The aim of this work is to assess the influence of Friction Stir Welding (FSW), process parameters, optimized tool traveling speed, and corrosion resistance of the 0.95 Mg-Al-alloy and pure copper weldment. Samples of aluminum-copper with and without deformation were characterized to investigate the metallurgical effects created during the welding deformation process. Effect of process parameters on microstructure and corrosion rate have been investigated for all the samples. All the electrochemical and polarization tests were done in 3.5 wt.% NaCl solution. Scanning Kelvin Probe (SKP) was done to detect the localized corrosion on the surface. Optical micrography observation indicated that the primary α-Al phase, which was formed during solidification can effectively limit the growth of Cu₉Al₄ phase. Finer acicular α-Al precipitates were observed in CuAl matrix during joining process that tends to coarser with the increase in tools travel speed. The electrochemical and polarization results showed that among all the tool travelling speed the specimen joined at tool travelling speed of 40 mm/min shows the best non-corrosive property.

In this study, the effect of increasing exposure time on microstructures, defectiveness, mechanical properties and corrosion behavior of selective laser melted sample Al-Si10-Mg powder have been investigated. The sample were processed at the same power (375 W) and scan speed (2000 mm/s) but with increasing exposure time. Exposure time equal to 40, 50 and 60 µs was applied. The features of the analyzed samples show that with increasing exposure time a better efficiency of the heat input has been obtained with larger size of melting pool and Si particles and lower defectiveness. Moreover, being the coarser microstructure associated a to lower level of voids, the average hardness is similar for the analyzed samples. The potentiodynamic curves of the samples show that the voids occurrence is more significant with respect to the scale of micro-structure on corrosion behavior being the sample processed at the highest exposure time the more resistant to corrosion. The experimental techniques used in the present study were Optical microscope, Sem microscope, Hardness and X-Ray Computed Tomography.