At present, in the field of aviation industry, titanium alloy is mainly used to manufacture parts such as compressor disc, blade and casing of aircraft engine. When working, titanium alloy parts produce high temperature due to high-speed running friction, which makes the high temperature oxidation resistance and friction resistance of titanium alloy greatly reduced. When their working environment contains salt, titanium alloys are subjected to thermal corrosion, which limits their wider practical applications. This paper introduce the aluminide coating and its preparation methods. The characteristics and functional mechanism of three functional coatings for service environment, such as high temperature resistant alumina-based coating, thermal corrosion resistant alumina-based coating and wear-resistant alumina-based coating are summarized. Finally, the development direction of composite coatings of titanium and titanium alloys for complex service environment is prospected.

High temperature titanium alloys are widely used in aerospace hot parts, however, the thermal barrier temperature of 600 oC limits its service temperature. In this paper, a two-step hot-dip plating method is proposed to prepare the composite coating containing Ce on the surface of titanium alloy, which can make the oxidation resistance temperature of titanium alloy reach 800 oC The microstructure, phase composition and element distribution of Ce-containing Ti-Al-Si hot-dip coating, Ce-containing Ti-Al-Si pre-oxidation coating and Ce-containing Ti-Al-Si high-temperature oxidation coating were studied by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS), respectively. The results show that the Ti-Al-Si hot-dip coating containing Ce is mainly composed of (Ti,Ce)(Al,Si)3 alloy phase layer, and the Ti-Al-Si pre-oxidation coating containing Ce is mainly composed of Ti-Al binary system phase layer and dense Al2O3 layer rich in CeO2. Ce in the high temperature oxidation coating of Ti-Al-Si containing Ce is mainly distributed in Ti3Al, TiAl, TiAl3+Ti5Si3 mixed phase layer and Al2O3. The addition of Ce can promote the formation of continuous Al2O3 layer, improve the uniformity of composite coating, prevent the spread of cracks, and improve the high temperature oxidation resistance of Ti-Al-Si coating.