Copper ferrite attracts a lot of interest from researchers as a material with unique magnetic, optical, catalytic and structural properties. In particular, the magnetic properties of this material are structurally sensitive and can be tuned by changing the distribution of Cu and Fe cations in octahedral and tetrahedral positions by controlling synthesis parameters. In this study, we propose a new simple and convenient method for the synthesis of copper ferrite nanoparticles using a strongly basic anion exchange resin in OH form. The effect and possible mechanism of polysaccharides addition on the elemental composition, yield and particle size of CuFe2O4 is investigated and discussed. It is shown that anion exchange resin precipitation leads to a mixture of unstable at standard temperature cubic (c-CuFe2O4) and stable tetragonal (t-CuFe2O4) phases. The effect of the reaction conditions on the c-CuFe2O4 stability is studied by temperature-dependent XRD measurements and discussed in terms of the cations distribution, Jahn−Teller distortion and Cu2+ and oxygen vacancies in the copper ferrite lattice. The obtained differences in the values of saturation magnetization and the coercive force of prepared samples are explained with a reference to variations in the particle sizes and the structural characteristics of copper ferrite.

During the past few decades, hybrid nanoparticles (HNPs) based on a magnetic material and gold have attracted interest for applications in catalysis, diagnostics and nanomedicine. In this paper, magnetic CoFe2O4/Au HNPs with an average particle size of 10–20 nm decorated with 2-nm gold clusters were prepared using methionine as a reducer and an anchor between CoFe2O4 and gold. The obtained nanoparticles were studied by X-Ray diffraction (XRD), transmission electron microscopy (TEM), Fourier-transform infrared (FT-IR) spectroscopy and X-Ray photoelectron spectroscopy (XPS) and UV-Vis spectroscopy techniques. The TEM images of the HNPs obtained after one, six and ten gold deposition cycles showed that the surface of cobalt ferrite was covered with gold nanoclusters, which slightly increased with an increase in the number of gold deposition cycles (from 2.12 ± 0.15 nm after one cycle to 2.46 ± 0.13 nm after ten cycles) without any change in surface density. The magnetic measurements showed that the obtained HNPs possessed typical ferrimagnetic behaviour, which corresponds to that of CoFe2O4 nanoparticles. The toxicity evaluation of the synthesised HNPs on Chlorella vulgaris indicated that they can be applied to biomedical applications such as magnetic hyperthermia, photothermal therapy, drug delivery, bioimaging and biosensing.