In this study, various diamine monomers were used to synthesize aramid polymer films via a low-temperature solution condensation reaction with diacid chloride. For diamines with relatively high basicity, the reaction system became opaque because amine salt formation inhibited polymer synthesis. Meanwhile, low-basicity diamines with strong electron-withdrawing groups, such as CF3 and sulfone, were smoothly polymerized without amine salt formation to provide highly viscous solutions. The acid byproduct HCl generated during polymerization was removed by adding propylene oxide to the reaction vessel and converting the acid into highly volatile inert substances. The resulting solutions were used as varnishes without any additional purification, and polymer films with an excellent appearance were easily obtained through a conventional casting and convection drying process. The films neither tore nor broke when pulled or bent by hand; furthermore, even when heated up to 400°C, they did not decompose or melt. Moreover, polymers prepared from 2,2-bis (trifluoromethyl) benzidine (TFMB) and bis (4-aminophenyl) sulfone (pAPS) did not exhibit glass transition until decomposition. The prepared polymer films showed a high elastic modulus of more than 4.1 GPa and a high tensile strength of more than 52 MPa. In particular, TFMB-, pAPS-, and 2,2-bis (4-aminophenyl) hexafluoropropane-based polymer films were colorless and transparent, with very high light transmittances of 95%, 96%, and 91%, respectively, at 420 nm and low yellow indexes of 2.4, 1.9, and 4.3, respectively.

Graphene materials synthesized using direct laser writing (laser-induced graphene; LIG) are fa-vorable sensor materials because of their large surface area, ease of fabrication, and cost effec-tiveness. In particular, LIG decorated with metal nanoparticles (NPs) has been used in various sensors, including chemical sensors and electronic and electrochemical biosensors. However, the effect of metal decoration on LIG sensors remains controversial; hypotheses based on computa-tional simulations do not always match experimental results, and even experimental results re-ported by different researchers have not been consistent. In the present study, we explored the effects of metal decorations on LIG gas sensors, with NO2 and NH3 gases as representative oxi-dizing and reducing agents, respectively. To eliminate unwanted side effects arising from metal salt residues, metal NPs were directly deposited by vacuum evaporation. Although the gas sen-sitivities of the sensors deteriorate upon metal decoration irrespective of the metal work function in the case of NO2 gas, they improve upon metal decoration in the case of NH3 exposure. A careful investigation of the chemical structure and morphology of the metal NPs in the LIG sensors shows that the spontaneous oxidation of metal NPs with a low work function changes the be-havior of the LIG gas sensors and that the sensor behaviors under NO2 and NH3 gases follow different principles.