Climate and its fluctuations have wide-ranging impacts on the tourism industry. High temperatures, as a typical meteorological and climatic factor, influence tourists' travel intentions and spatial behavior. This study conducted a descriptive analysis and market trend analysis of Chinese tourism during periods of high temperatures, revealing several key findings. Firstly, tourists seeking respite from summer heat exhibit a preference for short-distance trips and resource-rich destinations. Secondly, heat-escape tourism products undergo changes over time, gradually shifting towards mountainous areas and waterfront locations. Furthermore, taking Shanghai Disneyland as a case study demonstrates that the holiday system holds greater significance than temperature constraints. Despite experiencing a significant decline in the quality of their tourist experience in high-temperature environments, long-distance travelers are not deterred from choosing pre-booked tourism products by sudden bouts of hot weather.

Tungsten carbide (WC) was well known as a wear-resistant material. Iron-based pow-der was suitable for remanufacturing of cast iron engine parts. To improve the wear resistance of the remanufactured iron-based cast iron engine parts, WC-Co was intro-duced into iron-based powders to prepare composite coatings for cast iron engine components. In this work, FeAlC-x(WC-Co) composite coatings were prepared by plasma transfer arc on compacted graphite cast iron. The influences of WC-Co con-tents in the Fe-AlC-x(WC-Co) composite coatings on the microstructure and properties of the composite coatings were investigated. The composite coatings contained γ-Fe, α-Fe, WC and Fe3W3C mainly. The microhardness of FeAlC-x(WC-Co) composite coatings had the highest hardness of 814 HV0.2, the-lowest coefficient of 0.5 and the lest wear mass loss of 1.3mg when the weight content of WC-Co in the composite coating was 20wt%. As compared with the FeAlC coating, FeAlC-x(WC-Co) composite coating achieved the effect of reducing friction and wear resistance simultaneously, which resulted from the self-lubricating effect of graphite and high wear-resistance of carbides in the claddings.

CoCrFeNiMn high-entropy alloy coatings were prepared on compacted graphite iron（CGI） through plasma cladding to strength the CGI substrate. The effects of heat treatment temperatures and times on the microstructure and mechanical properties of the CoCrFeNiMn coatings were investigated. After heat treatment, a single FCC phase was remained in the coating as compared to the deposited one, with smaller dendrites, larger dendritic spacing and more Cr-rich compounds precipitated between dendrites. The coatings’ microhardness was increased after heat treatment. After heat treated at 660°C for 90 minutes, the coating had the highest microhardness of 563±6.9 HV0.2, the lowest frictional coefficient of 0.71 and the smallest wear mass loss of 1.12 mg, and it had the best wear resistance.