Porous structured metallic implants are preferable as bone graft substitutes due to their faster tissue integration mediated by bone in-growth and vascularization. The porous scaffolds/ implants should also mimic the graded structure of natural bone to ensure a match of mechanical properties. This article presents a method to design graded porous structured acetabular implant and identifies the suitable parameters for manufacturing the model through additive manufacturing. The design method is based on slice-wise modification to ensure continuity of gradation. Modification of the slices was achieved through the binary image processing route. A geodesic dome type design was adopted for developing the acetabular cup model from the graded porous structure. The model had a solid shell with the target porosity and pore size gradually changing from 65% and 950 µm, respectively, in the inner side to 75% and 650 µm, respectively, towards the periphery. The required dimensions of the unit structures, and the combinations of pore structure and strut diameter to obtain the target porosity and pore size were determined analytically. Suitable process parameters were identified to manufacture the model by Direct Metal Laser Sintering (DMLS) using Ti6Al4V powder after carrying out a detailed experimental study to minimize the variation of surface roughness and warping over different build angles of the strut structures. A dual contour scanning was implemented to simplify the scan strategy. The minimum diameter of struts that could be manufactured using the selected scanning strategy and scanning parameters was found to be 375 µm. Finally, the model was built and from the micro-CT data, the porosities and pore sizes were found to be closely conforming to the designed values. The stiffness of the structures, as found from compression testing, was also found to be well matching with that of human trabecular bone. Further, the structure exhibited compliant bending-dominated behavior under compressive loading.

17-4PH steel is a widely used grade for precipitation hardening. The growing demand for modern materials with high corrosion and tribological resistance has led to its increased use for the production of medical devices. With additive manufacturing (AM), complex functional shapes can be achieved for medical applications. Direct laser metal sintering (DMLS) technology makes it possible to obtain products with complex architectures, but it also faces various challenges, including imperfections in the surface layer of products due to the use of 3D printing technology itself. This study analyzed the abrasive wear resistance in 0.9% NaCl solution of 17-4PH steel produced by DMLS technology. In order to improve the properties of the surface layer after 3D printing and to improve the tribological wear resistance of the steel, a shot peening (SP) process using CrNi shot and ceramic beads (based on ZrO2) was applied. The chemical and phase composition of the materials obtained, Vickers hardness, surface roughness, and microscopic and SEM imaging were investigated. Tribological tests were carried out using the ball-on-disc method, and the surfaces that showed traces of abrasion to identify wear mechanisms were subjected to SEM analysis. The chemical composition was in accordance with the EOS manufacturer's declarations, and the presence of austenite and martensite was found in the post-production state, while a higher content of martensitic phase was found in the case of peened samples due to phase transformations. The surface hardness of the peened samples increased more than twice, and the post-treatment roughness increased by 12.8% after peening CrNi steels and decreased by 7.8% after peening ZrO2 relative to reference surfaces. Roughness has an identifiable effect on sliding wear resistance. Higher roughness promotes material loss. After the SP process, the coefficient of friction increased by 15.5% and 20.7%, while the wear factor (K) decreased by 25.9% and 32.7% for the samples peened with CrNi steels and ZrO2, respectively. Abrasive and adhesive mechanism were dominant featured with slight fatigue. The investigation showed a positive effect of SP on the tribological properties of DMSL 17-4PH.

A useful and increasingly common additive manufacturing (AM) process is the selective laser melting (SLM) or direct metal laser sintering (DMLS) process. SLM/DMLS can produce full-density metal parts from difficult materials, but it tends to suffer from severe residual stresses introduced during processing. This limits the usefulness and applicability of the process, particularly in the fabrication of parts with delicate overhanging and protruding features. The purpose of this study was to examine the current insight and progress made toward understanding and eliminating the problem in overhanging and protruding structures. To accomplish this, a survey of literature was undertaken, focusing on process modeling (general, heat transfer, stress and distortion, and material models), direct process control (input and environmental control, hardware-in-the-loop monitoring, parameter optimization, and post-processing), experiment development (methods for evaluation, optical and mechanical process monitoring, imaging, and design-of-experiments), support structure optimization, and overhang feature design; approximately 140 published works were examined. The major findings of this study were that a small minority of the literature on SLM/DMLS deals explicitly with the overhanging stress problem, but some fundamental work has been done on the problem. Implications, needs, and potential future research directions are discussed in-depth in light of the present review.