Recently many researches of EOS (Electric Arc Furnace Oxidizing Slag) on application to construction industry have been carried out with increasing its production and limited reclamation site. EOS can be used as a fine aggregate for construction material, however, its engineering properties vary with the manufacturing process and producing district, causing a quality differences in material performance. In the work, EOS is obtained from steel manufacturing plants in South Korea and the engineering properties are evaluated for EOS and the cement mortar with EOS, respectively. From the tests, EOS is mainly made up of CaO, SiO₂, and FeO with 18.2% of larnite which has a crystal structure of β-C₂S with similar cement mineral. EOS mortar shows an increasing compressive strength with more EOS content, which is affected by a considerable amount of larnite (β-C2S) in EOS. The EOS based mortar with ERS (Electric Arc Furnace Reduction Slag) shows unsatisfactory results over the criteria for rate of change, which implies that more consideration must be taken for the usage of the mixed ERS and EOS for cement mortar due to swelling effect of ERS on dimensional stability.

Polyglycolic acid (PGA) is a promising polymer in the packaging field owing to excellent hydrolysis, heat resistance and gas barrier properties, but there are limited in application due to poor toughness. For this reason, a covalently bonded chain extender is introduced to increase compatibility with flexible polymers. However, covalent bonds are unfavorable for application to degradable plastics because of require a lot of energy for reverse reactions. Therefore, it is intended to effectively control the ductility of blending plastics by using a novel ionic chain extender having a relatively weaker non-covalent bond than the existing covalent bond. Polycaprolactone (PCL), which has biodegradability and flexibility, was selected as a blending polymer. For comparison, a covalently reactive chain extender (G-CE) and a non-covalently ionic chain extender (D-CE) were synthesized and compounded to blending plastics. Each chain extenders were improved the compatibility between PGA and PCL, and the ductility of the PGA/PCL blending plastics were greatly enhanced with non-covalently bonding D-CE than with covalently bonding G-CE. At this time, the ductility of PGA/PCL blending plastic without CE is 7.2%, the ductility of 10D with D-CE is 26.6%, and the ductility of 10G with G-CE is 18.45%. Therefore, it was confirmed that the novel ionic chain extender inducing non-covalent bonds improves the compatibility between PGA and PCL and is more advantageous in enhancing ductility through a reversible reaction.