The blended perfluorinated sulfonic acid ionomers are prepared to have equivalent weight (EW) ~1000, 980, and 830. The catalyst layers (CLs) using blended PFSA ionomers with different side chain lengths and EWs are investigated, compared to the CLs utilizing single ionomers. The IEC results indicate that the blended ionomers have the targeted EWs. As a result, it is found that the blended ionomers exhibit higher ion conductivity than the single ionomers at all temperatures due to higher water uptake of the blended ionomers. Even though they have a similar EW, it implies that the blended ionomers have bulk structure to form competent free volume. The blended ionomers with short side chain (SSC) and low EW can help reduce the activation energy due to the enhanced hydrophobic and hydrophilic segregation. In addition, it is observed that the catalyst layers using the blended ionomer form more porous microstructure to help reduce the resistance of oxygen transport and attributes to lower mass transfer loss. This effect is significantly revealed in the fuel cell operation at not the lower temperature (70 °C) and full humidification (100%) but the elevated temperature (80 °C) and lower relative humidity (50 and 75%). The blended ionomer-based catalyst layers with higher water uptake and porous CL structure result in higher fuel cell performance and better mass transport than the single ionomer-based catalyst layers.

We describe the direct formation of mixed-phase (1T and 2H) MoS2 layers on Si as a photocathode via atomic layer deposition (ALD) for application in the photoelectrochemical (PEC) reduction of water to hydrogen. Without typical series-metal interfaces between Si and MoS2, our p-Si/SiOx/MoS2 photocathode showed efficient and stable operation in hydrogen evolution reactions (HERs). The resulting performance could be explained by spatially genuine device architectures in three dimensions (that is, laterally homo and vertically heterojunction structures). The ALD-grown MoS2 overlayer with the mixed-phase 1T and 2H homojunction passivates light absorber and surface states and functions as a monolithic structure for effective charge transport within MoS2. It is also beneficial in the operation of p-i-n heterojunctions with inhomogeneous barrier heights due to the presence of mixed-phase cocatalysts. The effective barrier heights reached up to 0.8 eV with optimized MoS2 thicknesses, leading to a 670 mV photovoltage enhancement without employing buried Si p-n junctions. The fast-transient behaviors via light illumination show that the mixed-phase layered chalcogenides can serve as efficient cocatalysts by depinning the Fermi levels at the interfaces. A long-term operation of ~ 70 h was also demonstrated in a 0.5 M H2SO4 solution.