The corrosion inhibition behavior of cetyl pyridinium chloride (CPC) on mild steel in 0.5 M H2SO4 solution was examined using measurement techniques such as Fourier Transform Infra-red Spectroscopy (FTIR), Field Emission Scanning Electron Microscopy (FESEM), and Atomic Force Microscopy (AFM). The studies were carried out within a 25°C temperature range. The surface morphology of the corroded steel samples was investigated using FESEM and AFM. The results show that cetyl pyridinium chloride (CPC), a mild steel corrosion inhibitor, effectively prevents corrosion in 0.5 M H2SO4 and, when present, increases corrosion resistance. CPC has a stronger inhibitory effect on mild steel. The FESEM and AFM images clearly show how surface morphology changes when additives are present. The weight loss results were confirmed by en-ergy dispersive X-ray (EDX) spectroscopy analysis, and a value of 98.54% was obtained from potentiodynamic polarization studies at 0.0077M CPC. CPC acts as an important corrosion in-hibitor.

Within the context of sustainable material development for the construction sector, this study explores the viability of panels composed of recycled newspaper-derived cellulose (9%), rice husk (14%), borax (15%), and polyvinyl acetate-based glue (62%). The methods employed involve water absorption and density tests, following ASTM C-1763 and C-303 standards. The fire resistance test conforming to the European standard UNE 23-725-90, and a mold growth test using AOAC 2002.11. The composite is prone to absorbing a significant amount of water when exposed to humid conditions. However, the incorporation of rice husk and borax can provide benefits such as improved moisture resistance compared to other cellulitic insulators, which may be advantageous in specific climates. Also, the developed composite has an intermediate density compared to other polymeric materials. This characteristic presents advantages in applications that demand a balance between strength and lightness. During the fire resistance tests, the samples with borax presented less fire propagation, and superficial damage compared with the specimens without borax. This is important, considering the fireproofing property, required in building materials. The presence of borax in the composite has an inhibitory effect on the growth of fungi and yeasts. These findings are consistent with previous research. Nevertheless, further research and testing are imperative to assess its viability and performance for commercial applications.

In this study, the impact of the addition of high-aspect-ratio nano-ettringite to photocurable epoxy acrylate resin was explored, with a specific focus on the changes observed in viscosity, shrinkage, tensile strength, and elongation at the break of composites formed. Herein, the nano-ettringite samples were modified using KH-570. The 3 wt% or 6 wt% KH-570-modified and unmodified nano-ettringite were dispersed into the resin by ultrasonic treatment in conjunction with mechanical stirring. The grafting effects of nano-ettringite onto KH-570 were analyzed through scanning electron microscopy (SEM), X-ray diffraction (XRD), thermogravimetric (TG) analysis, and Fourier transform infrared spectroscopy (FTIR). The results demonstrate that increased dosages of unmodified and modified nano-ettringite led to increased viscosity of the composite while reducing shrinkage. At the same dosage, the photocurable resin with modified nano-ettringite demonstrated a lower shrinkage and a higher tensile strength. Notably, when the amount of modified nano-ettringite was 3 wt%, the highest tensile strength of the composite was 64.61 MPa, presenting a 72.57% increase compared to the blank sample. Furthermore, the incorporation of modified nano-ettringite as a filler provides a new perspective for improving the performance of photocurable epoxy acrylate resin composites.

The commercial oxygen-free copper sheets were cold-rolled with reduction rates ranging from 20% to 87% reduction rate and annealed at 400, 500 and 600 °C. The microstructure and texture evolution during cold-rolling and annealing processes were studied using optical microscopy (OM), the scanning electron microscopy (SEM) and the electron back-scattered diffraction (EBSD). The results show that the deformation textures of {123} (S) , {112} (Copper) and {110} (Brass) were continuously enhanced with the increase of cold-rolling reduction. The orientations along the α-oriented fiber converged towards Brass and the orientation density of β fiber obviously increased when the rolling reduction exceeded 60%. The recrystallization texture was significantly affected by the cold-rolling reduction. After 60% cold-rolling reduction, Copper and S textures components gradually decreased and {011} recrystallization texture component formed with the increase of annealing temperature. After 87% cold-rolling reduction, a strong Cube texture formed and other textures were inhibited with the increase of annealing temperature. The strong Brass and S deformation texture was conducive to the formation of a strong Cube annealing texture. The density of annealing twin boundary decreased with the increase of annealing temperature, and more annealing twin boundaries formed in the oxygen-free copper sheets with the increase of cold rolling reduction.

In the article, the results of research on a NiTi alloy with a high nickel content (51.7 at.%), produced using the additive technology SLM method and subjected to isothermal aging after so-lution annealing, are presented. The study involved the determination of the sequence of phase transformations occurring using differential scanning calorimetry (DSC), and the determination of the temperature range of these transformations. In parallel, the phase composition was determined using the XRD method; hardness and the Young’s modulus were also determined. The analysis of the DSC results obtained indicates the following characteristic features of the NiTi alloy, which change with ageing time: (1) during cooling (from +1500C to -500C), the type of transformation changes from a one-step transformation after solution annealing to a two-step transformation after the ageing process over 1, 20 and 100 hours at 500°C; (2) during heating (from -500C to +1500C) for all the samples, regardless of the ageing time, only a one-step transformation from martensite M(B19’) to austenite A(B2) is observed; (3) the temperature at which the transformation starts increases with the ageing time, (4) the width of the total temperature range of the transformation M(B19’)  A(B2) during heating changes from large (∆T=49,7°C), after solution annealing, to narrow (∆T=19.3°C and ∆T=17.9°C after 20 h and 100 h of ageing) and, most importantly, (5) a comparison with literature data shows that, irrespective of the composition of the NiTi alloy and the manufacturing technology of the alloy samples (regardless of the fact whether this was traditional or additive technology), a sufficiently long ageing process period leads to the occurrence of the martensite  austenite transformation in the same temperature range.

Non-impregnated small pore graphite (NSPG) with the compact microstructure for using in molten salt reactors (MSR) was prepared by the novel process, and the pore diameter of the obtained graphite was reduced to ~800 nm. The irradiation evaluation of the prepared graphite was carried out by 7 MeV Xe26+ ion irradiation and the microstructural changes of the graphite were investigated with IG-110 as a comparison. The graphitization degree of NSPG was higher than that of IG-110, though it was not subjected to an impregnation process. Under low-dose ion irradiation (

Hydrogen storage in general is an indispensable prerequisite for the introduction of a hydrogen energy based infrastructure. In this respect, high-pressure metal hydride (MH) tank systems appear to be one of the most promising hydrogen storage techniques for automotive applications using proton exchange membrane (PEM) fuel cells. These systems bear the potential of achieving a beneficial compromise of comparably large volumetric storage density, a wide working temperature range, comparably low liberation of heat, and increased safety. The debatable term unstable metal hydride stands in the literature short for metal hydrides with high dissociation pressure at comparably low temperature. Such compounds may help to improve the merit of high-pressure MH tank systems. Consequently, in the last few years, some materials for possible on-board applications in such tank systems have been developed. This review summarizes the state-of-the-art developments of these metal hydrides, mainly including intermetallic compounds and complex hydrides and gives some guidelines for future developments. Since typical laboratory hydrogen uptake measurements are limited to 200 bar, a possible threshold for defining unstable hydrides could be a value of their equilibrium pressure of peq > 200 bar for T < 100°C. However, these values would mark a technological future target and most current materials, and those reported in this review, do not fulfill these requirements and need to be seen as current stages of development towards the intended target. For each of the aforementioned categories in the review, special care was taken not only to covers the pioneering and classical research, but also to portrait the current status and latest advances. For intermetallic compounds, key aspects focus on the influence of partial substitution on absorption/desorption plateau pressure, hydrogen storage capacity and hysteresis properties. For complex hydrides, the preparation procedures, thermodynamics and theoretical calculation are presented. Besides, challenges, perspectives, and development tendency of this field are also discussed.

Biochar is a carbonaceous material derived from the thermochemical conversion of biomass under oxygen-lean conditions. Its properties render it many applications in agriculture, environmental remediation, and catalysis. Commonly produced by pyrolysis under a nitrogen atmosphere, the biochar composition is influenced mainly by residence time, heating rate, and process temperature. The existing literature primarily assesses biochar properties, such as ultimate, proximate, calorific, porosity, and combustibility, generated under various thermo-conversion conditions. However, there is a notable lack of sufficient investigation and attention given to the practical application of biochar. This article seeks to bridge that gap by enhancing the comprehension of the necessary experimental assessment for specific biochar applications and proposing process optimization methods using Multi-Criteria Decision Analysis (MCDA). By delving into these aspects, the study offers a concise overview of biochar production and presents a comprehensive panorama based on articles and patents. Additionally, the research explores the physicochemical characterization techniques associated with biochar and its various applications in conjunction with MCDA. This comprehensive approach aims to uncover valuable insights that could further advance the practical and sustainable utilization of biochar in a wide range of fields.

The development of offshore wind farms requires robust bonding solutions that can withstand harsh marine conditions for the easy integration of secondary structures. This paper investigates the durability performance of two adhesives: Sikadur 30 adhesive and Loctite UK 1351 B25 for use in offshore wind environments. Tensile tests on adhesive samples and accelerated aging tests were carried out under a variety of temperature and environmental conditions, including both dry and wet conditions. The long-term effects of aging on adhesive integrity are investigated by simulating the operational life of offshore installations. The evolution of mechanical properties, studied under accelerated aging conditions, provides an important indication of the longevity of structures under normal conditions. The results show significant differences in performance be-tween the two adhesives, highlighting their suitability for specific operating parameters. It should also be noted that for both adhesives, their exposure to different environments (seawater, distilled water, humid climate) over a prolonged period has shown that i) Loctite adhesive has a slightly faster initial uptake than Sikadur adhesive, but the later reaches an asymptotic plateau with a lower maximum absorption rate than Loctite adhesive; and ii) a progressive deterioration in the tensile properties following an exponential function. Therefore, aging behavior results showed a clear correlation with Arrhenius' law, providing a predictive tool for the aging process. Thus, the aging process of the two adhesives follows Arrhenius kinetics.