Optical and mechanical properties of multilayer coatings depend on the selected layer materials and the deposition technology; therefore, knowledge of the performances of thin films is essential. In the present work, titanium dioxide (TiO2) and silicon dioxide (SiO2) thin films have been prepared by plasma ion-assisted deposition (PIAD). The optical, structural, and mechanical properties of thin films have been investigated using spectrometer/ellipsometer, X-ray diffraction (XRD), atomic force microscopy (AFM), and laser interferometer. The results show that TiO2 film fabricated by PIAD induces a high refractive index, wide optical band gap, amorphous structure, smooth surface, and tensile stress. In the case of SiO2 film, high bias voltage leads to dense structure and compressive stress. As an application, a three-wavelength high reflectance at 632.8, 808, and 1550nm is optimized and deposited. The dependence of total stress in the multilayer on the substrate temperature is studied as well. In conclusion, it is demonstrated that PIAD is an effective method for the preparation of ultralow stress TiO2/SiO2 multilayer films. The achieved stress is as low as 1.4Mpa. The result could provide guidance to the stress optimization of most optical components without prefiguring, backside coating, and post-deposition treatments.

With the development of industrialization, traditional manufacturing technologies are no longer able to meet the production needs of modern society. Additive manufacturing has successfully solved the problems existing in traditional manufacturing technology. Selective laser melting (SLM) is a powder bed melting technology that produces metal parts by selectively melting metal powders on a platform using a laser beam. It is widely used in additive manufacturing. This article introduces the characteristics and current development status of SLM technology, summarizes the main application fields and common defects of SLM, and finally explores and prospects the future development trend of SLM.

CoCrFeNiMn high-entropy alloy coatings were prepared on compacted graphite iron（CGI） through plasma cladding to strength the CGI substrate. The effects of heat treatment temperatures and times on the microstructure and mechanical properties of the CoCrFeNiMn coatings were investigated. After heat treatment, a single FCC phase was remained in the coating as compared to the deposited one, with smaller dendrites, larger dendritic spacing and more Cr-rich compounds precipitated between dendrites. The coatings’ microhardness was increased after heat treatment. After heat treated at 660°C for 90 minutes, the coating had the highest microhardness of 563±6.9 HV0.2, the lowest frictional coefficient of 0.71 and the smallest wear mass loss of 1.12 mg, and it had the best wear resistance.