Thin Pd-40%Cu films were obtained by the classical melting and rolling method, magnetron sputtering and modified with nanostructured functional coatings to intensify the process of hydrogen transport. The films were modified by electrodeposition according to the classical method of obtaining palladium black and "Pd-Au nanoflowers" with spherical and pentagonal particles, respectively. The experiment results demonstrated the highest catalytic activity (89.47 mA cm–2), good resistance to CO poisoning and long-term stability of Pd-40%Cu films with a pentagonal structured coating. The investigation of the developed membranes in the hydrogen transport processes in the temperature range of 25-300°C also demonstrated high and stable fluxes up to 475.28 mmol s–1 m–2 (deposited membranes) and 59.41 mmol s–1 m–2 (dense-metal membranes), which turned out to be up to 1.5 higher compared to membrane materials with classic niello. For all-metal modified membranes, the increase in flux was up to 7 times, compared with a smooth membrane made of pure palladium, and for deposited films, this difference was several tens of times. The membrane materials selectivity was also high up to 4419. The developed strategy for modifying membrane materials with functional coatings of a fundamentally new complex geometry can shed new light on the development and fabrication of durable and highly selective palladium-based membranes for gas steam reformers.

A unique method for synthesizing a surface modifier for metallic hydrogen permeable mem-branes based on non-classic bimetallic pentagonally structured Pd-Pt nanoparticles has been de-veloped. It was found that nanoparticles had unique hollow structure. This significantly reduces the cost of their production due to economical use of metal. According to the results of electro-chemical studies, synthesized bimetallic Pd-Pt/Pd-Ag modifier showed excellent catalytic activi-ty (up to 60.72 mA cm–2), long-term stability and resistance to COads poisoning in alkaline oxida-tion reaction of methanol. The membrane with pentagonally structured Pd-Pt/Pd-Ag modifier showed the highest hydrogen permeation flux density up to 27.3 mmol s–1 m–2. Obtained hy-drogen flux density were 2 times higher than that for membranes with classic Pdblack/Pd-Ag modifier and an order of magnitude higher than that for unmodified membrane. Since the rate of transcrystalline hydrogen transfer through a membrane increased, while the speed of transfer through defects remained unchanged, a one and a half times rise in selectivity of the developed Pd-Pt/Pd-Ag membranes was recorded and it amounted to 3514. Achieved results are due to both the synergistic effect of the combination of Pd and Pt metals in the modifier composition and the large number of available catalytically active centers, which are present as a result of non-classic morphology with high-index facets. The specific faceting, defect structure and unusual properties provide great opportunities for the application of nanoparticles in the areas of membrane reac-tors, electrocatalysis, petrochemical and hydrogen industries.