This work presents the production and incorporation of calcium hydrolyzed nano-solutions at three concentrations (1, 2, and 3 wt.%) in alkali-activated gold mine tailings (MTs) from Arequipa, Perú. A first activator solution of sodium hydroxide (NaOH) at 10M was used. The calcium hy-drolyzed nano-solutions acted as a secondary activator and as additional calcium resource for the alkali-activated materials (AAMs) based on the low-calcium gold MTs. High-resolution trans-mission electron microscopy/energy-dispersive x-ray spectroscopy (HR-TEM/EDS) analyses were carried out to characterize the morphology, size, and structures of the calcium hydrolyzed na-noparticles. Fourier transform infrared (FTIR) analyses then were used to understand the chemical bonding interactions in the calcium hydrolyzed nanoparticles and in the AAMs. Scanning electron microscopy/energy-dispersive X-ray spectroscopy (SEM/EDS) and Quantitative X-ray diffraction (QXRD) were performed to study the structural, chemical, and phase compositions of the AAMs; uniaxial compressive tests evaluated the compressive strength of the reacted AAMs; and Nitrogen adsorption-desorption analyses measured the porosity changes at nanostructure level in the AAMs. The results indicate that each increase in the concentration of the calcium hydrolyzed nano-solution had a direct/proportional effect on the mechanical properties of the AAMs samples. The AAMs with 3 wt.% calcium-hydrolyzed nano-solution had the highest compressive strength value of 15.16 MPa, which represented an increase of 62% compared to the original system without nanoparticles and aged under the same conditions of 70°C for seven days. These results provide useful information about the positive effect of calcium-hydrolyzed nanoparticles on gold MTs and their conversion into sustainable building materials through alkali activation.

The accumulation of microorganisms, plants, algae, or small animals on wet surfaces that have a mechanical function causes biofouling, which can result in structural or other functional deficiencies. The maritime shipping industry must constantly manage biofouling to optimize operational performance, which is a common and long-lasting problem. It can occur in any metal structure in contact or submerged in ocean water, which represents additional costs in terms of repairs and maintenance. This study is focused on the production of antifouling coatings, made with nanoparticles of copper selenide (CuSe) modified with gum arabic, within a water-base acrylic polymeric matrix. During the curing of the acrylic resin, the CuSe NPs remain embedded in the resin but this does not prevent the release of ions. The coatings presented to release copper and selenium ions for up to 80 days, selenium was the element that was released the most. The adhesion of film coatings to metallic substrates showed good adhesion, scale 5B (ASTM D3359 standard). Antimicrobial activity tests show that the coatings have an inhibitory effect on Escherichia coli and Candida albicans. The effect being more noticeable when the coating is detached from the substrate and placed on a growing medium, than compared to the coating on a substrate. Scanning electron microscopy (SEM) observations show that nanostructured CuSe coatings are made up of rod-shaped and spherical particles whose range ranges from 12 to 25 nm. The Energy Dispersive X-ray spectroscopy (EDS) studies showed that the ratio of selenium nanoparticles is greater than that of copper and that their distribution is homogeneous