In-situ observation on the austenite grain growth and martensite transformation in a developed NM500 wear-resistant steel were conducted on a Confocal Laser Scanning High-temperature Microscope (CSLM). Results indicated that the martensite nucleation did not synchronously proceed during quenching process. The selective prenucleation dominated in martensite nucleation, which dividing untransformed austenite into several regions, and resulting in the larger size of fresh martensite. Martensite can not only nucleate at parent austenite grain boundaries, but also nucleate in the preformed martensite laths and twins. Smaller constraint in the martensite growth was achieved in a larger parent austenite grain size, leading to the longer fresh martensite and secondary martensite. Besides, the transformation kinetics of martensite was accelerated in a higher quenching temperature. Moreover, the martensitic laths presented in parallel laths (0~2°) based on the pre-formed lath or distributed in triangle, parallelogram or hexagon with an angle of 60° or 120°. Interestingly, martensitic lath also traversed the unstable new parent austenitic grain boundaries. In addition, the size of austenite grains increased with the quenching temperature, and austenite grains coarsened in a short time at a higher quenching temperature of 1160 ℃. Furthermore, a large amount fine dispersed particles redissolved and ripped at 1160 ℃, resulting in the many large and visible carbonitrides.

Martensitic steels are used at a wide range of strength levels in environments which expose them to hydrogen or water vapor over a large range of partial pressures and temperatures. Hydrogen can cause catastrophic failures under many seemingly benign conditions. The effect of hydrogen on the dimension stability of high strength martensitic steels under such conditions has been poorly understood, and existing models do not seem to adequately account for it. Experiments were conducted to measure the variation in volume due to the uptake of hydrogen of such steels under near-ambient conditions, and the results were compared to theoretical estimates derived from the density of defects acting as hydrogen traps. Based on these results a new model for hydrogen embrittlement was developed. The hydrogen lattice dilation (HLD) model isolates volume expansion as a primary driver of hydrogen embrittlement. It provides and distinguishes two modes of failure acceleration: the fast, brittle, stress-intensity independent cracking under higher static crack loading, and a slower, highly stress-intensity dependent tearing mode at lower stress intensity. The relationship between the two is explained, as is how hydrogen absorption by defects accounts for the crack threshold and crack velocity of each.

Temper embrittlement is a major challenge encountered during the heat treatment of high-performance steels for large forgings. This study investigates the microstructural evolution and mechanical properties of Cr-Ni-Mo-V thick-walled steel, designed for new large forgings with a tensile strength of 1500 MPa, under different tempering cooling rates. Optical microscopy (OM), scanning electron microscopy (SEM), and electron backscatter diffraction (EBSD) were employed to analyze the microstructural features. The results demonstrate that the embrittlement occurring during air cooling after tempering is attributed to the concentration of impurities near Fe3C at the grain boundaries. The low-temperature impact toughness at -40°C after water quenching reaches 29 J due to the accelerated cooling rate during tempering, which slows down the diffusion of impurity elements towards the grain boundaries, resulting in reduced concentration and dislocation density, and increased stability of the grain boundaries, thereby enhancing toughness. the bainite content decreases and the interface between martensite and bainite undergoes changes after water quenching during tempering. These alterations influence the crack propagation direction within the two-phase microstructure, further modifying the toughness. These findings contribute to the understanding of temper embrittlement and provide valuable guidance for optimizing heat treatment processes to enhance the performance of high-performance steels in large forgings.

Current conventional methods of evaluating microstructures are characterized by a high degree of subjectivity and a lack of reproducibility. Modern machine learning (ML) approaches have already shown great potential in overcoming these challenges. Once trained with representative data in combination with an objective ground truth, the ML model is able to perform a task properly in a reproducible and automated manner. However, in highly complex use cases, it is often not possible to create a definite ground truth. This study addresses this problem using the underlying showcase of microstructures of highly complex quenched and quenched and tempered (Q/QT) steels. A patch-wise classification approach combined with a sliding window technique provides a solution for segmenting entire microphotographs where pixel-wise segmentation is not applicable due to the problem of reproducibly creating unambiguous training masks. Using correlative microscopy, consisting of light optical microscope (LOM) and scanning electron microscope (SEM) micrographs as well as corresponding data from electron backscatter diffraction (EBSD), a training dataset of reference states that covers a wide range of microstructures was acquired in order to train accurate and robust ML models. Despite the enormous complexity associated with the steels treated here, classification accuracies of 88.8% in the case of LOM images and 93.7% for high-resolution SEM images were achieved. These high accuracies are close to super-human performance, especially in consideration of the reproducibility of the automated ML approaches compared to conventional methods based on subjective evaluations through experts.

This study characterizes the microstructure and its associated crystallographic features of bulk maraging steels fabricated by selective laser melting (SLM) combined with a powder bed technique. The fabricated sample exhibited characteristic melt pools in which the regions had locally melted and rapidly solidified. A major part of these melt pools corresponded with the ferrite (alpha) matrix, which exhibited a lath martensite structure with a high density of dislocations. A number of fine retained austenite (gamma) with a <001> orientation along the build direction was often localized around the melt pool boundaries. The orientation relationship of these fine gamma grains with respect to the adjacent alpha grains in the martensite structure was (111) gamma // (011) alpha and [-101] gamma // [-1-11] apha (Kurdjumov–Sachs orientation relationship). Using the obtained results, we inferred the microstructure development of maraging steels during the SLM process. The results depict that new and diverse high-strength materials can be used to develop industrial molds and dies.

Conventional heat treatment is not capable of converting a sufficient amount of retained austenite into martensite in high-carbon or high-carbon and high-alloyed iron alloys. Cryogenic treatment induces the following alterations in the microstructures: (i) a considerable reduction in the retained austenite amount, (ii) formation of refined martensite coupled with an increased number of lattice defects, such as dislocations and twins, (iii) changes in the precipitation kinetics of nano-sized transient carbides during tempering, and (iv) an increase in the number of small globular carbides. These microstructural alterations are reflected in mechanical property improvements and better dimensional stability. A common consequence of cryogenic treatment is a significant increase in the wear resistance of steels. The current review deals with all the mentioned microstructural changes as well as the variations in strength, toughness, wear performance, and corrosion resistance for a variety of iron alloys, such as carburising steels, hot work tool steels, bearing and eutectoid steels, and high-carbon and high alloyed ledeburitic cold work tool steels.

Advanced high-strength steels (AHSS) have a wide range of applications in equipment safety and lightweight design, and enhancing the strength of AHSS to the ultra-high level of 2 GPa is currently a key focus. In this study, a new process of thermo-mechanical control process followed by direct quenching and partitioning (TMCP-DQP) is developed based on Fe-0.4C-1Mn-0.6Si (wt.%) low-alloy steel, and the effects of microstructure evolution on mechanical properties under TMCP-DQP process and conventional hot rolled quenched and tempered process (HR-QT) are comparatively studied. The results show that the TMCP-DQP process not only shortened the processing steps but also achieved outstanding comprehensive mechanical properties. The TMCP-DQP steel exhibits a tensile strength of 2.23 GPa, accompanied by 11.9% elongation and a Brinell hardness of 624 HBW, with an impact toughness of 28.5 J at -20 ℃. In contrast, the HR-QT steel exhibits tensile strengths ranging from 2.16 GPa to 1.7 GPa and elongations between 5.2% and 12.2%. The microstructure of TMCP-DQP steel primarily consists of lath martensite, containing thin-film retained austenite (RA), nanoscale rod-shaped carbides, and a minor number of nanoscale twins. The volume fraction of RA reaches 7.7%, with an average carbon content of 7.1 at.% measured by three-dimensional atom probe tomography (3DAP). Compared to the HR-QT process, the TMCP-DQP process results in finer microstructure, with a prior austenite grain (PAG) size of 11.91 μm, forming packets and blocks with widths of 5.12 μm and 1.63 μm. The TMCP-DQP process achieves the ultra-high strength of low-alloy steel through the synergistic effects of grain refinement, dislocation strengthening, and precipitation strengthening. The dynamic partitioning stage stabilizes the RA through carbon enrichment, while the relaxation stage reduces a small portion of the dislocations generated by thermal deformation, and the self-tempering stage eliminates internal stresses, all guaranteeing considerable ductility and toughness. The TMCP-DQP process may offer a means for industries to streamline their manufacturing processes and provide a technological reference for producing 2.2 GPa grade AHSS.

General derivation of the well-known Ren-Otsuka relation, 1/α (dTo)/dx=-α/β (where To, x, α and β(>0) are the transformation temperature, the composition, as well as the composition and temperature coefficient of the critical shear constant, c’, respectively) for shape memory alloys, SMAs, is provided based on the similarity of interatomic potentials in the framework of dimensional analysis. A new dimensionless variable, to(x)=(To (x))/(Tm (x) ), describing the phonon softening (where Tm is the melting point) is introduced. The dimensionless values of the heat of transformation, H, and entropy, S as well as the elastic constants c’, c44, A=c44/c' are universal functions of to(x) and have the same constant values at to(0) within sub-classes of host SMAs having the same type of crystal symmetry change during martensitic transformation. The ratio of (dto)/dx and α has the same constant value for all members of a given sub-class and relative increase of c’ with increasing composition should be compensated by the same decrease of to. In the generalized Ren-Otsuka relation the anisotropy factor, A appears instead of c’ and α as well as β are the differences of the corresponding coefficients for the c44 and c’ elastic constants. The obtained linear relation between h and to rationalizes the observed empirical linear relations between the heat of transformation measured by DSC (QAM) and the martensite start temperature, Ms.

To enhance the mechanical properties (i.e. strength and elongation) of the face-centered cubic (fcc) α-phase in the Au-Cu-Al system, this study focused on the introduction of the martensite phase (doubled B19 (DB19) crystal structure of Au2CuAl) via the manipulation of alloy compositions. Fundamental evaluations, such as microstructure observations, phase identifications, thermal analysis, tensile behavior examinations, and reflectance analysis have been conducted. The presence of fcc annealing twins was both observed in the optical microscope (OM) and the scanning electron microscope (SEM) images. Both the strength and elongation of the alloys were greatly promoted while the DB19 martensite phase was introduced into the alloys. Amongst all the prepared specimens, the 47Au41Cu12Al and the 44Au44Cu12Al alloys performed the optimized mechanical properties. The enhancement of strength and ductility in these 2 alloys was achieved while the stress plateau was observed during the tensile deformation. A plot of the ultimate tensile strength (UTS) against fracture strain was constructed to illustrate the effects of the introduction of the DB19 martensite phase on the mechanical properties of the alloys. Regardless of the manipulation of the alloy compositions and the introduction of the DB19 martensite phase, the reflectance stayed almost identical to pure Au.

A metastable β-Ti alloy, Ti–10V–3Fe–3Al (wt.%), was subjected to thermos-mechanical processing including the compression test at 725°C, which is below the β transus temperature (780°C), and at strain rate of 10-3s-1. The presence of phases was determined using transmission electron microscopy and X-ray diffraction. Although the dynamic recovery took place together with slip, both deformation-induced α˝ martensite and ω were detected as other operating mechanisms for the first time in metastable-β Ti alloys deformed in α+β region. The volume fraction of stress-induced α˝ was higher than that of the same alloy deformed at room temperature due to higher strain applied. Stress-induced twinning was not operational, which could be related to the priority of slip mechanism at high temperature resulted from thermally-assisted nucleation and lateral migration of kink-pairs.