Leather waste was carbonized at 800 °C in inert atmosphere. The resulting biochar was coated in situ with polypyrrole nanotubes produced by the oxidation of pyrrole in the presence of methyl orange. The composites of carbonized leather with deposited polypyrrole nanotubes of various composition were compared with similar composites based on globular polypyrrole. Their molecular structure was characterized by infrared and Raman spectra. Both conducting components formed a bicontinuous structure. The resistivity determined by four-point van der Pauw method was monitored as a function of pressure applied up to 10 MPa. The typical conductivity of composites was of the order of tenths to units S cm−1 and it was always higher for polypyrrole nanotubes than for globular polypyrrole. The conductivity decreased by 1–2 orders of magnitude after treatment with ammonia but still maintained a level acceptable for applications operating under non-acidic conditions. The composites were tested for dye adsorption, viz. cationic methylene blue and anionic methyl orange, using UV-spectroscopy. The composites are designed for the future use as functional adsorbents controlled by the electrical potential.

Interface solar steam generation (ISSG) are charming for its applications in desalination and wastewater treatment. Biomass is an attractive substrate for utilizing solar vapor evaporators because of its natural pore structure and water transportability. Polymers like polydopamine (PDA) and polypyrrole (PPy) with broadband spectrum absorption are fascinating in photothermal materials (PTMs). Herein, PDA coated daikon-based (PDA-DK) and PPy coated daikon-based (PPy-DK) PTMs have been exploited for solar steam generation. When polyethylene foam (PEF) was used as an insulating layer to limit heat loss from the PTMs to bulk water, the evaporation rate of PDA-DK and PPy-DK was raised from 0.82 kg m–2 h–1 and 0.96 kg m–2 h–1 to 1.50 kg m–2 h–1 and 1.60 kg m–2 h–1, respectively. Meanwhile, the corresponding photothermal conversion efficiency was increased to 89.01% and 98.97%, which was increased by nearly 40% under 1-sun irradiation. In addition, PDA-DK and PPy-DK exhibited remarkable stability for the solar steam generation without significant change through 15 cycles. Furthermore, PDA-DK and PPy-DK could effectively desalt seawater and purify dyeing wastewater. All the results indicate that PDA-DK and PPy-DK have great potential in real-world applications for solar steam generation.

Adhesion of polymers to surfaces is of upmost importance in timely applications such as protective coatings, biomaterials, sensors, new power sources and soft electronics. In this context, this work examines the role of molecular interactions in the adhesion of polypyrrole thin films to flexible Indium Tin Oxide (ITO) electrodes grafted with aryl layers from various diazonium salts, namely 4-carboxybenzenediazonium (ITO-CO₂H), 4-sulfonicbenzenediazonium (ITO-SO₃H), 4-N,N dimethylbenzenediazonium (ITO-N(CH₃)₂), 4-aminobenzenediazonium (ITO-NH₂), 4-cyanobenzenediazonium (ITO-CN) and 4-N-phenylbenzenediazonium (ITO-NHPh). It was demonstrated that PPy thin layers were adherent to these surfaces, whereas adhesion failure was noted on bare ITO, following simple solvent washing or sonication. Adhesion of the polypyrrole was investigated in terms of the hydrophilic/hydrophobic character of the underlying aryl layer as probed by contact angle measurements. It was found that sulfonic acid doped polypyrrole (PPy-BSA) thin films were preferably deposited on the most hydrophobic surfaces. More importantly, the redox properties and electrochemical impedance of PPy were closely related to the hydrophobic character of the aryl layers. This work demonstrates that diazonium compounds are unique molecular glues for conductive polymers, and permit to tune their interfacial properties. With diazonium-based robust, architectured interfaces, one can design high performance materials for e.g.sensors, printed soft electronics and flexible thermoelectrics.

Polypyrrole (PPy)-capped caped silver nanowire (Ag NW) nanomaterials (core–shell rod-shaped Ag NW@PPy) were synthesized suing a one–port suspension polymerization technique. The thickness of PPy layer on the 50-nm-thickness/15-μm-length Ag NW was effectively controlled to 10, 40, 50, and 60 nm. Thin films cast from one-dimensional conductive Ag NW@PPy formed a three-dimensional (3-D) conductive porous network structure and provided excellent electrochemical performance. The 3-D Ag NW@PPy network can significantly reduce the internal resistance of the electrode and maintain structural stability. As a result, a high specific capacitance of 625 F/g at a scan rate of 1 mV/s was obtained from the 3-D porous Ag NW@PPy composite film. The cycling performance over a long period exceeding 10,000 cycles was also evaluated. We expect that our core–shell-structured Ag NW@PPy composites and their 3-D porous structure network films can be applied as electrochemical materials for the design and manufacture of supercapacitors and other energy storage devices.

Hybrid organic/inorganic conducting and magnetic composites of core–shell type have been prepared by in-situ coating of nickel microparticles with polypyrrole. Three series of syntheses have been made. In the first, pyrrole was oxidized with ammonium peroxydisulfate in water in the presence of various amounts of nickel and the composites contained up to 83 wt% of this metal. The similar syntheses in 0.1 M sulfuric acid followed. Finally, the composites with polypyrrole nanotubes were prepared in water in the presence of structure-guiding methyl orange dye. FTIR and Raman spectroscopies confirmed the formation of polypyrrole. The resistivity of composite powders of the order of tens to hundreds Ω cm was monitored as a function of pressure up to 10 MPa. The resistivity of composites slightly increased with increasing content of conducting nickel. This apparent paradox is explained by the coating of nickel particles, which prevents their contacts and generation of metallic conducting pathways. Electrical properties were practically independent of the way of composite preparation or nickel fraction and were controlled by polypyrrole phase. On the contrary, magnetic properties were determined exclusively by nickel content. The composites were used as a solid phase to prepare a magnetorheological fluid. The test showed better performance when compared with a different nickel system.

A simple and effective surface modification of polyester fabrics with sulfuric acid to improve the interfacial deposition of polypyrrole was presented in our work. A range of sulfuric acid concentrations were analyzed by studying water contact angle. Effect of sulfuric acid modification on the deposition of polypyrrole was investigated by sheet resistance and color depth of fabric samples. Polyester fabrics coated with polypyrrole layer were confirmed by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), X-Ray diffraction spectra (XRD), Fourier transform infrared spectroscopy (FTIR). XPS showed that sulphur containing functional groups were obviously appeared on the polyester fiber surface after modification, which were advantageous to promote the deposition of polypyrrole onto polyester fabrics. The improved deposition increased electrical conductivity of fabric samples.

Highly sensitive multicomponent materials designed for the recognition of hazardous compounds request control over interfacial chemistry. The latter is key parameter in the construction of the sensing (macro)molecular architectures. In this work, multi-walled carbon nanotubes (in short, CNTs) were deposited on diazonium-modified flexible ITO electrodes prior to electropolymerization of pyrrole. This three step process, including diazonium electroreduction, deposition of CNTs and electropolymerization, provided adhesively bonded polypyrrole-wrapped CNT composite coatings on aminophenyl-modified flexible ITO sheets. The aminophenyl (AP) groups were attached to ITO by electroreduction of the in situ generated aminobenzenediazonium compound in aqueous, acidic medium. For the first time, polypyrrole (PPy) was electrodeposited in the presence of both benzenesulfonic acid (dopant) and ethylene glycol-bis(2-aminoethylether)-tetraacetic acid (EGTA) which acts as a chelator. The flexible electrodes were characterized by XPS, Raman and scanning electron microscopy (SEM) which provided strong supporting evidence for the wrapping of CNTs by the electrodeposited PPy. Indeed, the CNT average diameter increased from 182.6 nm to 274.8, 35.65.9 and 17520.1 after 1, 5 and 10 of electropolymerization of pyrrole. The PPy/CNT/NH2-ITO films generated by this strategy exhibit significantly improved stability and higher conductivity compared to a similar PPy coating without any embedded CNTs as assessed by from electrochemical impedance spectroscopy measurements. The potentiometric response was linear in the 10-83×10-7 mol.L-1 Pb(II) concentration range and the detection limit was 2.9×10-9 mol.L-1 at S/N=3. The EGTA was found to drastically improve selectivity for Pb(II) over Cu(II). To account for this improvement, density functional theory (DFT) was employed to calculate the EGTA-metal ion interaction energy which was found to be -374.6 and -116.4 kJ/mol for Pb(II) and Cu(II), respectively, considering solvation effects. This work demonstrates the power of a subtle combination of diazonium coupling agent, CNTs, chelators and conductive polymers to design high-performance electrochemical sensors for environmental applications.

A biomimetic, ion-imprinted polymer (IIP) was prepared by electropolymerization of pyrrole at the surface of gold electrodes decorated with vertically grown ZnO nanorods. The vertical growth of the nanorods was achieved via an ultrathin aryl monolayer grafted by reduction of diazonium salt precursor. Pyrrole was polymerized in the presence of L-cysteine as chelatant agent and Hg(II) (template). Hg(II)-imprinted polypyrrole (PPy) was also prepared on bare gold electrode in order to compare the two methods of sensor design (Au-ZnO-IIP vs Au-IIP). Non-imprinted PPy was prepared in the same conditions, however in the absence of any Hg2+ template. The strategy combining diazonium salt modification and ZnO nanorod decoration of gold electrodes permitted to increase considerably the specific surface and thus to improve the sensor performances. The limit of detection (LOD) of the designed sensor was ~1 pM, the lowest value ever reported in literature. The dissociation constants between PPy and Hg2+ were estimated at [Kd1 = (7.89 ± 3.63) mM and Kd2 = (38.10 ± 9.22) pM]. The sensitivity of the designed sensor was found to be 0.692 ± 0.034 μA/pM. The Au-ZnO-IIP was found to be highly selective towards Hg(II) compared to cadmium, lead and copper ions. This sensor design strategy could open up new horizons in monitoring toxic heavy metal ions in water and therefore contribute to enhance environmental quality.

This research aims to deepen the understanding of the relationship between conductivity and morphology in polypyrrole (PPy) via a comparison of the bipolaron to polaron ratios with a focus on the C-H deformation area. PPy samples were synthesized with different surfactants: sodium dodecyl sulfate (SDS), cetyltrimethylammonium bromide (CTAB), and tween 80 (TW). The study revealed that SDS significantly altered the bipolaron and polaron in C-H deformation region and showed higher conductivity than other surfactants. Notably, the morphological shifts to a sheet-like structure when using ammonium sulfate (APS) contrasted with the particle-like form observed with ferric chloride (FeCl3). These results showed that if the oxidant changed, the bi-polaron and polaron ratios in C-H deformation were unrelated to PPy morphology. However, this work showed a consistent relationship between SDS use, the bipolaron and polaron ratios in the C-H deformation, and the conductivity properties. Moreover, the natural positive charge of PPy and negatively charged SDS molecules may lead to an electrostatic interaction between PPy and SDS. This work assumes that this interaction might cause the transformation of polaron to bipolaron in the C-H deformation region, resulting in improved conductivity of PPy. This work offers more support for the future investigation of PPy characteristics.