The present study illustrates the strong effect of geometrical parameters on the magneto-structural properties of Co2MnSi glass-coated microwires prepared using the Taylor-Ulitovsky method. Thus, two samples with different geometrical aspect ratios (ρ= d / D) have been fabricated, where d is the metallic nuclei diameter and D is the total diameter of the Co2MnSi microwire. The XRD analysis shows a significant change by modifying the aspect ratio, for ρ = 0.46 the main peak with miller indices (220) is recognized as an A2-type disordered cubic structure. Meanwhile, in the sample with a low aspect ratio, ρ = 0.31, the perfect L21 ordered cubic structure is attained. In addition, a decrease in average grain size from 36.62 nm to 28.07 nm by increasing the aspect ratio from 0.46 to 0.31 is observed. The magnetic characterization has been done in a wide range of temperatures and magnetic fields. Both of Co2MnSi samples show ferromagnetic behavior in a whole measuring temperatures range. A significant increase in coercivity and normalized reduced remanence by decreasing the aspect ratio is observed. The change in the magnetic properties is attributed to the modification in the microstructure, which is induced during the fabrication process. Such a dependence on the microstructure and magnetic properties on the ρ-ratio can be associated either with the internal stresses distribution and magnitude or with different quenching rates of microwires with different aspect ratios. The current findings demonstrate the tunability of microstructure and magnetic properties of Co2MnSi-glass-coated microwires simply, by a small modification in the geometric properties during the manufacturing process and without excreting any additional post-processing. The variation in geometric parameters of Co2MnSi glass-coated microwires allows us to tune magnetic properties and structure, which is essentially advantageous for sensing devices development.

In current work, we illustrate the effect of adding small amount of Carbon to very common Co2MnSi Heusler alloy based-glass coated microwires. A significant change in the magnetic and structure structural properties has observed for the new alloy Co2MnSiC compared to the Co2MnSi alloy. The magneto-structural investigations have performed to clarify the main phys-ical parameters i.e., structural & magnetic at a wide range of measuring temperature. The XRD analysis illustrated the well-defined crystalline structure with average grain size (Dg = 29.16 nm) and a uniform cubic structure with A2-type compared to the mixed L21 and B2 cubic structures for Co2MnSi-based glass coated microwires. The magnetic behaviour has investigated at a tem-perature range (5 to 300 K) and an external applied magnetic field (50 Oe to 20 kOe). The adding of small amount of Carbon to the Co2MnSi matrix enhance the magnetic thermal stability, where the thermomagnetic behaviour of Co2MnSiC glass-coated microwires show a perfect stable be-haviour for a temperature range from 300 K to 5 k, the differences between the coercivity value is only 0.3 Oe compared to 4 Oe for Co2MnSi-sample. In addition, M-H loops measured at tempera-ture below 50 K show unsaturated loops; meanwhile the Co2MnSi loops shows a strong antifer-romagnetic coupling for the loops measured below 50 K. By studying the field cooling (FC) and field heating (FH) magnetizations curves at a wide range of external applied magnetic field we detected a critical magnetic field (H = 1 kOe) where FC and FH curves have a stable magnetic behavior for Co2MnSiC sample, such stability does not find in Co2MnSi sample. We proposed a phenomenal expression to estimate the magnetization thermal stability, ΔM (%), of FC and FH magnetization curves and the maximum value is detected at the critical magnetic field where ΔM (%) ≈ 98 %. The promising magnetic stability of Co2MnSiC glass-coated microwires with tem-perature is due to the changing of the microstructure induced by adding Carbon, as the A2-type structure show a unique stability by variation the temperature and the external magnetic field. In addition, a unique internal mechanical stress, which induced during the fabrication process and plays on controlling magnetic behavior with temperature and external magnetic field. The ob-tained results make Co2MnSiC promising candidate for magnetic sensing devices based Heusler glass-coated microwires.

In current study we have obtained Co2FeSi-glass coated microwires with different geometrical aspect ratio, ρ = d/Dtot (diameter of metallic nucleus, d and total diameter, Dtot). The structure and magnetic properties are investigated at a wide range of temperature. XRD analysis illustrates a notable changing in the microstructure by increasing the aspect ratio of Co2FeSi glass coated microwires. Amorphous structure is detected for the sample with the lowest aspect ratio (ρ = 0.23), whereas a growth of crystalline structure is observed in the other samples (aspect ratio ρ = 0.30 and 0.43). This change at the microstructure properties correlates with dramatic changing in magnetic properties. For the sample with the lowest ρ -ratio, non-perfect square loops are obtained with low normalized remanent magnetization. A notable enhancement in the squareness and coercivity are obtained by increasing ρ -ratio. Changing the internal stresses strongly affects the microstructure, resulting in a complex magnetic reversal process. The thermomagnetic curves show large irreversibility for the Co2FeSi with low ρ -ratio. Meanwhile, if we increase the ρ -ratio, the sample shows perfect ferromagnetic behavior without irreversibility. The current result illustrates the ability to control the microstructure and magnetic properties of Co2FeSi-glass-coated microwires by changing only their geometric properties without performing any addition heat treatment. The modification of geometric parameters of Co2FeSi glass-coated microwires allows to obtain microwires which exhibit an unusual magnetization behavior that offers opportunities to understand the phenomena of various types of magnetic domain structures, which is essentially helpful for designing sensing devices based on thermal magnetization switching.