The development of Al-Ni alloys with a controlled microstructure has had a great impact on the field of study of aluminum-based alloys. In the present research, the influence of thermal parameters on the grain structures resulting from the directional solidification process of Al-Ni alloys with different alloy content has been studied. It has also been evaluated how different structures and the distribution of second phases influence the corrosion behavior and microhardness of alloys. The columnar-to-equiaxed transition (CET) was observed to occur when the temperature gradient in the melt decreased to values between 1.3 to 2.9 ° C/cm. In addition, a small increase in the microhardness values was observed as a function of the Ni-content. When the Ni-content increase, the resistance to polarization decreases for samples with equiaxed grain structure, throughout the range of compositions studied. Furthermore, the equiaxed grain structure presents higher resistance to polarization values than the columnar grain zone, for alloys with a composition equal to or lower than the eutectic composition.

To obtain smooth coatings of TiO2 for building a new design of Ti-6Al-4V heart valve, the anodic oxidation technique in pre-spark conditions was evaluated. TiO2 coating is necessary for its recognize biocompatibility and corrosion resistance. A required feature on surfaces in contact with blood is a low level of roughness (Ra ≤ 50 nm) that not favor the formation of blood clots. The present paper compares the coatings obtained by anodic oxidation of the Ti-6Al-4V alloy using H2SO4 at different concentrations (0.1 M to 4 M) as electrolyte and applying different voltages (from 20 V to 70 V). Color and morphological analysis of coatings are performed using optical and scanning microscopy. The crystalline phases were analyzed by glancing X-ray diffraction. By varying the applied voltage different interference colors coatings were obtained. The differences in morphologies of the coatings, due to the change in concentration, are more evident at high voltages limiting the oxidation conditions for the desired application. Anatase phase was detected from 70 V for 1 M H2SO4. An increase in the concentration of H2SO4 decreases the voltage at which the transformation of amorphous to crystalline coatings occurs, i.e. with 4 M H2SO4 the anatase phase appears at 60 V.