The effects of the additives (silicon carbide and titania) and sintering temperatures on the phases developed, physical and mechanical properties of sintered mullite-carbon ceramic composite produced from kaolin and graphite was investigated. The kaolin and graphite of known mineralogical composition were thoroughly blended with 5 and 3 (vol.) % silicon carbide and titania respectively. From the homogeneous mixture of kaolin, graphite and titania, standard samples were prepared via uniaxial compaction. The test samples produced were subjected to firing (sintering) at 1300˚C, 1400˚C and 1500˚C. The sintered samples were characterized for the developed phases using x‐ray diffractometry analysis, microstructural morphology using ultra‐high resolution field emission scanning electron microscope (UHRFEGSEM). Various physical and mechanical properties were determined. It was observed that the addition of SiC/TiO2 additives to the samples made them to possess very low oxidation indices .This also resulted in improvement in the bulk densities and cold crushing strength of the sample when compared with those without additives. It was concluded that the addition of SiC/TiO2 additives improves on the high temperature oxidation resistance of the mullite-carbon ceramic composite sample.

In interceptive treatments in which impacted teeth (incisor or first permanent molar) should be included into the dental arch, the main clinical problem is the provision of an anchorage area and a suitable appliance. The use of laser sintered metal orthodontic grids, designed and printed digitally, has expanded the boundaries of orthodontic treatment, especially in its interceptive phase. Our aim is to describe a digital model for providing anchorage during orthodontic-surgical traction of impacted teeth in the mixed dentition period. We present the treatment of three clinical cases with digitally projected and printed metal grids used for anchorage. In the described clinical cases, individually designed anchorage systems were used. They were created through design software and after that the metal grids were printed. The devices are placed in the oral area and don’t disturb the aesthetics of the patient in any way. The advantages of individual designed metal support grids allow to accommodate the features of relief of the hard palate and alveolar bone. This makes the grids comfortable for the patient and rigid enough to perform orthodontic tractions at the same time. The printed additional grids are applicable in mixed dentition and in complicated clinical cases in permanent dentition. Their individuality allows segmental treatments or treatments in cases requiring additional anchorage further from the active force.

Abstract: Composite sintered bodies comprising silicon dioxide (SiO2) nanoparticles dispersed in β-tricalcium phosphate (β-TCP) were prepared. The addition of nano-sized colloidal SiO2 to the β-TCP produced well-dispersed secondary phase nanoparticles that promoted densification by suppressing grain growth and increasing volume shrinkage of the sintered bodies. The SiO2 was found not to react with the β-TCP at 1120 °C and the substitution of silicon for phosphorous to produce a solid solution did not occur. This lack of a reaction is ascribed to the absence of avail-able calcium ions to compensate for the increase in charge associated with this substitution. The SiO2 nanoparticles were found to be present near the intersections of grain boundaries in the β-TCP. A β-TCP composite sintered body containing 4.0 wt% SiO2 exhibited a bending strength comparable to that of cortical bone and hence could potentially be used as a bone filling material.

A sintered wick was formed in a heat pipe through the process of sintering a mixture of copper powder with particle sizes of 100㎛ and 200㎛, mixed with a pore-forming agent. On application to the heat pipes. The thermal resistance of heat pipes containing a sintered wick was calculated for different tilting angles (0°, 45°, and 90°) according to the type of powder, thickness of the sintered wick, and the filling ratio of the working fluid. The heat transfer efficiencies were evaluated through temperature tests. The capillary force, which is closely related to heat transfer efficiency, is determined by the effective pore radius resulting from the sintering of the copper powder. Furthermore, it was observed that the heat transfer performance of the heat pipe was at its best when the working fluid filling ratio was 30%. Additionally, the width of the wick was found to have a direct correlation with the heat transfer performance.