Fired bricks have shown tremendous potential as a construction material due to their properties. However, their use required some specifications in terms of quality, resistance, and durability. In developing countries, the lack of tools to make test specimens leads to many defects in these brick specimens responsible for low durability and weak precision during mechanical tests and shrinkage. In this study, a simple and traditional method of making test bricks is presented. This simple method allows the production of bricks with the required properties. This method is especially efficient for a firm or semi-soft pastes consistency. The handmade pastes do not stick into the walls of the mold like the case of steel molds and it gives specimens with standard shape, smooth surface, and sharp edges. The resulting fired bricks exhibit high mechanical strength comparable and even better than those of conventional methods.

The Black Steel slag (Ss) and phosphogypsum (PG) are industrial wastes produced in Morocco. In order to reduce these two wastes and to evaluate their pozzolanic reactivity in the presence of water, they were incorporated into bentonite (B) mixed with lime (L). The studied mixtures (BLW, BL-PG-W and BL-PG-Ss-W) were analyzed by X-ray diffraction, Infrared spectroscopy, Raman spectroscopy and SEM/EDX analysis. Compressive strength tests were performed on hardened specimens. The results obtained show that the hydration kinetics of the B-L-W and B-L-PG-W mixtures are slow. The addition of PG to a bentonite-lime mixture induces the formation of new microstructures such as hydrated calcium silicate (C-S-H) and ettringite, which increases the compressive strength of the cementitious specimens. The addition of the Ss to a mixture composed by 8%PG and 8%L-B accelerates the kinetics of hydration and activates the pozzolanic reaction. The presence of C2S in the slag helps to increase the mechanical strength of the mixture B-L-PG-Ss. The compressive strength of the mixtures BL-W, BL-PG-W and BL-PG-Ss-W increases from 15 to 28 days of setting. After 28 days of setting, 8% of Sc added to the mixture 8% PG-8%L-B is responsible for an increase of the compressive strength to 0.6 MPa.

Two peat cores from two bogs were used to reconstruct high–resolution changes in atmospheric Pb accumulation rate (Pb AR) in Belgium during the Roman period. The two records were compared to assess the reliability of peat cores as archives of atmospheric Pb deposition and to established histories of atmospheric emissions from anthropogenic sources. To address these issues we analyze Pb concentration and isotopes, using ICP-MS, LA-ICP-MS and MC-ICP-MS in two peat sections, spanning 1000 yr each. Lead concentrations in the two cores range from 0.1 to 60 μg g⁻¹, with the maxima between 15 and 60 μg g⁻¹. The average natural background of Pb AR was 0.005± 0.002 mg m^-2 yr^-1 and the maximum ranges from 0.7 to 1.2 mg m^-2 yr^-1 between 50 BC and AD 215. The highest Pb AR exceed the pre-Roman period values by a factor of 25-30. Pb isotopic composition indicates that mining and metallurgical activities were the predominant sources of pollution during the Roman period. The Pb AR and chronologies in the Belgian peat cores are consistent with those reported for other continental archives as lake sediments, peat and ice cores.