Nanocelluloses have gained significant attention in recent years due to singular properties (good biocompatibility, high optical transparency and mechanical strength, large specific surface area and good film-forming ability) and wide-ranging applications (paper, food packaging, textiles, electronics and biomedical). This article is a comprehensive review of nanocelluloses from the preparation methods to their applications in conservation and restoration of historical paper documents. The novelty lies in the information collected about nanocelluloses as renewable, environmentally friendly and sustainable materials in the field of preservation of cultural heritage as an alternative to conventional methods. Several studies have demonstrated that nanocelluloses, with or without other particles, impart to the paper documents excellent optical and mechanical properties, very good stability against temperature and humidity aging, stronger antibacterial and antifungal activity, high protection to UV light and do not require additional adhesive.

Cellulose nanofibrils (CNFs) are materials with high aspect ratio. Typically, TEMPO-oxidised, or cationic CNFs consist of long fibrils (up to 2 μm) with very low thickness (less than 10 nm). Derived from their high aspect ratio, CNFs form strong hydrogels with high elasticity at low concentrations. Thus, CNF suspensions appear as an interesting rheology modifier to be applied in cosmetics, paints, foods, as a mineral suspending agent, among other applications. The high viscosity results from the strong 3D fibril network, which is related to good fibrillation of the material, allowing the nanofibrils to overlap. The overlap concentration (c*) was found to vary from ca. 0.13 to ca. 0.60 wt.% depending on the type and intensity of the pre-treatment ap-plied during the preparation of the CNFs. The results confirm the higher tendency for the fibres treated with CHPTAC (cationic) and TEMPO to form a 3D network, resulting in the lowest c*. For the TEMPO-oxidised CNF suspensions, it was also found that aggregation is improved at acidic pH conditions due to lower charge repulsion among fibrils, leading to an increase in the suspension viscosity, as well as higher apparent yield stresses. TEMPO CNF suspensions with low content of carboxylic groups tend to precipitate at moderate acidic pH values.