Flammability was evaluated and the results showed the values of critical flux at extinguishment (CFE) as 49.5kW/㎡ on average, total heat release (Qt) as 0.21MJ on average, and peak heat release rate (Qp) as 0.66kW on average, which satisfied all of the thresholds presented by the IMO. Therefore, flame-retardant plywood, of which the flame-retardant performance was evaluated, was determined to be an applicable finishing material that satisfies fire safety standards.

As smoke toxicity is unregulated outside of the mass transport industry, there is no set methodology for assessing smoke toxicity of construction products, like OSB, on a large-scale. This research aims to assess the novel design of a modified ISO 9705 room corner test designed for smoke toxicity quantification. Three tests conditions will be assessed to determine if restriction of ventilation is enough to force a fire to transition to under-ventilated flaming, or if the fuel loading is much more important in affecting the fire severity and fire condition. The research found that fuel loading and test geometry has more significant impact on the fire condition than restricting the ventilation. While imposing restrictions on the test rooms ventilation did increase the equivalence ratio, it was not sufficient enough to force the transition into under-ventilated flaming. The addition of a door to the test room did not force the fire to transition to under-ventilated flaming. When doubling the fuel loading, there was sufficient fuel for the fire to transition to under-ventilated flaming. This research has provided the experimental methodologies to assess smoke toxicity at a range of ventilation conditions on a large-scale.

A novel type of phosphazene containing additive that act both as catalyst and as flame retardant for benzoxazine binders is presented in this study. The synthesis of a derivative of hexachlorocyclotriphosphazene (HCP) and meta-toluidine was carried out in the medium of the latter, which made it possible to achieve complete substitution of chlorine atoms in the initial HCP. Thermal and flammability characteristics of modified compositions are revealed. The modifier catalyzes the process of curing and shifts the beginning of reaction from 222.0 C for pure benzoxazine to 205.9 C for composition with 10 phr of modifier. The additive decreases the glass transition temperature of compositions. Achievement of the highest category of flame resistance (V-0 in accordance with UL-94) is ensured both by increasing the content of phenyl residues in the composition and by the synergistic effect of phosphorus and nitrogen. Brief research of the curing kinetics disclosed the complex nature of the reaction. An accurate two-step model is obtained using extended Prout-Tompkins equation for both steps.