Structural and morphological properties of the hydronium-potassium jarosite microstructures were investigated in this work, and their electrical properties were evaluated. All microstructures were synthesized at a reasonable temperature of 343 K with a reduced reaction time of 3 hours. Increase in the pH from 0.8 to 2.1 decreased the particle sized from 3 µm to 200 nm and increasing the aging time from 0, 3 to 7 days resulted in semispherical, spherical and euhedreal jarosite structures, respectively. A Rietveld analysis also was done, finding that increasing pH, the amount of hydronium substitution by potassium in the cationic site also increases, having a 77.72 % of hydronium jarosite (JH) plus 22.29 % potassium jarosite (JK) at pH 0.8; 82.44 % (JH) and 17.56 % (JK) at pH 1.1, and 89.98 % (JH) plus 10.02 % (JK) at pH 2.1. The results obtained in this work show that the obtained hydronium potassium jarosite microstructures with reduced particle size and euhedreal morphology can be used as anode materials for improving the life time of lithium ion batteries, due that during the analysis of the voltage obtained using electrodes made with this particles and graphite, this ranged from 0.89 to 1.36 V.

This report aimed to know the performance of local mineral-based composite ceramic. The materials used consist of Indonesian local minerals, which are jarosite and manganite minerals as sources of oxide iron and Mangan. The materials were synthesized using the precipitation method, whereas composite ceramic was fabricated using a screen printing method and fired at 600 oC using a furnace. The results of the characterizations indicate that the sample forms three phases on diffraction peaks. The differences in the resistance values in ambient and ethanol environments indicate that the sample has very different responses. The high porosity of the sample greatly support the gas adsorption process. Thus, the sample has a high level of sensitivity. With the above characteristics, the composite ceramic which was fabricated has the potential to be applied to gas sensors, especially ethanol gas sensors.

Arsenic, an element of environmental impact, can be incorporated into jarosite–type compounds and remain stabilised within the structure under a wide range of environmental conditions. In this study, a sample of ammonium–arsenic jarosite was synthesised by precipitation in sulphate medium at controlled pH of 1.2–1.8. The behaviour of arsenic during the thermal and chemical decomposition of jarosite was analysed; the degradation in alkaline medium of jarosite was also studied. According to the results, the synthesised jarosite is composed of joined rhombohedral crystals, forming tightly spherical shaped particles, 37–54 μm size. The ammonium jarosite produced possessed a high arsenic concentration; its calculated stoichiometry being (NH₄)Fe_2.45[(SO₄)_1.80(AsO₄)_0.20][(OH)_4.15(H₂0)_1.85]. It was found that arsenic is stabilised in the jarosite structure; upon heating, it remains in residual solids above 700°C, whilst in alkaline medium an incongruent dissolution takes place, with the arsenic retained in the solid phase along with iron. These solids, when exposed to high temperatures (1200°C), transform into a type of iron oxide known as hematite, so with arsenic it is retained an iron compound forming a stable compound which withstands high temperatures.