An ultra-low anti-reflection optical coating on both surfaces of a plastic cover slip was studied for use in confocal image measurement. The optical reflectance at a wavelength of 632.8 nm was less than 0.1% when the coated sample was placed in a liquid having a refractive index of 1.34 close to the aqueous solution of the biomaterial. The high- and low-index coating films, Substance-2 (PrTiO3) and silicon dioxide (SiO2), were measured by an ellipsometer to determine their optical refraction indices and extinction coefficients. Theoretically, when the two layer thicknesses are designed using the optical admittance diagram of the cover slip to approach the equivalent index of 1.34, a reflectance of 1.6×10-5% in the liquid could be obtained. Experimentally, the reflectance of the sample deposited on the two faces of the cover slip was 4.223±0.145% as measured in the air; and 0.050±0.002% as measured by a He-Ne laser in the liquid.

A typical white-light light-emitting diode (LED) can achieve a sunlight-like spectral profile in the visible spectrum by means of using an optical filter, with an inverted transmission profile to the white LED, fabricated using a deposition coating process. The unfiltered white LED generates white light by mixing light emitted by a blue LED (450 nm) with emission from the yellow phosphorescence excited by the blue light and differs significantly from the characteristics of the full-spectrum natural light. In this study, the spectral characteristics of the filtered LED light can be improved to reach a general color rendering index value (Ra) of 95.6 at the D65.

Surface-enhanced Raman spectroscopy (SERS) is commonly used for super-selective analysis through nanostructured silver layers in the environment, food quality, biomedicine, and materials science. To fabricate a high-sensitivity but more accessible device of SERS, dc magnetron sputtering technology was used to realize high sensitivity, low cost, stable deposition rate, and rapid mass production. This study investigated various thicknesses of a silver film ranging from 3.0 to 12.1 nm by field-emission-scanning-electron microscope, X-ray diffraction, and X-ray photoelectron spectroscopy. In the rhodamine 6G (R6G) testing irradiated by a He-Ne laser beam, the analytical enhancement factor (AEF) of 9.35x108, the limit of detection (LOD) of 10-8 M, and the relative standard deviation (RSD) of 1.61% were better than other SERS substrates fabricated by the same dc sputtering process because the results show that the 6 nm thickness silver layer has the highest sensitivity, stability, and lifetime. The paraquat and acetylcholine analytes were further investigated and high sensitivity was also achievable. The proposed SERS samples were evaluated and stored in a low humidity environment for up to forty weeks, and no spectrum attenuation could be detected. Soon, the proposed technology to fabricate high sensitivity, repeatability, and robust SERS substrate will be an optimized process technology in multiple applications.