Vanadium(IV) chalcogenide materials are of increasing interest for use in catalysis and energy conversion-related applications. Since no ternary compounds are yet known in the V–Se–Te system, we studied ternary VwSeyTe2–y (w = 1.10, 1.13; y = 0.42, 0.72) phases crystallizing in space group P3m1 (no. 164). Two single-crystal specimens with differing compositions of a solid solution were obtained using the ceramic method. All products were characterized by either single-crystal or powder X-ray diffraction. The lattice parameters increase with rising tellurium content in accordance to the larger ionic radius of the tellurium anion compared to selenium. The chemical compositions were confirmed by energy dispersive X-ray spectroscopy. Further, magnetic measurements revealed mostly antiferromagnetic properties. Simultaneous differential scanning calorimetry/thermogravimetric analyses in nitrogen atmosphere showed endothermic decomposition accompanied by the formation of VN. The results of this work can serve as a basis for the synthesis of new phases in the V–Se–Te and related vanadium chalcogenide systems.

Fe[C5H5N]2[N(CN)2]2 (1) was synthesized from a reaction of stoichiometric amounts of NaN(CN)2 and FeCl2·4 H2O in a methanol/pyridine solution. Single-crystal and powder diffraction show that 1 crystallizes in the monoclinic space group I2/m (no. 12), different from Mn[C5H5N]2[N(CN)2]2 (P21/c, no. 14) due to tilted pyridine rings, with a = 7.453(7) Å, b = 13.167(13) Å, c = 8.522(6) Å, β = 114.98(6)° and Z = 2. ATR-IR, AAS, and CHN measurements confirm the presence of dicyanamide and pyridine. Thermogravimetric analysis shows that π-stacking interactions of the pyridine rings play an important role in structural stabilization. Based on DFT-optimized structures, a chemical bonding analysis was performed using a local-orbital framework by projection from a plane-wave basis. The resulting bond orders and atomic charges are in good agreement with the expectations based on the structure analysis. SQUID magnetic susceptibility measurements show a high-spin state FeII compound with predominantly antiferromagnetic exchange interactions at lower temperatures.