This study investigates the cyclic load application impact on fly ash-based geopolymer composites that are reinforced with a low amount of fibre reinforcement. For reinforcement purposes, PVA and steel fibres are used. For testing purposes, four geopolymer composite mixes were made, 3 of which had fibre reinforcement. Simultaneously specimens were tested for shrinkage, static load-induced creep, and cyclic load-induced creep. For static and cyclic creep testing, specimens were loaded with 20% of their strength. For cyclic creep testing, load application and release cycles were seven days long. When each cycle was introduced, the load was added in steps. In 5 minutes, by 25% steps of the necessary load, the specimens were loaded or unloaded. Only plain specimens show that static creep strains are within cyclic creep strains. For all the other specimens, the static load is higher than the cyclic load-induced creep amplitude. Also, 1% PVA fibre-reinforced specimens show the most elastic characteristics under cyclic load, and 1% steel fibre-reinforced specimens appear to be the most resistant to the cyclic load introduction.

The current investigation presents porous ceramic materials prepared of cenospheres prepared by spark plasma sintering. The impact of sintering temperature, mould diameter (20 and 30 mm diameter) and cenosphere size on the properties of the sintered material was investigated. Shrinkage of the samples during sintering started at 900 °C. Sample shrinkage during sintering increases with increasing temperature and decreases with increasing mould size; increasing sample sintering temperature increases the apparent density of all sample series CS 63-150 µm in 20 mm mould from 0.97 to 2.3 g·cm-3 at 1050 - 1300 °C, in 30 mm mould 0.81 - 1.87 g·cm-3 at 1050 - 1200 °C, in 50 mm mould 0.54 - 0.75 g·cm-3 at 1050 - 1150 °C, while CS 150-250 µm in 20 mm mould 0.93 - 1.96 g·cm-3 at 1050 - 1200 °C. Total porosity decreases from 61.5% to 3.9% with increasing sintering temperature from 1050 to 1250 °C, while open porosity reduces at lower temperatures, with closed porosity being highest in samples sintered at 1150 °C. When the sintering temperature increases from 1050 to 1300 °C, the compressive strength of the CS 63-150 samples produced in a 20 mm mould increases from 11 MPa to 312 MPa. These results correlate with the Rice model, which describes an exponential dependence of compressive strength on material porosity and fully dense material compressive strength.