In the preparation of polymer-clay nanocomposites the chemical incompatibility between the clay surface and polyolefins can be overcome by using clays organically modified with short chain organic cations. The compatibility can be further enhanced by using functionalized polymer that wets the clay surface while being miscible with the non-polar polymer matrix. In this work we tried to modify the host polymer polypropylene (PP) by irradiating it with gamma-rays in air knowing that it undergoes oxidation and chain scission simultaneously. Thus lower molecular weight PP with highly polar surface due to oxidation can be expected to play double role of clay modifier and functional compatibilizer. This has been observed to be the case. Finely ground PP granules were irradiated in air in a ⁶⁰Co γ-irradiator at the dose rate of 0.08 kGy/h (low dose rate to enhance oxidation) to 5, 10, and 20 kGy total doses. The extent of oxidation and change in molecular weight were determined by ATR-FTIR and Melt Flow Rate measurements respectively. PP/MMT nanocomposites were prepared by using 20% γ-PP, 1-5 % MMT and pristine PP to make up the total 100 in a torque rheometer. Maleated PP was also used in similar quantities to compare the effectiveness of γ-PP as a compatibilizing agent. Nanocomposites prepared with 10 kGy irradiated PP was found to show optimum mechanical properties among all formulations, with 26% increase in E-modulus and 10% increase in tensile strength as compared to pristine PP. Ternary PP nanocomposites were characterized by XRD, SAXS and PALS studies.

In contrast to the traditional fillers, clay, in particular, natural smectite clay represents an environmentally significant alternative to improve the properties of polymers. Compared to con-ventional nanofillers, smectite clay can effectively enhance the physical and mechanical properties of polymer nanocomposites with a relatively small amount of addition (< 5 wt%). The present study focuses on investigating the reinforcing efficiency of different amounts (up to 5 wt%) of a natural Brazilian smectite clay on the mechanical and thermal properties of poly(butylene terephthalate) (PBT) nanocomposites. Natural Brazilian clay modified by addition of quaternary salt and sodium carbonate (MBClay) was infused into the PBT polymer by melt extrusion, using a twin-screw extruder. It was found that the best properties for PBT were obtained at 3.7 wt% of modified BClay. Tensile strength at break exhibited an increase of about 60 %, flexural strength increased by 24 % and flexural modulus increased by 17 %. In addition, an increase in the crystallinity percentage of PBT/BClay nanocomposite was confirmed by DSC and XRD analysis, and a gain of about 45 % in HDT was successfully achieved due to incorporation of 3.7 wt% of MBClay.

In this work, the surface of poly(ethylene terephthalate) track-etched membranes (PET TeMs) with pore sizes of 670-1310 nm was hydrophobized with 2,2,3,3,4,4,5,5,6,6,7,7-dodecafluoroheptyl acrylate (DFHA) by photoinitiated graft polymerization. Attenuated total reflection FTIR spec-troscopy (ATR-FTIR), scanning electron microscopy (SEM) coupled to an energy-dispersive X-ray spectrometer (EDX), and contact angle measurement were used to identify and characterize the TeMs. The optimal parameters for graft polymerization were determined as follows: polymeriza-tion time 60 min, monomer concentration of 30% and distance from the UV-source 7 cm. The wa-ter contact angle of the modified membranes reached 97° which is 51o for pristine membranes. The modified membranes were tested for water desalination using direct contact membrane distillation (DCMD) method. The effect of membrane pore size, the degree of grafting and salt concentration on the performance of membrane distillation process was investigated. According to the results obtained, it has been concluded that large pore size hydrophobic TeMs modified by using DFHA could be used for desalinating water.