In this study, a novel binary nanocomposite system based on TiO₂-SiO₂ was functionalized with trimethylolpropane triacrylate (TMPTA) and characterized by XPS and XRD. Results revealed that TiO₂-SiO₂ nanoparticles were covalently functionalized. Functionalized nanoparticles at low concentrations (0.1 wt% and 0.5 wt%) were dispersed in acrylic acid acting as a polymer matrix. Nanocomposite coatings analysis demonstrate to achieve superhydrophilic properties as well as very good optical characteristics. Water contact angle characterization showed the functionalization effect by achieving a superhydrophilic behavior with a contact angle less than 5°. UV-Vis measurements demonstrated high optical transmittance above 95% for the coatings. Based on the obtained results a mechanism describing the chemical interactions of the constituents responsible for the synergy in the nanocomposite as well as the morphological play role in the behavior are presented.

Renewable nanocellulose materials received increased attention owing to their small dimensions, high specific surface area, high mechanical characteristics, biocompatibility, and compostability. Nanocellulose coatings are among many interesting applications of these materials to functionalize different by composition and structure surfaces, including plastics, polymer coatings, and textiles with broader applications from food packaging to smart textiles. Variations in porosity and thickness of nanocellulose coatings are used to adjust a load of functional molecules and particles into the coatings, their permeability, and filtration properties. Mechanical stability of nanocellulose coatings in a wet and dry state are critical characteristics for many applications. In this work, nanofibrillated and nanocrystalline cellulose coatings deposited on the surface of polymer films and textiles made of cellulose, polyester, and nylon are studied using atomic force microscopy, ellipsometry, and T-peel adhesion tests. Methods to improve coatings adhesion and stability using physical and chemical cross-linking with added polymers and polycarboxylic acids are analyzed in this study. The paper reports on the effect of the substrate structure and ability of nanocellulose particles to intercalate into the substrate on the coating adhesion.

Deformation behavior of the composite "hen's eggshell - polymer plomb" under bending is examined. Polymer coating does not change the type of behavior of the composite based on eggshell that continues to be brittle despite the mechanical characteristics of the composite could vary in wide limits for brittle structure. Joining "hen's eggshell – polymer plomb" never crack under loading and, hence, it exhibits the high cohesion strength under stresses applied in these experiments. It seems that the composite "hen's eggshell - polymer plomb" could apply as the substitution of the composite "tooth enamel - polymer plomb" under elaboration of novel restorative materials for dentistry, namely, for estimation of their mechanical properties including cohesive strength.

Many bio-applicable materials, medical devices, and prosthetics combine both polymer and metal components to benefit from their complementary properties. This goal is normally achieved by their mechanical bonding or casting only. Here, we report an alternative easy method for the chemical grafting of a polymer on the surfaces of a metal or metal alloys using alkoxy amine salt as a coupling agent. The surface morphology of the created composites was studied by various microscopy methods, and their surface area and porosity were determined by adsorption/desorption nitrogen isotherms. The surface chemical composition was also examined by various spectroscopy techniques and electrokinetic analysis. Elements distribution on the surface was determined and successful bonding of the metal/alloys on one side with the polymer on the other one was confirmed by alkoxy amine. The composites show significantly increased wettability, reliable chemical stability of the bonding, excellent bacterial anti-adhesive properties and functionality, i.e. the characteristics promising for their application in biomedical field.

To combat infections on biomedical devices, antimicrobial coatings have attracted considerable attention, including coatings comprising naturally occurring antimicrobial peptides (AMPs). In this study the aim was to explore performance upon extended challenge by bacteria growing in media above samples. The AMPs LL37, Magainin 2, and Parasin 1 were covalently grafted onto a plasma polymer platform, which enables application of this multilayer coating strategy to a wide range of biomaterials. Detailed surface analyses were performed to verify the intended outcomes of the coating sequence. Samples were challenged by incubation in bacterial growth media for 5 and 20 hrs. Compared with the control plasma polymer surface, all three grafted AMP coatings showed considerable reductions in bacterial colonization even at the high bacterial challenge of initial seeding at 1x107 CFU, but there were increasing numbers of dead bacteria attached to the surface. All three grafted AMP coatings were found to be non-toxic to primary fibroblasts. These coatings thus could be useful to produce antibacterial surface coatings for biomaterials, though possible consequences arising from the presence of dead bacteria need to be studied further, and compared to non-fouling coatings that avoid attached dead bacteria.

In this study organic bulk heterojunction (BHJ) solar cell along with the spiro OMeTAD as a hole transport layer (HTL) and the PDINO as an electron transport layer (ETL) was simulated through the Solar Capacitance Simulator, one dimensional (SCAPS-1D) software to examine the performance of this type of polymer thin film organic solar cells. As an active layer the blend of polymer donor PBDB-T and non-fullerene acceptor ITIC-OE was used. Numerical simulation was performed by varying the thickness of HTL and active layer. Firstly, the HTL layer thickness was optimized to 50 nm, after that the active layer thickness varied up to 80 nm. These results of simulation demonstrated that the HTL thickness has rather little impact on efficiency while in the case of active layer thickness improves efficiency significantly. The temperature effect on the performance of solar cells was considered, by the simulation performed for temperature from 300 K up to 400 K and the efficiency of solar cell decreases with increasing temperature. Generally, polymer films usually are full of traps and defects, the density of defects (Nt) value was also introduced to the simulation, and it was confirmed that with the increasing of defect density (Nt), the efficiency of solar cell decreases. After thickness, temperature and defect density optimization, the reflection coating was also applied on it. It turned out that by introducing the reflection coating on the back side of solar cell, the efficiency increases by 2.5 %. Additionally, the positive effect of HTL and ETL doping on efficiency of this type of solar cells was demonstrated.

Synthesis of styrene butadiene hybrid latex was performed via emulsion polymerization technique using various amount of laponite clay as filler. Laponite clay was modified with cationic surfactant methyl triphenylphosphonium bromide (MTPB) with ion exchange technique prior to polymerization process. The main objective of the modification is to render the surface of the clay layers to more organophilic. Emulsion polymerization was performed under semi batch process using 2 L laboratory stainless steel reactor with temperature 85°C to 90°C for 8 hours. Polymer hybrid styrene butadiene latex was characterized for its physical and chemical properties with standard ASTM Methods. Characterization of its binding and printing properties were carried out with standard testing method (TAPPI Methods) using single coating formulation on 80 gsm woodfree paper. Polymer hybrid latex based on styrene and butadiene monomers with laponite clay enhanced binding and printing properties of coated paper, addition of laponite clay to 6.0 wt % increased the binding resistance of the coated paper two times higher than pure latex. Reducing binder level become possible for cost saving.

Laser direct writing allows for the fabrication of complex structures, which is particularly advantageous in micro-optic applications. However, the increasing demand for optics quality requires the lowest optical power loss, which can occur from unwanted reflections. This research demonstrates the possibility of forming an anti-reflective coating on hybrid-polymer micro-lenses fabricated by employing laser direct writing (LDW), without changing their geometry. Such coating deposited by atomic layer deposition (ALD) decreased the reflection from 3.3 % to 0.1 % at the wavelength of 633 nm for one surface of SZ2080™.

In this review, several cost-effective thin-film coating methods which include dip-coating, spin-coating, spray-coating, blade-coating, and roll-coating are presented. Each method has its set of advantages and disadvantages depending on the type of application. Not all of them are appropriate for large-scale production due to their certain limitations. That is why the coating method should be selected based on the type and size of substrate including the resolution of the required thin-films. The sol-gel method offers several benefits, such as simplicity in fabrication, excellent film uniformity, the capacity to cover surfaces of any size and over vast areas, and a low processing temperature. Nevertheless, these coating methods are somewhat economical and well managed in low-budget laboratories. Moreover, the produced thin-films are homogeneous and have low-surface roughness. Furthermore, some other thin-film deposition methods such as physical vapor deposition (PVD) and chemical vapor deposition (CVD) are also discussed. Since CVD is not restricted to line-of-sight deposition, a characteristic shared by sputtering, evaporation, and other PVD processes, many manufacturing methods favor it. However, these techniques require sophisticated equipment and cleanroom facility. We aim to provide the pros and cons of thin-film coating methods and let the readers decide the suitable technique for their specific application.

A new three-dimensional numerical model of a polymer electrolyte fuel cell (PEFC) with a single straight channel has been developed to primarily investigate the important impact of the double-sided microporous layer (MPL) coating on the overall performance of the fuel cell and the distribution of the current and the oxygen concentration within the cathode gas diffusion layers (GDLs). Realistic experimentally estimated interfacial contact resistance values between the gas diffusion layer and each of the bipolar plates and the catalyst layer values were incorporated into the model, and parametric studies were performed. The results showed that the double-sided MPL coating could significantly improve the fuel cell performance by up to 30%. Also, it was shown that the neglect of the contact resistance between the MPL and the catalyst layer could overestimate the fuel cell performance by up to 6%. In addition, the results showed that the fuel cell performance and the distribution of the current and oxygen are more sensitive to the porosity of the MPL facing the bipolar plate than the porosity of the MPL facing the catalyst layer. All the above results are presented and critically discussed in detail.

The application of distributed fiber optic strain and temperature measurement can be utilized to address a multitude of measurement tasks across a diverse range of fields, particularly in the context of structural health monitoring in the domains of building construction, civil engineering, and special foundation engineering. However, a comprehensive understanding of the influences on the measurement method and the sensors is essential to prevent misinterpretations or measurement deviations. In this context, this study investigated the effects of moisture exposure, including various salt solutions and a high pH value, on a distributed strain measurement using Rayleigh backscattering. Three fiber optic sensors with different coating materials and one uncoated fiber were exposed to five different solutions for 24 hours. The study revealed significant discrepancies in deformation between the three coating types depending on the surrounding solution. Furthermore, in contrast to the prevailing literature, which predominantly describes swelling effects, a negative deformation was observed in a magnesium chloride solution. The findings of this study indicate that corresponding effects can impact the precision of measurement, potentially leading to misinterpretations. Conversely, these effects could be used to conduct large-scale monitoring of chemical components using distributed fiber optic sensing.

The kinetic analysis of octogen coating with a polyurethane base containing hydroxyl-terminated polybutadi-ene (HTPB) was investigated using infrared spectroscopy. The coating process involved a solvent method, where octogen and liquid polyurethane were mixed, the solvent was evaporated, and curing took place at an elevated temperature. The ratio of HTPB to diisocyanate was equimolar. Initially, the curing process occurred in the solvent system, followed by further curing in the bulk system. The kinetic analysis was performed using a modified diffusion-autocatalytic model, which includes non-catalytic, autocatalytic, and diffusion compo-nents. This model was compared with others during the bulk reaction and proved to be effective in correcting errors, particularly in the gel time region. Thermodynamic parameters were evaluated using the Arrhenius and Eyring equations. The reaction rate was initially controlled by chemical reactivity, but after the gel time, diffusion became the controlling factor. In the HTPB-TDI system, both the non-catalytic and autocatalytic parts decreased with increasing temperature, while diffusivity increased. It is worth noting that diffusivity is temperature-dependent. Different diisocyanates, namely toluene diisocyanate (TDI), isophorone diisocyanate (IPDI), and hexamethylene diisocyanate (HMDI), were studied, revealing that HMDI exhibited higher reactivi-ty than TDI and IPDI. The catalyst effect on reaction rate HTPB-TDI system is investigated. Catalysts adding (0.1%) to HTPB-TDI system is really decrease their activation energy by efectivity DBTL>FeAA>TPB. Catalyst not change their diffusivity.

Positively charged polyelectrolytes hold significant potential as materials for creating antibacterial coatings. Water-soluble macromolecules can be easily deposited onto a treated surface through various techniques, forming a film that provides antimicrobial properties to the surface through electrostatic interactions with bacterial membranes. The structural and molecular weight characteristics of the polymers play a crucial role in the physical and mechanical properties of the coatings. In this study, we investigated the properties of branched polyethyleneimine (PEI) and linear polydiallyldimethylammonium chloride (PDADMAC) coatings with different molecular weights of polymer samples to determine their suitability as stable coatings with antibacterial properties against foodborne bacteria. Using thermogravimetric analysis, dynamometry, and dynamic light scattering, we examined the physicochemical and mechanical properties of the macromolecules in water solutions and in coatings. Microbiological study was conducted to analyze the biocidal activity of the polycations in solutions and on the surface of coatings. Our findings showed that the moisture saturation of the polycationic coatings did not significantly depend on the chemical nature of charged groups or the molecular weight or architecture of macromolecules. Moreover, biocidal activity was not found to depend on the molecular weights of PEI and PDADMAC. However, the lowering of the molecular weight of polymers resulted in the loss of cohesive forces in the coatings and to dramatically loss of the stability towards wash-off with water. The diffusion coefficient (D0) of macromolecules was identified as a key parameter for the wash-off mechanism. Films formed by molecules with D0 below 1×10-7 cm2/s demonstrated high resistance to wash-off procedures. We demonstrated that PEI and PDADMAC samples with high molecular weights showed high antimicrobial activity towards L. monocytogenes. Our results highlight the importance of macromolecule characteristics in the development of new biocidal coatings based on polycations.

This study explores the impact of carbon fiber length and content on the rheological properties and performance of coatings used in lost foam casting. The investigation encompassed fiber lengths of 1 mm, 3 mm, and 6 mm, and fiber contents of 0.2%, 0.5%, and 0.8%. The effects on coating viscosity, shear stress, coating weight, and surface morphology were meticulously evaluated. The results demonstrate that incorporating carbon fibers significantly enhances coating viscosity and shear stress compared to fiber-free coatings, with more pronounced effects observed at higher fiber contents and longer fiber lengths. Nevertheless, excessive fiber content and length can lead to agglomeration, negatively impacting coating uniformity. Optimal fiber length and content were identified, striking a balance between improved rheological properties and coating performance. These findings provide critical insights for the development and industrial application of high-performance coatings in lost foam casting.

This review provides a systematic analysis of the literature data on the electrodeposition of composite coatings using plating baths based on a new generation of room-temperature ionic liquids, known as deep eutectic solvents (DESs). Such systems offer several advantages over traditionally used aqueous electrolytes and organic solvent-based electrolytes. The colloidal-chemical properties of suspension and colloidal electrolytes for composite deposition are thoroughly examined. New theories describing the kinetics of co-deposition of composite layers are characterized. The kinetics and mechanism of electrochemical deposition processes of composite coatings with metallic matrices are discussed. Case studies regarding the electrodeposition of composite coatings based on electrodeposited copper, silver, zinc, tin, nickel, cobalt, and chromium from DES-assisted electroplating baths are described and systematized. The main prospective directions for further research in the discussed scientific area are highlighted.

Guava is a vital fruit worldwide, especially in Pakistan, and due to its nutritional value famous in each age group. Due to a very short shelf life, the marketing and export of this fruit faced severe constraints. Therefore, in the current study, edible coating of chitosan (0, 0.5, 1.0, 1.5, and 2.0%) was evaluated on postharvest shelf life when guava fruits were stored (room temperature and 4 °C temperatures) for 12 days. The chitosan treated coating fruits have shown reduced total sugars and malondialdehyde levels compared to untreated control samples. However, a significant difference (p ≤ 0.05) in total sugar and malondialdehyde levels exists between samples stored in m compared to refrigerated temperature (4 °C). The chitosan-coated samples have shown a greater amount of vitamin C, quercetin, rutin, and total phenolic contents than control samples. However, these nutritional parameters' levels were significantly different (p ≤ 0.05) in samples stored at room than samples stored at refrigerated temperature. However, the levels of crude fiber, potassium, and sodium were found statistically nonsignificant (p ≥0.05) in control versus chitosan treated coating treatments. The findings have documented that the coatings of 1.5 and 2.0% were most effective for extension in shelf life and maintaining the nutritional attributes of guava fruit.

In the present work, three different atmospheric plasma sprayed (APS) alumina coatings were fabricated using three fused and crushed alumina powders of different particle size fine, medium and coarse. The influence of the particle size on thermal properties and micro-structural features of the produced coating were investigated by thermal insulation test and detailed image analysis technique, respectively. The analyzed micro-structural features include the total porosity, pore size (fine, medium, and large) and cracks. All types of cracks were considered in calculations as voids and were evaluated according to their sizes as pores. All spray parameters except the particle size were fixed throughout the spraying process. The results revealed that the fine starting powder has produced the densest coating with the lowest total porosity and that the total porosity increases with an increasing particle size. This was expected as powders of smaller particle size will reach a higher in-flight temperature and velocity than powders of bigger particle sizes as long as the same spray parameters are applied. However, a detailed image analysis investigation on the three produced coatings showed that the fraction of fine pores and cracks versus the total porosity is substantially higher in coatings produced by using fine starting powders than those produced using medium and coarse powders. In this work, a connection between the thermal insulation and the porosity fraction, which includes fine pores and cracks, was revealed.

Several coatings configurations of combined aluminizing and diffusion layered aluminide on 316 steel were produced and characterized. These coatings, typically employed as thermal barrier coating (TBC), can also be effective as vibration reduction elements at intermediate and high temperatures. This preliminary work has been focused on the microstructural design and processing effects of the coatings. The damping of the produced specimens was measured up to 450°C and compared with that of the steel substrate. The most performing coatings contain an Al-Si layer and exhibit a steep damping increase above 200 °C, reasonably due to dislocation movements by plastic straining of soft alloy layer and to the interface sliding between layers with different elastic moduli.

Abstract: An Al-Co-Y diffusion coating was prepared on a TiAl alloy by pack cementation process at a low temperature range of 650-720 ℃. The influence of different activators and co-deposition temperatures on the coating’s microstructure and formation process, and high temperature oxida-tion performance was studied. The results showed that NaF was a more suitable activator for preparing the Al-Co-Y diffusion coating on TiAl alloy compared to NH4Cl and AlCl3. A more compact coating structure can be obtained when deposition was performed at 680 ℃ using NaF as the activator. The coating was mainly composed of a TiAl3 outer layer, a TiAl2 inner layer, and a thin Al-rich TiAl inter-diffusion layer. The growth of the coating exhibited a positive linear correlation between coating thickness increase and the square root of deposition time. The high-temperature oxidation tests showed that a dense scale mainly composed of Al2O3 and a small amount of TiO2 formed on the coating after oxidation at 950 ℃ for 100 h. The scale possessed excellent high-temperature oxidation resistance, with a parabolic rate constant of the oxidation weight gain approximately 4.9×10-3 mg2/cm4 h, which is lower than that of the TiAl substrate by about three orders of magnitude, and lower than that of the pure Al diffusion coating more than one order of magnitude.

Slot-die coatings are advantageous when used for coating large-area flexible devices; in particular, the coating width can be controlled, and simultaneous multi-layer coatings can be processed. Till date, the effects of ink widening and coating gap on the coating thickness have only been considered in a few studies. To this end, we developed two mathematical models to accurately estimate the coating width and thickness considering these two effects. We used root mean square deviation (RMSD) to experimentally verify the developed method. The coating width was seen to increase and the coating thickness was seen to decrease when the coating gap was increased. Experimental results showed that the estimation performances of the coating width and thickness models were as high as 98.46 % and 95.8 %, respectively. We believe that the developed models can be useful for determining the coating conditions according to the ink properties to coat a functional layer with user-defined widths and thicknesses in both lab- and industrial-scale roll-to-roll slot-die coating processes.

In this study, the efficiency of coating (alginate and carrageenan) and osmotic dehydration pre-treatment (NaCl and sucrose) on decreasing oil uptake of potato strips was assessed. It was examined how various pre-treatments affected the sample’s texture, morphology, color and density properties as well as their moisture content and effective moisture diffusion coefficient (Deff). Results showed that NaCl osmotic dehydration pre-treatment and sucrose solution decreased oil uptake by 30.76% and 41.75%. This is attributed to moisture removal increasing caused by improving dielectric properties. Osmotic dehydration and coating pre-treatment frequently enhanced product shrinkage, browning index, a* and ∆E. Conversely, density, lightness, breaking force, Deff and b* decreased. In control samples, SEM revealed a severely damaged internal structure in comparison to a tissue homogenous layer produced by coating. For moisture loss and oil uptake, the coefficient of determination (R2) and root mean square error (RMSE) of eight empirical models were compared. Finally, the Dehghannya and Krokida model (moisture loss) and the Movahhed and Naghavi model (oil uptake) were found the best fit to the experimental data. Although coating pre-treatment and osmotic dehydration can be used as an alternate de-oiling approach for potato chips, the mechanism of oil uptake reduction differ.

The powdered sorbents were applied in a batch system under "static" conditions and showed a much higher adsorption capacity than the granular one. These type of sorbents are more suitable for small quantities of water with a high concentration of arsenic. The possibilities of using all the tested methods for arsenic removal have been evaluated, and a scheme of the technological process has been proposed.

The surface plasmon resonance of gold nanoparticles causes visible light absorption and scattering effects that may be used in optical coatings for eliminating blue light emission from display monitors, blocking UV light and for decorative applications. This study examines the achievement of functional properties provided by gold nanoparticles in a commercially established C60 fullerene-coated eyewear product. The gold nanoparticles used were sourced from recycling rapid lateral flow tests (LFIA), which use gold nanoparticles as test markers. After the gold`s recovery Ultrasonic Spray Pyrolysis (USP) with freeze-drying was used for the synthesis of new gold nanoparticles, to be used in optical coatings. The gold nanoparticles were examined with SEM, TEM, DLS, zeta potential, BET, and Vis-NIR for characterising their shapes and sizes, required for determination of the surface plasmon resonance effect. After applying the newly produced gold nanoparticles with fullerene C60 in a combined coating for eyewear lenses, the absorption and transmission of the lenses was determined for establishing changes in the coating functionality. The results show that enhancing the fullerene C60 coating with gold nanoparticles improves light absorption and reflectance for blue and UV light further, which may be evaluated as beneficial for the eyewear user, as the reduction of eye strain is improved due to the coating.

Photoluminescent (PL) layers and electroluminescent (EL) systems have been extensively explored for constructing flat panels, screen monitors, and lighting systems. Due to their optical properties, our group is interested in the relationship between optical properties and dielectric constant is converted due to thermal change. In this study, we prepared a zinc sulfide (ZnS) fluorescent film on barium-calcium zirconium titanate ceramics. BCZT0.85 (Ba0.85Ca0.15Zr0.1Ti0.9O3) and BCZT0.9 (Ba0.9Ca0.1Zr0.1Ti0.9O3) were prepared using the solid-state reaction method for the dielectric layer. The BCZT powders were calcined at 1200 and 1250 °C and dwell times of 2 and 4h. The phase formation and microstructure characteristics were then determined using X-ray diffraction and scanning electron microscopy, respectively. The dielectric behavior and optical properties rela-tionship was then studied to determine the composition and optimal conditions for further use as thermal detectors in electric vehicle battery packs. All BCZT powders exhibited the tetragonal phase, which was confirmed by JCPDS No. 01-079-2265. The dielectric constant increased with increasing calcining temperature or dwell time. The dielectric properties showed the BCZT0.85 ceramic sintered had the maximum dielectric constant of 15342 at calcine temperature of 1250 °C for 4h. Therefore, in this study, this condition was optimal for preparing the dielectric film. The maximum dielectric constant film is 42. The electroluminescence intensity of the samples increased in a temperature-dependent manner, with the highest EL intensity at 80 °C. Moreover, the electroluminescence intensity value was enhanced with the increase of the dielectric constant. Our results show promise for developing applications for Opto-thermal sensors.

We demonstrated a new approach to the production of three-dimensional-coated patterns using liquid route. Metallic perovskite oxides were coated onto three-dimensional (3D) microstructured substrates with different aspect ratios. The success of the method relies on the solution viscosity monitored by adding viscous liquid. The process of oxide thin films consists in three steps: preparing the precursor solution, coating the solution by spin-coating process onto three-dimensional-Si substrates and post-annealing. The chemical solution 3D-coating is conformal.

Biocidal coatings are of great interest to the healthcare system. In this work, the biocidal activity of coatings based on a complex biocide containing polymer and inorganic active antibacterial c omponents was studied. Silver oxide was distributed in a matrix of a positively charged interpolyelectrolyte complex (IPEC) of polydiallyldimethylammonium chloride (PDADMAC) and sodium polystyrene sulfonate (PSS) using ultrasonic dispersion, forming nanoparticles with an average size of 5-6 nm. The formed nanoparticles in the matrix are not subject to agglomeration and changes in morphology during storage. It was found that the inclusion of silver oxide in a positively charged IPEC allows a 4-fold increase in the effectiveness of the complex biocide against E. coli K12 in comparison with the biocidal effect of PDADMAC and IPEC. Polycation, IPEC and the IPEC/Ag2O ternary complex form coatings on the glass surface due to electrostatic adsorption. Adhesive and cohesive forces in the resulting coatings were studied on micron-scale coatings using dynamometry. It was found that the stability of the coating is determined primarily by adhesive interactions. At the macro level, it is not possible to reliably identify the role of IPEC formation on adhesion. On the other hand, the use of the optical tweezers method makes it possible to analyze macromolecules in submicron scale and to evaluate the multiple increase in adhesive forces when forming a coating from IPEC compared to coatings from PDADMAC. Thus, the application of ternary IPEC/Ag2O complexes makes it possible to obtain coatings with increased antibacterial action and improved adhesive characteristics.

According to research, we have learned that Mg and TiO2 are new types material of marine protective coatings. We found that the addition of Mg can improve the performance of Zn-Al coating passivation film, and TiO2 has excellent photocatalytic self-cleaning performance. In this paper Zn-Al pseudo alloy coating was prepared by cold spray technique, and Zn-Al-Mg-TiO2 pseudo alloy composite coating was prepared by adding Mg and nano-TiO2. The effects of Mg and TiO2 to the marine protective properties of Zn-Al coatings were studied by friction and wear test, dynamic salt water corrosion test, electrochemical test, scanning electron microscope(SEM), energy dispersive spectrometer(EDS) and super deep scene 3D microscope. The results show that the addition of Mg and nano-TiO2 not only fills the gap of the coating and improves the density of the coating, but also generates grid-like flocculent corrosion products on the surface of the coating which can gather other corrosion products to improve the density of corrosion products, reduce the friction coefficient and corrosion rate of the coating surface, effectively prevent the invasion of Cl- in solution, and improve the wear and corrosion resistance of the coating.

This paper presents a new method of preparing a coating on the Ti65 titanium alloy by a two-step procedure comprising hot-dipped aluminum and solid carburization. The effects of the carburization in the presence of NaCl deposit at 810oC have been systematically studied. In this article, the microstructure, morphology, phase composition of the coating, and the corrosion products were investigated by SEM, EDS, and X-ray diffraction. Results indicated that the corrosion resistance of hot dip aluminum/carburizing composite coating was not significantly enhanced by hot dip aluminum coating. This can be attributed to the formation of TiC and Ti3AlC after carburization, which promoted the formation of loose and unprotected TiO2 in the coating during molten salt corrosion. In addition, the oxidation of the carbon atom into CO2 /CO leaded to a high concentration of vacancy in the coating, creating channels for NaCl to penetrate the coating and accelerated the corrosion rate.

In roll-to-roll (R2R) processing, uniformity of the web is a crucial factor that can guarantee high coating quality. To understand web defects due to thermal deformation, we analyzed the effects of web unevenness on the coating quality of an yttria-stabilized zirconia (YSZ) layer, a brittle electrolyte of solid oxide fuel cells (SOFCs). We used finite element analysis to analyze the thermal and mechanical deformations at different drying temperatures. A YSZ layer was also coated using R2R slot-die coating to observe effects of web unevenness on the coating quality. It was seen that web unevenness was generated by thermal deformation due the conduction and convection heat from the dryer. Owing to varying web unevenness with time, the YSZ layer developed cracks. At higher drying temperatures, more coating defects having larger widths were generated. Results indicated that web unevenness at the coating section led to coating defects, which could damage the SOFC and decrease its yield in the R2R process. From this study, we suggest that coating defects, generated by the web unevenness owing to the convection and conduction heat, should be considered for the high-volume production of brittle electrolytes using the R2R process.

The aerospace industry has made extensive use of titanium alloy material due to its exceptional qualities, which include high strength, low weight, and resistance to corrosion. However, these qualities also pose challenges for the material's processing. This paper examines the Ti6Al4V milling endmills coating. First, an analysis is done on the solubility of Ti and Si elements. It is discovered that W and Co elements are far more soluble in Ti than Si and Zr elements, which can effectively stop element diffusion. Next, the base's composition was planned. It was discovered that when the amount of Al increased, the base's surface roughness increased while its hardness and elastic modulus decreased. The binding force between the substrate and the base was greater at 50: 50 Ti:Al ratio. TiSiN and TiSiN/ZrN functional layer properties are examined. When Zr is added to TiSiN/ZrN coating, it improves the coating's hardness and elastic modulus, increases density, and decreases surface roughness and friction coefficient when compared to TiSiN coating. Lastly, an analysis of the initial and intermediate tool wear was done using the Ti6Al4V milling experiment. It was discovered that adding Zr element could successfully extend the tool's cutting life by preventing adhesive wear.

Coating of organic molecules from the solution phase can result in directional crystal growth under certain conditions, even on a smooth isotropic surface and without the need of any kind of graphoexpitaxial preparation of the substrate. Based on reviewing the results from a variety of coating techniques and conditions, we identify the condition that the coating speed should equal the growth speed of the fastest growing crystal plane as crucial for achieving a high degree of directional crystallization.

This study reports on the development of bio-based hydrophobic coatings for packaging papers through deposition of polyhydroxybutyrate (PHB) particles in combination with nanofibrillated cellulose (NFC) and plant wax. In a first approach, PHB particles in micrometer range (PHB-MP) were prepared through a phase-separation technique providing internally nanosized structures. The particles were transferred as a coating by dip-coating filter papers in the particle suspension, followed by sizing with a carnauba wax solution. This approach allowed partial to almost full surface coverage of PHB-MP over the paper surface resulting in static water contact angles of 105° to 122° and 129° to 144° after additional wax coating. In a second approach, PHB particles with submicron sizes (PHB-SP) were synthesized by an oil-in-emulsion (o/w) solvent evaporation method, and mixed in aqueous suspensions with 0 to 7 wt% NFC. After dip-coating filter papers in PHB-SP/NFC suspensions and sizing with a carnauba wax solution, static water contact angles of 112° to 152° were obtained. The intrinsic properties of the particles were analyzed by scanning electron microscopy, thermal analysis and infrared spectroscopy, indicating higher crystallinity for PHB-SP than PHB-MP. The chemical interactions between the more amorphous PHB-MP particles and paper fibers were identified as an esterification reaction, while the morphology of the NFC fibrillar network was playing a key role as binding agent in the retention of more crystalline PHB-SP at the paper surface, hence contributing to higher hydrophobicity.

This study explores the effects of powder-to-liquid ratio on the performance characteristics of lost foam casting coatings. The investigation focuses on how variations in this ratio affect key properties including apparent viscosity, shear thinning behavior, coating weight, and surface morphology. Through a series of controlled experiments, coatings were prepared with different powder-to-liquid ratios and assessed for their physical and application properties. The results indicate that increasing the powder-to-liquid ratio raises the apparent viscosity and modifies shear thinning behavior. Notably, ratios exceeding 2.0 result in a sharp increase in viscosity that impedes coating application. The optimal powder-to-liquid ratio was determined to be between 2.0 and 2.2, where coatings demonstrated enhanced uniformity, improved particle distribution, and superior surface morphology. Coating weight increased up to a ratio of 2.2 but decreased beyond this threshold due to excessive viscosity. Both microscopic and macroscopic analyses confirmed that a ratio of 2.0 to 2.2 strikes the best balance for coating performance. These findings underscore the importance of precise powder-to-liquid ratio control to optimize the quality of lost foam casting coatings, offering valuable insights for refining coating formulations and application techniques in industrial contexts.

Bioactive surface coatings have retained the attention of researchers and physicians due to their versatility and range of applications in orthopedics, particularly in infection prevention. Antibacterial metal nanoparticles (mNPs) are a promising therapeutic, with vast application opportunities on orthopedic implants. The current research aimed to construct a polyelectrolyte multilayer on a highly porous titanium implant using alternating thin film coatings of chitosan and alginate via the layer-by-layer (LbL) self-assembly technique, along with the incorporation of silver nanoparticles (AgNPs) or titanium dioxide nanoparticles (TiO2NPs), for antibacterial and osteoconductive activity. These mNPs were characterized for their physicochemical properties using quartz crystal microgravimetry with dissipation system, nanoparticle tracking analysis, scanning electron microscopy, and atomic force microscopy. Their cytotoxicity and osteogenic differentiation capabilities were assessed by AlamarBlue and alkaline phosphatase (ALP) activity assays, respectively. The antibiofilm efficacy of the mNPs tested against Staphylococcus aureus. The LbL polyelectrolyte coating was successfully applied to the porous titanium substrate. A dose-dependent relationship between nanoparticle concentration and ALP as well as antibacterial effects was observed. TiO2NP samples were also less cytotoxic than AgNP counterparts, although similarly antimicrobial. Together, these data serve as a proof-of-concept for a novel coating approach for orthopedic implants with antimicrobial and osteoconductive properties.

A comparative study of the photocatalytic decoloration of methylene blue (MB) dissolved in water was conducted, using three semiconductor oxides: zinc oxide (ZnO), tin oxide (SnO2) and titanium dioxide (TiO2) in the form of thin films and varying their thickness ~ 100, 200, and 300 nm for each film. All the films were deposited using the cost-effective dip-coating technique, at moderate temperature processing (400 °C) with sol-gel solutions on cheap glass substrates. The structural, morphological, and compositional properties of the films were analyzed by X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM), and Raman spectroscopy, respectively. The degradation of MB was studied by varying both thickness and type of semiconductor oxides through measurements of optical absorbance of decolorated liquid by photocatalytic process. Structural analysis shows that ZnO and SnO2 films were polycrystalline with preferential growth of (002) and (110) planes respectively, whereas, an amorphous structure was observed for TiO2 films. In addition, morphological properties confirms that the surfaces of all the films are conformed with nano grains in round and irregular shapes. Based on all results reported in this work, that authors believe that the degradation efficiency of MB depends on the thickness of the film and the type of semiconductor material used as a catalyst. The highest degradation efficiencies were recorded with an exposure time of 120 min and with an initial concentration of 10 mg/L for ZnO, SnO2, and TiO2 films were: 100, 88 %, and 76 %, respectively.

In this study electrophoretic deposition (EPD) technique is used to prepare chitosan-based coatings with enhanced antibacterial activity suitable for bone implants applications. We designed, prepared and compared physic-chemical and biological properties of coatings obtained with commercial chitosan, chitosan enriched with silver nanoparticles and chitosan obtained from insects. With the aim to consider the sustainability issue, silver nanoparticles were directly prepared in the chitosan solution by laser ablation in liquid technique, avoiding the use of chemicals and limiting the production of wastes. Moreover, a sustainable source of chitosan such as Hermetia Illucens exuviae was considered. The EPD process was optimized by adjusting parameters like voltage and deposition time to achieve ideal coating thickness and adhesion. The prepared films were characterized by spectroscopic and microscopic techniques such as SEM, XRD, and FTIR. Antimicrobial tests against E. coli and S. aureus revealed that silver nanoparticles enhanced the antibacterial properties of the polymer, whereas biological evaluation using the WST8 test on MG63 human osteoblasts-like cells showed that all coatings are non-toxic. Finally, chitosan obtained from insect showed comparable properties with respect to the commercial polymer, suggesting it could replace seafood-derived chitosan in biomedical applications, whereas the Ag@chitosan composite demonstrated superior antibacterial activity without compromising its biocompatibility.

A detailed review of the scientific literature was undertaken to examine the most recent developments in plasma processing in the field of medicine. The first part of the review includes a detailed breakdown of the different types of coatings that can be applied onto medical devices using plasma, with a specific focus on antimicrobial surfaces. The developments during 2023 in plasma deposited biocompatible, drug delivery and adhesive coatings are described and specific applications in additive manufacturing are highlighted. The use of plasma and plasma activated liquids as standalone therapeutics continues to evolve and pertinent advances in this field are described. In addition, the combination of plasma medicine with conventional pharmaceutical interventions was reviewed and key emerging trends were highlighted, including the use of plasma to enhance drug delivery directly into tissue. The potential synergies between plasma medicine and chemotherapeutics for oncology and infection treatment is a growing area and recent advancements are noted. Finally, the use of plasma to control excess antibiotics and to intentionally degrade such materials in waste streams is described.

We present an investigation on the fracture of a mold, comparing it with a normal part using specific techniques, such as EDX, SEM, and AES. The EDX analysis revealed that the composition of the normal part was consistent with that of low carbon steel, mainly comprising Fe and C. In contrast, the fractured part exhibited cracks due to nonconforming nonmetallic inclusions and reticular carbides, with fractures resulting from microporosity agglomeration and cleavage fracture. The SEM and AES analyses further presented the causes of mold fracture, highlighting the mechanism by which dimples on the specimen edge contributed to the fracture. The EDX analysis confirmed that the mold experienced thermal brittleness during use. To enhance mold durability and extend its lifespan, a double-pulse electrodeposition method was employed to create a NiCo alloy coating as a replacement for the Cr layer on the metal surface. The coating exhibited a smooth and scratch-free surface. The prepared NiCo special coating significantly increased the mold yield strength by approximately 313.8%, facilitated a 13% increase in plastic deformation, and reduced fracture strain by 25%, effectively preventing mold fracture and 3improving its service life.

The cape gooseberry (Physalis peruviana L.) is an exotic tropical fruit of great national and international importance due to its nutritional, and organoleptic properties. The objective of this study was to evaluate different postharvest treatments: Coating, Vacuum Impregnation, and Immersion, on the conservation of some quality characteristics of cape gooseberry fruit. Moreover, different conditions of the selected treatment were studied. The weight loss was assessed with gravimetric analysis for fresh and treated fruits. Firmness was determined by instrumental texture. The sensory analysis was conducted using a multidimensional profile approach. Of the treatments evaluated, the lowest weight loss was recorded with the use of coating and immersion. However, the immersion process resulted in the product with the highest overall quality according to the sensory analysis and presented the most appropriate texture according to the firmness values. Finally, in the evaluation of immersion, a significant influence of the CaCl2 immersion time (p<0.05) on the firmness values of the product was found, resulting in longer times leading to less firm products. Considering 10% as a commercial standard limit for weight loss, the fruit treated under immersion and coating processes can be stored for at least 12 days. The immersion process is highlighted because it improved the sensory characteristics with respect to the control (without treatment). Thus, it process gives added value to the fruit and is presented as a promising alternative for the postharvest treatment of cape gooseberries.

Strontium (Sr) is a trace element in human body that able to promote bone formation and inhibit bone absorption. The conversion coating of strontium phosphate (Sr-P) on the surface of titanium (Ti) can improve its biological properties, and has a wide application prospect in the fields of dentistry and orthopedics. In this present study, Sr-P coatings with SrHPO4 and Sr3(PO4)2 crystals on Ti are prepared by phosphate chemical conversion (PCC) treatment. And the effect of pH on the properties of Sr-P coatings is researched. The results prove that phase composition, morphology and corrosion resistance of coated Ti are different with the pH values in PCC solution. The morphologies of conversion deposition on Ti change from plat-like to cluster-like, and then homogeneous microcrystals, as pH value changed from 2.50 to 3.25. Only discrete SrHPO4 crystals are generating on substrate at lower pH value, while relative stable Sr3(PO4)2 and SrHPO4 crystals are growing and subsequently forming an integrated coating on Ti as pH is higher than 2.50. The corrosion resistance of coated Ti improves comparing with that of bare Ti because of forming Sr-P coatings with Sr3(PO4)2 phase. In addition, it is indicated that the Sr-P coatings can improve the adhesion and differentiation of BMSCs.

In this study, Ni50Ti50 powder was coated on the surface of graphite substrate (C) by plasma spraying process using a radio frequency inductively coupled plasma reactor. The coating was carried out by using 12- and 9-kW power under Ar atmosphere. The cross-section of coating layers and the surface were examined with SEM, EDX, XRD analysis and microhardness test. The thickness and quality of the coating increased with input power. Many pores were detected in the cross-sectional surface areas. Higher input power caused a better coating layer in NiTi alloy. The hardness of the coating layer decreases with higher input power.

Organic Coatings have potential applications in the prevention of metal corrosion in an aqueous solution. The protective effect of SEBS coated copper corrosion in NaCl 3% solution was investigated by using electrochemical methods. The main objective of this work is to find the optimal conditions of the protocol immersion to evaluate the effects of SEBS ratio and two-immersion time on the anticorrosive behaviour of copper in 3 wt % NaCl solution in order to determine the best conditions to produce a protective SEBS film on the copper surface. Response Surface Methodology (RSM) is used as an optimization method. The study’s findings show the combination of three environmental factors that minimize corrosion rate. The Box-Behnken Design (BBD) is working perfectly for the statistical significance of the model (ANOVA test). This analysis calculates the contribution value of each parameter in changing the value of the corrosion rate (CR) in not only individual but also synergistic cases. The optimized parameters were found to be a 2.17% of SEBS ratio, 20 min of immersion 1, and 21 min of immersion 2. The electrochemical impedance spectroscopy tests confirmed the results.

Advanced Nano structural hard coatings are thin materials films that range in thickness from a few nanometers to a few micrometers and are applied to different surfaces to increase their hardness and wear resistance. Physical vapor deposition (PVD) or chemical vapor deposition (CVD) methods are frequently used to deposit these coatings. These coating’s distinctive characteristics result from their microstructure, which is made up of material columns or grains with a diameter of only a few nanometers. Increased hardness, higher wear resistance, and improved tribological properties result from these short dimensions. In applications with significant wear and/or high contact pressures, such as cutting tools, bearings, and engine parts, the usage of sophisticated Nano structural hard coatings is crucial. Advanced Nano structural hard coatings include, 1. Amorphous carbon coatings with high hardness, low friction, and exceptional wear resistance are known as diamond-like carbon (DLC) coatings. DLC coatings are frequently used in a variety of industries, including the automotive, aerospace, and biomedical ones. 2. Coatings made of titanium nitride (TiN): These metallic coatings have high hardness and wear resistance. Cutting tool, machining, and aerospace industries frequently use TiN coatings. 3. Chromium nitride (CrN) coatings: These coatings have great corrosion resistance, good wear resistance, and high hardness. Cutting tools, gears, and bearings are just a few of the objects that use CrN coatings. 4. Tungsten carbide (WC) coatings: These coatings, which have a high degree of hardness and wear resistance, are frequently employed in cutting tools and other applications that require wear resistance. Advanced Nano structural hard coatings provide many advantages over conventional coatings, including better hardness, increased wear resistance, and improved tribological qualities. The automotive, aerospace, and biomedical industries are just a few that could use these coatings. In this paper the author will explain about the design synthesis and applications of advanced Nano structural hard coating in aerospace and automotive applications.

Biocidal compositions based on interpolyelectrolyte complexes and a low molecular weight antibiotic can become a promising material for creating biocidal coatings, as they combine wash-off resistance and dual biocidal action due to the biocide and the polycation. Molecular mass characteristics of polymers play essential role in physics and mechanical properties of the coatings. In this work, the properties of polydiallyldimethylammonium chloride (PDADMAC) coatings of various molecular weights are investigated and assumptions are made about the optimal molecular weight needed to create antibacterial compositions. To study the resistance to washing off and moisture saturation of the coatings, the gravimetric method was used, the adhesive properties of the coatings were studied by dynamometry. It has been established that an increase in molecular weight affects the wash-off resistance of coatings, but does not affect moisture absorption and adhesion mechanics of coatings. All samples of PDADMAC were demonstrated to exhibit the same antibacterial activity. Thus, when developing systems for creating antibacterial coatings, it must be taken into account that in order to create stable coatings. The requirement to use PDADMAC with a high degree of polymerization is necessary for control the desorption of coating during wash off-but not mandatory for the control of mechanical and antibacterial properties of the coating.

Millions of people use public transportation daily worldwide and frequently touch surfaces, thereby producing a reservoir of microorganisms on surfaces increasing the risk of transmission. Constant occupation makes sufficient cleaning difficult to achieve. Thus, an autonomous, perma-nent antimicrobial coating (AMC) could keep down the microbial burden on such surfaces. A photodynamic AMC was applied to frequently touched surfaces in buses. The microbial burden (colony forming units, cfu) was determined weekly and compared to equivalent surfaces in buses without AMC (references). The microbial burden ranged from 0 – 209 cfu/cm² on references and from 0 – 54 cfu/cm² on AMC. The means were 13.4 ± 29.6 cfu/cm² on references and 4.5 ± 8.4 cfu/cm² on AMC (p<0.001). The difference of microbial burden on AMC and references was al-most constant throughout the study. Considering a hygiene benchmark of 5 cfu/cm², the data yield an absolute risk reduction of 22.6 % and a relative risk reduction of 50.7 %. In conclusion, photo-dynamic AMC kept down the microbial burden, reducing the risk of transmission of microor-ganisms. AMC permanently and autonomously contributes to hygienic conditions on surfaces in public transportation. Photodynamic AMC therefore are suitable for reducing the microbial load and closing hygiene gaps in public transportation.

Background: Mucoadhesive polymers represent a major part of site-specific and localized retention strategies in oral drug delivery. Present research was designed to synthesize and characterize a novel mucoadhesive carbohydrate polymer (thiolated gum ghatti; TGG) which was further employed to fabricate mucoadhesive tablets of domperidone using an industrially viable compression coating technique. Methods: Thiolation of gum ghatti was achieved by the ester formation (esterification) between hydroxyl group and carboxyl group of gum ghatti and thioglycolic acid. Results: TGG was characterized by various physico-chemical techniques such as FTIR, XRD, SEM and DSC techniques. In rheological studies, the observed viscosities of pure gum-mucin were 45.45 and 71.75 mPas and that of thiolated gum were 78.7 and 112.58 mPas respectively in water and simulated gastric fluid. Signifi-cant increase in viscosity for thiolated gum may be attributed to increased macromolecular interactions responsible for enhanced mucoadhesive potential of thiolated gum. In-silico studies corroborate the role of mucin gum interaction and energetic stabilization for en-hanced mucoadhesion properties of thiolated gum. Ex-vivo mucoadhesion strength of gum ghatti and thiolated gum ghatti coated tablets was found to be ranging between 4.67± 0.79 to 8.99± 0.75 g and 11.76± 1.34 to 18.83± 2.07 g respectively. Conclusion: Thiolated gum ghatti may be regarded as a promising polymer for developing different mucoadhesive drug delivery systems.

In order to develop waterborne silicate anticorrosive coatings to replace solvent-based anticorrosive coatings used widely in ship’s industry, epoxy modified silicate emulsions were synthesized with different content of epoxy resin, then aqueous silicate zinc-rich coatings were prepared with synthesized silicate emulsion, triethylamine and zinc powder. The influence of the content of epoxy on the properties and chemical structure of modified emulsion, mechanical properties of silicate coatings, and the corrosion behavior of silicate zinc-rich coatings in 3.5% NaCl solution were investigated. The coating samples on steel were measured by immersion test, Tafel polarization test and electrochemical impedance spectroscopy (EIS) test with different immersion time. The results showed that epoxy modified silicate emulsions were successfully synthesized. With the increase of epoxy content, the viscosity and the solid content of modified emulsion increases, the impact resistance of the silicate coating raises, the pencil hardness decreases, but the adhesion is not affected. Epoxy modification can reduce to s certain extent the corrosion driving force of zinc rich coating and increase the impedance of the zinc-rich coating decreases with the increase of immersion time in 3.5% NaCl solution. With the increase of the epoxy content, the resistance value of the zinc-rich coating increases, indicating the ability of the coating to resist corrosive media is enhanced.

The concept of friction damper is widespread technique and used to reduce the structural vibrations in many industrial applications. These friction dampers are generally coated with low wear rate materials to reduce the fretting wear. This paper investigates the use of physical vapor deposition (PVD) nitride based AlTiN coating material applied over the stainless steel friction damper to enhance the damping capacity and to reduce the fretting wear. A friction test rig has been developed to measure the dynamic hysteresis characteristics of friction damper at high temperature (700 °C). The damping capacity and fretting wear analysis is carried out at room temperature, 300 °C and 600 °C. The force versus displacment characterisitcs curve is used to predict the damping capacity and fretting wear analysis is carried out at microscopic level for the comparision. It is observed that at room temperature AlTiN coated friction damper has not much influence to improve the damping capacity and to reduce the fretting-wear. However, at high temperature it has better damping capacity and less wear in comparision to uncoated friction damper. Wear behaviour in coated and uncoated damper is different at room temperature and at elevated temperature.

Background/Aim: There is continuing interest in engineering esthetic labial archwires. The aim of this study was to coat nickel-titanium (NiTi) and beta-titanium (β-Ti), also known as titanium molybdenum (TMA), archwires by plasma electrolytic oxidation (PEO) and to analyze the characteristics of the PEO-surfaces. Materials and Methods: PEO-coatings were generated on 0.014-inch NiTi and 0.19x0.25-inch β-Ti archwires. The surfaces were analyzed by scanning electron microscopy and stereomicroscopy. Cytocombability testing was performed with ceramized and untreated samples according to EN ISO 10993-5 in XTT-, BrdU- and LDH-assays. The direct cell impact was analyzed using LIVE-/DEAD-staining. In addition, the archwires were inserted in an orthodontic model and photographs were taken before and after insertion. Results: The PEO coatings were 15 to 20 µm thick and esthetically pleasing. The cytocompatibility analysis revealed good cytocompatibility results for both ceramized NiTi and β-Ti archwires. In the direct cell tests, the ceramized samples showed improved compatibility as compared to those of uncoated samples. However, bending of the archwires resulted in loss of the PEO-surfaces. Nevertheless, it was possible to insert the β-Ti PEO-coated archwire in an orthodontic model without loss of the PEO-ceramic. Conclusion: PEO is a promising technique for the generation of esthetic orthodontic archwires. Since the PEO-coating does not resist bending, its clinical use seems to be limited so far to orthodontic techniques using straight or pre-bended archwires.

The present study aims at deposition of zinc phosphate coatings with the incorporation of nano Titanium dioxide particles by chemical phosphating method. Zinc phosphate coatings were developed on low carbon steel by using nano TiO2 in the standard phosphating bath. The Coated low carbon steel samples were assessed for corrosion studies using electrochemical impedance spectroscopy and potentiodynamic polarisation techniques in 3.5% NaCl solution. Chemical composition of the coatings was analysed by energy dispersive X-ray spectroscopy (EDX). Significant variations in the coating weight, porosity and corrosion resistance were observed with the addition of nano TiO2 in the phosphating bath. Corrosion rate of nano TiO2 incorporated chemical phosphate coated samples was found to be 3.5 mpy which was 4 times less than the bare uncoated low carbon steel (~14 mpy). Electrochemical impedance spectroscopy studies revels in the reduction of porosity in nano TiO2 phosphate coated samples. It was found that nano TiO2 particles in the phosphating solution yielded phosphate coatings of higher coating weight, greater surface coverage and enhanced corrosion resistance than the normal zinc phosphate coatings (developed using normal phosphating bath).

The severe volumetric expansion of silicon nanoparticles (~400 %) limits their practical application as an anode material for next-generation lithium–ion battery (LIB). Here, we describe the fabrication and characterization of conformal polydopamine carbon shell encapsulating rattle-type silica@silicon nanoparticles (PDA−PEI@PVP−SiO2@Si) with tunable void structure prepared following a dual SiO2 template using (3–aminopropyl)triethoxysilane (APTES) as a self-catalytic, structure-directing agent to tetraethyl orthosilicate (TEOS) pretreated with polyvinylpyrrolidone (PVP K30) via modified Stöber process. Polyethylene imine (PEI) crosslinking facilitated the construction of interconnected three-dimensional bubble wrap-like carbon matrix structure through hydrothermal treatment, pyrolysis, and subsequent surface-protected etching. The composite anode material delivered 539 mAh·g−1 capacity after 100 cycles at 0.1 A·g−1, and 453 mAh·g−1 rate performance at 5 A·g−1. The satisfactory electrochemical performance of the PDA−PEI@PVP−SiO2@Si was attributed to the following: the rattle-type structure providing void space for Si volume expansion, PVP K30-pretreated APTES/TEOS SiO2 seeds via catalyst-free, hydrothermal-assisted Stöber protecting Si/C spheres upon etching, carbon coating strategy increasing Si conductivity while stabilizing the solid electrolyte interface (SEI), and PEI carbon crosslinks providing continuous conductive pathways across the electrode structure. The present work realizes a promising strategy to synthesize the tunable yolk–shell C@void@Si composite anode materials for high power/energy-density LIB applications.

The antifungal efficacy of coffee residues extracts (CRE) and chitosan nanoparticles (CNP) alone and with coffee residue extracts (CNP-CRE) were assessed on growth of Rhizopus stolonifer. Two nanostructured edible coatings, one based on chitosan nanoparticles (CCNP) another on coffee residue extracts encapsulated in chitosan nanoparticles (CCNP-CRE), were elaborated, characterised and applied on inoculated Naples tomatoes to evaluate their fungicidal activity and the effect on fruit quality. The tests consisted of evaluating physicochemical variables in tomato previously sprayed with CCNP and CCNP-CRE for 30 days preharvest and 14 days at 10°C postharvest. A CNP with a spherical shape and particle size of 2.4 ± 0.24 nm with a Z potential of −1.62 mV was observed, while CNP-CRE showed irregular and spherical shapes of 3.9 ± 0.55 nm with a Z potential of −0.89 mV. The FTIR spectrum showed the integration of CRE into the CCNP-CRE. A synergistic effect between CNP and 1 % CRE was observed since the greatest inhibition of mycelial growth (43%) was obtained. In the preharvest trials, the CCNP and CCNP-CRE showed differences with respect to the control in the variables of colour, total carotenoids and ethylene. In the postharvest test, both coatings showed differences in colour and CO2 production. The severity of the infection decreased 33% in tomatoes with coatings.

Organic electrophoretic coatings have gained significant attention due to their ability to provide a uniform and controlled coating thickness, high coating adhesion, and excellent corrosion protection properties. In this work, to investigate the aging behaviors of an organic electrophoretic coating for magnesium alloys, water absorption kinetics curves of the coatings after immersion in 3.5 wt.% NaCl at 20℃ and 40℃ were measured, and parameters such as the saturated water absorption and saturation time of the free film coatings were fitted to determine the densification evolution of the organic coatings. A tensile test was used to test the tensile strength of the organic coating during service to determine the evolution of the strength and toughness of the organic coating. The evolution of wet adhesion of organic coatings with service time was tested by ASTM D4541-02. The impedance spectra of the organic coatings under the above conditions were detected by EIS, and finally, the failure behavior of the organic coatings under immersion was analyzed.

Postbiotics are metabolites, cell components, and other bioactive molecules produced during the fermentation process by beneficial microorganisms such as probiotics. They can exhibit various biological activities, including immunomodulatory, antioxidant, anti-inflammatory, and antimicrobial properties. This study aimed to explore the in vitro antioxidant activity of postbiotics derived from Bifidobacterium bifidum DSM 20456 and B.bifidum BB12 strains, and to evaluate the effects of postbiotic-enriched alginate coatings on the microbial and physicochemical quality of turkey breast meat stored at refrigerator temperature for 7 days. Hence, the antimicrobial properties, total phenolic content (TPC), total flavonoid content (TFC), and 1,1-difenil-2-picrylhydrazyl radical scavenging activity (DPPH) of the postbiotics were determined. The results revealed that the TPC (87.13 ± 2.24-90.89 ± 1.63 mg GAE/100 mL), TFC (18.83 ± 2.21-24.20 ± 0.25 mg CE/ 100 mL), and DPPH (50.28 ± 0.20-51.56 ± 1.63 mg TEAC/100 mL) values of the tested postbiotics exhibited potential antioxidant capacity. The analysis results indicated that alginate coating with postbiotics caused significant differences in pH, b* (yellowness), and yeast/mold values of turkey meat during storage (p &lt; 0.05). The yeast and mold values increased significantly, while the pH and b* values of the samples (except for the control and bb groups) decreased during storage (p &lt; 0.05). On day 7, the abundance of yeast and mold in the bb group was 1.2 log CFU/g lower than in the control group (p &lt; 0.05). In contrast, L* (brightness), a* (redness), lipid oxidation, total aerobic mesophilic bacteria, psychrotrophic bacteria, lactic acid bacteria, and Listeria monocytogenes counts were not affected for 7 days (p &gt; 0.05). Our results showed that Bifidobacterium postbiotic treatment did not adversely affect the microbiological and physicochemical properties of turkey breast meats. In conclusion, our results demonstrate that postbiotic-enriched alginate coatings may be a practical solution for the meat industry to improve and maintain the quality features of poultry meat products during storage.

The reduction in rheological parameters and dissolution rate of precursors in geopolymer coatings during early hydration significantly contributes to sagging. This study aims to improve the sag resistance of these coatings by incorporating diatomite filler. Rheological testing was conducted to assess the impact of diatomite and its concentration on yield stress, plastic viscosity, and thixotropy of the geopolymer coatings. The results indicated that diatomite's large specific surface area and high reactivity have a significant influence on the rheological parameters and early dissolution rate of precursors. With a diatomite concentration of 1.1%, the coating exhibited a yield stress of 2.749 Pa and a plastic viscosity of 0.921 Pa·s, maintaining stability, homogeneity, and no sagging at a thickness of 600 μm. Furthermore, the highly active SiO2 in diatomite participates in the secondary hydration reaction of the geopolymer materials, leading to the formation of substantial C-(A)-S-H gel. This gel enhances internal interconnectivity within the coating, thereby improving its rheological and mechanical properties.

(1) Background: The aim of this study was to investigate the circadian rhythms of tongue features according to the effects of physiological phases over a 24-hour period. (2) Methods: Fifteen healthy participants aged 20 to 69 years were recruited. The participants did not have current chronic diseases or past diseases and had to meet the inclusion and exclusion criteria. The participants stayed at the Gil Hospital for a duration of 2 nights and 3 days. On the first day, at 18:00, they consumed their allocated portions of food and water and then completed a questionnaire. At approximately 21:00, their tongue images were acquired using a computerized tongue image acquisition system, following which they slept for 8 hours, commencing at 23:00. Measurements were taken from 07:00 through 21:00 on the second day, and the final acquisition was taken at 07:00 on the following morning, resulting in a total of eight images. The circadian rhythm was authenticated and quantified utilizing the single cosinor analysis, a technique for periodic regression analysis for fitting a 24-hour cosine curve. (3) Results: Cosinor analysis revealed that all tongue features were significantly related to circadian rhythm. (4) Conclusions: The results of this study may be important for considering the time of day at which the tongue is observed and tongue status is evaluated.

A new sustainable polypropylene terephthalate (PPT) coating was synthesized from recycled polyethylene terephthalate (PET) and applied on hydraulic concrete substrate to improve its durability. First step, PET bottles wastes were grinded and depolymerized by glycolysis using propylene glycol (PG), in a Vessel-type reactor (20–180 °C) to synthesize bis(2-hydroxypropyl)-terephthalate (BHPT), which was applied as coating to one-three layers on hydraulic concrete substrate, by brushing technique and polymerized (150 °C for 15 h) to obtain PPT. PET, BHPT and PPT were characterized by FT-IR, PET and PPT by TGA, and the PPT coatings by SEM (thickness), by ASTM-D3359-17 (adhesion) and by water contact angle (wettability). The durability of hydraulic concrete coated with PPT was studied by resist chloride ion penetration (ASTM-C1202-17), carbonation depth at 28 days (RILEM-CPC-18), and absorption water ratio (ASTM-C1585-20). The results demonstrated that the BHPT and PPT were synthetized (FT-IR), PPT had a similar thermal behaviour to PET (TGA); the PPT coatings had good adhesion to the substrate, with thicknesses of micrometric units; hydrophilic (similar to PET coatings), and the durability of hydraulic concrete coated with PPT (2-3 layers) improved (migration of chloride ions decreased, carbonation depth was negligible, and the absorption water ratio decreased).

Laser heat treatment is applied after coating. Evaluation of the results was performed by studying the microstructures by metallographic, SEM/EDX microscopy and the mechanical properties were obtained by microscopic hardness and abrasion resistance. The objective of this study was to investigate the effect of laser heat treatment on the wear resistance of metal coatings. The results show the influence of the microstructure and chemical composition of the electrodes used on the micro-hardness and wear resistance of the metal coatings.

A detailed structural investigation of a promising bio-based polymer, polyglycerol citrate poly-ester, obtained by bulk polycondensation of glycerol (Gly) against citric acid (Cit) under mild reaction was performed. This polymer was suggested to be well suited for coating seeds or similar agricultural applications. The reaction in conditions with and without catalyst use (sulfuric acid, H2SO4) was investigated, showing evidence that it is possible to modify the polymer solubility according to the ratio and catalyst utilization. 13C and 1H NMR indicated that synthesis catalyzed with Cit excess leads to higher esterification degrees of citrates groups. In contrast, the Gly moi-eties are more prominent in catalyzed polymers regardless of the excess monomers. Overall, a successful conversion of Gly and Cit into polyesters was attained, even without catalysis, enabling a simple route for large-scale production of this green material to be used as coating material. Tests on soybean seed coating with a PGCit solution of 75% indicated that the seed quality and ger-mination rate was not affected by PGCit coating, concluding that this polymer is promising for this application.

In order to further reduce the emissivity of the hydrophobic low infrared emissivity composite coating and improve the mechanical properties of the coating, the dispersant, adhesion enhancer, and defoamer were used to improve the dispersion state of the fillers, the interface structure, and the surface state of the hydrogen silicone oil modified polyurethane/Al composite coating. The effects of dispersant, adhesion enhancer, and defoamer on the micro-structure, emissivity, glossiness, hydrophobic property, and mechanical properties of the coating were systematically studied. The results show that the polycarboxylate anionic dispersant can obviously improve the dispersion state of flake Al powder and nano-SiO2 in the coating, so that the infrared emissivity of the coating can be reduced, and the coating can have higher hydrophobic and mechanical properties. The bonding strength between the resin matrix and the metal substrate of the coating can be significantly improved by the adhesion enhancer through the bridging action, so that the adhesion strength and impact strength of the coating can be significantly improved. The defoamer can significantly reduce the pores in the coating, so that the surface state of the coating can be significantly improved, and the mechanical properties of the coating can be significantly improved. The coating has the best emissivity (0.527), glossiness (4.3), adhesion strength (grade 1), impact strength (40 kg.cm), and hydrophobic property (water contact angle (WCA) is 140o) when the amount of dispersant, adhesion enhancer, and defoamer is 5 wt%, 4 wt%, and 1 wt%, respectively.

In the present study, a nanostructured FeAl coating was prepared by cold spraying of ball milled powder. Annealing treatment was applied to the coating to investigate its effect on the microstructure, phase structure and microhardness of the cold-sprayed nanostructured FeAl coating. The results showed that the FeAl phase was kept unchangeable when the coating annealed at the temperature above 500oC. Annealing temperature significantly influenced the microstructure and microhardness of cold-sprayed FeAl coating. With raising annealing temperature, the lamellar structure in the as-sprayed coating disappeared and a dense coating microstructure with fully bonding of deposited particles at their interfaces was achieved after annealing at 950oC. Nanograin growth of the FeAl phase occurred at an annealing temperature higher than 800oC. The microhardness of cold-sprayed FeAl coating remained about 400 Hv0.1 at the annealing temperature below 800oC and decreased to 300 Hv0.1 at 1100oC.

In this paper, applicability of the modified water-based yttria stabilized zirconia (YSZ) suspensions, including different dispersants, to produce plasma sprayed coatings with “columnar microstructure” is investigated. The effects of processing parameters like suspension liquid phase ethanol content, change of substrate roughness, and spray distance on the resulting coatings morphologies are investigated. The results showed that increasing ethanol concentration, substrate surface roughness, and the spray distance promote formation of coatings with columnar structure. Moreover, application of modified water-based suspensions including α-Terpineol dispersant has led to deposition of columnar coatings with comparable morphologies of coatings deposited from ethanol-based suspensions.

Peri-implantitis occurs at a significant rate, which is the leading cause of implant failure. The main reason for this unwanted complication is bacterial invasion and biofilm formation. To reduce the incidence of peri-implantitis, we constructed a carboxymethyl dextran (CMD) based nanomicelles antibacterial coating on microarc-oxidized titanium (MAO-Ti) surface. After cross-linking, the drug-loaded nanomicelles were spherical with a particle size of 130nm and uniformly dispersed. Zeta potential was negative, and the absolute value was greater than 10 mV, effectively avoiding micelles aggregation. It was observed by dynamic light scattering (DLS) that the stability of nanomicelles was significantly improved after cross-linking. The hemolysis rate of micelles was less than 5%, and the overall survival rate of human umbilical vein endothelial cells was more than 90%. After being coated on MAO-Ti surface, the cumulative drug release rate of drug-loaded nanomicelles reached 86.6% after 360 hours. Fluorescence staining of immobilized bacteria showed more dead bacteria on the coating surface, and the number of live bacteria was significantly reduced. It was concluded that dextran-based nanomicelles, which showed long-term drug release properties and excellent biocompatibility, are potential drug carriers for fabricating antibacterial coating on titanium surfaces.

Metallic thin-film materials and nanoparticles (mainly Silver (Ag)-based) are recently being used in many nano-technological applications including sensors, reflective heat-mirror coatings, and antibacterial coatings as well. The physical vapor deposition technique attracts significant attention for Ag-based nanocomposites with tailoring the structural and optical properties of metallic thin films thus allowing further improvements and application possibilities in various existing fields namely electronics, catalysis, magnetics, optics in alongside the environment and health and new emergent fields in, particularly thin-film coatings. This study highlights the preparation, characterization, properties, and possible future application directions of several types of Silver (Ag)-based nanocomposite thin films prepared by using physical vapor deposition techniques.

A phosphate/molybdate and cerium-modified phosphate/molybdate conversion coatings were deposited on a carbon steel surface and their protective and self-healing abilities were evaluated. Surface morphology and inner structure of the coatings were examined using FE-SEM-FIB and TEM techniques, chemical composition and element distribution depth profiles in conversion layers were determined using EDX measurements, whereas XPS was applied for the analysis of Mo and Ce oxidation states. Voltammetric measurements and EIS were performed to assess the corrosion behavior of the samples. The higher protective and stronger self-healing abilities were found for phosphate/molybdate/cerium conversion coating deposited in a sulphate-containing solution. This was attributed to higher values of both: total cerium and Ce(IV) content in the conversion layer as well as to lower number of structural defects in the coating. It was demonstrated that the micro-structural characteristics of protective coatings are also important in determining self-healing abilities.

This research was conducted to manufacture thermally expandable microspheres (TEMs) for vehicles’ underbody coating and to apply them on an industrial scale. TEMs heat resistance was studied depending on the ratios of a cross-linking agent and an initiator. This research focused on the content of a cross-linking agent and how it affected the results. The TEMs’ outer shell was thickened to solve the problem of the foam expansion ratio’s reduction that occurred due to the shrinkage after the maximum expansion (Tmax) was reached. After foaming, the cross-sectional thickness and surface of the sample with thickened outer shell were observed. The TEMs with the thickened shell showed the least shrinkage, which indicated excellent shrinkage stability, even after prolonged exposure to heat.

Electrochemical impedance (EI) measurements were performed to evaluate the nylon 66/-tetra-(para-aminophenyl) porphyrin (H₂T(p-NH₂)PP)/graphene oxide (GO) film coating on stainless steel and compared to the nylon/H₂T(p-NH₂)PP and nylon/GO film samples using 1M H₂SO₄ as electrolyte. The nylon/H₂T(p-NH₂)PP and nylon/GO composite films showed high electrochemical impedance in the order of 109 ohm-cm² and a system controlled by mass transfer, product of a diffusion process at low frequencies with a resistance up to 5 orders of magnitude, indicating the diffusion of protons through the coating and a decrease in the metal dissolution. Otherwise, the nylon/H₂T(p-NH₂)PP/GO film compound evaluated show good ionic conductivity and electrochemical stability in the acid environment, acting porphyrin as a catalyst to the passage of protons through the film, reducing its electrochemical impedance up to 7 orders of magnitude with respect to the compounds nylon/H₂T(p-NH₂)PP and nylon/GO. Likewise, good capacitance values are also shown by modifying the concentrations of porphyrin and GO reinforcing materials. These properties are important for technological applications, such as anticorrosion coating for bipolar plates or membrane in a fuel cell type PEM, super-capacitors, etc.

One method of creating a brass coating is through electrodeposition, which is most often completed in cyanide galvanic baths. Because of the toxicity of cyanides, many are working on the development of cyanide-free baths, which are promising but not satisfactory to replace the classic methods. The purpose of the study was to explore a new generation of non-aqueous cyanide-free baths based on 1-ethyl-3-methylimidazolium acetate ionic liquids. The study involved the formation of copper, zinc, and brass coatings. The influence of the bath composition, cathodic current density, and temperature was determined. The obtained coatings were characterized by their morphology, chemical composition, roughness, and corrosion resistance. It was found that the structure of the obtained coatings is strongly dependent on the process parameters. The three main structures observed were fine-grained, porous, and olive-like. To the best knowledge of the authors, it is the first time the olive-like structure was observed in the case of an electrodeposited coating. The Cu-Zn coatings consisted of 19–96 at.% copper and exhibited relatively strong corrosion resistance. High improvement of corrosion properties was found in the case of copper and brass coatings with an olive-like structure.

The study delved into the interaction between corn starch and ethyl maltol during innovative repeated-continuous heat-moisture treatment (RCHMT), and its impact on the quality of fried chicken nuggets. The results revealed that the complexation ratio of ethyl maltol in the corn starch-ethyl maltol complex remained stable, and the complex created dense microporous structures. Native starch and complex samples exhibited an A-type crystal structure, while the physical mixture sample showed a Ca-type. Additionally, the peak of C-O-H def., CH2 of the complex sample was red-shifted, and the hydrogen bond structure was enhanced. Moreover, the complex exhibited a higher resistant starch content and lower hydrolysis rate than the physical mixture sample. The starch-ethyl maltol formed by RCHMT is a non-inclusion complex. It has been shown to reduce oil absorption and enhance the crispness of fried chicken nuggets, matching that of commercial products. This finding provides a direction for the development of innovative coating powders.

Due to the high temperature limitation associated with silicon, SiC, Si₃N₄, TiC, TiN, TiB₂, cBN, CNx, SiO₂, Al₂O₃ and novel multicomponent nanocomposites polymer derived ceramics (PDC) based thin films like Si-C-N, Ti-Si-B-C-N and Si-O-CN that are compatible with silicon and have a wider range of operation in ambient conditions are being investigated. Apart from small scale electro-mechanical devices like N/MEMS, sensors, areas like metallurgical protection, water purification, energy storage, bio medical implants and aerospace have been benefited. The cross-sectional study involving the role of oxygen and nitrogen dissolution at different interfacial configurations has been presented.

CoCrFeNiMn high-entropy alloy coatings were prepared on compacted graphite iron（CGI） through plasma cladding to strength the CGI substrate. The effects of heat treatment temperatures and times on the microstructure and mechanical properties of the CoCrFeNiMn coatings were investigated. After heat treatment, a single FCC phase was remained in the coating as compared to the deposited one, with smaller dendrites, larger dendritic spacing and more Cr-rich compounds precipitated between dendrites. The coatings’ microhardness was increased after heat treatment. After heat treated at 660°C for 90 minutes, the coating had the highest microhardness of 563±6.9 HV0.2, the lowest frictional coefficient of 0.71 and the smallest wear mass loss of 1.12 mg, and it had the best wear resistance.

Tungsten carbide (WC) was well known as a wear-resistant material. Iron-based pow-der was suitable for remanufacturing of cast iron engine parts. To improve the wear resistance of the remanufactured iron-based cast iron engine parts, WC-Co was intro-duced into iron-based powders to prepare composite coatings for cast iron engine components. In this work, FeAlC-x(WC-Co) composite coatings were prepared by plasma transfer arc on compacted graphite cast iron. The influences of WC-Co con-tents in the Fe-AlC-x(WC-Co) composite coatings on the microstructure and properties of the composite coatings were investigated. The composite coatings contained γ-Fe, α-Fe, WC and Fe3W3C mainly. The microhardness of FeAlC-x(WC-Co) composite coatings had the highest hardness of 814 HV0.2, the-lowest coefficient of 0.5 and the lest wear mass loss of 1.3mg when the weight content of WC-Co in the composite coating was 20wt%. As compared with the FeAlC coating, FeAlC-x(WC-Co) composite coating achieved the effect of reducing friction and wear resistance simultaneously, which resulted from the self-lubricating effect of graphite and high wear-resistance of carbides in the claddings.

Electroluminescence (EL) is an innovative technology in the lighting area. The EL device's main structure consists of a phosphor layer sandwiched by two electrodes. In this work, several alternating current EL devices have been developed by applying a set of sequential layers with combinations of in-house prepared inks and commercially available ink as a phosphor layer. A flexible polyester textile substrate was functionalized with inks by spray coating technique, after knife-coated an interfacial layer directly on the surface. A thorough study was carried out on the phosphor layer composition to optimize the EL device performance, more precisely the illuminance intensity and the illuminance homogeneity. The developed phosphor layer was composed of zinc sulphide doped with copper (between 30.0 to 38.1 wt%) and diluted by using a diluent at different ratios (28.0 to 35.5 wt%). The best peak illuminance intensity of 61 lux was obtained when the phosphor ink presented 35.4% ZnS:Cu and was diluted with 33.0% diluent. The aim of this study to determine the best formulation of the phosphor layer, which can be highly promising for further developments of EL devices, taking in account different applications in market.

The (Ti, Nb)(C, B)/IN625 composite coating with both homogeneous and defect-free microstructure were successfully prepared by in situ on the surface of 42CrMo steel using the coupling of the ultra-high-speed laser cladding (EHLA in German) technology with the direct reaction synthesis (DRS) technology, and were comparatively analyzed with the IN625 coating prepared by the EHLA. The microstructure of the fused cladding layer was investigated by selected scanning electron microscopy (SEM), energy dispersive spectrometer (EDS) and double spherical aberration transmission electron microscopy (DSA-TEM). The residual stress distribution on both sides of the fused cladding interface was characterised by nanoindentation stress test based on the modified O&P method and the G&S energy method. The results show that the interface of (Ti, Nb)(C, B)/IN625 composite coatings is affected by about 670 kJ Joule heat released from the in-situ reaction, and the interfacial width reaches 24 μm, so that it is 6 times higher than that of IN625 coating prepared by EHLA, which effectively reduces the stress gradient in the interfacial region and alleviates the stress mismatch on both sides of the interface. However, the surface hardness of (Ti, Nb)(C, B)/IN625 composite coating is lower than that of the IN625 coating, with a value of about 240 HV0.2, and the average wear weight loss was only 10% of that of the IN625 coating, which is on the one hand attributed to the in-situ authigenic TiCB, TiC, NbMo3B4, and NbMo2B2 phases supporting the (Ti, Nb)(C, B)/IN625 composite coating substrate to achieve the abrasion reduction and wear resistance. On the other hand, it is attributed to the formation of nano-equiaxial ultrafine grains in the depth range of 250 nm below the wear surface area by the coupling of the three fields of plastic rheology-heat-force, which dynamically strengthens the wear surface.

Tablets are the most used solid dosage form in medical treatments. The realistic modeling 1 of such specific object shapes in computer simulations has been demonstrated already by the author 2 for bi-convex round tablets but needs to be extended for a wider range of tablet shapes. Moreover, 3 the number of tablets must be large enough to simulate industrial drum coaters, which are typically 4 used for film coating processes. Whilst this long lasting process where tablets flow continuously, 5 tablets are loaded by frequent changes of individual contacts. Using a tailored simulation tool named 6 pharmAssist , written for GPUs (modern massively parallel processors in graphics cards and HPC 7 accelerators), we implemented the widely used oblong tablet shape. We are able to simulate flows 8 involving industrial scale number of such tablets. Data mining allows for statistical analyzis of 9 pair-wise contacts of different geometric features. Our simulation results serves as an observation 10 space, which cannot be addressed by experimental analyzis and will help to avoid degradation of 11 tablets like chipping or other defect phenomena. This paper reflects current development work in 12 order to extend the DEM with a new shape class, which comprises the modelling of compacted or 13 extruded objects, which have a smooth exterior, a flat band and sharp contour edges

In recent years, there has been growing interest in thermal spray techniques using suspension or solution-based coatings. These techniques offer precise control over particle size and microstructure, improving feedstock flowability and allowing for high-quality coatings customization. Spray parameters, such as stand-off distance (SOD) and feedstock flow rate, can alter the performance and characteristics of these coatings. Geothermal power plant heat exchangers often face issues like corrosion, scaling, and fouling. These issues could be mitigated, at least in part, by the use of spray coatings. In this study, TiO2 coatings were applied to a carbon steel substrate using suspension plasma spray (SPS) to enhance the performance of geothermal heat exchanger materials. The impact of SOD (50, 75, and 100mm) and feedstock flow rate (10, 20, and 30 ml/min) on these coatings was examined through various techniques, including SEM, profilometry, XRD, and adhesion testing. The results demonstrated that coatings deposited using 10ml/min feedstock flow rate were well-adhered to the substrate due to efficient melting of coating material but as the SOD and feedstock flow rate increase due to poor thermal and kinetic energy exchange between the torch and feedstock particles, adhesion between coating and substrate decreases. smaller SODs led to more compact coatings, while higher feedstock flow rates increased coating porosity. Smaller SODs and lower flow rates resulted in well-adhered coatings, offering valuable insights for advancing geothermal heat exchanger coatings.

The process of Thermal spray is effective for creating a metal matrix composite (MMC) by embedding zirconium diboride reinforcement into a molybdenum matrix. This allows for the combination of beneficial properties in a new composite, as both materials have a high The materials Mo and ZrB2 possess different characteristics. For example, Mo has a melting point of 2622 ◦C while ZrB2 has a higher melting point of 3246 ◦C. Additionally, Mo has a high thermal conductivity of 139 W/m◦C compared to ZrB2's thermal conductivity of 24 W/m◦C. However, both materials have good thermal shock resistance, and Mo has a low coefficient of thermal expansion of 5.35 µm/m◦C while ZrB2 has a coefficient of thermal expansion of 5.8 × 10−6 K−1., as well as the ability to maintain strength at elevated temperatures and stability in extreme environments. The study focused on creating Mo/Zrb2 composites using a thermal spray coating technique, varying the parameters of spraying distance, number of passes, and gas pressure, and testing the resulting castings to evaluate their hardness and Young's Modulus. The primary objective of the research was to use the Taguchi technique for identifying the optimal parameters for generating the highest Young's Modulus and hardness for the castings. The Taguchi method integrates experimental and analytical principles to identify the most significant parameter affecting the response, which can significantly enhance overall performance. The study found that the optimal parameters were a spraying distance of 20 cm, gas pressure of 6 bar, and the number of passes of 18. The Taguchi method accurately predicted the parameters that produced the highest properties for the composite coatings, which demonstrated good surface formation without hot cracks and fewer pores, with well-formed metallurgical bonding between the coating and the substrate.

Microcrystalline and near nanocrystalline AlCrFeCoNi high-entropy alloy (HEA) coatings were applied on Inconel 718 superalloy using air plasma spraying (APS) process. High-temperature oxidation behavior of the microcrystalline and near nanocrystalline AlCrFeCoNi HEA coated superalloy were examined at 110°C under the air atmosphere for 50 cycles under cyclic heating and cooling (1 h for each cycle). The oxidation kinetics of both nanocrystalline and microcrystalline coated superalloy was accordingly analyzed by weight change measurement. It was noticed that the uncoated and coated followed the parabolic rate law of the oxidation. X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), energy dispersive X-ray analysis (EDS), and elemental mapping techniques were used to analyze the oxidized coated and uncoated samples. In the HEA coated superalloy, Fe, Ni, Co, and Al were oxidized in the inter-splat region, whereas the splats which consist mainly of Ni and Cr remained unoxidized. Because of the formation of compact and adhesive thin NiO, CoO oxides, and spinels together with the Al2O3 oxide scale on the surface of the coating during oxidation, the developed nanocrystalline HEA coating shows better oxidation resistance than the microcrystalline HEA coating.

In the present study, the corrosion resistance of amorphous coating and composite coatings in 3.5 wt.% NaCl, 0.5 M H₂SO₄ and 10 wt.% NaOH solution were studied. The composite coatings exhibit superior corrosion resistance. When the content of AT13 （Al₂O₃–13 wt.% TiO₂）was 15 wt.%, the composite coating has the lowest corrosion current density (1.75×10^-6 A cm^-2), which is 5.14×10^-5 A cm^-2 for Fe-based metallic glassy coating, and the highest corrosion potential (-411 mV), which is -580 mV for Fe-based metallic glassy coating. The breakdown potential of the passivation film in 3.5 wt.% NaCl solution was much higher than that of 316L.The long-time immersion corrosion tests carried out on different coatings showed that the corrosion protection effect of coating was enhanced with the increase of the amount of AT13 added.

This research project focuses on the optimization of the hybrid energy system together with the assistance of thin-film coatings aiming to achieve self-sustainable food and crop storage facilities which will run effectively with its own generated energy. An infrastructure will be designed and constructed that will comprise a hybrid power generation system accompanied by thin-film coated semitransparent and non-transparent construction materials for energy saving. Thin-film low emissivity (Low-E) type coatings will assist the transparent or semitransparent construction materials to reflect most of the infrared (IR-mostly heat) and UV spectra of sunlight without interrupting the visible spectrum and will lead to saving energy consumption by reducing the heat and lighting during day time

The process of preparing anti-glare thin films by spray-coating silica sol-gel to soda-lime glass was exclusively and statistically studied in this paper. The effects of sol-gel deliver pressure, air transport pressure, and spray gun displacement speed on the gloss, haze, arithmetic mean surface roughness, and total transmittance light were analyzed. The experimental results indicate that the factors of sol-gel deliver pressure, air transport pressure, and displacement speed exhibit significant effect on the haze, gloss, and Ra. In contrast, the variation of total transmittance light with these three factors are insignificant. Because the anti-glare property is predominantly determined by low gloss and high haze, therefore, we aim to minimize gloss and maximize haze to achieve high anti-glare. Central composite design and response rurface methodology are employed to analyze the main and interaction effects of the three factors through quadratic polynomial equations, which are confirmed by the analysis of variance and R². The response surface methodology predict the lowest gloss and highest haze are 9.2 GU and 57.0%, corresponding to the sol-gel deliver pressure, air-transport pressure, and displacement speed of 250 kPa, 560 kPa, and 140 mm/s, and 340 kPa, 620 kPa, and 20 mm/s, respectively. Comparing the predicted optimal data with the real experimental results validates the applicability of the mathematical model. This study provides an important basis for the subsequent production of anti-glare glass with different specifications to satisfy the market demand.

Synthesis of poly(o-phenylenediamine) (PoPD) and poly(o-phenylenediamine)-ZnO (PoPD-ZnO) nanocomposites on carbon steel by in-situ polymerization with HCl acid as doping acid Material coating. The composition and structure of PoPD-ZnO nanocomposites were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The corrosion protection ability of polymer coatings in 3.5% NaCl was studied by potentiodynamic polarization curves and electrochemical impedance spectroscopy. It can be seen from the electrochemical corrosion experimental data that PoPD-WPU coating (PWC) and PoPD-ZnO-WPU coating (PZWC) can effectively improve the corrosion resistance of the carbon steel substrate, and the corrosion rate is reduced by 2-3 orders of magnitude compared with carbon steel. The conclusion demontrates that PoPD can effectively extend the service life of carbon steel substrates. In addition, it is advantageous to form a compact and low-defect coating when added nano-particle ZnO, which is advantageous for the POPD film to develop its good barrier property and corrosion resistance.

Carbonous nanomaterials are promising additives for composite coatings for heat-dissipation materials because of their excellent thermal conductivity. Here, copper/carbonous nanomaterial composite coatings were prepared using nanodiamond (ND) as the carbonous nanomaterial. The copper/ND composite coatings were electrically deposited onto copper substrates from a continuously stirred copper sulfate coating bath containing NDs. NDs were dispersed by ultrasonic treatment, and the initial bath pH was adjusted by adding sodium hydroxide solution or sulfuric acid solution before electrodeposition. The effects of various coating conditions—the initial ND concentration, initial bath pH, stirring speed, electrical current density, and the amount of electricity—on the ND content of the coatings were investigated. Furthermore, the surface of the NDs was modified by hydrothermal treatment to improve ND incorporation. A higher initial ND concentration and a higher stirring speed increased the ND content of the coatings, whereas a higher initial bath pH and a greater amount of electricity decreased it. The electrical current density showed a minimum ND content at approximately 5 A/dm². Hydrothermal treatment, which introduced carboxyl groups onto the ND surface, improved the ND content of the coatings. A copper/ND composite coating with a maximum of 3.85 mass% ND was obtained.

An ultra-low anti-reflection optical coating on both surfaces of a plastic cover slip was studied for use in confocal image measurement. The optical reflectance at a wavelength of 632.8 nm was less than 0.1% when the coated sample was placed in a liquid having a refractive index of 1.34 close to the aqueous solution of the biomaterial. The high- and low-index coating films, Substance-2 (PrTiO3) and silicon dioxide (SiO2), were measured by an ellipsometer to determine their optical refraction indices and extinction coefficients. Theoretically, when the two layer thicknesses are designed using the optical admittance diagram of the cover slip to approach the equivalent index of 1.34, a reflectance of 1.6×10-5% in the liquid could be obtained. Experimentally, the reflectance of the sample deposited on the two faces of the cover slip was 4.223±0.145% as measured in the air; and 0.050±0.002% as measured by a He-Ne laser in the liquid.

The aim of this paper is to develop a composite coating on St 304 steel employing TIG process. Ti wire cored with graphite powder is used as the means of coating material. The process parameters are varied in order to develop coating with optimum characteristics (i.e., hardness and wear resistance). The microstructure of the coating is analyzed with SEM and XRD. It is found that both of the hardness and wear resistance increase as the current increases while both of these properties decrease as the travelling speed increases. It is found that the coated samples with composite layers have more hardness than the substrate and it could range up to 1100 HV being almost 4.5 times higher than the hardness of St 304. Likewise, the wear resistance of coating is observed to be 4.5 times higher than that of substrate. The high performance of coating, as revealed by microstructural analysis, is due to formation of TiC and Cr₂₃C₆ .The optimum conditions to produce the coating are proposed to be 120 A current and 3.17 mm/s travel speed.

In modern materials science and surface engineering, Reactive Plasma Spraying (RPS) occupies a key po-sition due to its ability to create high quality coatings with unique properties. However, the efficiency of this process is highly dependent on the physicochemical characteristics of the starting powder materials. Mechanical activation, as a pretreatment, can have a significant effect on the structure and reactivity of powders, thereby modifying and improving the RPS process. The present study focuses on analysing the changes that occur to powder materials after mechanical activation and their subsequent effects on the quality and performance of coatings produced by the RPS process. The study of these changes is of key importance for optimising the spraying process as well as developing new materials with improved methods. This is important not only to improve the efficiency of reactive plasma spraying technologies, but also to expand their applications in various industrial and scientific fields. Improved materials can be a decisive factor in increasing the productivity and prevalence of products, as well as creating new opportunities for innovation and development in various industries.

Aloe vera is well known for its biological properties as a bioflavonoid-anti-inflammatory, antibacterial agent. It has been used frequently in the food sector as food coating for its hygroscopic properties and as an ingredient in the lucrative industry. Studies have also included Aloe vera as an eco-friendly green solution based on these properties. The current research focuses on the use of Aloe vera gel in printing pastes as an alternative sustainable solution to synthetic thickeners, evaluating its wet performance and ease of fabric stitching, and has been inspired by studies that similarly used this substance measuring its effect on the fabric's coefficient of friction and antimicrobial action. In the current study, printing pastes with natural colourants and Aloe vera gel thickener derived from natural leaves from Crete increased the fabric's mechanical resistance to abrasion compared to the untreated pastes. The measured performance did not differ substantially from prints with traditional synthetic pastes, hence tolerating the substitution with the non-contaminant variant. The enhanced resistance to abrasion and wear prolongates the fabric's serviceable life and resulting garments, decreasing the need for high industry processing volumes and, as a result, reducing pollution. The resistance to wear was evaluated using the dominant method in textile testing of the Martindale apparatus, which measured the cycles to failure, weight loss, and general appearance deterioration using the official photographic standards.

This study investigates lost foam shell casting coatings, focusing on the effects of mixing time and standing time on the viscosity and rheological properties of the coatings. The results show that the viscosity of the coating decreases with increasing mixing time and eventually stabilizes. Conversely, the viscosity initially increases and then decreases with prolonged standing time. To ensure optimal coating performance, this study determined that the mixing time should be no less than 50 minutes, and the standing time should not exceed 40 hours.

This work investigated the influence of current density, plating solution flow rate, and nozzle outlet-cathode distance on the properties of Ni-diamond composite coatings. A multi-physics field simulation is employed to analyze the interplay between current density, plating solution flow rate, and nozzle outlet-cathode distance on the flow field and electric field distribution. Additionally, particle tracing simulations were incorporated into the model to evaluate the incorporation efficiency of diamond particles during composite electrodeposition. Experimental validation of the findings shows a significant increase in the diamond particle content of the coating. This combined approach provides valuable insights for optimizing the jet electrodeposition process for Ni-diamond composite coatings with superior properties.

Measurement of Globe temperature is essential for investigating thermal comfort in street canyon. Globe thermometer is the most common instrument used to measure globe temperature (GT), however its application in scale models is still uncertain and not thoroughly investigated as of today. Therefore, this study is explicitly conducted to investigate globe thermometer measurements and proposed an improvised customization of the globe thermometer size to enhance reliability in scale models. The experiments were carried out outdoors using a typical street canyon model (scale 1:100) with East-West street orientation. The experiment presented a comparison between a low solar reflective street canyon (albedo of 0.4) and a high solar reflective canyon (albedo of 0.6) in terms of surface temperatures, heat flux and globe temperature. Furthermore, this study also investigated the influence of solar orientation on the globe temperature using both experimental using scale models and microclimatic modelling using ENVI-met. It is observed that although the surface temperatures are lower with high solar reflective canyon compared to that with low solar reflective canyon, GT is higher in high reflective canyon during daytime, which could be due to combined effect of direct radiation and shortwave reflection. However, for hours after the sun set, GT becomes lower (up to 1°C) in the case of high reflective canyon compared to low reflective canyon.

Purpose: The aim of the study is an approach to a nanocomposite with copper nanoparticles, constituting a bacteriostatic surface for maintaining the human lung cells' function. Methods: The polyelectrolyte layer coating with copper nanoparticles incorporated was designed. As a bacteriostatic factor, copper nanoparticles were applied as a colloidal solution of copper nanoparticles (ColloidCuNPs) and solution of copper nanoparticles (CuNPs). The influence of polyelectrolytes on selected Gram(+) and Gram(-) strains was examined. The function of the human adenocarcinoma A549 cell line of epithelial human lung cells cultured in the presence of nanocomposite layer coatings was analyzed, as well as their morphology using flow cytometry, fluorescence microscopy, and scanning electron microscopy. In addition, the material of layer coating was assessed using AFM and SEM-EDX characterization. Results: It was observed that polyelectrolytes polyethylenimine and poly-L-lysine do not induce proliferation of E.coli strain. On the other hand, it induces the proliferation of S. aureus strain. Due to CuNPs effectiveness against E.coli strain, CuNPs were selected for further research. The designed coatings at proper NPs share sustained the function of human lung cells cultured within 10 days of culture. The AFM and EDX characterization confirmed copper presence in the layer coating nanomaterial. The presence of CuNPs in polyethyleneimine-based nanocomposite deepens the bacteriostatic effect on E. coli compared with PEI alone. Meanwhile, incorporating CuNPs in PLL at share allowed A549 cell maintenance, did not exert a bacteriostatic influence on the examined strain.Conclusion: The platform based on polyelectrolytes incorporated with copper nanoparticles ensuring the growth and morphology of the human lung epithelial cells can be considered an element of the system components for medical devices for maintaining the human lung cells' function.

This study investigated the impact of chitosan (CH, 1%) and aloe vera gel (AL, 30%) edible coatings on the preservation of blue honeysuckle quality during a 28-day storage at -1°C. Coating with CH, AL, and CH+AL led to notable enhancements in several key attributes. These included increased firmness, total soluble solids, acidity, pH, and antioxidant capacity (measured through DPPH, ABTS, and FRAP assays), as well as the preservation of primary (ascorbic acid) and secondary metabolites (TPC, TAC, and TFC). These coatings also resulted in reduced weight loss, respiration rate, color, abscisic acid, ethylene production, and malondialdehyde content. Notably, the CH+AL treatment excelled in preserving secondary metabolites and elevating FRAP-reducing power, demonstrating a remarkable 1.43-fold increase compared to the control after 28 days. Overall, CH+AL exhibited superior effects compared to CH or AL treatment alone, offering a promising strategy for extending shelf life and preserving quality of blue honeysuckle during storage.

Magnesium alloy stents have been extensively studied in the field of biodegradable metal stents due to their exceptional biocompatibility, biodegradability and excellent biomechanical properties. Nevertheless, the specific in vivo service environment causes magnesium alloy stents to degrade rapidly and fail to provide sufficient support for certain time. This paper presents an overview of the development history and protection strategies for magnesium alloy stents. Alloying, optimizing stent structure and preparing protective coating have improved the corrosion resistance of magnesium alloy stents. Based on the corrosion mechanism of magnesium alloy stents, as well as their deformation during use and environmental characteristics, we present some novel solution strategies aiming at reducing the corrosion rate of magnesium alloys and enhancing the comprehensive performance of magnesium alloy stents. These strategies include adapting protective coatings for the deformation of the stents, preparing rapid endothelialization coatings to enhance the service environment of the stent, and constructing coatings with self-healing functions. It is hoped that this review can help to understand the development of magnesium alloy cardiovascular stents and solve the problems related to magnesium alloy stents in clinical applications at the early implantation stage.

To achieve a fast testing on barrier properties of organic coatings, immersion test, AC-DC-AC test, and coupled test of AC-DC-AC with hydrostatic pressure were conducted in seawater for a glass flake epoxy coating. Electrochemical impedance spectroscopy (EIS) was used to characterize the degradation processes of the coating during the tests, and the surface of the coating was analyzed using optical microscope, scanning electron microscope (SEM) and Fourier transform infrared spectrometer (FTIR). The results show that the periodically cathodic polarization coupled with high hydrostatic pressure can accelerate the degradation of the coating by facilitating the diffusion and uptake of electrolyte and the delamination of the coating. The coupled test method has the largest acceleration due to the synergetic effect of AC-DC-AC and hydrostatic pressure.

Despite their anti-icing ability, hydrophobic coatings have the disadvantages of easy falling off and poor wear resistance, resulting in insufficient durability of ice/snow melting. To improve the surface stability and durability of superhydrophobic coatings, nanoparticle/epoxy coatings were prepared with three types of nanoparticles, two types of dispersion methods, three types of application methods and two types of introduction methods of epoxy resin. Water contact angles, ice adhesion force and icing rate of asphalt concrete coated with hydrophobic coatings were tested. The molecular structures of coatings were analyzed by Fourier transform infrared spectroscopy. The surface morphology of hydrophobic coatings was observed using Scanning electron microscopy. Results indicated that nano-ZnO, TiO2 and SiO2 particles can be modified into hydrophobicity by stearic acid. The hydrophobic coating could improve the hydrophobicity of concrete, reduce the adhesion strength of ice and asphalt concrete and delay the beginning icing time. Moreover, The dosages of stearic acid, nanoparticle and epoxy resin need to be in a certain range to ensure the best hydrophobicity and durability of coatings.

To prepare an edible coating with a good preservative effect on sweet cherries, carboxymethyl chitosan (CMCS) and gelatin (GL) were selected as the film-forming matrix in this experiment, and CaCl2 and ascorbic acid (AA) were added as crosslinking agents and antioxidants, respectively. First, the film was prepared by the casting method, and the film formula with better mechanical and barrier performance was filtered out by one-factor and response surface optimization test, and the differences in the preservation effect of different film formulations (CMCS-GL, CaCl2- CMCS-GL, AA -CaCl2- CMCS-GL) on sweet cherries were compared. and then the different film formulations were compared. The difference in film formulation on the preservation effect of sweet cherries was investigated. The results showed that the optimal formulation for an edible film based on CMCS-GL with good performance was CMCS: GL (w:w)=2:1, with the additional amount of 1% glycerol, 2% CaCl2, 0.1% Tween-20, 2% AA, the tensile strength, elongation at break, oxygen permeability and water vapor permeability of the film obtained with this formula were: 16.28 MPa, 71.46%, 1.39×10-12 g- cm/(cm2-s-Pa), 5.10×10-11 cm3-cm/(m2-s-Pa), respectively. In the preservation of sweet cherries, all three film formulations effectively reduced the rotting rate and weight loss during storage while preserving the high hardness and skin color of the fruit. Among them, the formulation AA -CaCl2- CMCS-GL showed the best preservation effect and can be used as a new method for postharvest preservation of sweet cherries.

Cross flow heat exchangers are commonly used in the thermal industry to transfer heat from hot tubes to cooling fluid. To protect the heat exchanger tubes from corrosion and dust accumulation, microscale coatings are often applied. In this study, we present machine-learning models for predicting heat transfer from hot tubes with different micro-sized coatings to cooling fluid in a turbulent flow using computational fluid dynamics simulations. A dataset of approximately 1000 cases was generated by varying the coating coverage thickness of each tube, the inlet Reynolds number, fluid flow inlet temperature, and wall temperature of tubes. The machine-learning models were generated to predict the overall heat flow rate in the heat exchanger, and it was found that combining the features based on their importance preserved the accuracy of the models while maintaining all the relevant information. The simulation results demonstrate that the proposed method increases the coefficient of determination (R2) for the models. The R2 values for unseen data for Random Forest, K-Nearest Neighbors, and Support Vector Regression were 0.9810, 0.9037, and 0.9754, respectively, indicating the usefulness of the proposed model for predicting heat transfer in various types of heat exchangers.

MCrAlYHf bond coats are employed in jet and aircraft engines, stationary gas turbines, and power plants, which require strong resistance to oxidation at high temperatures. The oxidation behavior of a free-standing CoNiCrAlYHf coating was investigated in this study. Isothermal oxidation tests were performed in air at 1050 °C on the specimens with various levels of surface roughness to investigate the oxidation kinetics. X-ray diffraction, focused ion beam, scanning electron microscopy (SEM), and scanning transmission electron microscopy were used to characterize the surface oxides. The surface roughness was examined using a contact profilometer and SEM. An empirical model was proposed to elucidate the impact of surface roughness on the oxidation behavior based on the correlation between the surface roughness level and oxidation rates.

in this work formulations of "environmentally compatible" silicone-based antifouling synthesized in the laboratory and based on copper and silver on silica/titania oxides have been characterized, capable of replacing the non-ecological antifouling paints currently on the market. The texture properties and the morphological analysis of these powders with an antifouling action indicate that their activity is linked to the nanometric size of the particles and to the homogeneous dispersion of the metal on the substrate. The presence of two metal species on the same support limits the for-mation of nanometric species and therefore the formation of homogeneous compounds. The presence of the antifouling filler (specifically the one based on TiO2 and Ag) facilitates the achievement of a higher degree of cross-linking of the pure resin, and therefore a better compactness and completeness of the coating. This leads to a consequent better degree of adhesion to the tie-coat and therefore to the steel support used for the construction of the boats.

The synergistic effect of silicon and cerium addition on the oxidation resistance of pack cementation aluminide coating applied on Ni-based superalloy substrate was investigated. The effect of cerium and silicon on the scale morphology, oxidation behavior, and scale spallation tendency are discussed based on the experimental results, using X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy-dispersive X-ray analyses (EDX). In addition, the oxidation resistance was evaluated by measuring the weight of samples after each 16-hour cycle at 1100˚C for 50 cycles. The experiments indicated that silicon addition to aluminide coating improves the oxidation resistance through the formation of β-NiAl1-nSin and δ-Ni2Al3-nSin and δ-Ni2Si phases. Furthermore, the addition of 1% cerium to modified aluminide enhances the formation of the fine-grained microstructure of the β-NiAl and δ-Ni2Al3 and reduces the outward/inward diffusion of elements (so-called blocking effect) which significantly modifies the hot oxidation resistance. The addition of 2% cerium, owing to the distortion of the β-NiAl and δ-Ni2Al3 phases, strictly decreases the hot oxidation resistance and the coating is exfoliated after 450 h at 1100 °C. The cyclic oxidation tests showed that the samples containing 1% cerium and 6% silicon possess the highest hot oxidation resistance in which 2 mg/cm2 weight loss of Ce-Si-aluminide was reported after 800 h. This is attributed to the simultaneous effect of cerium and silicon during the deposition process which reduces the oxygen diffusion and reduces the growth rate of α-Al2O3 during oxidation tests. The α-Al2O3 oxidation layer morphology showed that finer grains are formed in samples containing optimum ratios of cerium and silicon which indicates that these elements improve the coating adhesion and oxidation resistance simultaneously.