Ultra-thin Fe–6.5wt.%Si ribbons with 35 μm in thickness were prepared by melt-spinning. The magnetic properties were investigated before and after annealing 1000 ºC. DC properties and low-frequency (400 Hz ~ 10 kHz) iron losses have significantly improved after heat treatment. A simplified formula based on Steinmetz law which can be used to predict the AC iron loss is presented. According to the results of some iron losses data, a simplified formula has been determined, and the extent of AC iron losses can be predicted. The results obtained from the formula predict AC iron loss to a good degree. The method developed in this work could be extended to other magnetic materials for predicting AC iron loss with greater ease.

The microstructures and mechanical properties of the hot-rolled Fe-6.5wt.%Si sheet are analyzed. The microstructure of the hot-rolled sheet is layered along the thickness direction. The surface exhibits fine and equiaxed grains, whereas the center part shows coarse and elongated grains with a <101> fiber texture along the rolling direction. Serrated flow behavior is observed during tensile deformation of both the hot-rolled sheet and its center samples at 350 °C; thus, the serrated flow of the hot-rolled sheet is mainly attributed to the serration of the center part. The analyses of dislocation configurations, ordered structures, and crystal orientation show that the serrated flow behavior results from the interaction of solutes with mobile dislocations. Mobile dislocations are pinned by combining parallel forest dislocations with the pipe diffusion of solution atoms. This study provides a new perspective for the deformation mechanism of the Fe-6.5wt.%Si alloy.

The flow behavior of Fe-6.5wt.%Si alloys during hot compression was investigated at temperatures 650–950 °C and strain rates 0.01–10 s^-1. The results showed that the flow stress depended distinctly on the deformation temperatures and strain rates. The flow stress and work hardening rate increased with the decrease of temperature and the increase of strain rate. The activation energy under all the deformation conditions was calculated to be 410 kJ/mol. The constitutive equation with hyperbolic sine function and Zener–Hollomon parameter was developed. The peak stress, critical stress, and steady-state stress could be represented as σ=A+Bln(Z/A). Dynamic recrystallization occurred under the deformation conditions where the values of Z were lower than 10²⁰. Processing maps were established to optimize the processing parameters. The power dissipation efficiency decreased in the high temperature and low strain rate region, increased in the high temperature and high strain rate region, and remained unchanged in other regions with the increase of true strain. Furthermore, the unstable area expanded. The true strain of 0.7 was the optimum reduction according to the processing map. Based on the analysis of surface quality, microstructures, and ordered structures, the optimized processing parameters for the Fe-6.5wt.%Si alloys were the temperature and strain rate of higher than 900 °C and 0.01–10 s^-1, respectively, or 800–900 °C and lower than 0.4 s^-1, respectively.

Cylindrical Fe-6.5wt.% Si bars with 7.5 mm in diameter were successfully fabricated from as cast ingot through three rolling stages within 10 passes: rough rolling at 850–900 °C and 8–10 m/min, medium rolling at 800–850 °C and 10–15 m/min, and finish rolling at 800–850 °C and 12–18 m/min. The evolution of microstructure, texture and ordered structure, and the mechanical property are investigated. The results showed that the grains were refined by the hot bar rolling. Area fractions of the {100}<011> oriented grains and the {011}<100> oriented grains decreased to 0 during the hot bar rolling. Whereas, the {100}<001> component, the {011}<211> component and the {112}<110> component increased, and γ fiber with {111}<110> component was dominant. DO₃ ordered phase were suppressed, and B2 ordered domains were refined after the hot bar rolling. Ductility of the as rolled bar was higher than that of the rotary swaged bar, due to the absence of the DO₃ ordered phase and the fine grains in the rolled bar. Hence, the hot bar rolling technology is an excellent process to fabricate the Fe-6.5wt.% Si bars.