High density polyethylene (HDPE) and poly(lactic) acid (PLA) blends with different ratios of both polymers, namely 30:70, 50:50 and 70:30, were produced. Polyethylene grafted maleic anhydride and a random copolymer of ethylene and glycidyl methacrylate, were also proposed as compatibilizers to modify HDPE-PLA optimal blends and were added in the amounts of 1, 3 and 5 wt.%. Blends properties have been evaluated through different aspects by performing tensile tests, scanning electron microscopy to analyze blend morphology and interfaces, and thermomechanical analysis through differential scanning calorimetry, thermo-gravimetric analyses and infrared spectroscopy. The second blend, the one with equal amounts of HDPE and PLA seems to represent a good balance between high amount of bio-derived charge and acceptable mechanical properties. This suggests a good potential of these blends, which would be a good starting point for the production of composites with lingo-cellulosic fillers.

An immiscible blend of poly(hydroxy ether of bisphenol-A) (phenoxy) and poly(1,4-butylene terephthalate) (PBT) with phase separation was observed in as-blended samples. However, compatibilization of the phenoxy/PBT blends can be promoted through chemical exchange reactions of phenoxy with PBT upon annealing. In contrast to the as-blended samples, the annealed phenoxy/PBT blends had a homogeneous phase with a single T_g that could be enhanced by annealing at 260°C. Infrared (IR) spectroscopy demonstrated that phase homogenization could be promoted by annealing of the phenoxy/PBT blend, where alcoholytic exchange occurred between the dangling hydroxyl group in phenoxy and the carbonyl group in PBT in the heated blends. The alcoholysis reaction changes the aromatic linkages to aliphatic linkages in carbonyl groups, which initially led to the formation of a graft copolymer of phenoxy and PBT with an aliphatic/aliphatic carbonyl link. The progressive alcoholysis reaction resulted in the transformation of the initial homopolymers into block copolymers and finally into random copolymers, which promoted phase compatibilization in blends of phenoxy with PBT. Due to the fact that the amount of copolymers increased upon annealing, crystallization of PBT was inhibited by alcoholytic exchange in the blends.