In this paper, a novel synthesis for a chemical precursor for nanocrystalline VO2 coatings is elaborated. The compatibility of the precursor towards the substrate is optimized for spin coating. This is done by subjecting multiple solvents to contact angle measurements. A suitable thermal treatment is developed to densify the coating and to induce crystallization. Afterwards the microstructure of the coating is investigated using X-Ray diffraction, electron microscopy and ellipsometry techniques. To assess the thermochromic properties of the fabricated device, optical transmission experiments were conducted both at room temperature and at elevated temperature. A correlation between these thermochromic properties and coating thickness was investigated in order to obtain an optimized thermochromic device, where both high visual transparency and prominent thermochromic switching abilities are aimed for. In this work, an optimal coating thickness is proposed for a thermochromic coating with high switching ability and solar modulation.

The coordination polymer [Fe(NH₂trz)₃](2ns)₂ exhibits the rare phenomenon of spin crossover in an attractive temperature range, i.e., somewhat above room temperature. Spin crossover in [Fe(NH₂trz)₃](2ns)₂ is manifest by thermochromism, which is accompanied by a magnetic transition from diamagnetism to paramagnetism. However, [Fe(NH₂trz)₃](2ns)₂ is brittle and difficult to process, which limits its use. In this study, we show that [Fe(NH₂trz)₃](2ns)₂ can be co-processed with ultrahigh molecular weight polyethylene (UHMWPE), which possesses outstanding mechanical properties, particularly when tensile drawn. Therefore, [Fe(NH₂trz)₃](2ns)₂–UHMWPE blends were gel-processed by extrusion, employing a relatively poor solvent, which has recently been shown to offer advantages compared to good solvents. Uniform and flexible films, ribbons and fibers with [Fe(NH₂trz)₃](2ns)₂ fractions as high as 33.3% m/m were obtained that could be readily drawn. Spin crossover in the coordination polymer is retained in these materials, as evident from their thermochromism. The tensile strength and Young’s modulus of the blends exceed those of typical commodity polymers. Thus, the films, ribbons and fibers constitute a special class of multifunctional materials that combine the flexibility and excellent mechanical properties of drawn UHMWPE with the spin crossover behavior of [Fe(NH₂trz)₃](2ns)₂.