In this study, additive manufacturing of reinforced parts using metallic wire as both a reinforcement component and a shape memory stimulus through Fused Deposition Modeling (FDM) was investigated. A Shape Memory Polymer (SMP) restores its original shape and recovers it upon specific stimuli. This research employed chromium-nickel metal wire as a reinforcing component to enhance mechanical properties and introduce the capability for thermal stimulation of polylactic acid (PLA) via electrical current using the "in-situ impregnation" method within FDM process. Reinforced specimens were fabricated with wire with two diameters of 0.1 and 0.15 mm, along with two volume percentages of 5 and 10. Comprehensive evaluations encompassing mechanical (tensile and flexural) and thermal properties of the printed specimens were conducted. The outcomes revealed a significant enhancement in both tensile and flexural properties of the polymer matrix due to the embedding metallic wire, even under elevated temperatures during bending test. Furthermore, the thermal properties of the reinforced specimens were examined by subjecting them to various voltages, resulting in temperature ranging from 36.4 to 150.1°C. These findings highlight the ability to tailor a wide range of mechanical properties and shape recovery in the reinforced specimens by carefully selecting the wire volume fraction, voltage, and wire diameter, thus regulating the materials properties with specific application requirements.

In this research, a screw-barrel system was designed and implemented, coupled with material extrusion, to print high-melt-temperature thermoplastic materials. The aim was to integrate two methods: the direct extrusion of thermoplastic polymer pellets with material extrusion,utilize various polymers in the form of pellets, especially high melt temperature ones, instead of traditional filaments. This addresses one of the significant challenges in filament preparation for various materials that are not readily available in the market or nearly impossible to fabricate (such as highly filled plastics). First, the screw-barrel assembly performance and factors influencing feed rate were evaluated. Subsequently, specimens were printed with polyether ether ketone (PEEK), an advanced plastic material known for its outstanding mechanical properties, high-temperature tolerance, and broad applications in various sectors, such as medical. Additionally, the material was reinforced with 2.5% continuous glass fibers while printing, which presented a novel product. Upon comparing theoretical values with experimental data from the tensile testing, a notable observation emerged: the inclusion of 2.5% glass fibers led to an approximate 43% increase in the tensile strength of the material. Furthermore, SEM images provided visual evidence of satisfactory adhesion between layers and fibers.

In this study, 3D printing of poly-l-lactic acid (PLLA) scaffolds reinforced with graphene oxide (GO) nanoparticles via Digital Light Processing (DLP) was investigated to mimic bone tissue. Stereolithography is one of the most accurate additive manufacturing method, but the dominant available materials used in this method are toxic. In this research, a biocompatible resin (PLLA) was synthetized and functionalized to serve the purpose. Due to the low mechanical properties of the printed product with the neat resin, graphene oxide nanoparticles in three levels (0.5, 1, and 1.5 Wt.%) were added with the aim of enhancing the mechanical properties. At first, the optimum post cure time of the neat resin was investigated. Consequently, all the parts were post-cured for three hours after printing. Due to the temperature-dependent structure of GO, all samples were placed in an oven at 85 ° C for different time periods of 0, 6, 12, and 18 hours to increase mechanical properties. The compression test of heat treated samples reveals that the compressive strength of the printed parts containing 0.5,1, and 1.5 % of GO increased by 151,162 ad 235%, respectively. Scaffolds with the designed pore sizes of 750 microns and a porosity of 40% were printed. Surface hydrophilicity test was performed for all samples showing that the hydrophilicity of the samples increased with increasing GO percentage. The degradation behavior of the samples was evaluated in a PBS environment, and it revealed that by increasing GO, the rate of component degradation increased, but the heat treatment had the opposite effect and decreased the degradation rate. Finally, besides improving biological properties, a significant increase in mechanical properties under compression can introduce the printed scaffolds as a suitable option for bone implants.

In this study, an optimized multi-material system was designed and developed to print samples in various applications, including biomedical fields (e.g., mandibular bone loss). To improve the mechanical and biological properties of scaffolds utilized for dental bone loss applications, a multi-material setup was devised, which employs digital light processing technology. This setup consists of a linear system comprising two resin vats and one ultrasonic cleaning tank, enabling the integration of diverse materials and structures to optimize the composition of the scaffold. This approach was used to print multi-material PLLA scaffolds containing 20 wt.%. HA on the interior side, and PLLA containing 1 wt.% GO on the exterior surface of the scaffold, which were evaluated mechanically and biologically after printing. The scaffold was designed using a triply periodic minimal surface (TPMS) lattice structure, which is known to possess favorable mechanical and biological properties. Various multi-material samples were successfully printed and evaluated to illustrate the multiple-material setup's potential for ensuring proper function, cleaning, and adequate interface bonding. By numerically evaluating several TMPS structures, a novel Gyroid TPMS scaffold with a nominal porosity of 50% was developed and validated experimentally. The biological properties of the scaffolds were also evaluated, including surface morphology, (3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide) MTT assay, and cell adhesion. Based on the results, multi-material components with the least contaminations with suitable mechanical and biological properties were successfully printed. By combining PLLA-HA and PLLA-GO, this innovative technique holds tremendous potential for enhancing the effectiveness of regenerative procedures in the field of dentistry.