The present study aimed to characterize the microstructure of a temporary 3D printing resin (Resilab Temp), evaluating the optical properties and mechanical behavior according to different post-processing curing times. For the analysis of the surface microstructure and establishment of the best printing pattern, samples in bar format following ISO 4049 (25 x 10 x 3 mm) were designed in CAD software (Rhinoceros 6.0), printed on the W3D printer (Wilcos), and light-cured in Anycubic Photon at different times (without curing, 16 minutes, 32 minutes, and 1 hour). For the structural characterization, analyses were carried out in FTIR (Fourier Transform Infrared Spectroscopy) and Scanning Electron Microscopy (SEM). The mechanical behavior of the resin was based on flexural strength tests and Knoop microhardness. Color and translucency analysis were performed with a spectrophotometer (VITA Easy Shade Advanced 4.0), which was evaluated following CIELab, using gray, black, and white backgrounds. All analyses were performed immediately after making the samples and repeated after thermal aging with 2 thousand cycles (5-55 °C). The results obtained were statistically analyzed with a significance level of 5%. FT-IR analysis showed about a 46% degree of conversion on the surface and 37% in the center of the resin sample. The flexural strength was higher for the groups polymerized for 32 min and 1h, while the Knoop microhardness did not show a statistical difference between the groups. Color and translucency analysis also did not show statistical differences between groups. According to all the analyses carried out in this study, for the evaluated material, the post-polymerization time of 1 hour can be suggested to improve the mechanical performance of 3D-printed devices.

Mixtures of methacrylic polymers are the most common materials for making composites to be used as resins for dental and cosmetic applications. Some of these mixtures are composed by poly (ethyl methacrylate) (PEMA) and poly (methyl methacrylate) (PMMA), which constitute a solid component to be mixed with a liquid component made out of methacrylate monomers. The reaction between the thermal initiator benzoyl peroxyde (BPO) present in the solid component and the activator of the polymerization process, N,N-dimethyl-p-toluidine (DMT) present in the liquid component, gives rise to thermoset materials. In the present study, different liquid formulations composed by a mixture of two methacrylic monomers, ethyl methacrylate (EMA) and triethylene glycol dimethacrylate (TEGDMA) for cosmetic applications, were prepared and characterized, using a commercial powder (POW) composed by PEMA and PMMA. With the aim of improving workability during final application of the material, it was necessary to slow down the polymerization rate of liquid formulations. Their thermal behaviour was investigated by DSC in order to check the polymerization rate. Thermal stability of final materials was determined by TGA. DMTA, microindentation hardness and impact tests were performed on final materials, to assess their performance with respect to standard formulation. The combination of thermal and mechanical properties allows choosing which formulations could be suitable for use in cosmetics.

Cariogenic oral biofilms cause a considerable amount of recurrent dental caries around composite restorations every year, resulting in unprosperous oral health status and expensive restorative treatment for many patients. Quaternary ammonium monomers that can be copolymerized with the current dental resin systems have been increasingly explored for modulation of dental plaque biofilm growth over dental composite surfaces. Here, we investigated the effect of bis(2-methacryloyloxyethyl) dimethylammonium bromide (QADM), against human overlying mature oral biofilms grown intra-orally in human participants for 7 and 14 days, for the first time. Seventeen volunteers wore palatal devices containing composite specimens containing 10% by mass of QADM or a control composite without QADM. After 7 and 14 days, the adherent biofilms were collected for determination of bacterial counts via colony-forming unit (CFU) counts. The biofilm viability, chronological changes, and percentage coverage were also determined by live/dead staining. QADM composites caused a significant inhibition of S. mutans biofilm formation for up to seven days. No difference in the CFU values were found for the 14-day period. Our findings suggest that (1) QADM composite was successful in inhibiting 1-3 day biofilms in the oral environment in vivo; (2) QADM significantly reduced the portion of S.mutans group in a time course where patients at high risk of caries would develop initial enamel carious lesions; and (3) stronger antibiofilm activity is required for the control of mature long-term cariogenic biofilms. These results provide a perspective on the value of integrating bioactive restorative materials with traditional caries management approaches into clinical practice. Contact-killing strategies via dental materials aiming to prevent or at least reduce high numbers of cariogenic bacteria seem to be a promising approach in patients at high risk of recurrence of dental caries around composites.

This publication describes the influence of residue monomers in synthesized pressure-sensitive adhesives based on acrylics on main performance such as tack, peel adhesion, shear strength and shrinkage in form of transfer tapes used for joining wooden elements in furniture industry. The discussed carrier-free adhesive tapes are synthesized by photo-crosslinking and photopolymerization with UV radiation of photoreactive prepolymers sandwiched between two adhesive siliconized polyester films. The simultaneous crosslinking and polymerization process under UV lamps carried out under UV lamps placed simultaneously above and below the crosslinked photoreactive polymer layer leads to the production of a carrier-free adhesive film. In this test series it were investigated to what how the intensity of UV radiation and the time of its exposure affect the viscosity of photoreactive compositions, and then the content of unreacted monomers in them and, subsequently, the method of their crosslinking and polymerization, and the concentration of the photoreactive crosslinking compound leading to the obtaining of transfer adhesive tapes, and thus on their tray, peel adhesion, shear strength and shrinkage on the surface of the wood.

A new mesogenic non-symmetric dimeric monomer with a terminal olefin function, forming a twist bend nematic (Ntb) as well as a nematic (N) phase was synthesized, using an enhanced synthetic methodology, which avoids isomerization of the terminal double bond in the preparation of the dimer. This monomer was attached to a pentamethyldisiloxane group, resulting in SmA LC phase behaviour of the ensuing material. Linking the monomer to a siloxane main chain resulted in nematic phase behaviour. Detailed studies with the Ntb phase forming dimer DTC5C7 show full miscibility of the dimer and the new LC polymer in the LC state, suggesting that the side-chain LC polymer forms a Ntb phase as the low temperature nematic phase. Copolymerizing the monomer with a cyanobiphenyl based monomer allows to tune the glass transition and phase behavior further.