The dynamic effects observed in collisions represent a specific area of high-energy interaction located at the boundary of mechanics, hydrodynamics, shock wave physics, and alternating high-pressure regions. The paper shows that in the volume of a solid metal body, as a result of dynamic alloying by a high-speed stream of powder particles in the super-deep penetration mode (SDP), fibre structures of altering material arise, forming the framework of the composite material. The stream of powder particles in the metal obstacle following the path of least resistance and the impact of shock waves on particles results in a volumetric framework from the products of interaction between the injected and matrix materials. When using SDP, defective structural elements (channelled) - germs of reinforcing fibres arise. At the subsequent heat treatment, there is an intensive diffusion. The growth process of reinforcing fibres shifts to higher temperatures (as compared to the standard mode), leading to an increase in the bending strength of the fibre material up to 13 times for high-speed tool W6Mo5Cr4V2 steel. As a result of the completion of the growth of reinforcing fibres in the volume of the W6Mo5Cr4V2 steel, the material's bending strength in 1.2 times is realised. Simultaneously, it provides an increase of wear resistance 1.7-1.8 times.

Despite the development of technologies, modern methods of disposal of end-of-life tires most often represent either the incineration in cement kilns or the destruction of tires in special landfills, showing a lack of sustainable recycling of this valuable material. The fundamental role of recycling is evident, and the development of high-efficiency processes represents a priority for the European market. Therefore, investigation of end-of-life rubber processing methods is of high importance for manufacturers and recyclers of rubber materials. In this paper, methods of processing of end-of-life tires are reviewed in order to obtain rubber crumb, which can later be used in the production of new industrial rubber goods and composite The processes of separation end-of-life tire into fractions by type of materials using mechanical processing methods along with mechanochemical and mechanical processes of processing the materials of used tires in order to obtain crumb rubber of various fractions and chemical reactivity are considered.

A method of accuracy error compensation for the time interval is examined, allowing to eliminate the dependence of accuracy error on the duration of measured intervals and minimising the influence of destabilising factors - ambient temperature changes and the initial deviation of the meter clock generator frequency from the nominal value. The compensation method is based on a calibration procedure that measures precise time intervals under conditions of changing ambient temperature. Then the dependence of the accuracy error on temperature for a particular meter is recorded. Based on these data, a correction table is compiled containing correction factors and temperature values at which these factors were determined. Under real measurement conditions, the correction factor corresponding to the current temperature is determined from the table for measured results correction. The table with correction factor values could be stored in the memory of the meter or processing computer. Experimental verification of the method showed that applying a correction for a meter with a standard XO class clock generator (certificated instability of ±50 ppm) can obtain an equivalent clock generator instability of ±0.15 ppm. The application of the method is efficient in cases where the use of high-end clocking to ensure the required measurement accuracy is not economically feasible.

The current investigation presents porous ceramic materials prepared of cenospheres prepared by spark plasma sintering. The impact of sintering temperature, mould diameter (20 and 30 mm diameter) and cenosphere size on the properties of the sintered material was investigated. Shrinkage of the samples during sintering started at 900 °C. Sample shrinkage during sintering increases with increasing temperature and decreases with increasing mould size; increasing sample sintering temperature increases the apparent density of all sample series CS 63-150 µm in 20 mm mould from 0.97 to 2.3 g·cm-3 at 1050 - 1300 °C, in 30 mm mould 0.81 - 1.87 g·cm-3 at 1050 - 1200 °C, in 50 mm mould 0.54 - 0.75 g·cm-3 at 1050 - 1150 °C, while CS 150-250 µm in 20 mm mould 0.93 - 1.96 g·cm-3 at 1050 - 1200 °C. Total porosity decreases from 61.5% to 3.9% with increasing sintering temperature from 1050 to 1250 °C, while open porosity reduces at lower temperatures, with closed porosity being highest in samples sintered at 1150 °C. When the sintering temperature increases from 1050 to 1300 °C, the compressive strength of the CS 63-150 samples produced in a 20 mm mould increases from 11 MPa to 312 MPa. These results correlate with the Rice model, which describes an exponential dependence of compressive strength on material porosity and fully dense material compressive strength.

Present study focuses on the synthesis and characterisation of a lightweight ceramic material with electromagnetic interference (EMI) shielding properties, achieved using mullite containing micrometer-sized hollow spheres (cenospheres) and CoFe2O4 nanoparticles. The research explores compositions with varying CoFe2O4 content, ranging from 0 up to 20 wt.%. Сonventional sintering in an air atmosphere is carried out at a temperature between 1100-1300 °C. The addition of ferrite nanoparticles was found to enhance the sintering process of cenospheres, resulting in improved material density and mechanical properties. Furthermore, the study reveals a direct correlation between the concentration of ferrite nanoparticles and the electromagnetic properties of the. By increasing the concentration of ferrite nanoparticles, the electromagnetic shielding effect of the material (saturation magnetization (Ms) and remanent magnetization (Mr)) was observed to strengthen. These findings provide valuable insights into the design and development of lightweight ceramic materials with enhanced electromagnetic shielding capabilities. The synthesized ceramic material holds promise for various applications that require effective electromagnetic shielding, such as in electronics, telecommunications, and aerospace industries.

Among the various methods for collecting oil spills and oil products, including from the water surface, one of the most effective is the use of sorbents. In this work, three-component bio-based composite granular adsorbents were produced and studied for oil products pollution collection. A bio-based binder made of peat, devulcanised crumb rubber from used tyres, and part fly ash as cenospheres were used for absorbent production. The structure, surface morphology, porosity, mechanical properties, and sorption kinetics of the obtained samples were studied. Composite hydrophobicity and sorption capacity to oil products such as diesel fuel (DF) and motor oil (MO) were determined. The obtained pellets are characterised by a sufficiently pronounced ability to absorb oil products such as DF. As the amount of CR in the granules increases, the diesel absorption capacity increases significantly. The case of 30-70-0 is almost 3 times higher than the granules from homogenised peat. The increase in q is due to two factors: pronounced surface hydrophobicity of the samples (Θ = 152°) and a heterogeneous porous granule structure. The presence of the cenosphere in the biocomposite reduces its surface hydrophobicity while increasing the diesel absorption capacity. Relatively rapid realisation of the maximum saturation by the MO was noted. In common, the designed absorbent shows up to 0.7 g·g^-1 sorption capacity for MO and up to 1.55 g·g^-1 sorption capacity for diesel. A possible mechanism of DF absorption and the limiting stages of the process approximated for different kinetic models are discussed. The Weber-Morris diffusion model is used to primarily distinguish the limiting effect of external and internal diffusion of adsorbate on the absorption process

The present review is dedicated to using of peat on the example of fen peat in high added-value products and applications. Mainly, but not limited, last decade literature was analysed from the perspective of innovation potential of peat applications in environmental technologies on examples of studies from the Baltic Sea region. Paper covers a wide range of applications of peat products started from agriculture to medicine and cosmetics. A separate chapter is devoted to the deep-processed peat product - humic substances (humate, humic and fulvic salts and acids). Generalised dependence of product extraction rate and its properties, depending on the process parameters are provided. Widely are described applications of the humic sub-stance applications covering economic aspects, such as production costs. In the last chapter of the review are given recommendations for applications considering the most recent trends of peat-based product developments. This accumulated information could be useful for future production, development of new, environmentally friendly products and start-ups establishment.

The utilisation of the industrial residual products to develop new value-added materials and to reduce footprint is one of the critical challenges of science and industry. Development of the new multifunctional and bio-based composites materials is an excellent opportunity for the effective utilisation of industrial residual products. Keeping the different issues in mind, in this work, we describe the manufacturing and characterisation of the three-phases bio-based composites. The key components are bio-based binder made of peat, devulcanised crumb rubber (DCR) from used tires and part of the fly ash, i.e. the cenosphere (CS). The three-phase composite prepared in the form of a block were investigated for their mechanical properties and density. The three-phase composite was prepared in the form a) of a block were investigated for their mechanical properties, and density and b) a form of granules for determination of the water and oil products sorption were investigated. We have also investigated the dependence of the properties on the DCR and CS fraction. It has been found, that maximum compression strength (in block form) observed for composition without CS and DCR addition was- 79.3 MPa, while the second-highest value of compression strength is 11.2 MPa for composition with 27.3 wt% of CS. For compositions with bio binder content from 17.4 to 55.8 wt% and with DCR contents in range from 11.0 to 62.0 wt%, the compression strength is in the range from 1.1 to 2.0 MPa. Liquid sorption analysis (water and diesel) showed that the maximum saturation of liquids in both cases is set after 35 minutes and ranges from 1.05 to 1.4 g·g -1 for water and 0.77 to 1.25 g·g-1 for diesel. It was noted that 90% of the maximum saturation with diesel fuel comes after 10 minutes and for water after 35 minutes.

The utilisation of the industrial residual products to create new value-added materials and to reduce footprint is a modern challenge of science and industry. Development of the new multifunctional and bio-based composites is an excellent opportunity for complex utilisation of industrial residual products. The study describes the preparation and characterisation of the three-phases bio-based composites. The main components are bio-based binder made of peat, devulcanised crumb rubber (DCR) from used tires and part of the fly ash the cenosphere (CS). Three-phase composite prepared in the form of a block for investigation of the mechanical properties and density and a form of granules for determination of the water and oil products sorption was investigated. This work investigated the dependence of the properties on the main component DCR and CS fraction. Is found, that maximum compression strength (in block form) observed for composition without CS and DCR addition - 79.3 MPa, the second highest value of compression strength is 11.2 MPa for composition with 27.3 wt% of CS. For compositions with bio binder content from 17.4 to 55.8 wt% and with DCR contents in range from 11.0 to 62.0 wt% compression strength is in range 1.1 to 2.0 MPa. Liquid sorption analysis (water and diesel) showed that the maximum saturation of liquids in both cases is set after 35 minutes and ranges from 1.05 to 1.4 g·g -1 for water and 0.77 to 1.25 g·g-1 for diesel. It was noted that 90% of the maximum saturation with diesel fuel comes after 10 minutes and for water after 35 minutes.

The widespread use of epoxy resin (ER) in industry, owing to its excellent properties, aligns with the global shift toward greener resources and energy-efficient solutions, where utilizing metal oxides in 3D printed polymer parts can offer extended functionalities across various industries. ZnO concentrations in polyurethane acrylate composites impacted adhesion and thickness of DLP samples, with 1 wt.% achieving a thickness of 3.99±0.16 mm, closest to the target thickness of 4 mm, while 0.5 wt.% ZnO samples exhibited the lowest deviation in average thickness (±0.03 mm). Tensile strength in digital light processed (DLP) composites with ZnO remained consistent, ranging from 23.29 MPa (1 wt.%) to 25.93 MPa (0.5 wt.%), with an increase in ZnO concentration causing a reduction in tensile strength to 24.04 MPa and a decrease in the elastic modulus to 2001 MPa at 2 wt.% ZnO. The produced DLP samples, with their good corrosion resistance in alkaline environments, are well-suited for applications as protective coatings on tank walls. Customized DLP techniques can enable their effective use as structural or functional elements, such as in Portland cement concrete walls, floors and ceilings for enhanced durability and performance.