The flux growth of InVO4 bulk single crystals has been explored for the first time. The reported eutectic composition at a ratio of V2O5:InVO4 = 1:1 could not be used as a self-flux, since no sign of melting was observed up to 1100 °C. Crystals of InVO4 of typical size 0.5×1×7 mm3 were obtained using copper pyrovanadate (Cu2V2O7) as a flux, using Pt crucibles. XRD confirmed the orthorhombic Cmcm structure. Rests of flux material were observed on the sample surface, with occasional traces of Pt indicating some level of reaction with the crucible. X-ray absorption spectroscopy showed that oxidation states of indium and vanadium ions are +3 and +5, respectively. The size and high quality of the obtained InVO4 crystals makes them excellent candidates for the further study of their physical properties.

In this review, we summarize recent progress in crystal growth and understanding the influence of crystal structure on the superconductivity in pure and Pb-doped Bi2Sr2CuOy (Bi-2201) materials belonging to the overdoped region of high temperature cuprate superconductors. The crystal growth of Bi-2201 superconductors faces challenges due to intricate materials chemistry and lack of knowledge of corresponding phase diagrams. Historically, a crucible-free floating zone method has emerged as the most promising growth approach for these materials, resulting in high-quality single crystals. This review outlines the described in the literature and the authors' synthesis endeavors, encompassing Pb-doped Bi-2201 crystals, detailed structural characterization of as-grown and post-growth annealed samples, and highlights optimal growth conditions that yield large-size, single-phase, and compositionally homogeneous Bi-2201 single crystals.