The manufacturing parameters influence the properties of thermo-mechanically processed met-als such as Mg alloys. This paper presents how the mechanical properties, the microstructure and the degradation rate of extruded Mn-containing Mg-Gd-alloys can be modified. Gd as repre-sented REE-element is particularly interesting due to the influence on the texture development in Mg and therefore studied as a base alloy system. The contents of Gd were investigated be-tween 2 to 9 wt.% with Mn-addition of 0.5 and 1.0 wt.%. The grain sizes and the corresponding textures were modified by the extrusion parameters and the alloy content. It was shown that modification by Mn can decrease the grain size, but increase the degree of recrystallization and decrease the degradation rate in the biological medium compared to the binary Mg-Gd system from previous studies. The results suggest that the binary Mg-Gd system can be produced more efficiently by adding Mn and that the resulting properties are more robust.

The type of implant at the fracture site has effects not only from biological perspective but also from mechanical perspective in fracture healing. Biodegradable implants such as magnesium (Mg) based alloys have shown faster secondary bone healing properties as compared to bioinert implants such as titanium (Ti). The general reasoning behind this is the benefit of Mg from biocompatibility perspectives. We study the effect of Ti and Mg as base materials for implants with their different mechanical properties. The focus of our work is on the displacements at the fracture site of the tibia and their influence on the stimulus for bone healing. We have found that in comparison to Ti, Mg implants have minimal stress shielding problem, only which led to better mechanical stimulus at the fracture site.

Magnesium-silver alloys are of high interest for the use as temporary bone implants due to their antibacterial properties in addition to biocompatibility and biodegradability. Thin wires in particular can be used for scaffolding, but the determination of their degradation rate and homogeneity using traditional methods is difficult. Therefore, we have employed 3D imaging using X-ray near-field holotomography with sub-micrometer resolution to study the degradation of thin (250 μm diameter) Mg-2Ag and Mg-6Ag wires. The wires were studied in two states, recrystallized and solution annealed to assess the influence of Ag content and precipitates on the degradation. Imaging was employed after degradation in Dulbecco’s modified Eagle’s medium and 10% fetal bovine serum after 1 to 7 days. At 3 days of immersion the degradation rates of both alloys in both states were similar, but at 7 days higher silver content and solution annealing lead to decreased degradation rates. The opposite was observed for the pitting factor. Overall, the standard deviation of the determined parameters was high, owing to the relatively small field of view during imaging and high degradation inhomogeneity of the samples. Nevertheless, Mg-6Ag in the solution annealed state emerges as a potential material for thin wire manufacturing for implants.