Orofacial injuries are common occurrences during contact sports activities; however, there is an absence of data regarding the performance of hybrid occlusal splint mouthguards, especially during compressive loading. To evaluate the total deformation and stress concentration, a skull model was selected and duplicated to receive two different designs of mouthguard devices: one model received a conventional custom-made mouthguard (MG) with 4-mm thickness and the other received a novel hybrid occlusal splint-mouthguard (HMG) with the same thickness. Both models were subdivided into finite elements. The frictionless contacts were used, and a nonlinear analysis was performed simulating the compressive loading in occlusion. The results were presented in von-Mises stress maps (MPa) and Total Deformation (mm). A higher stress concentration in teeth was observed for the model with the conventional MG, while the HMG design displayed a promising mechanical response with lower stress magnitude. The HMG de-sign displayed a higher magnitude of stress on its occlusal portion than the MG design. The hybrid mouthguard (HMG) reduced (1) jaw displacement during chewing and (2) the generated stresses in maxil-lary and mandibular teeth.

The Dutch Konik is valued from a genetic conservation perspective and also for its role in preservation of natural landscapes. The primary management objective for the captive breeding of this primitive horse is to maintain its genetic purity, whilst also maintaining the nature reserves on which they graze. Breeding selection has traditionally been based on phenotypic characteristics consistent with the breed description, and the selection of animals for removal from the breeding program is problematic at times due to high uniformity within the breed. With the objective of identifying an additional non-invasive selection criterion with potential uniqueness to the Dutch Konik, this study investigates the anatomic parameters of the distal equine limb, with a specific focus on the relative lengths of the individual splint bones. Post-mortem dissections performed on distal limbs of Dutch Konik (n = 47) and modern domesticated horses (n = 120) revealed significant differences in relation to the length and symmetry of the 2nd and 4th Metacarpals and Metatarsals. Distal limb characteristics with apparent uniqueness to the Dutch Konik are described which could be an important tool in the selection and preservation of the breed.

Printed oral splints are a therapeutic alternative in the treatment of functional disorders. Their mechanical properties are crucial to their clinical success and their performance can vary depending on cleaning, post-polymerization, or build orientation. This in vitro study aimed to compare the biaxial flexural strength of the chosen materials depending on the aforementioned parameters. 720 discs (n = 15 per group, 16 mm x 2 mm) were printed from splint materials. Printing was performed under 90°, 45°, or 0° orientation to the building platform with supporting structures. Specimens were either automatically or manually cleaned with isopropanol. Post-polymerization was performed with LED- or Xenon-light. Biaxial flexural strength (BFS) was determined with a piston-on-3-ball test after 24 hours or 60 days water storage (37°C). Test specimens were preloaded with 0.5 N and the load was applied by a piston of 1.6 mm in diameter at 1 mm/min crosshead speed. Statistics were performed by using descriptive statistics, ANOVA, and Levene-tests. Mean BFS after 24 hours of storage varied between 79 MPa and 157 MPa. After 60 hours the BFS significantly decreased and revealed values ranging from 72-127 MPa (mean24 113 MPa, mean60 97 MPa; p<0.001). No significant differences could be determined between the materials (p=0.103) or between the different cleaning procedures (p=0.321). Post-polymerization yielded higher means with LED- (P1: 115 MPa) than with Xenon-light (P2: 95 MPa; p<0.001). Regarding position, the mean values ranged from 101 MPa for 0°, 102 MPa for 45°, and 115 MPa for 90°, which was significantly different (p<0.001). Build orientation of 90° and post-polymerization with LED-light provided significantly higher biaxial flexural strength and should be used to guarantee optimal strength of splint materials. Aging decreased the biaxial flexural strength of the tested specimens.