The damage caused by global warming is rapidly increasing, and its adverse effects become more evident with each passing day. Although it is known that the use of alternative binder materials in concrete would decrease this negative effect, reluctance to new composites continues. Waste use plays a vital role in sustainability studies. In this study, pure cement paste was prepared and enriched with carbon fiber. This study investigated the wide range of volume fraction of carbon fiber in cement-based composites. Two different industrial wastes, marble dust, and bottom ash were chosen and mixed with cement and four different (0.3%, 0.75%, 1.5%, and 2.5%) carbon fiber volume fractions. Based on physical, mechanical, and durability tests at 7, 28, and 56-days of curing, the composites were resistant to sulfate and seawater attack. The 0.75% carbon fiber addition seems to be an optimum volume percentage beyond which both physical and mechanical properties were adversely affected. The composites with 0.75% carbon fiber have reached 48.4 MPa and 47.2 MPa at 56-days of curing for marble dust and bottom ash mixture groups, respectively.

The world’s population is growing at a rapid pace, thus increasing the need for shelter, which, because of increased carbon emissions, is making our planet less inhabitable. Thus, supplementary cementitious materials (SCMs) are used to reduce the embodied carbon emissions in the building sector. Wood ash, as a replacement for cement in soil treatment, seems to be a promising material. In this study, we considered the strength, stiffness, and microstructural behavior of marine clay treated with cement and wood ash as a cement replacement. Since clay is abundant in nature, it could help stabilize waste to improve the mechanical behavior of produced composites. Portland cement (7%, 10%, and 13%) was replaced with various amount of wood ash (5% and 10%) with two different dry densities (1400 and 1600 kg/m3) and three distinct curing periods (7, 28, and 60 days). Unconfined compressive strength, direct shear, porosity, pulse velocity, x-ray diffraction, and scanning electron microscopy tests were performed on selected specimens to evaluate the structural and microstructural effect of clay–wood ash–cement interaction. The results revealed that the replacement of cement with 5% of wood ash yielded superior performance. The microstructure investigation of wood ash–cement–clay blends further showed the formation of a densified matrix with stable bonds. Furthermore, the porosity and strength properties of blends developed unique relationships, which were further confirmed by other supplementary materials and soils.

Marine clay deposits are commonly found worldwide. Considering the cost of dumping and the related environmental concerns, an alternative solution involving the reuse of soils that have poor conditions is crucial. In this research, the authors examined the durability of marine deposited clays and compiled a corresponding database. The use of slag alone as a binder, at any percentage, increased the accumulated mass loss (ALM) up to 2%. However, the use of lime as the third binder seemed to accelerate the chemical reactions associated with the hydration of clay and cementitious material and to enhance the chemical stability, i.e., samples that included both lime and slag experienced the same ALM as samples treated with cement only. Scanning electron microscopy analysis confirmed the durability improvements of these clays. The proposed unconfined compressive strength and accumulated mass loss relationship yielded practical approximation for the fine- and coarse-grained soils blended with up to three binders until 60 days of curing.

Extinction of natural resources builds up pressure on governments to invest in research to find more sustainable resources for construction sector. Earlier studies on mortar and concrete show that bottom ash and basalt fiber are independently alternative binder in the concrete sector. This study aims to use bottom ash and basalt fiber blends as alternative novel-based composites in pure cement paste. Strength and durability properties of two different percentages of bottom ash (40% and 50%) and three volume fractions of basalt fiber (0.3%, 0.75%, and 1.5%) were used at three curing periods (7, 28, and 56 days). In order to measure physical properties of the basalt-reinforced bottom ash cement paste composites flowability, dry unit weight, porosity and water absorption measurements at 7, 28, and 56 days of curing were performed. Furthermore, mechanical properties of composites determined by unconfined compressive strength and flexural strength tests. Finally, to assess the durability sulfate-resistance and seawater-resistance tests have been performed on composites at 28 and 56 days of curing. Results showed that addition of basalt fiber improves physical, mechanical and chemical stability properties of paste up to a limiting basalt fiber addition (0.3% volume fraction) where above an adverse effect have been monitored. It is clear that observed results can lead to development of sustainability strategies in the concrete industry by utilizing bottom ash and basalt fiber as an alternative binder.