Helicobacter pylori is a gastric pathogen that infects nearly half of the global population and is recognized as a group 1 carcinogen by the Word Health Organization. The global rise in antibiotic resistance has increased clinical challenges in treating H. pylori infections. Biofilm growth has been proposed to contribute to H. pylori’s chronic colonization of the host stomach, treatment failures, and the eventual development of gastric diseases. Several components of H. pylori have been identified to promote biofilm growth, and several of these may also facilitate antibiotic tolerance, including the extracellular matrix, outer membrane proteins, the coccoid morphology, modulated metabolism, efflux pumps, and virulence factors. Recent developments in therapeutic approaches targeting H. pylori biofilm have shown that synthetic compounds, such as small molecule drugs and plant-derived compounds, are effective at eradicating H. pylori biofilms. These combined topics highlight the necessity for biofilm-based research in H. pylori, to improve current H. pylori targeted therapeutic approaches and alleviate relative public health burden. In this review we discuss recent discoveries that have decoded the life cycle of H. pylori biofilms and current biofilm targeted treatment strategies.

A novel and simple method to improve the corrosion resistance of copper by constructing a 3D 1-dodecanethiol self-assembled monolayers (SAMs) in 3.5% NaCl solution is reported in this study. Several drops of 1% H3PO4 solution are thinly and uniformly distributed on copper surface to form a 3D nanostructure constituted by Cu3(PO4)2 nanoflowers. The anticorrosion properties of 1-dodecanethiol SAMs on copper surface and on copper surface treated with H3PO4 solution were evaluated. Results demonstrated that 1-dodecanethiol SAMs on bare copper surface exhibit good protection capacity, whereas a copper surface pretreated with H3PO4 solution can substantially enhance the corrosion resistance of 1-dodecanethiol SAMs.

To understand the enhanced protection mechanism of CoCrNiAlY-YSZ-LaMgAl11O19 dou-ble-layer ceramic coating with aluminum plating, a finite element simulation method was used to simulate the distribution of thermal stress in the coating in all directions. The results show that in the air exposure of the un-aluminized coating, high temperature causes a large radial thermal stress on the surface of the LaMgAl11O19 (LMA) layer, and it increases with the increase in temperature, which is the main reason for the initiation of axial cracks. After arc aluminum plating, the aluminum plating layer effectively inhibited the volume shrinkage of the coating through good adhesion to the coating and internal diffusion, the thermal stress of the coating was considerably reduced, and the CoCrNiAlY-YSZ-LMA coating had an effective enhancement and protection effect; however, there was still a certain amount of shear thermal stress inside the LMA layer, the top of the crack, and the bottom of the crack. This thermal stress caused the initi-ation of radial microcracks in the LMA layer, which also becomes a risk point for the failure of the aluminum coating.