A series of Zn-modified Hβ (Zn/Hβ) catalysts were prepared by using the different zinc precursors such as ZnSO4·7H2O, ZnCl2, C4H6O4Zn·2H2O and Zn(NO3)2·6H2O, and their catalytic performance in the ethanol conversion to propylene reaction was evaluated. Results indicate the amount and strength distribution of acid sites of the Zn/Hβ catalysts were easily tuned by employing different type of zinc precursors. More importantly, when the Zn species were introduced to the Hβ, the propylene yield was significantly enhanced, whereas the yields of the byproducts such as ethylene and C2-C4 alkanes were remarkably suppressed. For the catalyst prepared by using the ZnCl2 precursor (Zn/Hβ-C), a higher propylene yield up to 43.4% was achieved as a result of the moderate amount and distribution of acid sites. The average coking rate of the used Zn/Hβ catalysts strongly depended on the amount of total acid sites, especially the strong acid sites, i.e., the higher the amount of total acid sites of the catalyst, the greater the average coking rate. For the catalyst prepared by using the ZnSO4·7H2O precursor, Zn/Hβ-S exhibited a better stability even after depositing more coke, which is due to the higher amount of strong acid sites.

The conversion of CO2 into more synthetically flexible CO is an effective and potential method for CO2 remediation, utilization and carbon emission reduction. In this paper, the reaction of carbon-carbon dioxide (Boudouard reaction) was performed in a microwave fixed bed reactor using semi-coke (SC) as both the microwave absorber and reactant and was systematically compared with that heated in a conventional thermal field. The effects of the heating source, SC particle size, CO2 flow rate and additives on CO2 conversion and CO output were investigated. By microwave heating (MWH), CO2 conversion reached more than 99 %, while by conventional heating (CH), the maximum conversion of CO2 was approximately 29% at 900 °C. Meanwhile, for the reaction with 5 wt% Barium Carbonate added as a promoter, the reaction temperature was significantly reduced to 750 °C with almost quantitative conversion of CO2. Further kinetic calculations showed that the apparent activation energy of the reaction under microwave heating was 46.3 kJ/mol, which was only one-third of that observed under conventional heating. The microwave-assisted Boudouard reaction with catalytic barium carbonate is a promising method for carbon dioxide utilization.

The thermal degradation behaviour of 10:90 and 90:10 blends of Polyethylene Terephthalate (PET) and petroleum coke has been investigated using mechanical alloying (milling) at 300 rpm and for periods up to 1-10 hours. Milled specimens were characterised using SEM and x-ray diffraction; their thermal degradation behaviour was investigated using thermo-gravimetric analyser (TGA) for temperatures up to 1200°C. Whereas PET specimens showed a tendency towards flattening out and increased surface area during collisions in ball mills, petroleum coke particles tended to break down into smaller particles. 10:90 and 90:10 blends of PET and coke showed significant microstructural evolution with increasing speeds and time including fracture, strain hardening and re-welding. X-ray diffraction results showed clear evidence for increasing amorphous component in petroleum coke without much influence on PET crystallinity. Thermo-gravimetric results showed a significant increase in the overall degradation and much higher weight losses associated with mechanical alloying. This study has shown that mechanical alloying could be used to modify the degradation behaviour of coke/plastic blends and corresponding yield during pyrolysis with implications for plastic waste management.

In this study, graphite, the most stable form of carbon, was examined for its hexagonal crystalline structure with specific dimensions (ao=2.46 Ǻ; co=6.70 Ǻ). Its framework comprises parallel carbon atom planes forming regular hexagons (side length 1.415 Ǻ) and 120° angles between adjacent atoms. Two structural variations exist: hexagonal symmetry (1-2-1-2-1-2 planes) and rhomboidal symmetry (1-2-3-1-2-3 planes). The research aimed to produce high-density graphite utilizing carbonaceous raw materials. Graphite-based materials often exhibit high porosity, necessitating additional treatments. The study successfully obtained mesophase tar pitch (yield: 45%), a pivotal raw material, and high-density graphite. The resulting graphite underwent characterization for physical properties (apparent and real density, porosity and compression strength), demonstrating conformity with existing literature data.