Bi0.5Na0.5TiO3-0.06BaTiO3 (BNT-BT) thin films were prepared by both chemical solution (CSD) and pulsed laser deposition (PLD). The microstructure, dielectric, and ferroelectric properties were investigated. High stability of the dielectric permittivity (∆ɛ/ɛ(150 °C) ≤ ± 15%) over a wide temperature range from room temperature to 300 °C was obtained. Distinctly, the CSD film showed high TCC stability with variation of ± 5% up to 250°C. Furthermore, the CSD film showed an unsaturated ferroelectric hysteresis loop characteristic of the ergodic relaxor phase, however the PLD one exhibited almost saturated loop signature of the coexistence of both ergodic and non-ergodic states. The energy storage properties of the prepared films were determined using the P–E loops obtained at different temperatures. The results showed that these films exhibit stable and improved energy storage density comparable to the ceramic capacitors. Moreover, the CSD film exhibited more rigidity and better energy storage density that exceeds 1.3 J/cm3 under low applied field of 317 KV/cm as well as interesting efficiency in a large temperature range. The obtained results are very promising for energy storage capacitors operating at high temperatures.

Bismuth sodium titanate thin films (BNT) were deposited on Pt/SiN substrates by Sol-Gel spin coating technique under O2 atmosphere. Microstructural, structural, and electrical properties of the obtained film were investigated. Scanning electron microscopy and atomic force microscopy micrographs were used to analyze the microstructure of the films. Furthermore, EDX analysis revealed a Na-deficient composition for the obtained film. X-ray diffraction and Raman spectroscopy allowed the identification of a pure perovskite BNT phase. Dielectric, ferroelectric, and leakage current measurements revealed good frequency stability of the dielectric constant and dielectric losses for BNT thin film. The results are discussed in terms of Na-deficiency effects on the defect structure of BNT. Further, the film showed attractive electrostatic energy storage properties with energy density that exceeds 1.04 J/cm3 under E = 630 kV/cm.

The effect of ferromagnetic CaMnO3 (CMO) addition on structural, magnetic, dielectric, and ferroelec-tric properties of BiFeO3 are presented. X ray diffraction and Raman investigation allowed the identifi-cation of single pseudo cubic perovskite structure. The magnetic measurement showed that the pre-pared films exhibit a ferromagnetic behavior at low temperature with both coercive field and remnant magnetization increased with increasing CMO content. However, a deterioration of magnetization was observed at room temperature. Ferroelectric study revealed an antiferroelectric like behavior with a pinched P-E hysteresis loop for 5%CMO doping BFO resulting in low remnant polarization and double hysteresis loops. Whereas, high remnant polarization and coercive field with a likely square hysteresis loop are obtained for 10 % CMO addition. Furthermore, a bipolar resistive switching behavior with a threshold voltage of about 1.8V is observed for high doped film that can be linked to the ferroelectric polarization switching.

The purpose of this research work was to synthesis bio-derived nanocomposite films by incorporating Na0.5Bi0.5TiO3 (NBT) nanoparticles into Chitosan matrix. The NBT nanoparticles were synthesized using a traditional solid-state technique. Then, through a solution casting approach, flexible composite films were fabricated using Chitosan polymer. The morphology and structural assessments were carried out utilizing scanning electron microscopy (SEM), X-ray diffraction and fourier transform infrared technique. The SEM micrographs showed that NBT nanoparticles were randomly distributed and interconnected with other particles, forming interconnected grains with substantial interspaces within the matrix. The spectral response between 300 and 800 nm of the composites is mainly governed by light scattering of NBT particles with diameter sizes in the 100 - 400 nm range and the bandgap of the NBT phase. The dielectric studies demonstrated that the composite films exhibited higher dielectric values compared to the pure Chitosan film. Besides, the increase of NBT amount was found to increase the dielectric values. Additionally, local piezoelectric measurements reveal the expected piezoelectric and ferroelectric behavior for the NBT particles dispersed into the polymer matrix, as locally probed by Piezoresponse Force Microscopy. The studied system bears interest for advanced biocompatible opto- and piezo-electric materials.

NiV2O6 thin films were grown on glass slides with varying thicknesses using the nebulizer spray pyrolysis. The impact of thickness on the thin films' optical, structural, morphological, and electrical characteristics was systematically investigated. The X-ray diffraction and micro-Raman analysis confirmed the formation of the triclinic NiV2O6 system. Surface morphology and roughness variations in the as-deposited NiV2O6 films were studied using scanning electron microscopy (SEM) and a profilometer. Optical properties, including optical band gap (Eg), extinction coefficient (k), absorption coefficient (α), and refractive index (n), were determined through optical reflectance and transmittance measurements. The optical energy gap of the as-deposited NiV2O6 films decreased from 2.3 eV to 1.9 eV with increased layer thickness. Furthermore, the photo-detectivity of the films demonstrated an enhancement corresponding to the prolonged spray time. The sensitivity values obtained for visible irradiation are 328, 511, and 433 for samples S1, S2, and S3, respectively. The obtained results are imputed to the specific porous microstructure.

The beneficial effects of Lanthanide incorporation into 0.94Na0.5Bi0.5TiO3-0.06BaTiO3 (BNT-BT) matrix on its functional properties were investigated. The conventional solid-state method was used for synthesizing samples. The structural refinement revealed that all samples crystallized in R3c rhombohedral symmetry. Raman spectroscopy study was carried out using green laser excitation and revealed that no clear perceptible variation in frequency is observed. Dielectric measurements unveiled that the introduction of rare earth obstructed the depolarization temperature promoted in BNT-BT with decreasing the diffusive phase transition with increasing the lanthanide size. Only Dysprosium addition showed comparable diffusion constant and dielectric behavior as the unmodified composition. Further, the comparison of the obtained ferroelectric hysteresis and strain-electric field loops revealed that only Dy-phase exhibited interesting properties comparing parent composition. In addition, the incorporation of lanthanides Ln3+ into the BNT-BT matrix led to the development of luminescence characteristics in the visible and near infrared regions, depending on the excitation wavelengths. The simultaneous occurrence of photoluminescence and ferroelectric/piezoelectric properties opens up possibilities for BNT-BT-Ln to exhibit multifunctionality in a wide range of applications.Keywords: Sodium Bismuth Titanate; structural refinement; dielectric properties; ferroelectric properties; piezoelectric properties; Photoluminescence.