Atomic Layer Deposition Grown Zinc-Oxide Based MIS-Type Schottky Barrier Diode

We report on the fabrication and electrical characteristics of zinc-oxide (ZnO) based metal-insulator-semiconductor (MIS) type Schottky barrier diodes (SBHs). ZnO thin layer on the p-type silicon substrate was fabricated by atomic layer deposition (ALD). The structure and surface properties of the thin film were characterized by X-ray diffraction (XRD), atomic force microscope (AFM) and secondary ion mass spectrometer (SIMS). The current-voltage (I-V) characteristics of Al/ALD-grown ZnO/p-Si diodes were measured under dark at room temperature. The electrical parameters such as ideality factor (n), series resistance (R_s) and barrier height (ϕ_b) of the diodes were analyzed using standard thermionic emission (TE) theory, Norde and Cheung method. The barrier height value obtained from I-V and Cheung method was found to be 0.73 eV and 0.76 eV, respectively. The interface state density (Dit) of the diodes was determined from the I-V characteristics. The nonideal behavior of measured parameters suggested the presence of interface states. The obtained results showed that the prepared diode can be used for NIR Schottky photodetector applications.