics of polarization switching within the framework of the Landau-Ginzburg-Devonshire theory for homogeneous switching in ferroelectric polymer films is carried out. The study of the composite heterostructures of the “graphene-PVDF” type and calculations of their polarization switching times were presented too. It is shown that replacing PVDF with PVDF-TrFE significantly changes the polarization switching times in these thin polymer films, and that introducing various graphene layers into the PVDF layered structure leads to both an increase and a decrease in the polarization switching time. Here everything also depends on the position and displacement of the ferroelectric coercive field depending on the system damping parameters.

Concern over potential antimony mediated toxicity from mining and smelting activities has instigated novel concepts toward removing aqueous antimony ions. The iron based adsorbent Fe3O4/HCO was found to be efficient for treating antimony-containing wastewater However, ineffective methodology for preparation limited its effective adsorption capacity and thus wider application. In this study, a new type of HCO-doped-(Fe3O4)x adsorbent was prepared by co-precipitation method for doping Fe3O4 into HCO sludge (HCO), thereby improving adsorption performance for Sb(III) and Sb(V) ions, with the maximum adsorbing capacity being 44.46 mg/g and 47.91 mg/g, respectively. According to the results of BET, SEM-EDS, XRD and XPS, it were confirmed that the FeOOH and X≡Fe-OH were formed during the preparation process, bring about the increased the surface area, thus resulting in further increase of surface area, hydroxyl groups and the net negative ionic charge. Moreover, the adsorption kinetics followed the pseudo-second-order kinetic model which indicated that adsorption process of Sb(III)/Sb(V) by HCO-doped-(Fe3O4)x adsorbent was controlled by chemical reaction. The main adsorption mechanism is that antimony ion and amorphous iron oxide X≡Fe-OH undergo coordination exchange reaction and complexation reaction with CeO2 or Ce2O3. Furthermore, HCO-doped-(Fe3O4)x could adapt to wide pH and had stable adsorption ability after regeneration. The good adsorption performance of HCO-doped-(Fe3O4)x makes it a potential applications of adsorbent for removal of antimony.

The phase composition design principle is introduced to obtain balanced properties of ionic conductivity and thermo-tolerant for zirconia solid electrolytes used in solid oxide fuel cells (SOFCs). The zirconia ceramic solid electrolytes are fabricated by two-step free sintering. With increasing Y/Mg ionic ratio from 1.78:1 to 1.88:1, the content of monoclinic phase fluctuates little (±3%). The ionic conductivity, including the total electrical resistance; grain electrical resistance and grain boundary electrical resistance at 1223K, are all gradually declining with the increasing of Y/Mg ionic ratio. Furthermore, the enrichment of Mg ion in grain boundary acts as a disincentive to grain boundary ionic conductivity. In addition, the maximum total equivalent conductivity at 1223K in this study reaches to 0.143 Scm-1 which can compare with that of certain YSZ. It will be beneficial to SOFCs application profited from increasing ionic conductivity of ceramic solid electrolytes.

Ion beam-assisted deposition (IBAD) has been proposed as a promising texturing technology that uses film epitaxy method to obtain biaxial texture on a non-textured metal or compound substrate. Magnesium oxide (MgO) is the most well explored texturing material. In order to obtain the optimal biaxial texture, the actual thickness of the IBAD-MgO film must be controlled within 12 nm. Due to the bombardment of ion beams, IBAD-MgO has large lattice deformation, poor texture and many defects in the films. In this work, an additional homogeneous epitaxy MgO (epi-MgO) layer has been deposited on the IBAD-MgO layer by electron-beam evaporation. The biaxial texture can be optimized by the deposition of additional epi-MgO layer. The effects of growth temperature, film thickness, deposition rate and oxygen flux on the texture and morphology of the epi-MgO film were systematically studied. After the research of epi-MgO process, the best full width at half maximum (FWHM) values were 2.2 for the out-of-plane texture and 4.8° for the in-plane texture, respectively. Subsequently, the LaMnO3 cap layer and YBa2Cu3O7-x (YBCO) functional layer was deposited on the epi-MgO layer to test the quality of MgO layer. Finally, the critical current density of YBCO films is 6MA/cm2 (77K, 500nm, self-field), indicating that this research provides a high-quality MgO substrate for the YBCO layer.

Optical parametric amplification (OPA) represents a powerful solution to achieve broadband amplification in wavelength ranges beyond the scope of conventional gain media, for generating high-power optical pulses, optical microcombs, entangled photon pairs and a wide range of other applications. Here, we demonstrate optical parametric amplifiers based on silicon nitride (Si₃N₄) waveguides integrated with two-dimensional (2D) layered graphene oxide (GO) films. We achieve precise control over the thickness, length, and position of the GO films using a transfer-free, layer-by-layer coating method combined with accurate window opening in the chip cladding using photolithography. Detailed OPA measurements with a pulsed pump for the fabricated devices with different GO film thicknesses and lengths show a maximum parametric gain of ~24.0 dB, representing a ~12.2 dB improvement relative to the device without GO. We perform a theoretical analysis of the device performance, achieving good agreement with experiment and showing that there is substantial room for further improvement. This work demonstrates a new way of achieving high photonic integrated OPA performance by incorporating 2D materials.

UV induced photoluminescence of organosilica films with ethylene and benzene bridging groups in their matrix and terminal methyl groups on the pore wall surface is studied to reveal optically active defects and understand their origin and nature. Careful selection of the film’s precursors and conditions of deposition and curing, analysis of chemical and structural properties led to the conclusion that luminescence sources are not associated with the presence of oxygen-deficient centers, as in the case in pure SiO2. It is shown that the sources of luminescence are the carbon-containing components that are part of the low-k-matrix, as well as the carbon residues formed upon removal of the template and UV induced destruction of organosilica samples. A good correlation between the energy of the photoluminescence peaks and the chemical composition is observed. This correlation is confirmed by the results obtained by the Density Functional theory. The photoluminescence intensity increases with porosity and internal surface area. The spectra become more complicated after annealing at 400 °C, although Fourier transform infrared spectroscopy does not show these changes. The appearance of additional bands is associated with compaction of low-k matrix and segregation of template residues on the surface of the pore wall.

The current pandemic is urgently demanding to discover alternative materials capable of inactivate the severe acute respiratory syndrome coronavirus 2 (SARS-CoV-2) that causes the coronavirus 2019 (COVID-19) disease. Calcium alginate is a crosslinked hydrophilic biopolymer with an immense range of biomedical applications due to its excellent chemical, physical and biological properties. In this study, the cytotoxicity and antiviral activity of calcium alginate in the form of films were studied. The results showed that these films are biocompatible in human keratinocytes and are capable of inactivating enveloped viruses such as bacteriophage phi 6 with a 1.43-log reduction (94.92% viral inactivation) and SARS-CoV-2 Delta variant with a 1.64-log reduction (96.94% viral inactivation) in virus titers. The antiviral activity of these calcium alginate films can be attributed to its negative charge density that may bind to viral envelopes inactivating membrane receptors.

Amorphous silicon (α-Si) film present an inexpensive and promising material for optoelectronic and nanophotonic applications. Its basic optical and optoelectronic properties are known to be improved via phase transition from amorphous to polycrystalline phase. Infrared femtosecond laser radiation can be considered as a promising nondestructive and facile way to drive uniform in-depth and lateral crystallization of α-Si films that are typically opaque in UV-visible spectral range. However, so far only a few studies reported on utilization of near-IR radiation for laser-induced crystallization of α-Si providing no information regarding optical properties of the resultant polycrystalline Si films. The present work demonstrates efficient and gentle single-pass crystallization of α-Si films induced by their direct irradiation with near-IR femtosecond laser pulses coming at sub-MHz repetition rate. Comprehensive analysis of morphology and composition of laser-annealed films by atomic-force microscopy, optical, micro-Raman and energy-dispersive X-ray spectroscopy, as well as numerical modeling of optical spectra, confirmed efficient crystallization of α-Si and high-quality of the obtained films. Moreover, we highlight localized laser-driven crystallization of α-Si as a promising way for optical information encryption, anti-counterfeiting and fabrication of micro-optical elements.