In this work, we have studied microstructure and unusual ferromagnetic behavior in cobalt (Co)-implanted epitaxial tin dioxide (SnO2) films. The study was aimed to provide a comprehensive understanding of the interplay between cobalt implant distribution, crystal defects, such as oxygen vacancies, and magnetic properties in Co-implanted SnO2 films, which has potential applications in spintronics and memristor devices. The scanning electron microscopy (SEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), vibrating sample magnetometry (VSM), differential thermo-magnetic analysis (DTMA), and ferromagnetic resonance (FMR) were employed for investigations of SnO2 films implanted with 40 keV Co+ ions at room or the elevated temperatures of substrate. The experimental data showed that the Co ion implantation with high fluence of 1.0 1017 ions/cm2 induces significant changes in the microstructure of SnO2 films, leading to the appearance of ferromagnetism with the Curie temperature significantly above room temperature. Strong influence of implantation temperature and subsequent high-temperature annealing in air or in vacuum on magnetic properties of Co-implanted SnO2 films were established. Moreover, the chemical effect of ethanol on FMR spectra were observed. The obtained results are discussed within the model of two magnetic layers with different concentration and valence states of the implanted cobalt and with high content of oxygen vacancies.

The fusion of surface-modified steel with tungsten carbide (WC) and NiCrBSi powder through laser metal deposition has emerged as a formidable strategy for fortifying components against wear and corrosion in extreme operating environments. Meticulous selection of WC content, innovative pre-alloying techniques, and precise control of laser metal deposition profoundly influence the mechanical properties and microstructural evolution of WC-NiCrBSi coatings applied to surface-enriched commercial alloy steel (805M2, 832M13, and 827M40). These tailored coatings exhibit exceptional resilience, ideal for harsh industrial settings in Oil and gas drilling, petrochemical, and Mining sectors. Advanced materials testing techniques, including scanning electron microscopy, light optical microscopies, and microhardness testing, unveil the innate hardness attributes, with findings highlighting the unassailable fortitude of the Mixed matrix layer's side face. The amalgamation of these testing methodologies with laser metal deposition promises an unparalleled path to extend the operational lifespan of critical components in challenging working conditions. The research horizon for WC-NiCrBSi coatings remains broad, with the potential to enhance durability, operational efficiency, and cost-effectiveness across diverse applications.

This research program investigated the effects of layer thickness (50 and 100 microns) on the microstructure and mechanical properties of electron beam powder bed fusion (EBPBF) additive manufacturing of Inconel 625 alloy. The as-built 50 and 100 micron layer thickness components were also heat treated at temperatures above 1100 oC, which produced a recrystallized grain structure containing annealing twins in the 50 micron layer thickness components, and a duplex grain structure consisting of islands of very small equiaxed grains dispersed in a recrystallized, large-grain structure containing annealing twins. The heat treated component microstructures and mechanical properties were compared with the as-built components in both the build direction (vertical) and perpendicular (horizontal) to the build direction. Vickers microindentation hardness (HV) values for the vertical and horizontal geometries averaged 227 and 220 for the as-built 50 and 100 micron layer components, and 185 and 282 for the corresponding heat treated components. The yield stress values were 387 MPa and 365 MPa for the as-built layer horizontal and vertical 50 micron layer geometries, and 330 MPa and 340 MPa for the as-built 100 micron layer components. For the heat treated 50 micron components, the yield stress values were 340 and 321 MPa for the horizontal and vertical geometries, and 581 and 489 MPa for the 100 micron layer components, respectively. The elongation for the 100 micron layer as-built horizontal components was 28% in contrast to 65% for the corresponding 100 micron heat treated layer components, an increase of 132% for the duplex grain structure. However, the coarse grains containing annealing twins and the equiaxed small grain islands in the duplex structure for the heat treated components contained continuous carbides in the grain boundaries, and this may indicate sensitization and a reduction in corrosion resistance. These findings point to the potential mechanical property advantage for heat treatment of Inconel 625 alloy 100 micron layer thickness components fabricated by EBPBF.

The article presents results of research consisting in an attempt to assess the influence of temperature, heating time and cooling method on microstructure and residual strength properties of steel previously tempered during the production process. Simulated environmental conditions to which high-strength bolts, commonly used in steel construction, were subjected, were intended to reflect conditions of a natural fire that may occur in public facilities where the obligation to ensure safety of users and rescue teams is of key importance, also required by law. Furthermore, the tests carried out also comprised a simulated effect of a rescue and firefighting operation using shock, rapid cooling of some of the heated bolts. Samples cut out from the tested bolts, after they were properly prepared, were subjected to microstructural tests using light microscopy, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), phase analysis with the use of an X-ray diffractometer (XRD) and quantitative analysis of the microstructure involving, inter alia, measuring the surface area of grains, their equivalent diameter and mean diameter. As a result of the tests, considerable microstructure changes were identified occurring in the bolt material as a result of exposing it to fire conditions, leading to a change in key, from the point of view of structural safety, mechanical properties. The results of the microstructure tests were compared with the results of previous strength tests, including hardness of the material after the heat treatment and the residual tensile strength of the material Rm. A conducted comparative analysis showed a significant effect of all such factors as the temperature level of the simulated fire, its duration and the fire-fighting method on the mechanical properties of bolts. Results obtained were provided with required comments and the concept of using the microstructure for the post-fire assessment of steel structures was referred to.

Poly(hydroxyalkanoates) (PHAs) are currently considered competent candidates to replace traditional plastics in several market sectors. However, commercial PHA grades exhibit unsatisfactory smell that can negatively affect the quality of the final product. The cause of this typical rancid odour is attributed to oxidized cell membrane glycolipids, coming from Gram negative production strains, which remain frequently attached to PHAs granules after extraction. The aim of this research is the development of customised PHA nano-biocomposites for industrial applications containing organo-modified nanoclays with high adsorption properties able to capture volatile compounds responsible of the displeasing fragrance in PHAs. To this end, a methodology for the detection and identification of the key volatiles released due to oxidative degradation of PHAs has been established using a headspace solid-phase microextraction technique. We report the development of nine nano-biocomposite materials based on three types of commercial PHA matrices loaded with three species of nanoclays which represent a different polar behaviour. It has been demonstrated that although the reached outcome effect depends on the volatile nature, natural sepiolite (T2) might result in the most versatile candidate for all PHA matrices selected.

A facile and environmentally benign method for a single-phase barium titanate synthesis in water vapor medium was studied to reveal the mechanism of phase transformation of the initial simple oxides mixture and estimate the capability of the product to be used as a raw material for low-frequency dielectric ceramics. The composition and structure of the reaction mixture treated in vapor at 130…150 °C as well as 230 °C for various time were investigated by means of XRD, SEM, HRTEM, EDX, and FTIR methods. The kinetics of the occurring phase transformation was described by Johnson-Mehl-Avrami-Erofeev equation. The reaction between the initial oxides was considered as a topochemical process with an apparent activation energy of 74…80 kJ mol^-1. A crucial role in this process belonged to the water vapor medium, which facilitated the generation of the reaction zone and its spreading inward the solid particles. The synthesized tetragonal barium titanate powder (mean particle size of 135 ± 24 nm) was sintered by a conventional technique at 1250 °C to obtain ceramics with grains of about 2 μm. Capacitance measurements performed a dielectric constant and loss tangent of ceramics, which reached 3879 and 6.7 10^-3, respectively, at 1 kHz and room temperature.

Engineering application of additively manufactured (AM) metallic materials is quite limited by their fatigue behaviors which are very inconsistent with that of conventionally wrought or cast ones. Here, based on advanced material characterization techniques, such as focused ion beam (FIB), scanning electron microscopy (SEM) and transmission electron microscopy (TEM), the mi-crostructures underneath fracture surfaces were thoroughly investigated in an AM aluminium (AlSi10Mg) alloy with horizontal and vertical building orientation endured very-high-cycle fa-tigue (VHCF) loading under stress ratios R = –1, 0 and 0.5. Two VHCF failure specimens A and B were representatively selected to further SEM examine and TEM samples preparation via FIB milling. Specimen A was horizontally printed and failed at R = –1; specimen B was vertically printed and failed at R = 0. TEM samples A1 and B1 were lifted from locations near the crack ini-tiation sites on the fracture surfaces of specimens A and B; The locations of TEM samples A2 and B2 kept away from the crack origin sites but still within the “fish-eye” region of crack steady growth. TEM observations show that there was no characteristic microstructure induced by VHCF in different oriented specimens and under various R values.