The utilization of selective laser melting (SLM) for high entropy alloys (HEAs) holds significant promise in commercial applications, and substantial experimental research efforts have been directed toward this domain. To take advantage of the reported experimental data of SLM manufactured (SLM-ed) HEAs and reduce unnecessary experimentation, this study incorporates machine learning (ML) techniques for the phase and tensile properties prediction of SLM-ed HEAs, thus presenting a novel avenue for accelerating the discovery of new SLM-ed HEAs. Through the adjustment of material descriptors and machine learning models, a model has been developed with an impressive accuracy of 93.8% in distinguishing between face-centered cubic (FCC), body-centered cubic (BCC), and dual-phase (FCC+BCC). Additionally, optimized models have been devised for the prediction of tensile properties, namely ultimate tensile strength (UTS), yield strength (YS), and elongation (δ), achieving noteworthy MAPEs (mean absolute percentage errors) of 10.33%, 8.55%, and 28.48%, respectively. Furthermore, several HEAs were fabricated using SLM, and the experimental outcomes exhibited a favorable alignment with the predicted results. These efforts carry significant implications in advancing the utilization of SLM for HEAs.

To enhance the applicability of dual-phase high-entropy alloys (HEAs) like Fe32Cr33Ni29Al3Ti3, fabricated via selective laser melting (SLM), a focus on improving their mechanical properties is essential. As part of this effort, heat treatment was explored. This study compares the microstructure and mechanical properties of the as-printed sample with those cooled in water after undergoing heat treatment at temperatures ranging from 1000 to 1200 ℃ for 1 hour. Both pre- and post-treatment samples reveal a dual-phase microstructure comprising FCC and BCC phases. Although heat treatment led to a reduction in tensile and yield strength, it significantly increased ductility compared to the as-printed sample. This strength-ductility trade-off is related to changes in grain sizes with ultrafine grains enhancing strength and micron grains optimizing ductility, also the influence of the content of FCC/BCC phases and dislocation density. In particular, the sample heat-treated at 1000 °C for 1 hour and then water-cooled exhibited a better combination of strength and ductility, a yield strength of 790 MPa, and an elongation of 13%. This research offers innovative perspectives on crafting dual-phase HEA of Fe32Cr33Ni29Al3Ti3, allowing for tailorable microstructure and mechanical properties through a synergistic approach involving SLM and heat treatment.