In this work, nanocomposite photoelectrodes of the TiO2/ Au composition were manufactured, in which the size of plasmonic Au nanoparticles was varied, and the morphology of the TiO2 layer, depending on the thickness, changed from an island to a continuous layer. The influence of the morphology of plasmonic Au nanoparticles and the TiO2 layer on the optical and photoelectrochemical characteristics of hybrid photoelectrodes was studied. It has been shown that continuous coating of Au nanoparticles with a TiO2 layer (layer thickness 10 and 15 nm) leads to a decrease in the photoelectric response, and the decrease in photocurrent density and photoconversion efficiency decreases in proportion to the thickness of the TiO2 layer. The indicated drop in characteristics when plasmonic particles are located under the TiO2 layer is presumably associated with the scattering and recombination of charge carriers in the semiconductor layer. The best performance was shown by a system in which large Au nanoparticles (10 nm) are coated with a 5 nm thick layer of titanium dioxide; in this geometry, Au nanoparticles are decorated with TiO2 nanoparticles, as a result of which the photoelectrode-electrolyte interface has a more complex structure.

For the first time, an environmentally friendly waste-free closed cycle for the formation of EMI shielding materials that are promising for 5G communications is considered. Based on the proposed closed technological cycle, two types of EMI shielding materials have been obtained; both materials have significant prospects for signal shielding in all ranges that are allocated in different countries for 5G communication. The first type of materials are transparent conductive meshes with a transparency of more than 80% and with a shielding efficiency of more than 40 dB in the S and L bands and about 30 dB in the K and Ka bands. The study of signal reflection characteristics in the S, L, C, K and Ka bands showed the promise of using these materials as transparent 5G signal reflectors. The reflection coefficient in all considered ranges is above 90% (-0.5 dB). The second type of shielding material are continuous silver micro caps films characterized by a shielding efficiency of 90.1 dB at a thickness of 6.2±1.2 µm. We have also shown that silver micro caps can separate into silver flakes and ribbons when sonicated. These materials can also be used to produce EMI shielding coatings and composites. A detailed analysis of the shielding properties showed that each type of materials obtained in a closed technological cycle is comparable with the best literature results and significantly wins in terms of cost.