Facile Synthesis of Di-Mannitol Adipate Ester-Based Zinc Metal Alkoxide As Bi-Functional Additives for PVC

A new di-mannitol adipate ester-based zinc metal alkoxide (DMAE-Zn) was synthesized as a bi-functional PVC thermal stabilizer for the first time. The materials were characterized with Fourier-transform Infrared spectroscopy (FT-IR) and thermogravimetric analysis (TGA). Characterization results confirmed the formation of Zn-O bonds in DMAE-Zn; and that DMAE-Zn had a high decomposition temperature and a low melting point. The thermal stability of DMAE-Zn on PVC also was tested by conductivity test, thermal aging test, and UV-visible spectroscopy (UV-VIS) test. PVC stabilized by DMAE-Zn had a good initial color and excellent long-term stability. UV-VIS also showed that the conjugated structure in PVC stabilized by DMAE-Zn was almost all of the triene, suggesting that the addition of DMAE-Zn would suppress the formation of conjugated structures above tetraene. Dynamic processing performance of PVC samples tested by torque rheometer indicated that, having a good compatibility with PVC chains in the amorphous regions, DMAE-Zn contributed good plasticizing effect to PVC. DMAE-Zn thus effectively demonstrates bi-functional roles, e.g., thermal stabilizers and plasticizers to PVC. Furthermore, FT-IR, HCl absorption capacity test, and complex ZnCl₂ test were also used to verify the thermal stability mechanism of DMAE-Zn for PVC.