Metal-organic frameworks (MOFs) are investigated for the oxygen evolution reaction (OER) due to their structure diversity, high specific surface area, adjustable pore size and abundant active sites. However, the poor conductivity of most MOFs restricts this application. Herein, through a facile one-step solvothermal method, the Ni-based pillared metal-organic framework [Ni2(BDC)2DABCO] (BDC = 1,4-benzenedicarboxylate, DABCO = 1,4-diazabicyclo[2.2.2]octane), its bimetallic nickel-iron form [Ni(Fe)(BDC)2DABCO] and their modified Ketjenblack (mKB) composites were synthesized and tested towards OER in an alkaline medium (KOH 1 mol L–1). A synergistic effect of the bimetallic nickel-iron MOF and the conductive mKB additive enhance the catalytic activity of the MOF/mKB composites. All MOF/mKB composite samples (7, 14, 22, 34 wt.% mKB) indicated much higher OER performances than the MOFs and mKB alone. The Ni-MOF/mKB14 composite (14 wt. % of mKB) demonstrated an overpotential of 294 mV at a current density of 10 mA cm–2 and Tafel slope of 32 mV dec–1, which is comparable with commercial RuO2 commonly used as a benchmark material for OER. The catalytic performance of Ni(Fe)MOF/mKB14 (0.57 wt% Fe) was improved further to an overpotential of 279 mV at a current density of 10 mA cm–2. The low Tafel slope of 25 mV dec–1 as well as a low reaction resistance due to electrochemical impedance spectroscopy (EIS) measurement confirm the excellent OER performance of the Ni(Fe)MOF/mKB14 composite. For practical applications, the Ni(Fe)MOF/mKB14 electrocatalyst was impregnated into commercial nickel foam (NF), where overpotentials of 247 and 291 mV at current densities of 10 and 50 mA cm–2, respectively, were realized. The activity was maintained for 30 h at the applied current density of 50 mA cm–2. The electrocatalytic system consisting of earth-abundant Ni and Fe metals only would be attractive for the development of efficient, practical and economical energy conversion materials for efficient OER activity.

Iron-containing nickel sulfides, selenides, and sulfoselenides were synthesized via a simple two-step hydrothermal reaction (temperature 160 °C) for their application as electrocatalysts in the oxygen evolution reaction (OER) in an alkaline solution (1 mol L–1 KOH). The study demonstrated that iron-containing nickel cobalt sulfides and selenides exhibit superior OER performance with lower overpotentials compared to iron-free nickel cobalt sulfide and selenide, which highlights the significant role of iron in enhancing OER nickel cobalt electrocatalysts: Fe0.1Ni1.4Co2.9(S0.87O0.13)4, η50 = 318 mV; Fe0.2Ni1.5Co2.8(S0.9O0.1)4, η50 = 310 mV; Fe0.3Ni1.2Co2.5(S0.9O0.1)4, η50 = 294 mV; Fe0.6Ni1.2Co2.5(S0.83O0.17)4, η50 = 294 mV, Fe0.4Ni0.7Co1.6(Se0.81O0.19)4, η50 = 306 mV compared to Ni1.0Co2.1(S0.9O0.1)4, η50 = 346 mV and Ni0.7Co1.4(Se0.85O0.15)4, η50 = 355 mV (all values at current densities η50 of 50 mA cm–2). Furthermore, the iron-containing nickel cobalt sulfoselenide Fe0.5Ni1.0Co2.0(S0.57Se0.25O0.18)4 displayed exceptional OER performance with η50 = 277 mV, surpassing the benchmark RuO2 electrode with η50 = 299 mV. The superior performance of the sulfoselenide was attributed to its low charge transfer resistance (Rct) of 0.8 Ω at 1.5 V vs. the reversible hydrogen electrode (RHE). Moreover, the sulfoselenide demonstrated remarkable stability, with only a minimal increase in overpotential (η50) from 277 mV to 279 mV after a 20 h chronopotentiometry test. These findings suggest that trimetallic iron, nickel and cobalt sulfide, selenide and especially sulfoselenide materials hold promise as high-performance, cost-effective, and durable electrocatalysts for sustainable OER reactions. This study provides a valuable approach for the development of efficient electrocatalytic materials, contributing to the advancement of renewable energy technologies.